CN105176221A - Environmentally-friendly multi-effect nanometer water-based paint - Google Patents
Environmentally-friendly multi-effect nanometer water-based paint Download PDFInfo
- Publication number
- CN105176221A CN105176221A CN201510730565.XA CN201510730565A CN105176221A CN 105176221 A CN105176221 A CN 105176221A CN 201510730565 A CN201510730565 A CN 201510730565A CN 105176221 A CN105176221 A CN 105176221A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- nano
- environment
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses environmentally-friendly multi-effect nanometer water-based paint. The water-based paint is prepared from, by weight, 40-60 parts of macromolecular synthesis resin emulsion, 3-6 parts of nanometer scale silicon dioxide, 0.5-2 parts of nanometer titanium dioxide, 1-2 parts of water-based paint thickening agents, 0.5-2 parts of polyether type surface active agents, 0.4-1 part of preservative, 1-3 parts of anti-freezing agents, 1-2 parts of solidifying agents, 0.4-1.2 parts of dispersing agents, 25-45 parts of filling and 10-30 parts of water. The environmentally-friendly multi-effect nanometer water-based paint is waterproof, high in hardness, resistant to washing, high in adhesive force, smoothness and cleanness and resistant to oil stains, ageing and bacteria, meanwhile the content of VOC and formaldehyde is low, and the water-based paint is safe, environmentally friendly, excellent in performance and wide in application range.
Description
Technical field
The present invention relates to technical field of aqueous paint, particularly relate to a kind of environment-friendly type multiple-effect nano-waterborne coating.
Background technology
Building trade water-proof material used is generally divided into three major types: coiled material class, solvent based, pitch ointment class.But all there is high temperature trickling, low-temperature embrittleness, the problems such as tensile strength is low, unit elongation is little, poor adhesive force, meanwhile, three kinds of material color and lusters are black, therefore strong, the easily be full of cracks of these product heat absorptivities, aging and contaminate environment etc.And, do not accomplish the effect of seamless waterproof at all, the global problem of buildings waterproof cannot be solved.
China's existing concrete structure exterior wall major part decoration still at use exterior wall tile, exterior wall tile generally the weight of every square more than eight kilograms because the increase of wall weight has influence on the work-ing life of buildings greatly.And wall brick is non-watertight, easily come off and potential potential safety hazard.Meanwhile, a large amount of uses of wall brick are passive large to the Nonrenewable resources such as soil, coal.
In addition, solvent based coating only has single effect, does not possess the function of multiple-effect, in use must add conditioning agent again, and the content of formaldehyde and organic compound VOC is high, and digestion time is short, big for environment pollution.Meanwhile, coating is rigid, and thickness can only accomplish 0.02-0.03mm.And water-borne coatings seldom, does not fire the advantages such as not quick-fried high security, non yellowing, brushing area be large with its asepsis environment-protecting, odorlessness, volatilizable thing, along with the enhancing of people's environmental consciousness, more and more be subject to the welcome in market, but, how to make water-borne coatings have more function simultaneously, such as high resilience, waterproof, the performance such as antirust, weather-proof, thus make water-borne coatings have more wide application market, be a problem needing constantly research.
The application of nanotechnology is the mark of world technology.Nanotechnology, at the application and development of coating industry, impels coating to update, and has started breakthrough new era for coating becomes real Green Product.Nano paint has been identified as the special product of Olympic Village's construction work, shows the using value of nano paint in building field.It utilizes unique photocatalysis technology to have strong decomposition, eliminating effect to toxic gas in air.The obnoxious flavour such as PARA FORMALDEHYDE PRILLS(91,95), ammonia has the function absorbing and eliminate, and makes room air more pure and fresh.After tested, to various mould kill press down rate reach more than 99%.There is long-term mildew-resistant algae preventive effect, be suitable for the application of family, hospital, hotel and school.Nano-external wall paint, the two thin mechanism of the lotus leaf utilizing nano material binary collaborative, lower surface tension, there is high-strength sticking power, the high and flexible of hardness of paint film, excellent self-cleaning function, powerful anti-dust and the adhesive capacity of anti-foul, hydrophobicity is splendid, easily the performance of cleaning dirt.Washing fastness is more than 10000 times, and have good guarantor's light and protect look function, anti-uv-ray is extremely strong.Work-ing life reaches more than 10-15.Particle footpath is tiny, can go deep into body of wall, and the silicates material coordination reaction with metope, makes it firmly be combined into one, strong adhesion, non-scale, do not peel off, anti-aging.Its nanometer frost resistance functional paint, except possessing the various Optimality of Nano type coating, can within 0 degree Celsius to-25 degrees Celsius normal construction.Breach the precedent that building coating can not be constructed below 0 degree Celsius.And nano paint again can wet coating, has broken the regulation of building coating requirement body of wall humidity below 10%, building trade is constructed and shortens the duration, improve effect.How nanotechnology is applied to paint field processability and the more excellent product of security, needs further research.
Summary of the invention
Based on the technical problem that background technology exists, the present invention proposes a kind of environment-friendly type multiple-effect nano-waterborne coating.
A kind of environment-friendly type multiple-effect nano-waterborne coating that the present invention proposes, comprise the composition of following weight part: high molecular synthetic resin emulsion 40 ~ 60 parts, nanometer grade silica 3 ~ 6 parts, nano titanium oxide 0.5 ~ 2 part, water-borne coatings thickening material 1 ~ 2 part, polyether surfactant 0.5 ~ 2 part, sanitas 0.4 ~ 1 part, frostproofer 1 ~ 3 part, 1 ~ 2 part, solidifying agent, dispersion agent 0.4 ~ 1.2 part, filler 25 ~ 45 parts, 10 ~ 30 parts, water;
Its preparation method is as follows:
S1, first water, dispersion agent, sanitas liquid material to be dropped in dispersion tank, stir, under whipped state, filler, nanometer grade silica, nano titanium oxide are dropped into successively, and accelerate dispersion 30 minutes, obtain mixture;
S2, the mixture in S1 is transferred to paint mixing tank, in paint mixing tank, drops into high molecular synthetic resin emulsion, then add water-borne coatings thickening material, polyether surfactant, frostproofer, solidifying agent, stir 15 minutes, to completely evenly, obtain rough coating;
S3, the rough coating in S2 filtered and removes coarse particles and impurity, detect discharging, obtain environment-friendly type multiple-effect nano-waterborne coating.
Preferably, nano-waterborne coating comprises the composition of following weight part: high molecular synthetic resin emulsion 45 ~ 55 parts, nanometer grade silica 4 ~ 5 parts, nano titanium oxide 1 ~ 1.5 part, water-borne coatings thickening material 1.2 ~ 1.8 parts, polyether surfactant 0.8 ~ 1.6 part, sanitas 0.6 ~ 0.8 part, frostproofer 1.5 ~ 2.5 parts, dispersion agent 0.7 ~ 0.9 part, filler 30 ~ 40 parts, 15 ~ 25 parts, water.
Preferably, nano-waterborne coating comprises the composition of following weight part: high molecular synthetic resin emulsion 50 parts, nanometer grade silica 4.5 parts, nano titanium oxide 1.2 parts, water-borne coatings thickening material 1.5 parts, polyether surfactant 1.2 parts, sanitas 0.7 part, frostproofer 2 parts, dispersion agent 0.8 part, filler 35 parts, 20 parts, water.
Preferably, described high molecular synthetic resin emulsion is at least one in benzene emulsion, pure-acrylic emulsion, acrylate and vinyl acetate emulsion.
Preferably, described sanitas is the one in isothiazolinone, nitrogenous sulphur ring compound, s-triazine.
Preferably, described filler is at least one in water-ground limestone, light calcium carbonate, talcum powder, wollastonite, kaolin, barite, mica powder.
In the present invention, add nano titanium oxide and nano titanium oxide, utilize the two thin mechanism of nano material, film coated surface tension force is less, and coating presents certain repellency, makes the discharge of the water effective of coating, and stop the intrusion of outside moisture, make film have the performance of breathing; Utilize specific function and its scintilla structure of nano material, the inorganic siliceous and calcareous generation coordination reaction of nano material and body of wall, make body of wall and film form firmly claw-like infiltration, the continuity of film improves, film can not be come off, non-scale, have high-strength hardness and abrasion resistance; The particle diameter of nano titanium oxide and nano silicon is little, specific surface area is large, surface atom number is many, surface energy is high, therefore has very strong surfactivity and adsorptive power, and the negatively charged ion easily and in emulsion plays bonding action, thus the bonding strength improved between film and matrix, increase sticking power; Utilize the physical property principle at super two interface of nano material, nano silicon has tridimensional network, have huge specific surface area, show great activity, reticulated structure can be formed when coating is dry, add intensity and the smooth finish of coating simultaneously, and improve the suspension of pigment, the color of coating can be kept not fade for a long time, effectively discharge the intrusion of dust and greasy dirt, make body of wall have good self-cleaning function; Utilize the photocatalysis technology of nano material, nano titanium oxide has special optical characteristics, has and decomposes efficiently and eliminating effect, and can reduce the ultraviolet radiation of decomposition to the obnoxious flavour in air, the resistance of aging of coating is strengthened, there is the performance purified air; Utilize the activation technique of nano material, the antimicrobial coating that coating is formed can play destruction to the cytolemma such as intestinal bacteria, golden yellow staphylococcus, thus effectively kills the breeding of row or anti-bacteria; Have waterproof, high rigidity, washability, strong adhesive force, high bright and clean, oil-stain-preventing, anti-aging, antibacterial, have low VOC, formaldehyde content, be the water-borne coatings of a kind of safety and environmental protection, excellent performance, use range is extensive simultaneously.
Embodiment
Below in conjunction with specific embodiment, further explanation is done to the present invention.
Embodiment one
In the present embodiment, a kind of environment-friendly type multiple-effect nano-waterborne coating, comprises the composition of following weight part: high molecular synthetic resin emulsion 40 parts, nanometer grade silica 3 parts, nano titanium oxide 0.5 part, water-borne coatings thickening material 1 part, polyether surfactant 0.5 part, sanitas 0.4 part, frostproofer 1 part, 1 part, solidifying agent, dispersion agent 0.4 part, filler 25 parts, 10 parts, water;
Its preparation method is as follows:
S1, first water, dispersion agent, sanitas liquid material to be dropped in dispersion tank, stir, under whipped state, filler, nanometer grade silica, nano titanium oxide are dropped into successively, and accelerate dispersion 30 minutes, obtain mixture;
S2, the mixture in S1 is transferred to paint mixing tank, in paint mixing tank, drops into high molecular synthetic resin emulsion, then add water-borne coatings thickening material, polyether surfactant, frostproofer, solidifying agent, stir 15 minutes, to completely evenly, obtain rough coating;
S3, the rough coating in S2 filtered and removes coarse particles and impurity, detect discharging, obtain environment-friendly type multiple-effect nano-waterborne coating.
Embodiment two
In the present embodiment, a kind of environment-friendly type multiple-effect nano-waterborne coating, comprises the composition of following weight part: high molecular synthetic resin emulsion 45 parts, nanometer grade silica 4 parts, nano titanium oxide 0.8 part, water-borne coatings thickening material 1.2 parts, polyether surfactant 0.8 part, sanitas 0.6 part, frostproofer 1.5 parts, 1.2 parts, solidifying agent, dispersion agent 0.6 part, filler 30 parts, 15 parts, water;
Its preparation method is as follows:
S1, first water, dispersion agent, sanitas liquid material to be dropped in dispersion tank, stir, under whipped state, filler, nanometer grade silica, nano titanium oxide are dropped into successively, and accelerate dispersion 30 minutes, obtain mixture;
S2, the mixture in S1 is transferred to paint mixing tank, in paint mixing tank, drops into high molecular synthetic resin emulsion, then add water-borne coatings thickening material, polyether surfactant, frostproofer, solidifying agent, stir 15 minutes, to completely evenly, obtain rough coating;
S3, the rough coating in S2 filtered and removes coarse particles and impurity, detect discharging, obtain environment-friendly type multiple-effect nano-waterborne coating.
Embodiment three
In the present embodiment, a kind of environment-friendly type multiple-effect nano-waterborne coating, comprises the composition of following weight part: high molecular synthetic resin emulsion 50 parts, nanometer grade silica 4.5 parts, nano titanium oxide 1.2 parts, water-borne coatings thickening material 1.5 parts, polyether surfactant 1.2 parts, sanitas 0.7 part, frostproofer 2 parts, 1.5 parts, solidifying agent, dispersion agent 0.8 part, filler 35 parts, 20 parts, water;
Its preparation method is as follows:
S1, first water, dispersion agent, sanitas liquid material to be dropped in dispersion tank, stir, under whipped state, filler, nanometer grade silica, nano titanium oxide are dropped into successively, and accelerate dispersion 30 minutes, obtain mixture;
S2, the mixture in S1 is transferred to paint mixing tank, in paint mixing tank, drops into high molecular synthetic resin emulsion, then add water-borne coatings thickening material, polyether surfactant, frostproofer, solidifying agent, stir 15 minutes, to completely evenly, obtain rough coating;
S3, the rough coating in S2 filtered and removes coarse particles and impurity, detect discharging, obtain environment-friendly type multiple-effect nano-waterborne coating.
Embodiment four
In the present embodiment, a kind of environment-friendly type multiple-effect nano-waterborne coating, comprises the composition of following weight part: high molecular synthetic resin emulsion 55 parts, nanometer grade silica 5 parts, nano titanium oxide 1.6 parts, water-borne coatings thickening material 1.8 parts, polyether surfactant 1.6 parts, sanitas 0.8 part, frostproofer 2.5 parts, 1.8 parts, solidifying agent, dispersion agent 1 part, filler 40 parts, 25 parts, water;
Its preparation method is as follows:
S1, first water, dispersion agent, sanitas liquid material to be dropped in dispersion tank, stir, under whipped state, filler, nanometer grade silica, nano titanium oxide are dropped into successively, and accelerate dispersion 30 minutes, obtain mixture;
S2, the mixture in S1 is transferred to paint mixing tank, in paint mixing tank, drops into high molecular synthetic resin emulsion, then add water-borne coatings thickening material, polyether surfactant, frostproofer, solidifying agent, stir 15 minutes, to completely evenly, obtain rough coating;
S3, the rough coating in S2 filtered and removes coarse particles and impurity, detect discharging, obtain environment-friendly type multiple-effect nano-waterborne coating.
Embodiment five
In the present embodiment, a kind of environment-friendly type multiple-effect nano-waterborne coating, comprises the composition of following weight part: high molecular synthetic resin emulsion 60 parts, nanometer grade silica 6 parts, nano titanium oxide 2 parts, water-borne coatings thickening material 2 parts, polyether surfactant 2 parts, sanitas 1 part, frostproofer 3 parts, 2 parts, solidifying agent, dispersion agent 1.2 parts, filler 45 parts, 30 parts, water;
Its preparation method is as follows:
S1, first water, dispersion agent, sanitas liquid material to be dropped in dispersion tank, stir, under whipped state, filler, nanometer grade silica, nano titanium oxide are dropped into successively, and accelerate dispersion 30 minutes, obtain mixture;
S2, the mixture in S1 is transferred to paint mixing tank, in paint mixing tank, drops into high molecular synthetic resin emulsion, then add water-borne coatings thickening material, polyether surfactant, frostproofer, solidifying agent, stir 15 minutes, to completely evenly, obtain rough coating;
S3, the rough coating in S2 filtered and removes coarse particles and impurity, detect discharging, obtain environment-friendly type multiple-effect nano-waterborne coating.
The above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (6)
1. an environment-friendly type multiple-effect nano-waterborne coating, is characterized in that, comprises the composition of following weight part: high molecular synthetic resin emulsion 40 ~ 60 parts, nanometer grade silica 3 ~ 6 parts, nano titanium oxide 0.5 ~ 2 part, water-borne coatings thickening material 1 ~ 2 part, polyether surfactant 0.5 ~ 2 part, sanitas 0.4 ~ 1 part, frostproofer 1 ~ 3 part, 1 ~ 2 part, solidifying agent, dispersion agent 0.4 ~ 1.2 part, filler 25 ~ 45 parts, 10 ~ 30 parts, water;
Its preparation method is as follows:
S1, first water, dispersion agent, sanitas liquid material to be dropped in dispersion tank, stir, under whipped state, filler, nanometer grade silica, nano titanium oxide are dropped into successively, and accelerate dispersion 30 minutes, obtain mixture;
S2, the mixture in S1 is transferred to paint mixing tank, in paint mixing tank, drops into high molecular synthetic resin emulsion, then add water-borne coatings thickening material, polyether surfactant, frostproofer, solidifying agent, stir 15 minutes, to completely evenly, obtain rough coating;
S3, the rough coating in S2 filtered and removes coarse particles and impurity, detect discharging, obtain environment-friendly type multiple-effect nano-waterborne coating.
2. a kind of environment-friendly type multiple-effect nano-waterborne coating according to claim 1, it is characterized in that, nano-waterborne coating comprises the composition of following weight part: high molecular synthetic resin emulsion 45 ~ 55 parts, nanometer grade silica 4 ~ 5 parts, nano titanium oxide 1 ~ 1.5 part, water-borne coatings thickening material 1.2 ~ 1.8 parts, polyether surfactant 0.8 ~ 1.6 part, sanitas 0.6 ~ 0.8 part, frostproofer 1.5 ~ 2.5 parts, 1.2 ~ 1.8 parts, solidifying agent, dispersion agent 0.7 ~ 0.9 part, filler 30 ~ 40 parts, 15 ~ 25 parts, water.
3. a kind of environment-friendly type multiple-effect nano-waterborne coating according to claim 1, it is characterized in that, nano-waterborne coating comprises the composition of following weight part: high molecular synthetic resin emulsion 50 parts, nanometer grade silica 4.5 parts, nano titanium oxide 1.2 parts, water-borne coatings thickening material 1.5 parts, polyether surfactant 1.2 parts, sanitas 0.7 part, frostproofer 2 parts, 1.5 parts, solidifying agent, dispersion agent 0.8 part, filler 35 parts, 20 parts, water.
4. a kind of environment-friendly type multiple-effect nano-waterborne coating according to claim 1, is characterized in that, described high molecular synthetic resin emulsion is at least one in benzene emulsion, pure-acrylic emulsion, acrylate and vinyl acetate emulsion.
5. a kind of environment-friendly type multiple-effect nano-waterborne coating according to claim 1, is characterized in that, described sanitas is the one in isothiazolinone, nitrogenous sulphur ring compound, s-triazine.
6. a kind of environment-friendly type multiple-effect nano-waterborne coating according to claim 1, it is characterized in that, described filler is at least one in water-ground limestone, light calcium carbonate, talcum powder, wollastonite, kaolin, barite, mica powder.