CN105219356A - A kind of fused salt mixt heat transfer accumulation of heat working medium and application thereof - Google Patents
A kind of fused salt mixt heat transfer accumulation of heat working medium and application thereof Download PDFInfo
- Publication number
- CN105219356A CN105219356A CN201510719282.5A CN201510719282A CN105219356A CN 105219356 A CN105219356 A CN 105219356A CN 201510719282 A CN201510719282 A CN 201510719282A CN 105219356 A CN105219356 A CN 105219356A
- Authority
- CN
- China
- Prior art keywords
- fused salt
- heat transfer
- heat
- working medium
- salt mixt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to energy storage material fused salt mixt field, particularly relate to a kind of fused salt mixt heat transfer accumulation of heat working medium, it is characterized in that, by Ca (NO
3)
24H
2o, KNO
3, NaNO
3and LiCO
3composition, its quality proportioning is Ca (NO
3)
24H
2o:10-25wt%; KNO
3: 15-40wt%; NaNO
3: 25-55wt%; LiCO
3: 6-20wt%.An application for fused salt mixt heat transfer accumulation of heat working medium, is characterized in that, it can be applicable to solar energy thermal-power-generating energy storage, abandon wind abandons high temperature heat transfer accumulation of heat field in photoelectricity and " coal changes electricity " storage heating or industrial afterheat recovery storage etc.The composition cost of the preparation of fused salt mixt of the present invention is low, blending process is extremely simple, fused salt mixt of the present invention hot physical property performance is highly stable, there will not be the separation phenomenon of a certain composition in use procedure, at liquid warm area, there is good heat transfer property, and saturated vapour pressure is lower than 2 normal atmosphere.Working medium of the present invention is little to metal protection.
Description
Technical field
The invention belongs to energy storage material fused salt mixt field, particularly relate to a kind of fused salt mixt heat transfer accumulation of heat working medium and application thereof.
Background technology
The fields such as solar energy thermal-power-generating, nuclear power, middle high-temperature heat accumulation, heat supply and chemical industry, drying, process industrial all need middle high temperature heat transfer accumulation of heat working medium.One of application aspect that middle high temperature heat transfer working medium is main, namely solar energy thermal-power-generating technology is developed so far from the eighties in last century, employ and comprise water and steam, air or nitrogen, liquid metal, the multiple heat transfer accumulation of heat such as thermal oil and melting salt working medium, because melting salt has higher use temperature, high thermal stability, high specific heat capacity, high convective heat-transfer coefficient, low viscosity, low saturated vapor pressure, the advantage of low price etc. " four high three low ", be subject to domestic and international expert to pay much attention to, it is one of main application and development direction of current solar heat power generation system heat transfer accumulation of heat working medium.
One-component fused salt fusing point is too high, cannot meet the demand of heat-transfer working medium to fusing point.Several fused salt significantly can reduce the fusing point of eutectic molten salt mixture after mixing and forming eutectic fused salt mixt, and can in liquid warm area steady running, and the fused salt working medium therefore in industrial application is all this mixing eutectic fused salt.The fields such as solar energy thermal-power-generating, nuclear power, middle high-temperature heat accumulation, heat supply and chemical industry, drying, process industrial are all not quite similar to the requirement of heat transfer accumulation of heat working medium, the invention provides a kind of fused salt mixt with the diversified middle high temperature heat transfer accumulation of heat working medium demand of satisfied industry.
Summary of the invention
In order to promote the application of fused salt mixt in middle high temperature heat transfer hold over system, the invention provides a kind of fused salt mixt heat transfer accumulation of heat working medium.
In order to achieve the above object, the technical solution used in the present invention is, a kind of fused salt mixt heat transfer accumulation of heat working medium, is characterized in that, by Ca (NO
3)
24H
2o, KNO
3, NaNO
3and LiCO
3composition;
The quality proportioning of each component is: Ca (NO
3)
24H
2o:10-25wt%; KNO
3: 15-40wt%; NaNO
3: 25-55wt%; LiCO
3: 6-20wt%.
A preparation method for fused salt mixt heat transfer accumulation of heat working medium, the method step is as follows:
(1) first by Ca (NO to be mixed
3)
24H
2o, KNO
3, NaNO
3and LiCO
3material pulverizes grinding respectively, makes Solids Particle Diameter be less than 3cm, in proportion each material is put into stainless steel vessel, mix and blend;
(2) fused salt mixt is progressively heated, and do not stop to be stirred to about 120 DEG C and keep 10 minutes, by the water evaporates in fused salt mixt simultaneously;
(3) continue to be warming up to about 200 DEG C and maintain this temperature, strengthening stirring dynamics, by Ca (NO
3)
24H
2crystal water removing in O, after water vapour is got rid of completely, stop stirring after fused salt cooling, namely this mixing eutectic fused salt has newly configured.
An application for fused salt mixt heat transfer accumulation of heat working medium, is characterized in that, can be applicable to solar energy thermal-power-generating energy storage, abandons wind and abandon high temperature heat transfer accumulation of heat field in photoelectricity and " coal changes electricity " storage heating or industrial afterheat recovery storage etc.
Compared with prior art, the present invention has following beneficial effect:
1, the composition cost of the preparation of fused salt mixt of the present invention is low, blending process is extremely simple.
2, fused salt mixt of the present invention hot physical property performance is highly stable, there will not be the separation phenomenon of a certain composition in use procedure, has good heat transfer property at liquid warm area, and saturated vapour pressure is lower than 2 normal atmosphere.
3, working medium of the present invention is little to metal protection.
Embodiment
Below to the present invention is described further in conjunction with the embodiments.
Embodiment: a kind of fused salt mixt heat transfer accumulation of heat working medium, is characterized in that, by Ca (NO
3)
24H
2o, KNO
3, NaNO
3and LiCO
3composition;
The quality proportioning of each component is: Ca (NO
3)
24H
2o:10-25wt%; KNO
3: 15-40wt%; NaNO
3: 25-55wt%; LiCO
3: 6-20wt%.
A preparation method for fused salt mixt heat transfer accumulation of heat working medium, method steps is as follows:
(1) first by Ca (NO to be mixed
3)
24H
2o, KNO
3, NaNO
3and LiCO
3material pulverizes grinding respectively, makes Solids Particle Diameter be less than 3cm, in proportion each material is put into stainless steel vessel, mix and blend;
(2) fused salt mixt is progressively heated, and do not stop to be stirred to about 120 DEG C and keep 10 minutes, by the water evaporates in fused salt mixt simultaneously;
(3) continue to be warming up to about 200 DEG C and maintain this temperature, strengthening stirring dynamics, by Ca (NO
3)
24H
2crystal water removing in O, after water vapour is got rid of completely, stop stirring after fused salt cooling, namely this mixing eutectic fused salt has newly configured.
An application for fused salt mixt heat transfer accumulation of heat working medium, is characterized in that, can be applicable to solar energy thermal-power-generating energy storage, abandons wind and abandon high temperature heat transfer accumulation of heat field in photoelectricity and " coal changes electricity " storage heating or industrial afterheat recovery storage etc.
Protection scope of the present invention is not limited to the above embodiments, everyly in technical foundation of the present invention, makes equivalents, all falls within protection scope of the present invention.
Claims (2)
1. a fused salt mixt heat transfer accumulation of heat working medium, is characterized in that, by Ca (NO
3)
24H
2o, KNO
3, NaNO
3and LiCO
3composition;
The quality proportioning of each component is: Ca (NO
3)
24H
2o:10-25wt%; KNO
3: 15-40wt%; NaNO
3: 25-55wt%; LiCO
3: 6-20wt%.
2. the application of a kind of fused salt mixt heat transfer accumulation of heat working medium according to claim 1, is characterized in that, be applied to solar energy thermal-power-generating energy storage, abandons the middle high temperature heat transfer accumulation of heat field that wind abandons photoelectricity and " coal changes electricity " storage heating or industrial afterheat recovery storage.