CN105217976A - A kind of cement clinker - Google Patents
A kind of cement clinker Download PDFInfo
- Publication number
- CN105217976A CN105217976A CN201410247722.7A CN201410247722A CN105217976A CN 105217976 A CN105217976 A CN 105217976A CN 201410247722 A CN201410247722 A CN 201410247722A CN 105217976 A CN105217976 A CN 105217976A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement clinker
- wingdale
- fiber
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to cement technology field, particularly a kind of cement clinker, take Wingdale as major ingredient, comprise according to mass fraction meter: Wingdale 100-120 part, clay 25-40 part, iron powder 3-8 part, stablizer 10-15 part, fiber 15-20 part.Wherein, 100 parts, Wingdale, clay 30 parts, iron powder 5 parts, epoxy ester 10 parts, glass fibre 15 parts of effects are best.After adopting above-mentioned formula, cement clinker of the present invention well improves the stability of cement clinker entirety by stablizer; In addition, well enhanced the cohesive force of cement clinker by fiber, improve the performance of cement clinker entirety.
Description
Technical field
The present invention relates to cement technology field, particularly a kind of cement clinker.
Background technology
Cement clinker for main raw material, is mixed with raw material by suitable proportion with Wingdale and clay, ferriferous raw material, burns to part or all of melting, and the work in-process obtained through cooling.In Cement industry, the most frequently used Portland clinker main chemical compositions is calcium oxide, silicon-dioxide and a small amount of aluminum oxide and ferric oxide.Essential mineral consists of tricalcium silicate, Dicalcium Phosphate (Feed Grade), tricalcium aluminate and tetracalcium aluminoferrite.Portland clinker add proper amount of gypsum jointly levigate after, silicate cement.
Chinese invention patent CN103011633A discloses a kind of cement clinker, and described cement clinker is made up of the raw material of following weight ratio: Wingdale 75-85; Carbide slag 15-20; Yellow sand rock 5-15; Iron powder 2-5.Although this invention well make use of carbide slag, stability and cohesive force inadequate.
Summary of the invention
The technical issues that need to address of the present invention are to provide a kind of good stability, cement clinker that cohesive force is strong.
For solving above-mentioned technical problem, a kind of cement clinker of the present invention take Wingdale as major ingredient, comprises according to mass fraction meter: Wingdale 100-120 part, clay 25-40 part, iron powder 3-8 part, stablizer 10-15 part, fiber 15-20 part.
Further, described stablizer is the one in epoxy ester, N.F,USP MANNITOL, phosphorous acid ester.
Further, described fiber is the one in steel fiber, glass fibre, synthon, natural fiber.
Further, 100 parts, Wingdale, clay 30 parts, iron powder 5 parts, epoxy ester 10 parts, 15 parts, glass fibre.
After adopting above-mentioned formula, cement clinker of the present invention well improves the stability of cement clinker entirety by stablizer; In addition, well enhanced the cohesive force of cement clinker by fiber, improve the performance of cement clinker entirety.
Embodiment
Embodiment one:
110 parts, Wingdale, clay 25 parts, iron powder 3 parts, epoxy ester 15 parts, steel fiber 20 parts.
Embodiment two:
100 parts, Wingdale, clay 30 parts, iron powder 5 parts, epoxy ester 10 parts, 15 parts, glass fibre.
Embodiment three:
115 parts, Wingdale, clay 35 parts, iron powder 5 parts, phosphorous acid ester 13 parts, synthon 15 parts.
Embodiment four:
120 parts, Wingdale, clay 40 parts, iron powder 8 parts, 12 parts, N.F,USP MANNITOL, 18 parts, natural fiber.
Although the foregoing describe the specific embodiment of the present invention; but those skilled in the art are to be understood that; these only illustrate; various changes or modifications can be made to present embodiment; and not deviating from principle of the present invention and essence, protection scope of the present invention is only defined by the appended claims.
Claims (4)
1. a cement clinker, is major ingredient with Wingdale, it is characterized in that, comprise according to mass fraction meter: Wingdale 100-120 part, clay 25-40 part, iron powder 3-8 part, stablizer 10-15 part, fiber 15-20 part.
2. according to a kind of cement clinker according to claim 1, it is characterized in that: described stablizer is the one in epoxy ester, N.F,USP MANNITOL, phosphorous acid ester.
3. according to a kind of cement clinker according to claim 1, it is characterized in that: described fiber is the one in steel fiber, glass fibre, synthon, natural fiber.
4. according to a kind of cement clinker according to claim 1, it is characterized in that: 100 parts, Wingdale, clay 30 parts, iron powder 5 parts, epoxy ester 10 parts, 15 parts, glass fibre.