CN105239130A - High-antiseptic aluminum alloy anode oxide film non-nickel sealant and preparation method thereof - Google Patents

High-antiseptic aluminum alloy anode oxide film non-nickel sealant and preparation method thereof Download PDF

Info

Publication number
CN105239130A
CN105239130A CN201510614645.9A CN201510614645A CN105239130A CN 105239130 A CN105239130 A CN 105239130A CN 201510614645 A CN201510614645 A CN 201510614645A CN 105239130 A CN105239130 A CN 105239130A
Authority
CN
China
Prior art keywords
oxide film
parts
sealant
tetrabutyl titanate
nickel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510614645.9A
Other languages
Chinese (zh)
Inventor
吴传兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maanshan Jiechuang Plastic Science & Technology Co Ltd
Original Assignee
Maanshan Jiechuang Plastic Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Maanshan Jiechuang Plastic Science & Technology Co Ltd filed Critical Maanshan Jiechuang Plastic Science & Technology Co Ltd
Priority to CN201510614645.9A priority Critical patent/CN105239130A/en
Publication of CN105239130A publication Critical patent/CN105239130A/en
Pending legal-status Critical Current

Abstract

The invention discloses a high-antiseptic aluminum alloy anode oxide film non-nickel sealant. The sealant is prepared from, by weight, 8-8.5 parts of magnesium acetate, 19-20 parts of triethanolamine, 3-3.2 parts of ammonium acetate, an appropriate amount of deionized water, 1.3-1.5 parts of sodium molybdate, 0.7-0.8 part of benzimidazole, 0.4-0.5 part of glucose, 0.4-0.5 part of lithium silicate, 2.6-2.8 parts of Dodecafluoroheptyl-propyl-trimethoxysilane, 1-1.2 parts of tetrabutyl titanate, 45-48 parts of ethyl alcohol, 8.6-9 parts of ammonium hydroxide and 0.3-0.4 part of fluorine-containing surfactants. The sealant is good in permeability, cohesiveness and hydrophobicity; the sealing efficiency is improved through the sodium molybdate, the benzimidazole and the glucose; a chemical oxide film is formed on the surface of a hole in a combining mode after the hole is sealed through the sealant, the oxide film is high in antiseptic capacity, and the sealant is environmentally friendly and free of pollution.

Description

A kind of high anticorrosion aluminium alloy anode oxide film is without nickel hole sealing agent and preparation method thereof
Technical field
The present invention relates to aluminium alloy anode oxide film without nickel hole sealing agent technical field, particularly relate to a kind of high anticorrosion aluminium alloy anode oxide film without nickel hole sealing agent and preparation method thereof.
Background technology
At present, Aluminum-aluminum alloy generally adopts anodized surface guard technology, certain thickness oxide film is formed on Aluminum-aluminum alloy surface, there is a large amount of micropore in the surface due to oxide film, must suitable sealing treatment be carried out, common enclosure method mainly contain boiling water (or steam) close, nickel salt close, macromolecule resin close.Boiling water (or steam) enclosure method energy consumption is high and cannot meet the requirement compared with high anti-corrosion; Conventional nickel salt encapsulant is containing Ni 2+, F -to human body and the effect of environmental toxic evil, its stripping quantity is subject to the strict restriction of the regulations such as European Union 94/27/EEC nickel instruction; The molecular volume of macromolecule resin is too large, cannot diffuse into pore interior and realize good closed performance.Therefore, the demand energy-efficient, the green aluminum anodized film sealing technique of asepsis environment-protecting is developed is urgent, wherein, the hole sealing agent being main component with an alkali metal salt or alkaline earth salt has the characteristics such as resource is wide, with low cost, environmental friendliness, is a kind of novel green anode oxide film hole sealing agent.The U.S., Wuhan Inst. of Material Protection of China have successively carried out the technical study of alkaline earth salt sealing of hole." 6063 aluminium alloy anode oxide films are without the optimization of nickel hole-sealing technology " literary composition take magnesium acetate as hole sealing agent main component, orthogonal experiment is adopted to have studied the impact of hole-sealing technology parameter on sealing quality, obtain the Optimization Technology without nickel hole sealing technology, and the technique applied research of anti-ion interference has been carried out to this technique.Result shows, can the realizing in 80 DEG C antianode oxide film under temperature without nickel hole-sealing technology and carry out sealing pores of optimization, and sealing quality is good, anti-Na +interference performance is given prominence to, and achieves sealing of hole process without Ni 2+deng environomental pollution source, environmental protection, and the reduction of sealing of hole temperature is conducive to reducing energy consumption, and energy-saving benefit is remarkable.But this technique still has weak point, anti-SO 4 2-disturb poor, and perviousness is bad, the space closure of the oxide film bottom of bottom is bad, also there is the problem that the performances such as germ resistance, solidity to corrosion, thermotolerance, salt fog resistance, wear resistance, oxidation-resistance are not good, and the toughness of encapsulant, hardness, shrinking percentage etc. also can affect closure, need to improve.
Summary of the invention
The object of the invention is exactly the defect in order to make up prior art, provides a kind of high anticorrosion aluminium alloy anode oxide film without nickel hole sealing agent and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of high anticorrosion aluminium alloy anode oxide film, without nickel hole sealing agent, is made up of the raw material of following weight part: magnesium acetate 8-8.5, trolamine 19-20, ammonium acetate 3-3.2, deionized water are appropriate, Sodium orthomolybdate 1.3-1.5, benzimidazolyl 0.7-0.8, glucose 0.4-0.5, lithium silicate 0.4-0.5, ten difluoro heptyl propyl trimethoxy silicane 2.6-2.8, tetrabutyl titanate 1-1.2, ethanol 45-48, ammoniacal liquor 8.6-9, fluorochemical surfactant 0.3-0.4.
Described heat-treated under medium temperature aluminium alloy anode oxide film, without the preparation method of nickel hole sealing agent, comprises the following steps:
(1) by tetrabutyl titanate, ethanol mixing, stirring obtains tetrabutyl titanate ethanolic soln, by lithium silicate, ten difluoro heptyl propyl trimethoxy silicanes, fluorochemical surfactant mixing, the water adding 5-6 weight part stirs, obtain solution, to instill in tetrabutyl titanate ethanolic soln under described solution stirring, 1.5-1.8h is stirred under 250-300r/min condition, obtain mixture, then ammoniacal liquor is slowly dripped in people's said mixture, at 30-35 DEG C, obtain emulsion after stirring reaction 3-3.5h;
(2) mixing solutions is prepared, magnesium acetate 8g/L, trolamine 19g/L, ammonium acetate 3g/L;
(3) emulsion (1) step obtained adds in the solution that (2) step obtains by 1.6-1.8g/L, then adds other remaining component, mixes, and regulates pH=5, is heated to 60-65 DEG C, aluminium section bar is flooded 18-22min, to obtain final product.
Advantage of the present invention is: the present invention uses tetrabutyl titanate to form nano titanium oxide, employ lithium silicate, ten difluoro heptyl propyl trimethoxy silicanes, fluorochemical surfactant simultaneously, through reaction, the perviousness of hole sealing agent, cohesiveness, hydrophobicity can be improved, improve sealing of hole effect, improve the oxidation-resistance of oxide film and anti-SO simultaneously 4 2-interference; By using Sodium orthomolybdate, benzimidazolyl, glucose, improve sealing of hole efficiency, and forming chemical oxide film, the resistance to corrosion of oxide film in its surface bonding after hole sealing agent sealing pores, and hole sealing agent is environment friendly and pollution-free.
Embodiment
A kind of high anticorrosion aluminium alloy anode oxide film, without nickel hole sealing agent, is made up of the raw material of following weight part (kilogram): magnesium acetate 8, trolamine 19, ammonium acetate 3, deionized water are appropriate, Sodium orthomolybdate 1.3, benzimidazolyl 0.7, glucose 0.4, lithium silicate 0.4, ten difluoro heptyl propyl trimethoxy silicane 2.6, tetrabutyl titanate 1, ethanol 45, ammoniacal liquor 8.6, fluorochemical surfactant 0.3.
Described heat-treated under medium temperature aluminium alloy anode oxide film, without the preparation method of nickel hole sealing agent, comprises the following steps:
(1) by tetrabutyl titanate, ethanol mixing, stirring obtains tetrabutyl titanate ethanolic soln, by lithium silicate, ten difluoro heptyl propyl trimethoxy silicanes, fluorochemical surfactant mixing, the water adding 5 weight parts stirs, and obtains solution, will instill in tetrabutyl titanate ethanolic soln under described solution stirring, 1.5h is stirred under 250r/min condition, obtain mixture, then ammoniacal liquor is slowly dripped in people's said mixture, at 30 DEG C, obtain emulsion after stirring reaction 3h;
(2) mixing solutions is prepared, magnesium acetate 8g/L, trolamine 19g/L, ammonium acetate 3g/L;
(3) emulsion (1) step obtained adds in the solution that (2) step obtains by 1.6g/L, then adds other remaining component, mixes, and regulates pH=5, is heated to 60 DEG C, aluminium section bar is flooded 18min, to obtain final product.
Experimental data:
Detect according to GB/T8753.2-2005, sealing of hole weightlessness is 12.6mg/dm 2; According to GB/T8753.4-2005, dyeing grade is 0, and anti-dye high adsorption capacity, illustrates that seal quality is qualified.
Studied by anti-ion interference, even if when result display Na+ content increases to 400mg/L, sealing of hole weightlessness is also only 16.5mg/dm 2, be less than 30mg/dm 2, sealing quality is good, and anti-Na+ interference performance is given prominence to; Work as SO 4 2-content when being 500mg/L, sealing of hole weightlessness is 17.2mg/dm 2, be less than 30mg/dm 2, sealing of hole effect is better, anti-SO 4 2-disturb.
By carrying out electron-microscope scanning to oxide film surface, see that a large amount of micropores on the surface of oxide film are nearly all closed, pore space structure is few, and sealing of hole is comparatively even.

Claims (2)

1. high anticorrosion aluminium alloy anode oxide film is without a nickel hole sealing agent, it is characterized in that being made up of the raw material of following weight part: magnesium acetate 8-8.5, trolamine 19-20, ammonium acetate 3-3.2, deionized water are appropriate, Sodium orthomolybdate 1.3-1.5, benzimidazolyl 0.7-0.8, glucose 0.4-0.5, lithium silicate 0.4-0.5, ten difluoro heptyl propyl trimethoxy silicane 2.6-2.8, tetrabutyl titanate 1-1.2, ethanol 45-48, ammoniacal liquor 8.6-9, fluorochemical surfactant 0.3-0.4.
2. heat-treated under medium temperature aluminium alloy anode oxide film according to claim 1 is without the preparation method of nickel hole sealing agent, it is characterized in that comprising the following steps:
(1) by tetrabutyl titanate, ethanol mixing, stirring obtains tetrabutyl titanate ethanolic soln, by lithium silicate, ten difluoro heptyl propyl trimethoxy silicanes, fluorochemical surfactant mixing, the water adding 5-6 weight part stirs, obtain solution, to instill in tetrabutyl titanate ethanolic soln under described solution stirring, 1.5-1.8h is stirred under 250-300r/min condition, obtain mixture, then ammoniacal liquor is slowly dripped in people's said mixture, at 30-35 DEG C, obtain emulsion after stirring reaction 3-3.5h;
(2) mixing solutions is prepared, magnesium acetate 8g/L, trolamine 19g/L, ammonium acetate 3g/L;
(3) emulsion (1) step obtained adds in the solution that (2) step obtains by 1.6-1.8g/L, then adds other remaining component, mixes, and regulates pH=5, is heated to 60-65 DEG C, aluminium section bar is flooded 18-22min, to obtain final product.
CN201510614645.9A 2015-09-24 2015-09-24 High-antiseptic aluminum alloy anode oxide film non-nickel sealant and preparation method thereof Pending CN105239130A (en)