CN105253981A - 一种矿物质滤芯及其制造方法 - Google Patents
一种矿物质滤芯及其制造方法 Download PDFInfo
- Publication number
- CN105253981A CN105253981A CN201510737119.1A CN201510737119A CN105253981A CN 105253981 A CN105253981 A CN 105253981A CN 201510737119 A CN201510737119 A CN 201510737119A CN 105253981 A CN105253981 A CN 105253981A
- Authority
- CN
- China
- Prior art keywords
- filter core
- powder
- mineral
- mineral substance
- kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种矿物质滤芯及其制造方法，滤芯包括以下质量百分比的组分：木鱼石粉20%～35%，麦饭石粉20%～35%，活化硒矿粉10%～20%，硅藻泥10%～20%，水5%～10%。矿物质滤芯的制造方法，包括以下步骤：步骤一，按照上述比例将木鱼石粉、麦饭石粉、活化硒矿粉、硅藻泥和水置入容器内搅拌混合均匀，获得混合物；步骤二，将步骤一获得的混合物倒入模具内；步骤三，将装有混合物的模具放入窑炉中进行烧结；步骤四，将模具从窑炉中取出冷却至常温，模具内经过烧结的混合物即为矿物质滤芯。本发明不仅过滤效果好，而且过滤后的水中会含有对人体和动植物有益的矿物质和微量元素，保健养生效果优秀。
Description
技术领域
本发明涉及一种矿物质滤芯及其制造方法。
背景技术
目前，全国各地水域都有不同程度的污染，如重金属污染、农药残留物污染等，给广大人民群众的生存安全和健康造成了极大的威胁，而现今市场上的净水器滤芯功能单一，保健养生效果不太明显。
因此，如何解决这一技术问题成为了该领域技术人员亟待解决的问题。
发明内容
本发明的目的就是提供一种矿物质滤芯及其制造方法，能产生人体或动植物所必需的矿物质和微量元素，解决了现有技术功能单一、保健养生效果不太明显的技术问题。
本发明的目的通过下述技术方案来实现：
一种矿物质滤芯，其特征在于，包括以下质量百分比的组分：木鱼石粉20%～35%，麦饭石粉20%～35%，活化硒矿粉10%～20%，硅藻泥10%～20%，水5%～10%。
作为优选，木鱼石原石球磨为800目的木鱼石粉。
作为优选，麦饭石原石球磨为400目的麦饭石粉。
作为优选，所述活化硒矿粉为2000目以上。
上述任一项矿物质滤芯的制造方法，其特征在于，包括以下步骤：
步骤一，按照上述比例将木鱼石粉、麦饭石粉、活化硒矿粉、硅藻泥和水置入容器内搅拌混合均匀，获得混合物；
步骤二，将步骤一获得的混合物倒入模具内；
步骤三，将装有混合物的模具放入窑炉中进行烧结；
步骤四，将模具从窑炉中取出冷却至常温，模具内经过烧结的混合物即为矿物质滤芯。
进一步，所述步骤三中，窑炉的窑温控制在1200℃～1300℃。
进一步，所述步骤三中，装有混合物的模具需要在窑炉中烧结2～3小时。
进一步，所述步骤四中，模具从窑炉中取出采用自然冷却的方式，冷却至常温。
木鱼石粉作为此滤芯的部分原料，经实践证明：木鱼石含有偏硅酸、锶、钼、锂、锌、硒等十多种对人体有益的微量元素，有很强的保健和美容作用。经木鱼石浸泡的水在五分钟后，就可以达到优质矿泉水的标准、甘甜爽口。
麦饭石粉作为此滤芯的部分原料，经实践证明：麦饭石自然溶出性优越。经水质溶出对人体和生物有用的全部常量元素K、Ca、Mg及Si、Zn、Gn、Cu、Mo、Se、Mn、Sr、Ni、V、Li、Co、Cr、I、Ge、Ti等微量元素，能溶出的元素达40余种之多，麦饭石在水中还能溶出人体所必需的氨基酸。其中偏硅酸、Sr、Zn、k、Mo、Ge等溶出较好，可使一般的饮用水成为优质矿泉水，而有害重金属元素Pb、Cd、Hg、As等溶出极少，溶出量均大大低于联合国卫生组织规定的饮用水标准。
麦饭石吸附性强。麦饭石中含铝硅酸盐类（长石），对色素和细菌有吸附能力，对有害的金属元素也有很好的吸附作用。麦饭石能吸附水中游离子，吸附PH达98%以上，吸附Cd、Hg、As量分别为80%、50%、60%。因此麦饭石处理后的水又称活性水，对细菌吸附作用极佳，能吸附大肠杆菌、葡萄球菌达96%以上。
麦饭石具有双向调节饮用水PH值的缓冲能力，可将较大范围的弱酸、弱碱介质PH值5-11调节到PH值为7.2-8.7左右的弱碱性水。
麦饭石具有一定的生物活性，无毒性反应，长期饮用麦饭石处理的水可以调节和促进生物的新陈代谢及内分泌活动，洗涤细胞排除人体内的毒素和有害物质，具有利尿、健胃、保肝、舒筋活血，增强心肺活力、杀菌消炎之功效，可用来预防和辅助治疗高血压、血管硬化等。
另外麦饭石对清除各种化学毒素特别有效并可释放对人体有益的红外线。麦饭石经水释放的各种微量元素对酶和荷尔蒙的合成起到重要作用。麦饭石释放多种矿物质的原因是它由25000多种成分组成，并且1克麦饭石的表面积达到几百平方米，是同量活性碳的20000倍。故作为该矿物质滤芯原料的首选。
活化硒矿粉作为此滤芯的部分原料，经实践证明：硒是动物和人体中一些抗氧化酶和硒-P蛋白的重要组成部分，在体内起着平衡氧化还原氛围的作用。研究证明具有提高动物免疫力的作用，是人体必需的微量元素。目前，中国营养学会推荐的成人摄入量为每日50-250微克，而我国2/3地区硒摄入量远低于推荐值。科学证实，正是由于硒的高抗氧化作用，适量补充能起到防止器官老化和病变，延缓衰老、增强免疫、抵御疾病。实践证明有机硒能清除体内自由基、排除体内毒素、抗氧化、能有效的抑制过氧化脂质的产生、防止血凝块、清除胆固醇、增强人体免疫功能；防止糖尿病，硒是构成谷胱甘肽过氧化物酶的活性成分，它能防止胰岛β细胞氧化破坏，使其功能正常，促进糖份代谢，降低血糖和尿糖，改善糖尿病患者的症状；防止白内障，视网膜由于接触电脑辐射等较多，易爱损伤，硒可保护视网膜，增强玻璃体的光洁度，提高视力，有防止白内障的作用；防止心脑血管疾病，硒是维持心脏正常功能的重要元素，对心脏肌体有保护和修复的作用，人体血硒水平的降低，会导致体内清除自由基的功能减退，造成有害物质沉积增多，血压升高、血管壁变厚、血管弹性降低、血流速度变慢、送氧功能大降，从而诱发心脑血管疾病的发病率升高。硒与金属的结合力很强能抵抗镉对肾，生殖腺和中枢神经的毒害。硒与体内的汞、铅、锡、铊等重金属结合，形成金属蛋白的复合而解毒、排毒。科学证明：补硒可使肝癌发病率下降35%，使有肝癌家史者发病率下降50%。因此活化硒粉作为此滤芯的重要成分，其作用无疑是优良的。
硅藻泥作为此滤芯的部分原料，经实践证明：硅藻是一种亿万年形成的海洋和湖泊中藻类，它创造了70%地球生命赖以生存的氧气，是地球生命的摇篮，它主要成分为蛋白石，富含多种人体有益矿物质，质地轻软。电子显微镜显示其粒子表面具有无数微小的孔穴，孔隙率达90%，表面积高达65㎡/g，与木鱼石、麦饭石、活化硒粉充分搅拌烧制成的滤芯其通水率得到极大提高。
与现有技术相比，本发明的有益效果在于：不仅过滤效果好，而且过滤后的水中会含有对人体和动植物有益的矿物质和微量元素，保健养生效果优秀，能完全满足人们日益增长的使用要求。而且将酒经过该滤芯过滤后还可以增加酒的纯度和口感。
附图说明
图1是本发明矿物质滤芯的结构示意图；
图2是矿物质滤芯安装外壳后的结构示意图。
具体实施方式
下面结合具体实施例和附图对本发明作进一步的说明。
一种矿物质滤芯，包括以下质量百分比的组分：木鱼石粉20%～35%，麦饭石粉20%～35%，活化硒矿粉10%～20%，硅藻泥10%～20%，水5%～10%。
木鱼石原石球磨为800目的木鱼石粉。麦饭石原石球磨为400目的麦饭石粉。所述活化硒矿粉为2000目以上。
实施例一
一种矿物质滤芯，包括以下质量百分比的组分：木鱼石粉20%，麦饭石粉30%，活化硒矿粉20%，硅藻泥20%，水10%。
上述矿物质滤芯的制造方法，包括以下步骤：
步骤一，按照上述比例将木鱼石粉、麦饭石粉、活化硒矿粉、硅藻泥和水置入容器内搅拌混合均匀，获得混合物；
步骤二，将步骤一获得的混合物倒入模具内；
步骤三，将装有混合物的模具放入窑炉中烧结2～3小时，窑炉的窑温控制在1200℃～1300℃；
步骤四，将模具从窑炉中取出自然冷却至常温，模具内经过烧结的混合物即为矿物质滤芯。
本发明的矿物质滤芯可以根据需要选用不同的模具制造成任意形状，如长方体、正方体、锥形、圆柱体等等。如图1和图2所示，本实施例优选制造成圆柱体，该圆柱体具有内腔1，并开设有与内腔1相通的出水口2。将该矿物质滤芯3安装在外壳4内，底端安装密封盖5，密封盖5上连接管道6与矿物质滤芯3的出水口2连通，矿物质滤芯3外壁与外壳4内壁之间有进水腔8，外壳4上开设进水口7，水从进水口7进入进水腔内8，水从矿物质滤芯3外壁渗入内腔1中，最后从出水口2流出。由于水经过了矿物质滤芯3的过滤，过滤了水中的有害杂质，并且矿物质滤芯3中含有的矿物质和有益微量元素会有部分溶入水中，因此经过该矿物质滤芯过滤的水会有保健养生效果。
该矿物质滤芯长期使用后，其外表面会被杂质堵塞，该堵塞层打磨掉后，矿物质滤芯还可以继续使用。
实施例二
一种矿物质滤芯，包括以下质量百分比的组分：木鱼石粉25%，麦饭石粉25%，活化硒矿粉20%，硅藻泥20%，水10%。
上述矿物质滤芯的制造方法与实施例一相同。
实施例三
一种矿物质滤芯，包括以下质量百分比的组分：木鱼石粉35%，麦饭石粉20%，活化硒矿粉20%，硅藻泥20%，水5%。
上述矿物质滤芯的制造方法与实施例一相同。
实施例四
一种矿物质滤芯，包括以下质量百分比的组分：木鱼石粉35%，麦饭石粉35%，活化硒矿粉15%，硅藻泥10%，水5%。
上述矿物质滤芯的制造方法与实施例一相同。
实施例五
一种矿物质滤芯，包括以下质量百分比的组分：木鱼石粉35%，麦饭石粉35%，活化硒矿粉10%，硅藻泥15%，水5%。
上述矿物质滤芯的制造方法与实施例一相同。
实施例六
一种矿物质滤芯，包括以下质量百分比的组分：木鱼石粉22%，麦饭石粉28%，活化硒矿粉20%，硅藻泥20%，水10%。
上述矿物质滤芯的制造方法与实施例一相同。
实施例七
一种矿物质滤芯，包括以下质量百分比的组分：木鱼石粉28%，麦饭石粉22%，活化硒矿粉20%，硅藻泥20%，水10%。
上述矿物质滤芯的制造方法与实施例一相同。
实施例八
一种矿物质滤芯，包括以下质量百分比的组分：木鱼石粉35%，麦饭石粉35%，活化硒矿粉10%，硅藻泥12%，水8%。
上述矿物质滤芯的制造方法与实施例一相同。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种矿物质滤芯，其特征在于，包括以下质量百分比的组分：木鱼石粉20%～35%，麦饭石粉20%～35%，活化硒矿粉10%～20%，硅藻泥10%～20%，水5%～10%。
2.根据权利要求1所述的矿物质滤芯，其特征在于：木鱼石原石球磨为800目的木鱼石粉。
3.根据权利要求1所述的矿物质滤芯，其特征在于：麦饭石原石球磨为400目的麦饭石粉。
4.根据权利要求1所述的矿物质滤芯，其特征在于：所述活化硒矿粉为2000目以上。
5.根据权利要求1-4任一项所述的矿物质滤芯的制造方法，其特征在于，包括以下步骤：
步骤一，按照上述比例将木鱼石粉、麦饭石粉、活化硒矿粉、硅藻泥和水置入容器内搅拌混合均匀，获得混合物；
步骤二，将步骤一获得的混合物倒入模具内；
步骤三，将装有混合物的模具放入窑炉中进行烧结；
步骤四，将模具从窑炉中取出冷却至常温，模具内经过烧结的混合物即为矿物质滤芯。
6.根据权利要求5所述的制造方法，其特征在于：所述步骤三中，窑炉的窑温控制在1200℃～1300℃。
7.根据权利要求5所述的制造方法，其特征在于：所述步骤三中，装有混合物的模具需要在窑炉中烧结2～3小时。
8.根据权利要求5所述的制造方法，其特征在于：所述步骤四中，模具从窑炉中取出采用自然冷却的方式，冷却至常温。