CN105231586A - Health care insole and preparation method thereof - Google Patents
Health care insole and preparation method thereof Download PDFInfo
- Publication number
- CN105231586A CN105231586A CN201510501377.XA CN201510501377A CN105231586A CN 105231586 A CN105231586 A CN 105231586A CN 201510501377 A CN201510501377 A CN 201510501377A CN 105231586 A CN105231586 A CN 105231586A
- Authority
- CN
- China
- Prior art keywords
- layer
- preparation
- medicine layer
- medicine
- massage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a health care insole which has massaging and health care effects on feet. The health care insole comprises a bottom layer, a medicine layer and a massaging layer, wherein the bottom layer comprises the following raw materials in percentage by weight: 50%-70% of polyester, 15%-25% of polypropylene and 15%-25% of ABS (acrylonitrile butadiene styrene) resin; the medicine layer comprises the following raw materials in percentage by weight: 70%-80% of magnetite magnetitum and 20%-30% of rosin; the massaging layer comprises the following raw materials in percentage by weight: 40%-60% of animal fibers, 18%-30% of plant fibers and 18%-30% of chemical fibers; the medicine layer is accumulated at a position with the area of 2cmx2cm and corresponds to the position of a Yongquan acupoint of an arch of a foot of a user; the thickness of the medicine layer is 3mm; and accumulated edges of the medicine layer are subjected to chamfering treatment. The insole has an excellent health care effect and is long in service life; a preparation method is simple; materials of the medicine layer, the massaging layer and the bottom layer are combined tightly; and the quality of the health care insole is stable and reliable.
Description
Technical field
The invention belongs to sock Material Field, particularly relate to a kind of health insoles and preparation method thereof.
Background technology
Foot and whole body relationship between Zang-Fu and channels-collaterals closely, bear health total weight, therefore have person foot to be the mankind's " the second hearts ".Stimulate sufficient cave can adjust Whole Body function, treatment internal organs pathology.Yongquan acupoint at the bottom of frequent massage foot has good help to treatment hypertension, insomnia, hysteria, epilepsy, infantile convulsion, nervous headache, the enuresis, the retention of urine etc.Health is the eternal themes of the mankind, has health care, the massage insole product of environment-friendly function will more and more be subject to liking of people.
Chinese patent CN201410427130.3 discloses a kind of massaging health-care insoles and preparation method thereof, belongs to health treatment field.Medicinal herb components and massage composition is filled with in described massaging health-care insoles; Described medicinal herb components comprises root of kudzu vine fiber, luffa fibers, caulis piperis futokadsurae, reticulate millettia, frutus cnidii, the coptis, golden cypress, giant knotweed, parasitic loranthus, PORIA ALBA, anise; Described massage composition comprises SEMEN COICIS, Chinese prickly ash and white pepper.Described shoe-pad is divided into 6 layers, is the anti-skidding garrha bed of material of bottom respectively, SEMEN COICIS, Chinese prickly ash, pepper massage layer, root of kudzu vine fibrage, herb powder combination layer, the anti-skidding garrha bed of material of luffa fibers layer and top layer.But massaging health-care insoles makes complicated, layering is too many, and preparation cost is too high, is not suitable for the demand of the marketization.
Chinese patent CN201510008699.0 discloses a kind of massaging health-care insoles, comprises body, and body is provided with at least three little perforation, and the heel of body is provided with large perforation, and the equal buckle of little perforation has little button pad, and large perforation buckle has large button pad; Little button pad is made up of the cotton of medicine block and parcel medicine block, and the shape of medicine block is consistent with button pad.But the medicine block of massaging health-care insoles loses effect along with the increase of service time, and wash resistant or sweat do not soak, and service life is not long, and medicine block easily comes off, quality is unstable.
Therefore a kind of long service life, reliable in quality, health insoles that preparation cost is low and preparation method thereof is badly in need of, to meet the needs of consumer.
Summary of the invention
The present invention is directed to the problems referred to above, a kind of health insoles and preparation method thereof is provided.
The present invention's adopted technical scheme that solves the problem is: a kind of health insoles, health care massage effect can be played to foot, comprise bottom, medicine layer and massage layer, shoe-pad can play good health-care effect, especially for Patients with Cardiovascular/Cerebrovascular Diseases, good health protection and therapeutic action can be played, wherein, form the raw materials by weight meter of bottom and comprise: the polyester of 50% ~ 70%, the polypropylene of 15% ~ 25% and 15% ~ 25% ABS resin; The raw materials by weight meter forming medicine layer comprises: the magnet powder of 70% ~ 80% and the rosin of 20% ~ 30%; Form the raw materials by weight meter of massage layer to comprise: the animal origin of 40% ~ 60%, 18% ~ 30% string and 18% ~ 30% chemical fibre; Medicine layer is deposited in 2cm × 2cm range position corresponding to arch of the foot Yongquan acupoint position, and drug layer thickness is 3mm, the edge chamfer process that medicine layer is piled up.Yongquan acupoint is the important acupuncture point of the kidney channel of foot-Shaoyin, carries out magnetic therapy physiotherapy to this acupuncture point, can promote the metabolism of human normal, and conditioning endocrine, sets the mind at rest, stabilizing blood pressure of calming the nerves.
Further, the particle diameter of magnet powder is 20 μm ~ 60 μm.Shoe-pad carries out magnetic therapy by magnetite to the Yongquan acupoint of human body, and effect is lasting, safety, and preparation is simple, and cost performance is high.
Further, in massage layer, animal origin is selected from milk filaments and/or silk; String is selected from bamboo fibre and/or ramee.
Further, in massage layer, chemical fibre is selected from terylene and/or acrylic fibers.
According to another object of the present invention, be the preparation method providing a kind of health insoles, preparation method is simple, medicine layer, massage layer are combined with primer closely, and steady quality is reliable, long service life, do not need to add binding agent to bond, the concrete steps of preparation method are:
Step one, prepared by medicine layer: melted by rosin, add magnet powder, stir, make the medicine layer of 2cm × 2cm × 3mm, the process of medicine layer edge chamfer;
Step 2, prepared by massage layer: animal origin, string, chemical fibre braiding after heat are pressed into grid cloth;
Step 3, prepared by bottom: polyester, polypropylene, ABS resin are melted, mix, pour in mould, underlayer thickness is 3mm;
Step 4: compressing: medicine layer is pressed onto before bottom does not solidify arch of the foot Yongquan acupoint correspondence position, compression distance is 1mm, then spreads massage layer, cooling immediately makes shoe-pad shaping.
Further, in step one, the temperature that rosin melts is 120 DEG C.
Further, in step 2, grid cloth has the grid projection of 2mm × 2mm × 0.5mm, the spacing of grid projection is 1mm.The massage layer of the shoe-pad of preparation is massaged sole by projection grid, can stimulate circulation.
Further, in step 3, melt as carrying out under vacuum.
Further, in step 4, cooling is for be placed in-30 DEG C ~-18 DEG C environment immediately immediately, to insole material hardened forming, then takes out.
Advantage of the present invention is:
1. the shoe-pad that prepared by the present invention can play good health-care effect, especially for Patients with Cardiovascular/Cerebrovascular Diseases, can play good health protection and therapeutic action;
2. the shoe-pad that prepared by the present invention carries out magnetic therapy by magnetite to the Yongquan acupoint of human body, and effect is lasting, safety, and preparation is simple, and cost performance is high;
3. the massage layer of shoe-pad that prepared by the present invention is massaged sole by projection grid, can stimulate circulation;
4. preparation method of the present invention is simple, and medicine layer, massage layer are combined with primer closely, and steady quality is reliable, long service life.
Except object described above, feature and advantage, the present invention also has other object, feature and advantage.Below with reference to detailed description of the invention, the present invention is further detailed explanation.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in detail, but the multitude of different ways that the present invention can be defined by the claims and cover is implemented.
Embodiment 1
A kind of health insoles, it consists of:
5kg polyester, 2.5kg polypropylene, 2.5kgABS resin, 8kg particle diameter are magnet powder, 2kg rosin, 0.4kg milk filaments, 0.3kg bamboo fibre, the 0.3kg terylene of 20 μm.
Embodiment 2
A kind of health insoles, it consists of:
7kg polyester, 1.5kg polypropylene, 1.5kgABS resin, 7kg particle diameter are magnet powder, 3kg rosin, 0.6kg silk, 0.18kg ramee, the 0.22kg acrylic fibers of 60 μm.
Embodiment 3
A kind of health insoles, it consists of:
6kg polyester, 2kg polypropylene, 2kgABS resin, 7.5kg particle diameter are magnet powder, 2.5kg rosin, 0.26kg milk filaments, 0.26kg silk, 0.15kg bamboo fibre, 0.15kg ramee, 0.09kg terylene, the 0.09kg acrylic fibers of 40 μm.
Embodiment 4
A kind of preparation method of health insoles is:
(1) medicine layer preparation: 2kg rosin is melted at 120 DEG C, adds the magnet powder that 8kg particle diameter is 20 μm, stir, make the medicine layer of 2cm × 2cm × 3mm, the process of medicine layer edge chamfer;
(2) massage layer preparation: the grid projection, the spacing that 0.4kg milk filaments, 0.3kg bamboo fibre, the after heat of 0.3kg terylene woven are pressed into 2mm × 2mm × 0.5mm are the grid cloth of 1mm;
(3) bottom preparation: 5kg polyester, 2.5kg polypropylene, 2.5kgABS resin are melted under vacuum, mix, pour in mould, underlayer thickness is 3mm;
(4) compressing: medicine layer is pressed onto before bottom does not solidify arch of the foot Yongquan acupoint correspondence position, compression distance is 1mm, then spreads massage layer, be placed in-30 DEG C of environment immediately, to insole material hardened forming, then take out.
Embodiment 5
A kind of preparation method of health insoles is:
(1) medicine layer preparation: 3kg rosin is melted at 120 DEG C, adds the magnet powder that 7kg particle diameter is 60 μm, stir, make the medicine layer of 2cm × 2cm × 3mm, the process of medicine layer edge chamfer;
(2) massage layer preparation: 3kg rosin, 0.6kg silk, 0.18kg ramee braiding after heat are pressed into the grid projection of 2mm × 2mm × 0.5mm, spacing is the grid cloth of 1mm;
(3) bottom preparation: 7kg polyester, 1.5kg polypropylene, 1.5kgABS resin melt under vacuum, mix, and pour in mould, and underlayer thickness is 3mm;
(4) compressing: medicine layer is pressed onto before bottom does not solidify arch of the foot Yongquan acupoint correspondence position, compression distance is 1mm, then spreads massage layer, be placed in-18 DEG C of environment immediately, to insole material hardened forming, then take out.
Embodiment 6
A kind of preparation method of health insoles is:
(1) medicine layer preparation: 2.5kg rosin is melted at 120 DEG C, adds the magnet powder that 7.5kg particle diameter is 40 μm, stir, make the medicine layer of 2cm × 2cm × 3mm, the process of medicine layer edge chamfer;
(2) massage layer preparation: 0.26kg milk filaments, 0.26kg silk, 0.15kg bamboo fibre, 0.15kg ramee, 0.09kg terylene, 0.09kg acrylic fibers braiding after heat are pressed into the grid projection of 2mm × 2mm × 0.5mm, spacing is the grid cloth of 1mm;
(3) bottom preparation: 6kg polyester, 2kg polypropylene, 2kgABS resin are melted under vacuum, mix, pour in mould, underlayer thickness is 3mm;
(4) compressing: medicine layer is pressed onto before bottom does not solidify arch of the foot Yongquan acupoint correspondence position, compression distance is 1mm, then spreads massage layer, be placed in-24 DEG C of environment immediately, to insole material hardened forming, then take out.
Experimental example
In this experimental example, test the performance of shoe-pad prepared by the present invention 4 ~ 6 by experiment.
1. test material
Experimental group: shoe-pad prepared by the embodiment of the present invention 4 ~ 6;
Control group: general wellness shoe-pad.
2. test method
Shoe-pad prepared by the test embodiment of the present invention 4 ~ 6, the indices performance of general wellness shoe-pad.
3. result of the test
Analyze after the shoe-pad embodiment of the present invention 4 ~ 6 prepared, the indices performance test of general wellness shoe-pad, experimental result is in table 1.
Table 1. test result
Experimental result shows, compared with general wellness shoe-pad, the health of shoe-pad under square one of the embodiment of the present invention 4 ~ 6 preparation, resistance to water, flexibility, the results of property of average life measure and are better than general wellness shoe-pad, and preparation method is applicable to promoting, and product quality is better.
These are only the preferred embodiments of the present invention and experimental example, be not limited to the present invention, for a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., within the protection domain that all should be included in invention.
Claims (10)
1. a health insoles, health care massage effect can be played to foot, comprise bottom, medicine layer and massage layer, it is characterized in that, the raw materials by weight meter of described bottom comprises: the polyester of 50% ~ 70%, the polypropylene of 15% ~ 25% and 15% ~ 25% ABS resin; The raw materials by weight meter forming described medicine layer comprises: the magnet powder of 70% ~ 80% and the rosin of 20% ~ 30%; The raw materials by weight meter forming described massage layer comprises: the animal origin of 40% ~ 60%, 18% ~ 30% string and 18% ~ 30% chemical fibre; Described medicine layer is deposited in 2cm × 2cm range position corresponding to arch of the foot Yongquan acupoint position, and described drug layer thickness is 3mm, the edge chamfer process that described medicine layer is piled up.
2. health insoles according to claim 1, is characterized in that, the particle diameter of described magnet powder is 20 μm ~ 60 μm.
3. health insoles according to claim 1, is characterized in that, in described massage layer, described string is selected from bamboo fibre and/or ramee.
4. health insoles according to claim 1, is characterized in that, in described massage layer, described animal origin is selected from milk filaments and/or silk; Described string is selected from bamboo fibre and/or ramee.
5. health insoles according to claim 4, is characterized in that, in described massage layer, described chemical fibre is selected from terylene and/or acrylic fibers.
6. a preparation method for health insoles as claimed in claim 1, it is characterized in that, the concrete steps of described preparation method are:
Step one, prepared by medicine layer: melted by rosin, add magnet powder, stir, make the medicine layer of 2cm × 2cm × 3mm, the process of medicine layer edge chamfer;
Step 2, prepared by massage layer: animal origin, string, chemical fibre braiding after heat are pressed into grid cloth;
Step 3, prepared by bottom: polyester, polypropylene, ABS resin are melted, mix, pour in mould, underlayer thickness is 3mm;
Step 4: compressing: medicine layer is pressed onto before bottom does not solidify arch of the foot Yongquan acupoint correspondence position, compression distance is 1mm, then spreads massage layer, cooling immediately makes shoe-pad shaping.
7. preparation method according to claim 6, is characterized in that, in step one, the temperature that described rosin melts is 120 DEG C.
8. preparation method according to claim 6, is characterized in that, in step 2, described grid cloth has the grid projection of 2mm × 2mm × 0.5mm, and the spacing of grid projection is 1mm.
9. preparation method according to claim 6, is characterized in that, in step 3, described thawing is for carry out under vacuum.
10. preparation method according to claim 6, is characterized in that, in step 4, described cooling immediately, for be placed in-30 DEG C ~-18 DEG C environment immediately, to insole material hardened forming, is then taken out.