CN105238266B - The lasting brightener of nano self-cleaning type tire and its manufacturing method - Google Patents
The lasting brightener of nano self-cleaning type tire and its manufacturing method Download PDFInfo
- Publication number
- CN105238266B CN105238266B CN201510692027.6A CN201510692027A CN105238266B CN 105238266 B CN105238266 B CN 105238266B CN 201510692027 A CN201510692027 A CN 201510692027A CN 105238266 B CN105238266 B CN 105238266B
- Authority
- CN
- China
- Prior art keywords
- lasting
- brightener
- cleaning type
- nano self
- type tire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of lasting brighteners of nano self-cleaning type tire.The lasting brightener of nano self-cleaning type tire is made of following raw materials, including：Mother liquor, diluent, environmentally friendly grade recessiveness reflective powder, antistatic agent, plant fragrance original essential oil, the invention also discloses a kind of manufacturing methods of the lasting brightener of nano self-cleaning type tire.The lasting brightener of nano self-cleaning type tire provided by the invention and its manufacturing method use condition require it is low, it is easy to operate, only need a gently spray, love wheel tire can be kept clean for a long time shiny black, recessive reflectorized material keeps tyre surface still shiny black daytime simultaneously, reflective after night irradiation, improves traffic safety.
Description
Technical field
The present invention relates to car detailing care products technical field more particularly to a kind of nano self-cleaning type tire are persistently bright
Agent and its manufacturing method.
Background technology
With universal and pursuit of the people to car civilization of family's sedan-chair, automobile tire long-term " dirty, native, mud, water stain dirt
Trace " phenomenon is at the common worry of car owners, and dirty tire and clean shiny car body are extremely uncoordinated, just as very straight Western-style clothes
The leather shoes that a pair of is stained with mud and dirt are mixed, demeanour halves.
People use the existing lasting brightener of nano self-cleaning type tire for a long time, can only keep one day even 8
To 9 hours, these of short duration brighteners made of the water mixings such as liquid wax and malt sugar keep car owners extremely disappointed.
Invention content
In order to solve the above technical problem, the present invention provides a kind of lasting brighteners of nano self-cleaning type tire.
The lasting brightener of nano self-cleaning type tire provided by the invention is made of following raw materials, including：Mother liquor, dilution
Agent, antistatic agent, plant fragrance original essential oil.
In a kind of preferred embodiment of the lasting brightener of nano self-cleaning type tire of the present invention, the nano self-cleaning type tire
Lasting brightener further includes environmentally friendly grade recessiveness reflective powder.
In a kind of preferred embodiment of the lasting brightener of nano self-cleaning type tire of the present invention, the nano self-cleaning type tire
Lasting brightener is made using following weight than raw material, including：The lasting brightener of nano self-cleaning type tire is using following heavy
Amount is made than raw material, including：Mother liquor 65-75%, diluent 35-25% amount to 100%, miscible fluid are made, then with described miscible
Environmentally friendly grade recessiveness reflective powder 10-15%, antistatic agent 5-15%, plant fragrance original essential oil 0.1-1% is added in liquid total amount.
In a kind of preferred embodiment of the lasting brightener of nano self-cleaning type tire of the present invention, the mother liquor includes：Hydroxyl
Containing hydrogen silicone oil, nanoscale SiO2, dispersant, silane/siloxane concentrate, propylene glycol, atoleine, isopropanol, fluorine element surface
Activating agent.
In a kind of preferred embodiment of the lasting brightener of nano self-cleaning type tire of the present invention, the mother liquor is using following heavy
Amount is made than raw material：Hydroxyl hydrogen silicone oil 35-45%, nanoscale SiO220-30%, dispersant 5-15%, silane/siloxane are dense
Contracting object 1-3%, propylene glycol 1-5%, atoleine 1-5%, isopropanol 1-5%, fluorosurfactant 5-10%.
In a kind of preferred embodiment of the lasting brightener of nano self-cleaning type tire of the present invention, the nanoscale SiO2Grain
Diameter is 5-15nm.
In a kind of preferred embodiment of the lasting brightener of nano self-cleaning type tire of the present invention, the nano self-cleaning type tire
Lasting brightener is sprayed on surface of tyre, is applied to antifouling, the long-acting bright and reflecting at night of tire.
In a kind of preferred embodiment of the lasting brightener of nano self-cleaning type tire of the present invention, the nano self-cleaning type tire
Lasting brightener antifouling, anti-shadow scratch applied to Automobile paint surface hydrophobicity, glass, reflective mirror are hydrophobic antifog, electric wire anti-caking
Ice, clothing, tarpaulin bilge water resisting, anti-snow frost, building glass curtain wall waterproof is self-cleaning, stainless steel product, glassware anti-fingerprint.
The invention also discloses a kind of manufacturing methods of the lasting brightener of nano self-cleaning type tire, include the following steps：
Container is provided, container is persistently stirred, while pressing component by hydroxyl hydrogen silicone oil, nanoscale SiO2, dispersant, silicon
Alkane/silicon
Oxygen alkane concentrate, propylene glycol, atoleine, isopropanol, fluorosurfactant sequentially add container；
After the completion of raw material is added, to raw material high speed shear 30 minutes in container, mother liquor is made；
In mother liquor be added absolute ethyl alcohol dilution after formed miscible fluid and by component sequentially add environmentally friendly grade recessiveness reflective powder,
Antistatic agent, plant fragrance original essential oil；
After the completion of raw material is added, stirring at low speed is continued to container；The lasting brightener of nano self-cleaning type tire is made.
Further include spraying in a kind of preferred embodiment of the lasting brightener manufacturing method of nano self-cleaning type tire of the present invention
Tank, the aerosol can include receiving space, and the lasting brightener of nano self-cleaning type tire is contained in the receiving space.
Compared to the prior art, the lasting brightener of nano self-cleaning type tire provided by the invention and its manufacturing method have such as
Lower advantageous effect：
1, all-transparent imitates the formation of lotus leaf nano coating, and surface of tyre is made to have significant super-hydrophobic self-cleaning, anti-pollution water, resist
Mud, oil rub resistance, antistatic adsorption function；
2, surface of tyre finish, brightness are greatly improved, and the duration is 15-30 times of regular-type foam brightener,
Make surface of tyre that factory state be presented always, be always on Chang Xin, solves second day tire after people's carwash just " return soil, return dirty "
It is worried；
3, so that tire is had reflecting at night function initiatively, improve driving at night safety；
4, nano surface micro-structure forms flexible rubber protective layer, and uvioresistant prevents tyre surface aging, cracking, extends
Life of Tyre；
5, dust is brushed off substantially totally just without special scrub tire using preceding, directly sprayed.Its is easy to operate, makes
It is required with condition low.
6, pH value：It is neutral.Formula materials select property mild safe, beneficial, colourless, tasteless, stingless to rubber protection
Swash property, non-corrosive, it is skin friendly, do not hinder tire, does not hinder vehicle paint and other objects；Non- explosives, flash-point is high, storage and transportation peace
Entirely.Though alcohol diluent therein is solvent, but not rubber for tire is damaged, and in spraying can flash evapn without
Tyre surface can be stayed in.
Specific implementation mode
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only it is a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
All other embodiment that art personnel are obtained without making creative work belongs to the model that the present invention protects
It encloses.
The lasting brightener of nano self-cleaning type tire provided by the invention is made of following raw materials, including：Mother liquor, dilution
Agent, environmentally friendly grade recessiveness reflective powder, antistatic agent, plant fragrance original essential oil.
The lasting brightener of nano self-cleaning type tire is made using following weight than raw material, including：The Nano self-cleaning
The lasting brightener of type tire is made using following weight than raw material, including：Mother liquor 65-75%, diluent 35-25% amount to
100%, miscible fluid is made, then environmentally friendly grade recessiveness reflective powder 10-15%, antistatic agent 5- are added with the miscible fluid total amount
15%, plant fragrance original essential oil 0.1-1%.
The mother liquor includes：Hydroxyl hydrogen silicone oil, nanoscale SiO2, dispersant, silane/siloxane concentrate, propylene glycol,
Atoleine, isopropanol, fluorosurfactant.
The mother liquor is made using following weight than raw material：Hydroxyl hydrogen silicone oil 35-45%, nanoscale SiO220-30%,
Dispersant 5-15%, silane/siloxane concentrate 1-3%, propylene glycol 1-5%, atoleine 1-5%, isopropanol 1-5%, fluorine
Plain surfactant 5-10%.
Preferably, the nanoscale SiO2Grain size be 5-15nm.
The lasting brightener of nano self-cleaning type tire is sprayed on surface of tyre, is applied to antifouling, the long-acting light of tire
And reflecting at night.
When not adding the environmentally friendly grade recessiveness reflective powder, the lasting brightener of nano self-cleaning type tire can be applied to
Automobile paint surface hydrophobicity is antifouling, anti-shadow scratch, and glass, reflective mirror are hydrophobic antifog, and electric wire is anti-freeze, clothing, tarpaulin are antifouling
Water, anti-snow frost, building glass curtain wall waterproof is self-cleaning, stainless steel product, glassware anti-fingerprint.
The invention also discloses a kind of manufacturing methods of the lasting brightener of nano self-cleaning type tire, include the following steps：
Container is provided, container is persistently stirred, while pressing component by hydroxyl hydrogen silicone oil, nanoscale SiO2, dispersant, silicon
Alkane/siloxanes concentrate, propylene glycol, atoleine, isopropanol, fluorosurfactant sequentially add container；
After the completion of raw material is added, to raw material high speed shear 30 minutes in container, mother liquor is made；
In mother liquor be added absolute ethyl alcohol dilution after formed miscible fluid and by component sequentially add environmentally friendly grade recessiveness reflective powder,
Antistatic agent, plant fragrance original essential oil；
After the completion of raw material is added, stirring at low speed is continued to container；The lasting brightener of nano self-cleaning type tire is made.
Further include spraying in a kind of preferred embodiment of the lasting brightener manufacturing method of nano self-cleaning type tire of the present invention
Tank, the aerosol can include receiving space, and the lasting brightener of nano self-cleaning type tire is contained in the receiving space.
Further, the dilution weight ratio of the mother liquor and solvent is：Mother liquor 65~75%, solvent are 35~25%, are closed
Meter 100%, the solvent is alcohols solvent or kerosene, specifically, the solvent is absolute ethyl alcohol.
The present invention also provides three kinds of preferred embodiments of the lasting brightener manufacturing method of nano self-cleaning type tire, specifically such as
Under：
Embodiment 1：
It weighs：33.5 grams of hydroxyl hydrogen silicone oil, nanoscale SiO220 grams, 15 grams of dispersant, silane/siloxane concentrate
1.5 grams, 5 grams of propylene glycol, atoleine 5,15 grams of isopropanol, 5 grams of fluorosurfactant；Mother liquor each component stirs in order to be added
Continue high speed shear after entering to be made after 30 minutes；Mother liquor dilutes formation with absolute ethyl alcohol 35% with 65% under stirring at low speed to be mixed
Solution, while pressing miscible fluid total amount again and environmentally friendly 10 grams of grade recessiveness reflective powder is added, 5 grams of antistatic agent, plant fragrance original essential oil is fitted
Amount.
Embodiment 2：
It weighs：30 grams of hydroxyl hydrogen silicone oil, nanoscale SiO225 grams, 10 grams of dispersant, silane/siloxane concentrate 1
Gram, 7 grams of propylene glycol, atoleine 7,10 grams of isopropanol, 10 grams of fluorosurfactant；Mother liquor each component stirs addition in order
Continue high speed shear afterwards to be made after 30 minutes；Mother liquor diluted under stirring at low speed with absolute ethyl alcohol 30% with 70% formed it is miscible
Liquid, while pressing miscible fluid total amount again and environmentally friendly 20 grams of grade recessiveness reflective powder is added, 8 grams of antistatic agent, plant fragrance original essential oil is appropriate.
Embodiment 3：
It weighs：35.5 grams of hydroxyl hydrogen silicone oil, nanoscale SiO218 grams, 12.5 grams of dispersant, silane/siloxane concentration
3.5 grams of object, 4.5 grams of propylene glycol, 5.5 grams of atoleine, 13 grams of isopropanol, 7.5 grams of fluorosurfactant；Mother liquor each component is pressed
Order stirring continues high speed shear after being added and is made after 30 minutes；Mother liquor is with 75% and absolute ethyl alcohol 25% under stirring at low speed
Dilution forms miscible fluid, while pressing miscible fluid total amount again and environmentally friendly 8 grams of grade recessiveness reflective powder, 8 grams of antistatic agent, plant fragrance is added
Former essential oil is appropriate.
Compared to the prior art, the lasting brightener of nano self-cleaning type tire provided by the invention and its manufacturing method use item
Part requirement is low, easy to operate, only needs a gently spray, so that it may keep liking that wheel tire is clean for a long time shiny black, while recessive reflective material
Material keeps tyre surface still shiny black daytime, reflective after night irradiation, improves traffic safety.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (6)
1. a kind of lasting brightener of nano self-cleaning type tire, which is characterized in that the lasting brightener of nano self-cleaning type tire is adopted
It is made than raw material with following weight, including：Mother liquor 65-75%, diluent 35-25% amount to 100%, are made miscible fluid, then with
Environmentally friendly grade recessiveness reflective powder 10-15%, antistatic agent 5-15%, plant fragrance original essential oil 0.1- is added in the miscible fluid total amount
1%,
The mother liquor is made using following weight than raw material:Hydroxyl hydrogen silicone oil 35-45%, nanoscale SiO220-30%, divide
Powder 5-15%, silane/siloxane concentrate 1-3%, propylene glycol 1-5%, atoleine 1-5%, isopropanol 1-5%, fluorine element
Surfactant 5-10%.
2. the lasting brightener of nano self-cleaning type tire according to claim 1, which is characterized in that the nanoscale SiO2's
Grain size is 5-15nm.
3. the lasting brightener of nano self-cleaning type tire according to claim 1, which is characterized in that the nano self-cleaning type wheel
The lasting brightener of tire is sprayed on surface of tyre, is applied to antifouling, the long-acting bright and reflecting at night of tire.
4. the lasting brightener of nano self-cleaning type tire according to claim 1, which is characterized in that the nano self-cleaning type wheel
The lasting brightener of tire antifouling, anti-shadow scratch applied to Automobile paint surface hydrophobicity, glass, reflective mirror are hydrophobic antifog, and electric wire is anti-
Icing, clothing, tarpaulin bilge water resisting, anti-snow frost, building glass curtain wall waterproof is self-cleaning, stainless steel product, glassware anti-fingerprint.
5. a kind of manufacturing method of the lasting brightener of nano self-cleaning type tire, which is characterized in that including：Container is provided, to container
Lasting stirring, while component is pressed by hydroxyl hydrogen silicone oil, nanoscale SiO2, dispersant, silane/siloxane concentrate, propylene glycol,
Atoleine, isopropanol, fluorosurfactant sequentially add container；After the completion of raw material is added, raw material high speed in container is cut
It cuts 30 minutes, mother liquor is made；Miscible fluid is formed after absolute ethyl alcohol dilution is added in mother liquor and sequentially adds environmentally friendly grade by component
Recessive reflective powder, antistatic agent, plant fragrance original essential oil；After the completion of raw material is added, stirring at low speed is continued to container；It is made described
The lasting brightener of nano self-cleaning type tire.
6. the manufacturing method of the lasting brightener of nano self-cleaning type tire according to claim 5, which is characterized in that further include
Aerosol can, the aerosol can include receiving space, and the lasting brightener of nano self-cleaning type tire is contained in the receiving space
It is interior.