CN105172003A - Mirror face treatment method for resin products - Google Patents
Mirror face treatment method for resin products Download PDFInfo
- Publication number
- CN105172003A CN105172003A CN201510413964.3A CN201510413964A CN105172003A CN 105172003 A CN105172003 A CN 105172003A CN 201510413964 A CN201510413964 A CN 201510413964A CN 105172003 A CN105172003 A CN 105172003A
- Authority
- CN
- China
- Prior art keywords
- resin
- naval stores
- mirror face
- flaky material
- mirror process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to resin products and discloses a mirror face treatment method for the resin products. The mirror face treatment method for the resin products comprises the steps that 1, a flaky material with the smooth surface being a mirror face is taken; 2, the flaky material is arranged on the table top, the mirror face faces upwards, and non-condensed resin adhesives are dropwise added on the mirror face; 3, the face to be subjected to mirror face treatment of one resin product makes contact with the non-condensed resin adhesive solution on the mirror face material aslant, the resin product is put flat after contact, and bubbles between the product and the mirror face material are removed; and 4, after the resin is condensed, the resin product is taken down from the surface of the flaky material, and the four edges of the resin product are trimmed, namely mirror face treatment of the single face of the resin product is completed. When the resin products need to be subjected to multi-face mirror face treatment, the first to fourth steps can be repeated. Special polishing and grinding machines are not needed; mirror face treatment can be conducted on a large number of resin products at a time and efficiency is high; the operation process saves labor and time, a large amount of dust is avoided, and the method is very environmentally friendly.
Description
Technical field
The present invention relates to naval stores, especially relate to the method for a kind of naval stores mirror process being mainly used in resin craft.
Background technology
The resin craft of resin craft, particularly biological sample, the smoothness requirements for resin surface is very high.The naval stores that surface is smooth, its light transmission is better, and the quality of product is higher.Traditional naval stores surface finish process generally adopts the polishing step by step of varigrained sand paper, finally takes turns high speed polishing with wool.Such as, adopt the product of the common square silica gel mould demoulding, its surface is general in sub-light state, at this moment needs to adopt 100#, the sand paper of 200#, 800#, 1600#, 3000# is polished step by step, finally carry out polishing with wool wheel, whole process wastes time and energy, and operating efficiency is very low.Carry out in the process of high speed polishing at use wool wheel, careless slightlyly often occur that naval stores is by wool wheel bullet situation about flying, very dangerous.Loaded down with trivial details technique and lower efficiency significantly increase the cost of naval stores.
Summary of the invention
The object of the invention is to the problems such as resin craft polishing process for cubic type common on market is complicated, a kind of method of naval stores mirror process is provided.
The present invention includes following steps:
1) flaky material that smooth surface is minute surface is got;
2) be placed on desktop by flaky material, minute surface upward, minute surface drips and does not condense resin glue;
3) naval stores treated the one side of mirror process and specular material do not condense resin glue solution inclination contact, after contact, naval stores being set level, getting rid of the bubble between product and specular material;
4) after hardening of resin, naval stores is taken off from flaky material surface, naval stores four limit is repaired, namely completes the mirror process of a naval stores one side.
In step 1) in, described smooth surface is the flaky material of minute surface, preferably surface without scratch, foreign, without dust, not with resin-bonding, described smooth surface is the one that the flaky material of minute surface can select in polyethylene, silica gel, silanized glass etc.
In step 2) in, described desktop is preferably level, clean and tidy desktop; The described resin glue that do not condense can adopt and consistent with naval stores not condense resin glue;
When naval stores needs to carry out multiaspect mirror process, can step 1 be repeated) ~ 4).
The present invention has the following advantages:
1) without the need to special polishing, polishing machine;
2) once can carry out surperficial mirror process to a large amount of naval stores, efficiency is high simultaneously;
3) operating process saving of labor, laborsaving, does not have a large amount of dust and produces, very environmental protection.
Detailed description of the invention
The embodiment of the present invention comprises the following steps:
1) get the flaky material that smooth surface is minute surface, guarantee surface without scratch, foreign, without dust, simultaneously this flaky material not with resin-bonding, available sheet material is as the glass etc. of polyethylene, silica gel, silanization;
2) be placed in by flaky material on level, clean and tidy desktop, upward, according to the size of polished material surface area, what on minute surface, dropping was consistent with naval stores does not condense resin glue to minute surface;
3) naval stores is treated that the one side of mirror-polishing process contacts with the resin glue solution small angle inclination of not condensing in specular material, slowly naval stores is set level after contact, get rid of the bubble between product and specular material;
4) after hardening of resin, taken off by product from flaky material surface, simple finishing is done on four limits, one side is that the naval stores of minute surface just machines;
5) if mirror finish all will be carried out in six faces, step 1 can be repeated) ~ 4), until six faces are all minute surface.
Claims (6)
1. a method for naval stores mirror process, is characterized in that comprising the following steps:
1) flaky material that smooth surface is minute surface is got;
2) be placed on desktop by flaky material, minute surface upward, minute surface drips and does not condense resin glue;
3) naval stores treated the one side of mirror process and specular material do not condense resin glue solution inclination contact, after contact, naval stores being set level, getting rid of the bubble between product and specular material;
4) after hardening of resin, naval stores is taken off from flaky material surface, naval stores four limit is repaired, namely completes the mirror process of a naval stores one side.
2. the method for a kind of naval stores mirror process as claimed in claim 1, is characterized in that in step 1) in, described smooth surface is the flaky material of minute surface, be adopt surface without scratch, foreign, without dust, not with the flaky material of resin-bonding.
3. the method for a kind of naval stores mirror process as claimed in claim 1, is characterized in that in step 1) in, described smooth surface is the one that the flaky material of minute surface selects in polyethylene, silica gel, silanized glass.
4. the method for a kind of naval stores mirror process as claimed in claim 1, is characterized in that in step 2) in, described desktop is level, clean and tidy desktop.
5. the method for a kind of naval stores mirror process as claimed in claim 1, is characterized in that in step 2) in, the described resin glue that do not condense adopts and consistent with naval stores does not condense resin glue.
6. the method for a kind of naval stores mirror process as claimed in claim 1, is characterized in that when naval stores needs to carry out multiaspect mirror process, repeats step 1) ~ 4).