CN105198061A - Flocculant composition and application thereof - Google Patents
Flocculant composition and application thereof Download PDFInfo
- Publication number
- CN105198061A CN105198061A CN201510727449.2A CN201510727449A CN105198061A CN 105198061 A CN105198061 A CN 105198061A CN 201510727449 A CN201510727449 A CN 201510727449A CN 105198061 A CN105198061 A CN 105198061A
- Authority
- CN
- China
- Prior art keywords
- weight
- agent composition
- flocculating agent
- polyacrylamide
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides flocculant composition and an application thereof. The flocculant composition, in terms of 100% by weight, mainly comprises components as follows: 12%-18% of potassium ferrate by weight, 25%-40% of poly aluminum chloride by weight, 5%-10% of polyacrylamide by weight, 25%-30% of PSAF by weight, 5%-20% of ferric chloride by weight and 1%-3% of an activating agent by weight. The flocculant composition can be used for wastewater treatment, when the dosage is 200 mg/L, the removal rate of wastewater turbidity can exceed 95%, the removal rate of total phosphorus can exceed 90%, the removal rate of the COD (chemical oxygen demand) can exceed 33%, the flocculant composition has the better flocculation effect, besides, the dosage of the polyacrylamide in the flocculant composition is small, little polyacrylamide is left in water, and the composition is safer.
Description
Technical field
The invention belongs to water-treatment technology field, relate to a kind of flocculating agent composition and application thereof.
Background technology
The coagulating treatment of water is one of key link in wastewater treatment, turbid scrubbing can be gone, reduce the pollution load of sewage subsequent disposal, and flocculation agent is the key factor determining coagulating treatment effect, all has material impact to the operation conditions of follow-up flow process, final outflow water water quality and cost etc.
Flocculation agent can be divided into inorganic flocculating agent and organic floculant two class according to its Chemical Composition, wherein, inorganic flocculating agent can be divided into low molecule flocculation agent and polymeric flocculant again, low molecule flocculation agent is as the aluminium such as Tai-Ace S 150, aluminum chloride salt system and the molysite such as iron(ic) chloride and ferric sulfate system, low molecule flocculation agent cost is lower, but, the shortcomings such as flocculation sediment speed is slow, medicine consumption is high that it has; Polymeric flocculant, as aluminum chloride hydrocarbon complex (PAC), polyaluminium sulfate, bodied ferric sulfate etc., overcome the shortcoming that the processing efficiency of low molecule flocculation agent existence is low, but its cost is higher, and treatment effect is poor when low-temperature and low turbidity.Organic floculant is generally high molecular polymer, as polyamine flocculation agent, Quaternary Ammonium Starch base flocculation agent and polyacrylamide flocculant etc., wherein, polyacrylamide has the advantages such as the pH value that consumption is few, primary water mass-energy power is strong, flocculation rate soon, is not subject to water affects, the sludge quantity of generation is few and is applied widely, but polyacrylamide has strong neurotoxicity and certain carinogenicity, large weight polyacrylamide remains for the treatment of producing polymer during waste water, destroy aqueous bio chain, and then have influence on human health.
CN1393410A discloses a kind of Inorganic whisker type flocculation agent and production method thereof, this kind of flocculation agent comprises the polymkeric substance of Dicyanodiamide and formaldehyde, Polyaluminium Sulfate Chloride and/or Polyaluminium Sulfate Chloride calcium, prepare by the following method: first by aluminium salt hydrolysis, then in described hydrolysate, add calcium salt and carry out polyreaction, add again after Dicyanodiamide and formaldehyde carry out polycondensation and obtain described Inorganic whisker type flocculation agent, it is low that this flocculation agent has medicine consumption, the advantages such as good waste water treatment effect, but this flocculation agent take formaldehyde as raw material, production process easily produces environmental pollution, also containing a large amount of free formaldehyde in the flocculation agent obtained, be detrimental to health.
CN102295335A openly knows clearly a kind of flocculating agent composition, comprising: the ferrate of 1wt% ~ 10wt%; The poly-aluminum calcium chloride of 20wt% ~ 50wt%; The aluminum contained compound of 10wt% ~ 40wt% and/or calcium containing compound; The iron(ic) chloride of 5wt% ~ 25wt% and the polyacrylamide of 1wt% ~ 20wt%.When flocculating agent composition usage quantity provided by the invention is 0.6g/L, be that in the sanitary sewage of 300mg/L ~ 400mg/L, turbidity removal rate can reach more than 93% to COD, the clearance that total tp removal rate can reach more than 90%, COD can reach more than 31%.But the consumption of flocculating agent composition is higher when disposing of sewage in the present invention.
Therefore, it is few that this area expects to develop a kind of consumption, and can play the safer flocculation agent of better flocculating effect.
Summary of the invention
For the deficiencies in the prior art, the object of the present invention is to provide a kind of flocculating agent composition and application thereof.
For reaching this object, the present invention by the following technical solutions:
The invention provides a kind of flocculating agent composition, described flocculating agent composition mainly comprise in the weight of flocculating agent composition be 100% following component:
In flocculating agent composition of the present invention, the content of potassium ferrate is 12 ~ 18 % by weight, such as 12 % by weight, 13 % by weight, 14 % by weight, 15 % by weight, 16 % by weight, 17 % by weight or 18 % by weight.
In flocculating agent composition of the present invention, the content of polymerize aluminum chloride is 25 ~ 40 % by weight, such as 25 % by weight, 26 % by weight, 27 % by weight, 28 % by weight, 29 % by weight, 30 % by weight, 31 % by weight, 32 % by weight, 33 % by weight, 34 % by weight, 35 % by weight, 36 % by weight, 37 % by weight, 38 % by weight, 39 % by weight or 40 % by weight.
In flocculating agent composition of the present invention, described polyacrylamide is cationic-type polyacrylamide and/or anion-polyacrylamide, the content of described polyacrylamide is 5 ~ 10 % by weight, such as 5 % by weight, 5.3 % by weight, 5.5 % by weight, 5.8 % by weight, 6 % by weight, 6.3 % by weight, 6.5 % by weight, 6.8 % by weight, 7 % by weight, 7.3 % by weight, 7.5 % by weight, 7.8 % by weight, 8 % by weight, 8.3 % by weight, 8.5 % by weight, 8.8 % by weight, 9 % by weight, 9.3 % by weight, 9.5 % by weight, 9.8 % by weight or 10 % by weight.
In flocculating agent composition of the present invention, the content of polymeric aluminium ferrum silicate is 25 ~ 30 % by weight, such as 25 % by weight, 25.5 % by weight, 26 % by weight, 26.5 % by weight, 27 % by weight, 27.5 % by weight, 28 % by weight, 28.5 % by weight, 29 % by weight, 29.5 % by weight or 30 % by weight.
In flocculating agent composition of the present invention, the content of iron(ic) chloride is 5 ~ 20 % by weight, such as 5 % by weight, 6 % by weight, 7 % by weight, 8 % by weight, 9 % by weight, 10 % by weight, 11 % by weight, 12 % by weight, 13 % by weight, 14 % by weight, 15 % by weight, 16 % by weight, 17 % by weight, 18 % by weight, 19 % by weight or 20 % by weight.
In flocculating agent composition of the present invention, the content of activator is 1 ~ 3 % by weight, such as 1 % by weight, 1.2 % by weight, 1.4 % by weight, 1.6 % by weight, 1.8 % by weight, 2 % by weight, 2.2 % by weight, 2.4 % by weight, 2.6 % by weight, 2.8 % by weight or 3 % by weight.
In flocculating agent composition of the present invention, activator is expanded perlite micro mist and/or flyash micro mist, the weight ratio scope of wherein said expanded perlite micro mist and flyash micro mist is 3:2 ~ 5:3, such as 3:2,3:2.5,3:3,4:1,4:2,4:3,5:1,5:2 or 5:3.
On the other hand, the invention provides flocculating agent composition described herein application in the treatment of waste water, it can be used for the process of trade effluent or sanitary sewage, in the treatment of waste water, the dosage of described flocculating agent composition adds 200 ~ 400mg for often liter of waste water, and such as often liter of waste water adds flocculating agent composition 200mg, 210mg, 220mg, 230mg, 240mg, 250mg, 260mg, 270mg, 280mg, 290mg, 300mg, 310mg, 320mg, 330mg, 340mg, 350mg, 360mg, 370mg, 380mg, 390mg or 400mg.
Flocculating agent composition of the present invention has the advantage of inorganic flocculating agent and organic floculant concurrently, wherein polymerize aluminum chloride, polyacrylamide and polymeric aluminium ferrum silicate have been the main components of throwing out, iron(ic) chloride and potassium ferrate play the effect of auxiliary flocculation by forming the effects such as colloidal precipitation, strengthen the flocculating effect of flocculating agent composition.With the addition of potassium ferrate in flocculating agent composition provided by the invention, flocculating effect can not only be promoted, reduce flocculation cost, and make flocculation agent have sterilization, except algae function, algae and water can be suppressed to break out.With the addition of a small amount of polyacrylamide in flocculating agent composition of the present invention, while improving flocculating effect, decrease polyacrylamide remaining in water outlet, decrease the toxic action to aqueous bio chain.In addition, activator is with the addition of in flocculating agent composition provided by the invention, this activator not only improves the flocculation flocculating effect of principal constituent and the nucleation performance of gel effectively, be conducive to reducing charging capacity, promote water treatment capacity, the proportion of flocculation jello can be regulated simultaneously, increase the deposition capability of flocculation agent gel, thus improve water treatment efficiency, reduce secondary pollution, improve the quality of process water.
Relative to prior art, the present invention has following beneficial effect:
Flocculating agent composition provided by the invention can be used for wastewater treatment, when the dosage of flocculating agent composition provided by the invention is 200mg/L, can more than 95% be reached to turbidity of wastewater clearance, total tp removal rate can reach more than 90%, the clearance of COD can reach more than 33%, has good flocculating effect, and the consumption of polyacrylamide is few in this flocculating agent composition, residual few, safer in water.
Embodiment
Technical scheme of the present invention is further illustrated below by embodiment.Those skilled in the art should understand, described embodiment is only help to understand the present invention, should not be considered as concrete restriction of the present invention.
Embodiment 1
In the present embodiment, flocculating agent composition comprises following component:
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Embodiment 2
In the present embodiment, flocculating agent composition comprises following component:
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Embodiment 3
In the present embodiment, flocculating agent composition comprises following component:
Wherein in activator, the weight ratio of expanded perlite micro mist and flyash micro mist is 4:3;
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Embodiment 4
In the present embodiment, flocculating agent composition comprises following component:
Wherein in activator, the weight ratio of expanded perlite micro mist and flyash micro mist is 3:2;
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Embodiment 5
In the present embodiment, flocculating agent composition comprises following component:
Wherein in activator, the weight ratio of expanded perlite micro mist and flyash micro mist is 5:3;
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Comparative example 1
In this comparative example, flocculating agent composition comprises following component:
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Comparative example 2
In this comparative example, flocculating agent composition comprises following component:
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Comparative example 3
In this comparative example, flocculating agent composition comprises following component:
Wherein in activator, the weight ratio of expanded perlite micro mist and flyash micro mist is 4:3;
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Comparative example 4
In this comparative example, flocculating agent composition comprises following component:
Wherein in activator, the weight ratio of expanded perlite micro mist and flyash micro mist is 3:2;
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Comparative example 5
In this comparative example, flocculating agent composition comprises following component:
Wherein in activator, the weight ratio of expanded perlite micro mist and flyash micro mist is 5:3;
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
Comparative example 6
In this comparative example, flocculating agent composition comprises following component:
Wherein in activator, the weight ratio of expanded perlite micro mist and flyash micro mist is 5:3;
Mix after said components is weighed by described weight ratio and obtain flocculating agent composition.
By flocculating agent composition prepared by embodiment of the present invention 1-5 and comparative example 1-6, be applied to wastewater treatment, dosage is decided to be 200mg/L, and investigate turbidity of wastewater clearance, total tp removal rate and COD clearance, specific experiment result is as shown in table 1.
Table 1 turbidity of wastewater clearance, total tp removal rate and COD clearance
As shown in Table 1, flocculating agent composition prepared by embodiment of the present invention 1-5 to turbidity of wastewater clearance, total tp removal rate and COD clearance all apparently higher than flocculating agent composition prepared by comparative example 1-6, this is because in comparative example 1-6 some component proportion beyond limited range of the present invention, such as, in comparative example 1 potassium ferrate content higher than 18%; In comparative example 2, potassium ferrate content is lower than 12%, and polymer aluminium silicate iron level is higher than 30%; In comparative example 3, polymerize aluminum chloride content is higher than 40%, and polymer aluminium silicate iron level is lower than 25%; In comparative example 4, polymerize aluminum chloride content is lower than 25%, and polyacrylamide amine content is higher than 10%; In comparative example 5, polyacrylamide amine content is lower than 5%, and iron(ic) chloride content is higher than 20%; In comparative example 6, iron(ic) chloride content is lower than 5%, and activator levels is lower than 1%.The flocculating effect of the flocculating agent composition that above comparative example is made is significantly lower.This also illustrates that in flocculating agent composition of the present invention, between each component, organic cooperation just can play good flocculating effect.
Therefore, the present invention utilizes the potassium ferrate of 12 ~ 18 % by weight, the polymerize aluminum chloride of 25 ~ 40 % by weight, the polyacrylamide of 5 ~ 10 % by weight, the polymeric aluminium ferrum silicate of 25 ~ 30 % by weight, the flocculating agent composition that the activator of iron(ic) chloride and 1 ~ 3 % by weight of 5 ~ 20 % by weight is prepared from, can be used for processing waste water, when dosage is 200mg/L, can more than 95% be reached to turbidity of wastewater clearance, total tp removal rate can reach more than 90%, the clearance of COD can reach more than 33%, namely good flocculating effect can be obtained, and the consumption of polyacrylamide is few in this flocculating agent composition, residual few in water, safer.
Applicant states, the present invention illustrates flocculating agent composition of the present invention by above-described embodiment, but the present invention is not limited to above-described embodiment, does not namely mean that the present invention must rely on above-described embodiment and could implement.Person of ordinary skill in the field should understand, any improvement in the present invention, to equivalence replacement and the interpolation of ancillary component, the concrete way choice etc. of each raw material of product of the present invention, all drops within protection scope of the present invention and open scope.
Claims (5)
1. a flocculating agent composition, is characterized in that, described flocculating agent composition mainly comprise in the weight of flocculating agent composition be 100% following component:
2. flocculating agent composition according to claim 1, is characterized in that, described polyacrylamide is cationic-type polyacrylamide and/or anion-polyacrylamide.
3. flocculating agent composition according to claim 1 and 2, is characterized in that, described activator is for being expanded perlite micro mist and/or flyash micro mist.
4. the flocculating agent composition according to any one of claim 1-3, is characterized in that, the weight ratio scope of described expanded perlite micro mist and flyash micro mist is 3:2-5:3.
5. the application in the treatment of waste water of the flocculating agent composition according to any one of claim 1-4.