CN105175940A - Self-adsorption vibration-proof film - Google Patents
Self-adsorption vibration-proof film Download PDFInfo
- Publication number
- CN105175940A CN105175940A CN201510580763.2A CN201510580763A CN105175940A CN 105175940 A CN105175940 A CN 105175940A CN 201510580763 A CN201510580763 A CN 201510580763A CN 105175940 A CN105175940 A CN 105175940A
- Authority
- CN
- China
- Prior art keywords
- parts
- self
- priming
- film
- shockproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of films and particularly relates to a self-adsorption vibration-proof film comprising substances containing the following components in parts by weight: 10-27 parts of PVC, 20-40 parts of silica gel, 15-29 parts of polypropylene, 3-19 parts of a cationic surfactant, 1-5 parts of a curing agent and 9-18 parts of elastomer. The components of the existing film are improved, so that the self-adsorption vibration-proof film simultaneously has a self-adsorption function and a vibration-proof function and can be widely applied to transportation protection and daily protection of various machines.
Description
Technical field
The invention belongs to film field, be specially a kind of self-priming shockproof film.
Technical background
Need to carry out shockproof and WATER REPELLENT to machine in the wrapping process of new precision instrument, in the wrapping process of existing machine, after usually carrying out bagging, adopt bumper bag or shockproof foam to process.But this mode can not ensure the transport at the medium-and-large-sized element part of long-distance transport process.
If carry out simple pad pasting process to machine, one is that operation is more complicated, and two is that the pasted shockproof antifriction poor performance of film well can not ensure that machine stands intact.
Summary of the invention
In order to solve the problems of the technologies described above, the invention provides a kind of self-priming shockproof film, its composition improving existing film realizes possessing from adsorption function and shockproof function simultaneously, can be widely used in the transport protection of all kinds of machine and daily protection.
A kind of self-priming shockproof film, comprises the material of following components by weight percent
PVC10-27 part
Silica hydrogel 20-40 part
Polypropylene 15-29 part
Cats product 3-19 part
Solidifying agent 1-5 part
Elastomerics 9-18 part.
As preferred technical scheme of the present invention, also comprise magnetic, the weight part of magnetic is 2-9 part.
As preferred technical scheme of the present invention, described elastomerics is preferably polyurethane elastomer, polyolefin elastomer or the two is arbitrarily than mixture.
As preferred technical scheme of the present invention, the consumption of described cats product is 15-19 part.
As preferred technical scheme of the present invention, also comprise white carbon black, the weight part of white carbon black is 27-38 part
Beneficial effect of the present invention:
In film of the present invention, add Silica hydrogel, elastomerics makes the elasticity that possesses of film prepared thus certain resistance performance can be born; The effect one of cats product is for dispersion agent; Two is the corrosion-free performances of cats product, is being applied on mechanical pad pasting and can not damaging mechanical surface; Three is when carrying out pad pasting, after adding the cats product of 3-19 part, the electronics that cats product has enough electric charges can attract in mechanical surface metal, but the adsorption between cats product and metal is not enough to make electron detachment metal in metal, therefore, cats product act on ability film being possessed be adsorbed in metallic surface.
The main auxiliary film of effect adding magnetic is adsorbed in metallic surface, makes film in long-distance transport not because jolting of road is dropped at self gravitation, is conducive to the long-distance transport of machinery.
Add white carbon black and improve film strength and crocking resistance, prevent machinery in transportation, be subject to frictional wear and damaged.
Embodiment
In order to better explain technical scheme of the present invention, be described in detail below in conjunction with embodiment.
Embodiment 1
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC27 part
Silica hydrogel 20 parts
Polypropylene 29 parts
15 parts, thanomin sodium
5 parts, solidifying agent
Polyurethane elastomer 9 parts
Magnetic 9 parts
White carbon black 27 parts,
Concrete implementation result
The amplitude that can bear is 20cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 2
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC10 part
Silica hydrogel 40 parts
Polypropylene 15 parts
Tetrahydroglyoxaline 19 parts
1 part, solidifying agent
Polyolefin elastomer 18 parts
Magnetic 2 parts
White carbon black 38 parts,
Concrete implementation result
The amplitude that can bear is 40cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 3
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC17 part
Silica hydrogel 20 parts
Polypropylene 19 parts
Moroxydine 19 parts
5 parts, solidifying agent
Polyurethane elastomer 1 part
Polyolefin elastomer 8 parts
Magnetic 2 parts
White carbon black 27 parts,
Concrete implementation result
The amplitude that can bear is 40cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 4
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC18 part
Silica hydrogel 29 parts
Polipropene 25 part
Trolamine 16 parts
3 parts, solidifying agent
Polyurethane elastomer 9 parts
Polyolefin elastomer 9 parts
Magnetic 9 parts
White carbon black 38 parts,
Concrete implementation result
The amplitude that can bear is 40cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 5
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC19 part
Silica hydrogel 24 parts
Polypropylene 18 parts
17 parts, polyethylene polyamines sodium
3 parts, solidifying agent
Thermoplastic sulfurized rubber 10 parts
Magnetic 7 parts
White carbon black 28 parts,
Concrete implementation result
The amplitude that can bear is 19cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 6
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC21 part
Silica hydrogel 28 parts
Polypropylene 16 parts
13 parts, polyethylene polyamines sodium
3 parts, solidifying agent
Melt processible thermoplastic elastomer 10 parts
Magnetic 7 parts
White carbon black 30 parts,
Concrete implementation result
The amplitude that can bear is 25cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 7
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC25 part
Silica hydrogel 35 parts
Polypropylene 27 parts
16 parts, diethanolamine potassium
1,23 parts, polybutadiene thermoplastic's elastomericss
14 parts, elastomerics
Magnetic 7 parts
White carbon black 35 parts,
Concrete implementation result
The amplitude that can bear is 25cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 8
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC21 part
Silica hydrogel 37 parts
Polipropene 25 part
Quaternary surfactant 16 parts
3 parts, solidifying agent
Polyacrylic rubber 14 parts
Magnetic 5 parts
White carbon black 36 parts,
Concrete implementation result
The amplitude that can bear is 25cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 9
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC14 part
Silica hydrogel 27 parts
Polipropene 25 part
Quaternary surfactant 13 parts
3 parts, solidifying agent
Epichlorohydrin rubber 14 parts
Magnetic 3 parts
Implementation result
The amplitude that can bear is 20cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 10
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC12 part
Silica hydrogel 25 parts
Polypropylene 17 parts
Moroxydine 8 parts
3 parts, solidifying agent
Hydrogenation butyronitrile rubber 12 parts
Magnetic 6 parts
Implementation result
The amplitude 20cm that can bear, extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 11
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC25 part
Silica hydrogel 27 parts
Polypropylene 28 parts
Quaternary surfactant 18 parts
3 parts, solidifying agent
Trifluoropropyl siloxane 10 parts
Magnetic 5 parts
Implementation result
The amplitude that can bear is 19cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 12
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC24 part
Silica hydrogel 34 parts
Polypropylene 26 parts
Quaternary ammonium salt cationic surfactant 15 parts
3 parts, solidifying agent
Ethylene copolymer thermoplastic elastomer 11 parts
Magnetic 4 parts
Implementation result
The amplitude that can bear is 20cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 13
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC22 part
Silica hydrogel 25 parts
Polypropylene 26 parts
Moroxydine 17 parts
3 parts, solidifying agent
Chlorosulfonated polyethylene 14 parts
Magnetic 7 parts
Implementation result
The amplitude that can bear is 20cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 14
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC25 part
Silica hydrogel 37 parts
Polypropylene 18 parts
Quaternary surfactant 7 parts
4 parts, solidifying agent
Thermoplastic sulfurized rubber 15 parts
White carbon black 28 parts,
Implementation result
The amplitude that can bear is 20cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 15
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC18 part
Silica hydrogel 29 parts
Polypropylene 19 parts
Tetrahydroglyoxaline 8 parts
4 parts, solidifying agent
Ethylene copolymer thermoplastic elastomer 14 parts
White carbon black 30 parts,
Implementation result
The amplitude that can bear is 20cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 16
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC18 part
Silica hydrogel 29 parts
Polypropylene 16 parts
Quaternary surfactant 4 parts
2 parts, solidifying agent
12 parts, polyester-type thermoplastic's elastomerics
White carbon black 28 parts,
Implementation result
The amplitude that can bear is 20cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 17
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC21 part
Silica hydrogel 23 parts
Polypropylene 23 parts
Tetrahydroglyoxaline 7 parts
3 parts, solidifying agent
Thermoplastic polyolefin elastomer 15 parts
White carbon black 30 parts,
Implementation result
The amplitude that can bear is 20cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 18
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC17 part
Silica hydrogel 32 parts
Polypropylene 19 parts
Tetrahydroglyoxaline 9 parts
5 parts, solidifying agent
12 parts, silicon rubber
Implementation result
The amplitude that can bear is 10cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 19
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC25 part
Silica hydrogel 28 parts
Polypropylene 21 parts
Quaternary surfactant 16 parts
3 parts, solidifying agent
15 parts, silicon rubber
Implementation result
The amplitude that can bear is 10cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Embodiment 20
A kind of self-priming shockproof film, comprises the material of following components by weight percent:
PVC21 part
Silica hydrogel 34 parts
Polypropylene 26 parts
Tetrahydroglyoxaline 16 parts
3 parts, solidifying agent
Natural rubber 13 parts
Implementation result
The amplitude that can bear is 10cm, and extreme pressure and antiwear behavior meets the requirement of production application.
Claims (5)
1. a self-priming shockproof film, is characterized in that: the material comprising following components by weight percent
PVC10-27 part
Silica hydrogel 20-40 part
Polypropylene 15-29 part
Cats product 3-19 part
Solidifying agent 1-5 part
Elastomerics 9-18 part.
2. the self-priming shockproof film of one according to claim 1, is characterized in that: also comprise magnetic, and the weight part of magnetic is 2-9 part.
3. the self-priming shockproof film of one according to claim 1, is characterized in that: described elastomerics is preferably polyurethane elastomer, polyolefin elastomer or the two is arbitrarily than mixture.
4. a kind of self-priming shockproof film according to claim 1, is characterized in that: the consumption of described cats product is 15-19 part.
5. a kind of self-priming shockproof film according to claim 1, it is characterized in that: also comprise white carbon black, the weight part of white carbon black is 27-38 part.