CN105133303A - Manufacturing technology for backpack waist protecting portion fabric - Google Patents
Manufacturing technology for backpack waist protecting portion fabric Download PDFInfo
- Publication number
- CN105133303A CN105133303A CN201510555029.0A CN201510555029A CN105133303A CN 105133303 A CN105133303 A CN 105133303A CN 201510555029 A CN201510555029 A CN 201510555029A CN 105133303 A CN105133303 A CN 105133303A
- Authority
- CN
- China
- Prior art keywords
- fabric
- parts
- oven dry
- protecting portion
- mosquito repellent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of luggage production and processing, in particular to a manufacturing technology for a backpack waist protecting portion fabric. The manufacturing technology is characterized by comprising the following steps that firstly, a blended fabric is soaked into mosquito repellent medicament for 4 h and then taken out for drying, and the drying temperature is 90-110 DEG C; secondly, the dried fabric is coated with a layer of waterproof adhesive, and the coating amount is 150-200 g/m<2>; thirdly, the coated fabric is dried and plasticized to obtain the backpack waist protecting portion fabric, the drying temperature is 145-160 DEG C, and the plasticizing temperature is 190-200 DEG C. The backpack waist protecting portion fabric contains mosquito repellent plant fiber, in addition, the fabric contains a large number of mosquito repellent components after being soaked with the mosquito repellent medicament, so that the mosquito repellent effect can be effectively achieved in the using process, fixation is firmer after treatment through a waterproof agent, the effect is more lasting, and the backpack waist protecting portion fabric is non-toxic and environmentally friendly.
Description
Technical field:
The present invention relates to the production and processing field of case and bag, more specifically to the manufacturing technique of a kind of knapsack waist support position fabric.
Background technology:
Fabric is the material of main part of case and bag product, and fabric not only directly affects the image appearance of product, and, be related to the market sale price of product, attention very must be given when designing and selecting.Style moulding, material and color are design three elements.Case and bag color and material two factors are directly embodied by fabric, and the style moulding of case and bag also relies on the characteristics such as the softness of material, well-pressed and thickness weight to ensure.So be also to pay attention to emphatically at conceptual design expression effect, out of doors in knapsack, user carries knapsack and shuttles back and forth out of doors, particularly summer, and mosquito is more, and user must carry mosquito repellent articles for use, and this just adds additional heavy burden.
Summary of the invention:
Technical problem to be solved by this invention is to overcome the manufacturing technique that existing technological deficiency provides a kind of knapsack waist support position fabric with function of driving mosquitoes.
Technical problem to be solved by this invention adopts following technical scheme to realize:
A manufacturing technique for outdoor knapsack waist support position fabric, is characterized in that comprising the following steps:
(1) blended yarn woven fabric to be immersed in anophelifuge 4 hours, then take out oven dry, bake out temperature is 90-110 DEG C;
(2) by the fabric brushing one deck marine glue after oven dry, brushing amount is 150-200g/m
2;
(3) by brushing after fabric carry out oven dry and plastics processing after and get final product, temperature during oven dry is 145-160 DEG C, and temperature during plasticizing is 190-200 DEG C.
Further, described blended yarn woven fabric comprises the component of following weight portion: 70-80 part cotton fiber, 20-30 part linen fibre, 10-20 part Wormwood fiber capable, 5-9 part common nepenthes fiber, 5-9 part lavender fiber.
Further, described anophelifuge is formed by the component infusion of following weight portion: 15-20 part tarragon, 3-9 part purple perilla, 6-11 part cloves, 14-17 part peppermint, 2-4 part root of Dahurain angelica, 1-3 part dried orange peel, 1-2 part calamus, 6-9 part wrinkled giant hyssop, 15-20 part honeysuckle.
Further, described marine glue comprises the component of following weight portion: mineral wax 67 parts, 20 parts, acetone, POLYPROPYLENE GLYCOL 36 parts, 42 parts, gelatine, sodium soap 18 parts, titanium sulfate 18 parts.
Containing mosquito repellent string in fabric of the present invention, in addition again through the immersion of anophelifuge, make in fabric containing a large amount of mosquito repellent composition, thus in use effectively can carry out mosquito repellent, and it is fixing more firm to make through waterproofing agent process, and effect is more lasting, nontoxic, environmental protection.
Detailed description of the invention:
The technological means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
A manufacturing technique for outdoor knapsack waist support position fabric, is characterized in that comprising the following steps:
(1) blended yarn woven fabric to be immersed in anophelifuge 4 hours, then take out oven dry, bake out temperature is 110 DEG C;
(2) by the fabric brushing one deck marine glue after oven dry, brushing amount is 150g/m
2;
(3) by brushing after fabric carry out oven dry and plastics processing after and get final product, temperature during oven dry is 160 DEG C, and temperature during plasticizing is 200 DEG C.
Blended yarn woven fabric comprises the component of following weight portion: 80 parts of cotton fibers, 30 parts of linen fibres, 20 parts of Wormwood fiber capables, 9 parts of common nepenthes fibers, 9 parts of lavender fibers.
Anophelifuge is formed by the component infusion of following weight portion: 20 portions of tarragons, 9 parts of purple perillas, 11 portions of cloves, 14 portions of peppermints, 2 parts of roots of Dahurain angelica, 1 part of dried orange peel, 1 portion of calamus, 6 portions of wrinkled giant hyssops, 15 portions of honeysuckles.
Marine glue comprises the component of following weight portion: mineral wax 67 parts, 20 parts, acetone, POLYPROPYLENE GLYCOL 36 parts, 42 parts, gelatine, sodium soap 18 parts, titanium sulfate 18 parts.
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (4)
1. a manufacturing technique for outdoor knapsack waist support position fabric, is characterized in that comprising the following steps:
(1) blended yarn woven fabric to be immersed in anophelifuge 4 hours, then take out oven dry, bake out temperature is 90-110 DEG C;
(2) by the fabric brushing one deck marine glue after oven dry, brushing amount is 150-200g/m
2;
(3) by brushing after fabric carry out oven dry and plastics processing after and get final product, temperature during oven dry is 145-160 DEG C, and temperature during plasticizing is 190-200 DEG C.
2. the manufacturing technique of a kind of outdoor knapsack waist support position according to claim 1 fabric, is characterized in that described blended yarn woven fabric comprises the component of following weight portion: 70-80 part cotton fiber, 20-30 part linen fibre, 10-20 part Wormwood fiber capable, 5-9 part common nepenthes fiber, 5-9 part lavender fiber.
3. the manufacturing technique of a kind of outdoor knapsack waist support position according to claim 1 fabric, is characterized in that described anophelifuge is formed by the component infusion of following weight portion: 15-20 part tarragon, 3-9 part purple perilla, 6-11 part cloves, 14-17 part peppermint, 2-4 part root of Dahurain angelica, 1-3 part dried orange peel, 1-2 part calamus, 6-9 part wrinkled giant hyssop, 15-20 part honeysuckle.
4. the manufacturing technique of a kind of outdoor knapsack waist support position according to claim 1 fabric, is characterized in that described marine glue comprises the component of following weight portion: mineral wax 67 parts, 20 parts, acetone, POLYPROPYLENE GLYCOL 36 parts, 42 parts, gelatine, sodium soap 18 parts, titanium sulfate 18 parts.