CN105235960A - Label plate of rotary labeling machine and vulcanization technology between glue panel and arc panel - Google Patents
Label plate of rotary labeling machine and vulcanization technology between glue panel and arc panel Download PDFInfo
- Publication number
- CN105235960A CN105235960A CN201510681198.9A CN201510681198A CN105235960A CN 105235960 A CN105235960 A CN 105235960A CN 201510681198 A CN201510681198 A CN 201510681198A CN 105235960 A CN105235960 A CN 105235960A
- Authority
- CN
- China
- Prior art keywords
- reinforced rib
- label plate
- reinforcing ribs
- panel
- arc panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a label plate of a rotary labeling machine. The label plate comprises an arc panel and a shaft sleeve. Reinforcing ribs are arranged on the inner side of the arc panel and connected with the shaft sleeve. The reinforcing ribs comprise the two umbrella-shaped reinforcing ribs which are parallel to the axial direction of the arc panel and are symmetrically arranged. The middles of the umbrella-shaped reinforcing ribs are provided with transverse reinforcing ribs perpendicular to the umbrella-shaped reinforcing ribs. The middle of the arc panel is provided with a middle reinforcing rib parallel to the axial direction of the arc panel. The structural strength of the whole label plate of the rotary labeling machine is supported through the two umbrella-shaped reinforcing ribs which penetrate the edge of the arc face of the label plate; two longitudinal reinforcing ribs are overall arranged on the arc panel; the condition that the supporting arc faces of umbrella-shaped structures are overall stressed evenly is the key that the label plate does not deform when the edge of the label plate is stressed, stress is most stable through three-point supporting, and the weight of the stainless steel label plate is greatly reduced through the structure; in addition, after a glue face of the label plate reaches the service life, the glue face can be reused through repeated rubber face vulcanization, and the characteristics of energy conservation and environment protection are achieved.
Description
Technical field
The present invention relates to the target on a kind of labelling machine, particularly relate to a kind of mark version of swinging labelling machine.
Background technology
Target is the key that its operation precision of labelling machine core component directly has influence on labeling quality, target sound construction, remove material internal stress whether completely, whether whether withstanding corrosion aspect can give prominence to, with at the bottom of the bond strength height of rubber, all directly affect in poster process reliable and stable.In actual poster process, target is less by external force, but the internal stress of target may be target distortion.
Conventional aluminum material target, stability of material is poor, the target body of heat treatment mode to machine-shaping can not be adopted to carry out Re-stress process, simple natural ageing can not be removed again internal stress completely and cause aluminum target in use to there will be plate face depression, causes the millimeter paper pasted to play the defects such as bulging, wrinkling when being used in labelling machine.
Tradition corrosion-resistant steel target complex structure is heavy, and easy glue face cracking in the course of processing.
Summary of the invention
The problem to be solved in the present invention is to provide a kind of corrosion-resistant steel target of not easily depressed deformation, by arranging more reasonably reinforced rib, solving the distortion of target, completely eliminated target internal stress by rational heat treatment.
For solving the problems of the technologies described above, swinging billboard of brander of the present invention, comprise curved panel and axle sleeve, arrange reinforced rib inside described curved panel to be connected with axle sleeve, curved panel arranged outside glue panel, described reinforced rib comprises the umbrella shape reinforced rib axially parallel with curved panel, described umbrella shape reinforced rib is symmetrical arranged two panels, the cross reinforcing vertical with umbrella shape reinforced rib is set in the middle part of described umbrella shape reinforced rib, the middle reinforced rib axially parallel with curved panel is set at the middle part of curved panel.
The length of described middle reinforced rib is equal with the length of axle sleeve, and the length of described umbrella shape reinforced rib is greater than the length of axle sleeve.
The sizing material of glue panel is grouped into by the one-tenth of following weight ratio example, nitrile rubber 55%, carbon black 40%, rubber chemicals 5%.
The invention still further relates to the sulphurization technique of the glue panel manufactured on above-mentioned target, treatment process comprises the following steps,
(1) surface treatment of corrosion-resistant steel target blank: first pickling is carried out to corrosion-resistant steel target blank before corrosion-resistant steel target face and rubber face bond, then sand-blast finish is carried out, requirement reaches smart rugosity at RZ60um ~ 80um, the all pressurized air of inject process is through apparatus for supercooling and oil water separator process, to ensure compressed-air actuated drying, without oil, compressed air pressure is 0.7MPa, nozzle keeps the distance of 100mm ~ 300mm to base metal surface, and the angle of injection direction and base metal surface normal controls in 15 ~ 30 scopes;
(2) press row part by weight and get sizing material, government rubber 55%, carbon black 40%, rubber chemicals 5%, the rubber semi-finished product of homogeneous after heat refining is good, will be made in 10 minutes;
(3) control of sulfuration process: be coated with one deck silicone oil on target surface, the consumption of silicone oil is that the blank of every sq cm uses 0.2 gram, then carries out sulfuration;
(4) within every five minutes, check pressure, make pressure at 20MPa ± 100kpa
(5) curing temperature 160 ± 10 DEG C, the control of time is at 10 ~ 15min.
By this sulfuration process, rust steel target face and rubber face bond more firm.
Swinging billboard of brander overall construction intensity of the present invention adopts umbrella shape reinforced rib to support, article two, umbrella shape reinforced rib runs through target cambered surface edge, article two, waling integral layout is in cambered plate, umbrella character form structure support the overall uniform force of cambered surface be target edge stressed time indeformable key, supported at three point is stressed the most stable.Cross side reinforced rib supports firm lateral forces, can effectively alleviate target thickness and weight, compared by stress analysis and meet designing requirement, thus ensure that target is in use indeformable for a long time, the service efficiency improving target decreases target and changes number of times, rational structure is convenient to batch manufacturing, and in target manufacturing process, mold releasability is easy.
Accompanying drawing explanation
Below in conjunction with the drawings and specific embodiments, the present invention is further detailed explanation.
Fig. 1 is the front view of swinging billboard of brander of the present invention.
Fig. 2 is the cutaway view along A-A line in Fig. 1.
Fig. 3 is the cutaway view along B-B line in Fig. 1.
Detailed description of the invention
As shown in Figure 1 to Figure 3, swinging billboard of brander of the present invention, comprise curved panel 1 and axle sleeve 2, outer 1 side of curved panel arranges glue panel 6, arrange reinforced rib inside curved panel 1 to be connected with axle sleeve 2, reinforced rib comprises the umbrella shape reinforced rib 3 axially parallel with curved panel 1, umbrella shape reinforced rib 2 is symmetrical arranged two panels, the cross reinforcing 4 vertical with umbrella shape reinforced rib 3 is set in the middle part of umbrella shape reinforced rib 3, the middle reinforced rib 5 axially parallel with curved panel 1 is set at the middle part of curved panel 1.The length of middle reinforced rib 5 is equal with the length of axle sleeve 2, and the length of umbrella shape reinforced rib 3 is greater than the length of axle sleeve 2.
Target adopts Novel steel and special process process, improves surface corrosion resistance, not oxidizable.
The invention still further relates to one and can to ensure between glue panel and curved panel firmly sulphurization technique, treatment process comprises the following steps,
(1) surface treatment of corrosion-resistant steel target blank: first pickling is carried out to corrosion-resistant steel target blank before corrosion-resistant steel target face and rubber face bond, then sand-blast finish is carried out, requirement reaches smart rugosity at RZ60um ~ 80um, the all pressurized air of inject process is through apparatus for supercooling and oil water separator process, to ensure compressed-air actuated drying, without oil, compressed air pressure is 0.7MPa, nozzle keeps the distance of 100mm ~ 300mm to base metal surface, and the angle of injection direction and base metal surface normal controls in 15 ~ 30 scopes
(2) sizing material proportionally nitrile rubber 55%, carbon black 40%, compounding ingredient 5% ~ 10% heat refining good after to make the rubber semi-finished product of homogeneous in 10 minutes.Bloom phenomenon may be there is more than 10 minutes materials.It is without air and moisture that the heat of sizing material practices index of quality.Participate in except wanting abundant heat refining for returning charge, returning charge ratio can not there will be material folding delamination splitting phenomenon more than 15%.
(3) control of sulfuration process: be coated with one deck silicone oil on target surface, the consumption of silicone oil is that the blank of every sq cm uses 0.2 gram, then carries out sulfuration.
(4) within every five minutes, pressure is checked, make pressure can not fluctuate at 20MPa ± 100kpa pressure otherwise sizing material internal pressure in curing process can be made to be greater than sulfide stress, therefore sulfide stress is crossed conference and is made sizing material heavy compression, when molding pressure sharply decline cause sulfuration volume increase other parts due to mould restriction can not increase can people cause cracking phenomena for causing stress, if correct way be make sulfide stress be reduced to 20Mpa proper level can not after the excessive too small dropping force of pressure overlap increase after this reduce feeding quantity to increase spew groove, must cool such benefit again under die pressure for ensureing not come unglued is offset cooling meat phenomenon.
(5) curing temperature 160 ± 10 DEG C, the control of time at 10 ~ 15min, according to target size, manual control.If after the outside sulfuration of goods because of sizing material conduct heat slow inside be also in the unvulcanized state time can not in 10 ~ 15min, volatile matter when step-down molding in inner vulcanization reaction can overflow rapidly, reduction with temperature produces to shrink and just produces unbalanced stress, grope the long-time sulfuration of low temperature will to be adopted to send out for thick sizing material according to repetition test and elevated temperature cure simultaneously checkout facility pressure stage by stage, control the die-filling time, joint close will be strictly on guard against and only overflow in sizing material gap, must be noted that time of cure simultaneously, time of cure is short all can be caused curing process to produce volatile matter can not to get rid of in time and cause bubble phenomenon.Correct way delays according to exhaust gas conditions, mould slowly to be closed at all.
(6) direct spraying way is cancelled in the control of mold release, and mold release inequality can be caused to produce because of trickling phenomenon, uses to be coated on bond site and to be coated with that not affect stripping result be good less, avoids too much mold release and can invade in sizing material.
Claims (4)
1. a swinging billboard of brander, comprise curved panel and axle sleeve, arrange reinforced rib inside described curved panel to be connected with axle sleeve, curved panel arranged outside glue panel, it is characterized in that: described reinforced rib comprises the umbrella shape reinforced rib axially parallel with curved panel, described umbrella shape reinforced rib is symmetrical arranged two panels, arranges the cross reinforcing vertical with umbrella shape reinforced rib in the middle part of described umbrella shape reinforced rib, arranges the middle reinforced rib axially parallel with curved panel at the middle part of curved panel.
2. according to swinging billboard of brander according to claim 1, it is characterized in that: the length of described middle reinforced rib is equal with the length of axle sleeve, the length of described umbrella shape reinforced rib is greater than the length of axle sleeve.
3. according to swinging billboard of brander according to claim 2, it is characterized in that: the sizing material of glue panel is grouped into by the one-tenth of following weight ratio example, nitrile rubber 55%, carbon black 40%, rubber chemicals 5%.
4. a sulphurization technique for the glue panel on the target of manufacturing claims 1-3, is characterized in that: treatment process comprises the following steps,
(1) surface treatment of corrosion-resistant steel target blank: first pickling is carried out to corrosion-resistant steel target blank before corrosion-resistant steel target face and rubber face bond, then sand-blast finish is carried out, requirement reaches smart rugosity at RZ60um ~ 80um, the all pressurized air of inject process is through apparatus for supercooling and oil water separator process, to ensure compressed-air actuated drying, without oil, compressed air pressure is 0.7MPa, nozzle keeps the distance of 100mm ~ 300mm to base metal surface, and the angle of injection direction and base metal surface normal controls in 15 ~ 30 scopes;
(2) press row part by weight and get sizing material, government rubber 55%, carbon black 40%, rubber chemicals 5%, the rubber semi-finished product of homogeneous after heat refining is good, will be made in 10 minutes;
(3) control of sulfuration process: be coated with one deck silicone oil on target surface, the consumption of silicone oil is that the blank of every sq cm uses 0.2 gram, then carries out sulfuration;
(4) within every five minutes, check pressure, make pressure at 20MPa ± 100kpa
(5) curing temperature 160 ± 10 DEG C, the control of time is at 10 ~ 15min.