CN105219503A - A kind of electric hammer grease composition and preparation method - Google Patents
A kind of electric hammer grease composition and preparation method Download PDFInfo
- Publication number
- CN105219503A CN105219503A CN201510696090.7A CN201510696090A CN105219503A CN 105219503 A CN105219503 A CN 105219503A CN 201510696090 A CN201510696090 A CN 201510696090A CN 105219503 A CN105219503 A CN 105219503A
- Authority
- CN
- China
- Prior art keywords
- base oil
- agent
- composition
- electric hammer
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of electric hammer grease composition and preparation method, composition comprises base oil, viscosifying agent, dispersion aids and additive; Viscosifying agent is wilkinite, and base oil is that mineral oil and synthetic oil are composite, and additive comprises: oxidation inhibitor, extreme pressure anti-wear additives, rust-preventive agent, tackifier.Base oil is joined in refining still, start and stir, keep whipped state, slowly add the wilkinite viscosifying agent of metering, it is made to mix with base oil, add dispersion aids, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, and add oxidation inhibitor, extreme pressure agent, anti-wear agent, rust-preventive agent, tackifier successively, filling after three-roller rolls oily four times.This lubricating grease is used for electric hammer, extends the life cycle of electric hammer cushion rubber, reduces the wearing and tearing of gear and cylinder, can extend the work-ing life of electric hammer simultaneously.
Description
Technical field
The invention belongs to technical field of lubricating grease, particularly relate to composition and the preparation method of electric hammer lubricating grease.
Background technology
Electric hammer is the class in electric drill, is mainly used to hole on concrete, floor, brick wall and stone material.Also have multifunctional electric hammer, be adjusted to appropriate location and mix suitable drill bit and can replace common electric drill, electric pick uses.
Electric hammer is made up of electric motor, gear reducer, crank connecting link beater mechanism, rotating drill rod mechanism, overload protection arrangement, power switch and power supply coupling unit part etc.
The rotary motion of electric motor, by gears meshing, is transferred to the rotating drill rod mechanism of eccentric link beater mechanism and straight bevel gear pair, respectively to obtain required ballistic work and torque.
Shock motion by gear driven eccentric rod gear, makes displacer reciprocating in cylinder sleeve by electric motor rotary motion, produces air cushion between displacer and impact piston simultaneously.Impact piston is hammering drilling rod afterbody with displacer synchronous reciprocating, thus makes to build work drilling holes.Due to the formation of air cushion, play again shock absorption during machine stress rebound.
Turn pricker motion by electric motor by gear driven a pair straight bevel gear, cylinder sleeve is rotated together with six square sets through overload protection arrangement, and transmitting torque is to drilling rod.Like this, define with beater mechanism the compound motion impacting and be with and rotate simultaneously.Impact is main, rotates to be auxiliary, hammers not only but also turn, thus makes to build the propelling of work brill, breaks into required circular hole gradually.
Electric hammer mechanical part fault is topmost is exactly do not impact and impact unable, and the main reason of not impacting is exactly that cushion rubber on piston and block stamp is aging, and insufficient lubrication also may impact unable, and these two kinds of fault modes are all closely related with the character of lubricating grease.
The present invention adds from base plinth oil ﹑ multiviscosisty agent ﹑ and adds agent ﹑ grease making process and physical and chemical index etc. and contrast, and the work characteristics in conjunction with electric hammer is that impact load, cylinder spot temperature are high.The present invention can reduce the senile abrasion of air cylinder of electric hammer O-ring seal, improves barrier propterty, can extend the life cycle of electric hammer simultaneously.Special product for equipment characteristic exploitation can improve lubricating efficiency, reduces unnecessary loss.
Summary of the invention
The object of this invention is to provide a kind of electric hammer grease composition and preparation method: select wilkinite as electric hammer grease thickener, by adding composite base oil, oxidation inhibitor, extreme pressure agent, anti-wear agent, rust-preventive agent, tackifier form a kind of lubricating grease with property.Lubricating grease of the present invention is widely used in Power Tools Industries, extends the life cycle of electric hammer cushion rubber, reduces the wearing and tearing of cylinder, can extend the work-ing life of electric hammer simultaneously.
Technical scheme of the present invention is as follows:
Electric hammer grease composition; Comprise base oil, viscosifying agent, dispersion aids and additive; It is characterized in that: component and weight percent are:
Base oil: 80 ~ 90%;
Viscosifying agent: 10 ~ 20%;
In viscosifying agent in lubricating grease and base oil total amount for 100%:
Outer doping: 5 ~ 10%;
Additional dispersion aids: be 20% of multiviscosisty dosage.
Described base oil mass ratio is mineral oil and the synthetic oil of 3:7 ~ 7:3, and its 40 DEG C of viscosity are 100 ~ 600mm
2/ s, pour point is-25 DEG C.
Described viscosifying agent is organobentonite.
Binder component and content as follows:
(a) oxidation inhibitor, content is 1 ~ 3%;
(b) extreme pressure anti-wear additives, total content is 1 ~ 3%;
(c) rust-preventive agent, content is 0.5 ~ 3%;
D () tackifier, content is 0.5 ~ 4%.
Described dispersion aids is methyl alcohol, ethanol, acetone, propyl carbinol, propylene carbonate or water.
Described extreme pressure anti-wear additives is the mixture of sulfide isobutene, borate, organic-molybdenum salt; Quality proportioning is 2:5:1.
Rust-preventive agent is sebacic acid disodium.
The mixture of described oxidation inhibitor to be oxidation inhibitor be N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol, quality proportioning is 1:1.
Described tackifier are polymethacrylate.
Electric hammer lubricating grease preparation method of the present invention, base oil is joined in refining still, start and stir, add viscosifying agent, it is made to mix with base oil, add dispersion aids, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, and add oxidation inhibitor, extreme pressure anti-wear additives, rust-preventive agent, tackifier successively, filling after three-roller rolls oily four times.
Effect of the present invention: lubricating grease of the present invention, owing to having selected suitable proportioning raw materials, for electric hammer, extends the life cycle of electric hammer cushion rubber, reduces the wearing and tearing of gear and cylinder, can extend the work-ing life of electric hammer simultaneously.This lubricating grease has good high temperature and abrasion resistance.The present invention gives full play to the synergistic effect of complex additive, makes it meet electric hammer gear and cylinder position lubricating requirement.
Embodiment
Effect of the present invention is further illustrated by the following examples.But should understand, the following examples do not limit the scope of the invention, any change not exceeding design of the present invention and scope, all within the scope of the present invention.
Embodiment 1:
Base oil: 80%;
Viscosifying agent: 20%;
Dispersion aids (additional): 20% of viscosifying agent content
Additive (additional): 7%;
Wherein base oil is:
Mineral oil: 24%
Synthetic oil: 56%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol: quality proportioning is 1:1, below embodiment proportioning identical in quality): 1%;
Extreme pressure anti-wear additives (sulfide isobutene, T361, molybdenum dialkyl-dithiophosphate: quality proportioning is 2:5:1, below embodiment proportioning identical in quality): 2%;
Rust-preventive agent (sebacic acid disodium), content is 2%;
Tackifier (polyphenylmethyl olefin(e) acid ester), content is 2%;
Be that the synthetic oil PAO10 of the mineral oil 150BS and 56% of 24% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 20% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids ethanol measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 1%, extreme pressure anti-wear additives (sulfide isobutene, T361, molybdenum dialkyl-dithiophosphate) mass fraction is 2%, rust-preventive agent (sebacic acid disodium) mass fraction is 2%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 2%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum A
Embodiment 2:
Base oil: 85%;
Viscosifying agent: 15%;
Dispersion aids (additional): 20% of viscosifying agent content;
Additive (additional): 9%;
Wherein base oil is:
Mineral oil: 42.5%
Synthetic oil: 42.5%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol): 1.5%;
Extreme pressure anti-wear additives (sulfide isobutene, T361, molybdenum dialkyl-dithiophosphate): 1.5%;
Rust-preventive agent (sebacic acid disodium), content is 2%;
Tackifier (polyphenylmethyl olefin(e) acid ester), content is 4%;
Be that the synthetic oil PAO40 of the mineral oil HVI750 and 42.5% of 42.5% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 15% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids propyl carbinol measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 1.5%, extreme pressure anti-wear additives (sulfide isobutene, T361, molybdenum dialkyl-dithiophosphate) mass fraction is 1.5%, rust-preventive agent (sebacic acid disodium) mass fraction is 2%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 4%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum B
Embodiment 3:
Base oil: 90%;
Viscosifying agent: 10%;
Dispersion aids (additional): 20% of viscosifying agent content;
Additive (additional): 7.5%;
Wherein base oil is:
Mineral oil: 63%
Synthetic oil: 27%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol): 1.5%;
Extreme pressure anti-wear additives (sulfide isobutene, T361, molybdenum dialkyl-dithiophosphate): 1.5%;
Rust-preventive agent (sebacic acid disodium), content is 2%;
Tackifier (polyphenylmethyl olefin(e) acid ester), content is 2.5%;
Be that the synthetic oil PAO100 of the mineral oil HVI650 and 27% of 63% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 9% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids ethanol measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 1.5%, extreme pressure anti-wear additives (sulfide isobutene, T361, molybdenum dialkyl-dithiophosphate) mass fraction is 1.5%, rust-preventive agent (sebacic acid disodium) mass fraction is 2%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 2.5%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum C
Embodiment 4:
Base oil: 90%;
Viscosifying agent: 10%;
Dispersion aids (additional): 20% of viscosifying agent content;
Additive (additional): 6.5%;
Wherein base oil is:
Mineral oil: 45%
Synthetic oil: 45%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol): 1%;
Extreme pressure anti-wear additives (sulfide isobutene, PTB, T351): 1%;
Rust-preventive agent (sebacic acid disodium): 0.5%;
Tackifier (polyphenylmethyl olefin(e) acid ester): 4%;
Be that the synthetic oil PAO6 of the mineral oil 150BS and 45% of 45% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 10% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids ethanol measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 1%, extreme pressure anti-wear additives (sulfide isobutene, PTB, T351) mass fraction is 1%, rust-preventive agent (sebacic acid disodium) mass fraction is 0.5%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 4%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum D
Embodiment 5:
Base oil: 87%;
Viscosifying agent: 13%;
Dispersion aids (additional): 20% of viscosifying agent content;
Additive (additional): 10%;
Wherein base oil is:
Mineral oil: 25%
Synthetic oil: 62%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol): 3%;
Extreme pressure anti-wear additives (sulfide isobutene, T361, molybdenum dialkyldithiocarbamacompositions): 2.5%;
Rust-preventive agent (sebacic acid disodium), content is 1.5%;
Tackifier (polyphenylmethyl olefin(e) acid ester), content is 3%;
Be that the synthetic oil PAO8 of the mineral oil 150BS and 62% of 25% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 13% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids ethanol measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 3%, extreme pressure anti-wear additives (sulfide isobutene, T361, molybdenum dialkyldithiocarbamacompositions) mass fraction is 2.5%, rust-preventive agent (sebacic acid disodium) mass fraction is 1.5%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 3%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum E.
Embodiment 6:
Base oil: 85%;
Viscosifying agent: 15%;
Dispersion aids (additional): 20% of viscosifying agent content;
Additive (additional): 6%;
Quality amounts to: 100%
Wherein base oil is:
Mineral oil: 54%
Synthetic oil: 30%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol): 1%;
Extreme pressure anti-wear additives (sulfide isobutene, T361A, molybdenum dialkyldithiocarbamacompositions): 1.5%;
Rust-preventive agent (sebacic acid disodium), content is 1.5%;
Tackifier (polyphenylmethyl olefin(e) acid ester), content is 2%;
Be that the synthetic oil PAO40 of the mineral oil HVI750 and 35% of 50% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 10% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids acetone measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 1%, extreme pressure anti-wear additives (sulfide isobutene, T361A, molybdenum dialkyldithiocarbamacompositions) mass fraction is 1.5%, rust-preventive agent (sebacic acid disodium) mass fraction is 1.5%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 2%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum F.
Embodiment 7:
Base oil: 88%;
Viscosifying agent: 12%;
Dispersion aids (additional): 20% of viscosifying agent content;
Additive (additional): 10%;
Wherein base oil is:
Mineral oil: 44%
Synthetic oil: 44%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol): 3%;
Extreme pressure anti-wear additives (sulfide isobutene, T361, MOLYVANA): 2.5%;
Rust-preventive agent (sebacic acid disodium), content is 1.5%;
Tackifier (polyphenylmethyl olefin(e) acid ester), content is 3%;
Be that the synthetic oil PAO40 of the mineral oil HVI650 and 44% of 44% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 12% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids ethanol measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 3%, extreme pressure anti-wear additives (sulfide isobutene, T361, MOLYVANA) mass fraction is 2.5%, rust-preventive agent (sebacic acid disodium) mass fraction is 2.5%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 3%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum G
Embodiment 8:
Base oil: 82%;
Viscosifying agent: 18%;
Dispersion aids (additional): 20% of viscosifying agent content;
Additive (additional): 8%;
Wherein base oil is:
Mineral oil: 35%
Synthetic oil: 47%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol): 2%;
Extreme pressure anti-wear additives (sulfide isobutene, T361, T351): 2%;
Rust-preventive agent (sebacic acid disodium), content is 2%;
Tackifier (polyphenylmethyl olefin(e) acid ester), content is 2%;
Be that the synthetic oil PAO40 of the mineral oil HVI650 and 47% of 35% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 18% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids ethanol measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 2%, extreme pressure anti-wear additives (sulfide isobutene, T361, T351) mass fraction is 2%, rust-preventive agent (sebacic acid disodium) mass fraction is 2%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 2%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum H.
Embodiment 9:
Base oil: 90%;
Viscosifying agent: 10%;
Dispersion aids (additional): 20% of viscosifying agent content;
Additive (additional): 5%;
Wherein base oil is:
Mineral oil: 25%
Synthetic oil: 65%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol): 1%;
Extreme pressure anti-wear additives (sulfide isobutene, T361, T351): 2%;
Rust-preventive agent (sebacic acid disodium), content is 1%;
Tackifier (polyphenylmethyl olefin(e) acid ester), content is 1%;
Be that the synthetic oil PAO10 of the mineral oil HVI650 and 65% of 25% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 10% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids ethanol measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 1%, extreme pressure anti-wear additives (sulfide isobutene, T361, T351) mass fraction is 2%, rust-preventive agent (sebacic acid disodium) mass fraction is 1%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 1%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum I.
Embodiment 10:
Base oil: 80%;
Viscosifying agent: 20%;
Dispersion aids (additional): 20% of viscosifying agent content;
Additive (additional): 8.3%;
Wherein base oil is:
Mineral oil: 56%
Synthetic oil: 24%
Wherein additive is:
Oxidation inhibitor (N-phenyl-a-naphthylamine, 2,6 ditertiary butyl p cresol): 1.8%;
Extreme pressure anti-wear additives (sulfide isobutene, T361, T351): 3%;
Rust-preventive agent (sebacic acid disodium), content is 3%;
Tackifier (polyphenylmethyl olefin(e) acid ester), content is 0.5%;
Be that the synthetic oil PAO100 of the mineral oil HVI500 and 24% of 56% joins in refining still by mass fraction, start and stir, keep whipped state, slowly 20% organobentonite viscosifying agent of metering is added, it is made to mix with base oil, add the dispersion aids ethanol measured, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, add oxidation inhibitor (N-phenyl-a-naphthylamine successively, 2, 6-ditertbutylparacresol) mass fraction is 1.8%, extreme pressure anti-wear additives (sulfide isobutene, T361, T351) mass fraction is 3%, rust-preventive agent (sebacic acid disodium) mass fraction is 3%, tackifier (polyphenylmethyl olefin(e) acid ester) mass fraction is 0.5%, abundant stirring is after 30 minutes, namely lubricating grease finished product is obtained after three-roller rolls oily four times.Sample number into spectrum J.
Table 1 analyzing test data contrasts
Claims (10)
1. electric hammer grease composition; Comprise base oil, viscosifying agent, dispersion aids and additive; It is characterized in that: component and weight percent are:
Base oil: 80 ~ 90%;
Viscosifying agent: 10 ~ 20%;
In viscosifying agent in lubricating grease and base oil total amount for 100%:
Outer doping: 5 ~ 10%;
Additional dispersion aids: be 20% of multiviscosisty dosage.
2. composition as claimed in claim 1, it is characterized in that base oil mass ratio is mineral oil and the synthetic oil of 3:7 ~ 7:3, its 40 DEG C of viscosity are 100 ~ 600mm
2/ s, pour point is-25 DEG C.
3. composition as claimed in claim 1, is characterized in that viscosifying agent is organobentonite.
4. composition as claimed in claim 1, it is characterized in that binder component and content as follows:
(a) oxidation inhibitor, content is 1 ~ 3%;
(b) extreme pressure anti-wear additives, total content is 1 ~ 3%;
(c) rust-preventive agent, content is 0.5 ~ 3%;
D () tackifier, content is 0.5 ~ 4%.
5. composition as claimed in claim 4, is characterized in that described dispersion aids is methyl alcohol, ethanol, acetone, propyl carbinol, propylene carbonate or water.
6. composition as claimed in claim 4, is characterized in that described extreme pressure anti-wear additives is the mixture of sulfide isobutene, borate, organic-molybdenum salt; Quality proportioning is 2:5:1.
7. composition as claimed in claim 4, is characterized in that rust-preventive agent is sebacic acid disodium.
8. composition as claimed in claim 4, is characterized in that described oxidation inhibitor be oxidation inhibitor is N-phenyl-a-naphthylamine, 2,6-
The mixture of ditertbutylparacresol, quality proportioning is 1:1.
9. composition as claimed in claim 4, it is characterized in that described tackifier are polymethacrylate, total content is 1 ~ 3%.
10. the electric hammer lubricating grease preparation method of claim 1, it is characterized in that base oil being joined in refining still, start and stir, add viscosifying agent, it is made to mix with base oil, add dispersion aids, continue stirring more than 40 minutes, until thing forms grease structure in still, Hybrid Heating is warming up to 40 ~ 70 DEG C, and keep more than 30 minutes in this temperature, and add oxidation inhibitor, extreme pressure anti-wear additives, rust-preventive agent, tackifier successively, filling after three-roller rolls oily four times.