CN105150335A - Production process for wood floor - Google Patents
Production process for wood floor Download PDFInfo
- Publication number
- CN105150335A CN105150335A CN201510487217.4A CN201510487217A CN105150335A CN 105150335 A CN105150335 A CN 105150335A CN 201510487217 A CN201510487217 A CN 201510487217A CN 105150335 A CN105150335 A CN 105150335A
- Authority
- CN
- China
- Prior art keywords
- fiberboard
- fiber board
- drying
- production process
- oil film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process for a wood floor. The production process comprises the specific steps of selecting a fiber board with the density being 0.6-1.0 g/cm<3>; performing steam injection on the fiber board in a drying room for 6-8 minutes, and then heating and drying the fiber board; coating the surface of the fiber board with undercoat, and then drying the fiber board until the undercoat on the surface of the fiber board is completely cured; forming an oil film on the surface of the fiber board through a vibration mill; coating the surface of the fiber board with a finishing coat, and then drying the fiber board until the finishing coat on the surface of the fiber board is completely cured; forming an oil film on the surface of the fiber board through the vibration mill; pasting the surface of the fiber board with a layer of decorative film adhesive; and packaging the fiber board after the fiber board is manually checked to be qualified. The production process has the advantages that the process is simple, and the product quality is good.
Description
Technical field
The present invention relates to a kind of timber floor production technology, be applied to the production and processing field of timber floor.
Background technology
Along with improving constantly of people's living standard, timber floor is common in daily life, but existing timber floor production technology remains some traditional production technologies, the timber floor produced not only poor quality, and technics comparing is complicated, cost is high, is not suitable for and extensively promotes the use of.
Summary of the invention
For solving the defect of prior art, the invention discloses that a kind of timber floor quality produced is good, the simple timber floor production technology of technique.
The invention discloses a kind of timber floor production technology, concrete steps are as follows:
Step one: select density at the fiberboard of 0.6-1.0 gram/cc, the thickness of fiberboard is at 8-10mm;
Step 2: in drying shed, 6-8 minute is steamed to fiberboard spray, and then heat drying is carried out to fiberboard, until the water content of fiberboard is down to 8%-10%;
Step 3: to the surface spraying priming paint of fiberboard, the priming paint of then drying to fibreboard surface solidifies completely;
Step 4: use the surface of vibrating ball-mill to fiberboard to buy oil film;
Step 5: to the surface spraying finish paint of fiberboard, the finish paint of then drying to fibreboard surface solidifies completely;
Step 6: use the surface of vibrating ball-mill to fiberboard to buy oil film;
Step 7: paste one deck decorative film adhesive on the surface of fiberboard;
Step 8: carry out after desk checking is qualified packing.
The timber floor produced by timber floor production technology of the present invention not only quality is good, wear-resisting, long service life, and technics comparing is simple, be beneficial to operation, and cost is low, is suitable for wide popularization and application.
Detailed description of the invention
The invention discloses a kind of timber floor production technology, concrete steps are as follows:
Step one: select density at the fiberboard of 0.6-1.0 gram/cc, the thickness of fiberboard is at 8-10mm;
Step 2: in drying shed, 6-8 minute is steamed to fiberboard spray, and then heat drying is carried out to fiberboard, until the water content of fiberboard is down to 8%-10%;
Step 3: to the surface spraying priming paint of fiberboard, the priming paint of then drying to fibreboard surface solidifies completely;
Step 4: use the surface of vibrating ball-mill to fiberboard to buy oil film;
Step 5: to the surface spraying finish paint of fiberboard, the finish paint of then drying to fibreboard surface solidifies completely;
Step 6: use the surface of vibrating ball-mill to fiberboard to buy oil film;
Step 7: paste one deck decorative film adhesive on the surface of fiberboard;
Step 8: carry out after desk checking is qualified packing.
Embodiment 1
Step one: select density at the fiberboard of 0.8 gram/cc, the thickness of fiberboard is at 9mm;
Step 2: to fiberboard spray steaming 7 minutes in drying shed, and then heat drying is carried out to fiberboard, until the water content of fiberboard is down to 9%;
Step 3: to the surface spraying priming paint of fiberboard, the priming paint of then drying to fibreboard surface solidifies completely;
Step 4: use the surface of vibrating ball-mill to fiberboard to buy oil film;
Step 5: to the surface spraying finish paint of fiberboard, the finish paint of then drying to fibreboard surface solidifies completely;
Step 6: use the surface of vibrating ball-mill to fiberboard to buy oil film;
Step 7: paste one deck decorative film adhesive on the surface of fiberboard;
Step 8: carry out after desk checking is qualified packing.
Above embodiment only in order to the present invention is described and and unrestricted technical scheme described in the invention; Therefore, although this description with reference to each above-mentioned embodiment to present invention has been detailed description, those of ordinary skill in the art should be appreciated that and still can modify to the present invention or equivalent to replace; And all do not depart from technical scheme and the improvement thereof of the spirit and scope of the present invention, it all should be encompassed in right of the present invention.
Claims (1)
1. a timber floor production technology, is characterized in that: concrete steps are as follows:
Step one: select density at the fiberboard of 0.6-1.0 gram/cc, the thickness of fiberboard is at 8-10mm;
Step 2: in drying shed, 6-8 minute is steamed to fiberboard spray, and then heat drying is carried out to fiberboard, until the water content of fiberboard is down to 8%-10%;
Step 3: to the surface spraying priming paint of fiberboard, the priming paint of then drying to fibreboard surface solidifies completely;
Step 4: use the surface of vibrating ball-mill to fiberboard to buy oil film;
Step 5: to the surface spraying finish paint of fiberboard, the finish paint of then drying to fibreboard surface solidifies completely;
Step 6: use the surface of vibrating ball-mill to fiberboard to buy oil film;
Step 7: paste one deck decorative film adhesive on the surface of fiberboard;
Step 8: carry out after desk checking is qualified packing.