CN105199176A - Luggage anti-cutting rubber fabric - Google Patents
Luggage anti-cutting rubber fabric Download PDFInfo
- Publication number
- CN105199176A CN105199176A CN201510651946.9A CN201510651946A CN105199176A CN 105199176 A CN105199176 A CN 105199176A CN 201510651946 A CN201510651946 A CN 201510651946A CN 105199176 A CN105199176 A CN 105199176A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- agent
- minute
- case
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of luggage production and processing, more specifically a luggage anti-cutting rubber fabric. The luggage anti-cutting rubber fabric is characterized by comprising the following raw materials in parts by weight: 120-130 parts of modified chloroprene rubber, 5-7 parts of coumarone indene resin, 1-2 parts of sulfur, 10-15 parts of carbon black, 4-6 parts of zinc oxide, 0.5-1 part of anti-scorching agent, 10-15 parts of calcium carbonate, 2-4 parts of bone gelatin, 1-2 parts of aluminum sulfate, 2-3 parts of paraffin, 0.2-0.8 part of antioxidant, 0.5-1.5 parts of anti-aging agent, 0.3-0.6 part of plasticizer and 1-1.5 parts of rosin. A sharp object can only leave a slight scratch on the surface of the rubber fabric, but can not slit the fabric. The rubber fabric has the advantages of certain flexibility, high strength and cutting resistance.
Description
Technical field:
The present invention relates to the process for processing field of case and bag, cut rubber plus more specifically to a kind of case and bag are anti-.
Background technology:
People's out on tours or often can carry various case and bag when going on business to hold article, the variation of knapsack material, corium, plastic material, terylene, canvas, nylon, the quality case and bag trends ahead of fashions such as linen-cotton.Meanwhile, more and more bragging about the period of individual character, all kinds of style such as brief, pseudo-classic, cartoon also never ipsilateral to pander to the trend of the times the demand of personage's showing personality.The style of case and bag also by traditional business case, school bag, traveling bag to expansions such as pen bag, change bag, sachets, rubber plus can be used in case and bag material, existing rubber plus quality is soft, but existence is easily left cut by some sharp-pointed things on surface, or the problem scratched.
Summary of the invention:
Technical problem to be solved by this invention is that overcoming existing technological deficiency provides a kind of case and bag to prevent cutting rubber plus.
Technical problem to be solved by this invention adopts following technical scheme to realize:
A kind of case and bag are anti-cuts rubber plus, it is characterized in that the raw material composition comprising following weight part: 120-130 part modified chloroprene rubber, 5-7 part coumarone indene resin, 1-2 part sulphur, 10-15 part carbon black, 4-6 part zinc oxide, 0.5-1 part scorch retarder, 10-15 part calcium carbonate, 2-4 part gelatine, 1-2 part Tai-Ace S 150,2-3 part paraffin, 0.2-0.8 part oxidation inhibitor, 0.5-1.5 part anti-aging agent, 0.3-0.6 part softening agent, 1-1.5 part rosin.
Further, described modified natural rubber is made up of the raw material of following weight part: 70-80 part chloroprene rubber, 5-7 part emulsifying agent, 50-60 part hydrochloric acid, 20-26 part fortifying fibre, 3-5 part nano silica fume, 6-7 part Whitfield's ointment, 1-2 part whipping agent, 0.5-1.5 part diacetyl oxide, 0.2-0.8 part succinimide, 3-4 part ammonium phosphate, 2-3 part Magnesium Silicate q-agent, 5-6 part pitch, 1-2 part captax, 8-10 part wilkinite.
Further, described fortifying fibre comprises the composition of following weight part: 10-11 part glass fibre, 2-3 part carbon fiber, 6-8 part nylon fiber, 1-2 part fibrous magnesium silicate, 12-15 part chromium fiber.
Further, described modified natural rubber preparation method is: pulverized by chloroprene rubber, size is 100-150 order, then reactor is put into, add hydrochloric acid, emulsifying agent and Whitfield's ointment, be heated to 80-90 DEG C, use nitrogen bubble 10 minutes, then add diacetyl oxide, succinimide, ammonium phosphate and Magnesium Silicate q-agent, temperature rises to 150-160 DEG C, stirring reaction 2-3 minute, be cooled to 70-80 DEG C, then add surplus stock, reaction 3-4 hour, puts into kneader after extraction drying and mediates 10 minutes and get final product.
A kind of case and bag prevent the preparation method cutting rubber plus, it is characterized in that: modified chloroprene rubber and coumarone indene resin, carbon black mixing are put into Banbury mixer and to plasticate 2-3 minute, then calcium carbonate, zinc oxide, softening agent is added, paraffin, anti-aging agent, Tai-Ace S 150 is added again after mixing 5-6 minute, mixing 1-2 minute, leave standstill after 10 minutes, add discharging after the mixing 2-5 of remaining raw material minute, then obtained rubber plus.
The rubber plus that the present invention obtains, sharp-pointed thing can only leave slight cut on surface, and can not cut fabric, and the present invention has certain flexibility, high, the anti-advantage cut of intensity.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1: a kind of case and bag are anti-cuts rubber plus, is characterized in that the raw material composition comprising following weight part: 120 parts of modified chloroprene rubbers, 5 parts of coumarone indene resins, 1 part of sulphur, 10 parts of carbon blacks, 4 parts of zinc oxide, 0.5 part of scorch retarder, 10 parts of calcium carbonate, 2 parts of gelatine, 1 part of Tai-Ace S 150,2 parts of paraffin, 0.2 part of oxidation inhibitor, 0.5 part of anti-aging agent, 0.3 part of softening agent, 1 part of rosin.
Modified natural rubber is made up of the raw material of following weight part: 70 parts of chloroprene rubbers, 5 parts of emulsifying agents, 50 parts of hydrochloric acid, 20 parts of fortifying fibres, 3 parts of nano silica fumes, 6 parts of Whitfield's ointments, 1 part of whipping agent, 0.5 part of diacetyl oxide, 0.2 part of succinimide, 3 parts of ammonium phosphate, 2 parts of Magnesium Silicate q-agents, 5 parts of pitches, 1 part of captax, 8 parts of wilkinites.
Fortifying fibre comprises the composition of following weight part: 10 parts of glass fibre, 2 parts of carbon fibers, 6 parts of nylon fibers, 1 part of fibrous magnesium silicate, 12 parts of chromium fibers.
Embodiment 2: a kind of case and bag are anti-cuts rubber plus, is characterized in that the raw material composition comprising following weight part: 130 parts of modified chloroprene rubbers, 7 parts of coumarone indene resins, 2 parts of sulphur, 15 parts of carbon blacks, 6 parts of zinc oxide, 1 part of scorch retarder, 15 parts of calcium carbonate, 4 parts of gelatine, 2 parts of Tai-Ace S 150,3 parts of paraffin, 0.8 part of oxidation inhibitor, 1.5 parts of anti-aging agent, 0.6 part of softening agent, 1.5 parts of rosin.
Modified natural rubber is made up of the raw material of following weight part: 80 parts of chloroprene rubbers, 7 parts of emulsifying agents, 60 parts of hydrochloric acid, 26 parts of fortifying fibres, 5 parts of nano silica fumes, 7 parts of Whitfield's ointments, 2 parts of whipping agents, 1.5 parts of diacetyl oxides, 0.8 part of succinimide, 4 parts of ammonium phosphate, 3 parts of Magnesium Silicate q-agents, 6 parts of pitches, 2 parts of captaxs, 10 parts of wilkinites.
Fortifying fibre comprises the composition of following weight part: 11 parts of glass fibre, 3 parts of carbon fibers, 8 parts of nylon fibers, 2 parts of fibrous magnesium silicates, 15 parts of chromium fibers.
Modified natural rubber preparation method is: pulverized by chloroprene rubber, size is 100-150 order, then puts into reactor, add hydrochloric acid, emulsifying agent and Whitfield's ointment, be heated to 80-90 DEG C, use nitrogen bubble 10 minutes, then add diacetyl oxide, succinimide, ammonium phosphate and Magnesium Silicate q-agent, temperature rises to 150-160 DEG C, stirring reaction 2-3 minute, is cooled to 70-80 DEG C, then adds surplus stock, reaction 3-4 hour, puts into kneader after extraction drying and mediates 10 minutes and get final product.
A kind of case and bag prevent the preparation method cutting rubber plus, it is characterized in that: modified chloroprene rubber and coumarone indene resin, carbon black mixing are put into Banbury mixer and to plasticate 2-3 minute, then calcium carbonate, zinc oxide, softening agent is added, paraffin, anti-aging agent, Tai-Ace S 150 is added again after mixing 5-6 minute, mixing 1-2 minute, leave standstill after 10 minutes, add discharging after the mixing 2-5 of remaining raw material minute, then obtained rubber plus.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (5)
1. case and bag are anti-cuts a rubber plus, it is characterized in that the raw material composition comprising following weight part: 120-130 part modified chloroprene rubber, 5-7 part coumarone indene resin, 1-2 part sulphur, 10-15 part carbon black, 4-6 part zinc oxide, 0.5-1 part scorch retarder, 10-15 part calcium carbonate, 2-4 part gelatine, 1-2 part Tai-Ace S 150,2-3 part paraffin, 0.2-0.8 part oxidation inhibitor, 0.5-1.5 part anti-aging agent, 0.3-0.6 part softening agent, 1-1.5 part rosin.
2. a kind of case and bag according to claim 1 are anti-cuts rubber plus, it is characterized in that described modified natural rubber is made up of the raw material of following weight part: 70-80 part chloroprene rubber, 5-7 part emulsifying agent, 50-60 part hydrochloric acid, 20-26 part fortifying fibre, 3-5 part nano silica fume, 6-7 part Whitfield's ointment, 1-2 part whipping agent, 0.5-1.5 part diacetyl oxide, 0.2-0.8 part succinimide, 3-4 part ammonium phosphate, 2-3 part Magnesium Silicate q-agent, 5-6 part pitch, 1-2 part captax, 8-10 part wilkinite.
3. a kind of case and bag according to claim 2 are anti-cuts rubber plus, it is characterized in that described fortifying fibre comprises the composition of following weight part: 10-11 part glass fibre, 2-3 part carbon fiber, 6-8 part nylon fiber, 1-2 part fibrous magnesium silicate, 12-15 part chromium fiber.
4. a kind of case and bag according to claim 2 are anti-cuts rubber plus, it is characterized in that described modified natural rubber preparation method is: pulverized by chloroprene rubber, size is 100-150 order, then reactor is put into, add hydrochloric acid, emulsifying agent and Whitfield's ointment, be heated to 80-90 DEG C, use nitrogen bubble 10 minutes, then diacetyl oxide is added, succinimide, ammonium phosphate and Magnesium Silicate q-agent, temperature rises to 150-160 DEG C, stirring reaction 2-3 minute, be cooled to 70-80 DEG C, then surplus stock is added, reaction 3-4 hour, put into kneader after extraction drying mediate 10 minutes and get final product.
5. case and bag prevent the preparation method cutting rubber plus, it is characterized in that: modified chloroprene rubber and coumarone indene resin, carbon black mixing are put into Banbury mixer and to plasticate 2-3 minute, then calcium carbonate, zinc oxide, softening agent is added, paraffin, anti-aging agent, Tai-Ace S 150 is added again after mixing 5-6 minute, mixing 1-2 minute, leave standstill after 10 minutes, add discharging after the mixing 2-5 of remaining raw material minute, then obtained rubber plus.