CN105131843A - Paint surface crystal polishing protection hard wax and preparing method thereof - Google Patents
Paint surface crystal polishing protection hard wax and preparing method thereof Download PDFInfo
- Publication number
- CN105131843A CN105131843A CN201510612979.2A CN201510612979A CN105131843A CN 105131843 A CN105131843 A CN 105131843A CN 201510612979 A CN201510612979 A CN 201510612979A CN 105131843 A CN105131843 A CN 105131843A
- Authority
- CN
- China
- Prior art keywords
- wax
- lacquer painting
- hard wax
- crystal polishing
- paint surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of a vehicle paint surface polishing wax, in particular to a paint surface crystal polishing protection hard wax and a preparing method thereof. Pure natural wax is taken as a main film forming substance and a dearomatization aliphatic series solvent is used, so that the product is more environment-friendly; by adding silicon-containing resin, the product has a paint face repairing capability; a silicon-containing high-molecular polymer is added, so that the product has higher paint surface luster texture and dewatering capability. The product can form a hard and compact wax protection layer on the paint surface of a vehicle body, the wax protection layer is good in luster texture, has excellent water splashing performance, and prevents the paint surface of the vehicle from scrapes and aging, and corrosion to the paint surface of the vehicle from acid rain and ultraviolet rays, and is excellent in paint surface protection capability and small in toxicity.
Description
Technical field
The present invention relates to automobile lacquer mirror polish wax technical field, particularly relate to a kind of lacquer painting crystal polishing protection hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.
Background technology
The main component of car wax is polythene wax emulsion or silicone macromolecular compound, and containing lubricant component.Because the added ingredients be rich in car wax is different, makes its physical form performance is distinguished to some extent, and then be divided into different kinds.Car wax can be divided into solid wax and liquid wax two kinds by the difference according to car wax physical condition, and in ongoing operations, liquid wax is applied relatively extensive.First effect of car wax is cosmetology function, namely keeps vehicle body beautiful, is secondly defencive function (should be the function of protection cere self timeliness strictly speaking), namely resists the effect of external environment infringement.For realizing two basic functions above, car wax generally all needs to comprise solvent, these four kinds of compositions of grinding composition, binder and brightening agent.Car paint oxide film and general dirt are removed in the effect of solvent (sanitising agent also belongs to solvent strictly speaking, and wax itself also can be classified as solvent based); The effect of grinding composition increases car paint surface smoothness and uniform color degree; The effect of binder mainly allows the cere accomplished fluently can produce adhewsive action to car clear coat, and this wherein can be subdivided into again physical property attachment and chemical attachment; The effect of brightening agent mainly allows cere produce beautiful effect.But it is short that existing car wax still exists work-ing life, poor adhesive force is low to the protective efficacy of lacquer painting, the problem that gloss texture is low.
Summary of the invention
The present invention is directed to existing finish polishing wax, to there is work-ing life short; poor adhesive force; low to the protective efficacy of lacquer painting; the problem that gloss texture is low; there is provided a kind of sticking power good, the life-span is long, and toxicity is low; there is the lacquer painting crystal polishing protection hard wax of excellent properties, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.
For achieving the above object, the present invention by the following technical solutions.
A kind of lacquer painting crystal polishing protection hard wax, is made up of each component of following mass percent: the pure natural wax of 60-90%, the containing silicone resin of 0.5-10%; the Porous deproteinized bone aliphatic solvent of 5-15%; the siliceous high molecular polymer of 2.5-20%, the silicone oil of 1-10%, and each component sum is 100%.
Preferably, the mass percent of each component is: the pure natural wax of 60-81%, the containing silicone resin of 1-10%, the Porous deproteinized bone aliphatic solvent of 10-15%, the siliceous high molecular polymer of 5-20%, the silicone oil of 2-10%, and each component sum is 100%.
Preferably, described lacquer painting crystal polishing protection hard wax comprises the spices of 0.1-0.3%.
Preferably, described pure natural wax is at least one in beeswax, palm wax, haze tallow.
Preferably, described Porous deproteinized bone aliphatic solvent is at least one in straight-chain paraffin and isoparaffin.
Preferably, described containing silicone resin is the synthetic resins containing Si and C-structure and at least one contained in the synthetic resins of Si, C and F structure.
Preferably, described siliceous high molecular polymer is containing at least one in the silane polymer of Si and C.
The preparation method of the above lacquer painting crystal polishing protection hard wax, comprises the following steps:
S1 is molten in advance: pure natural wax, silicone oil, Porous deproteinized bone aliphatic solvent is admixed together, then mixture is heated to 50-100 DEG C and mixture is dissolved, obtain pre-molten thing;
S2 modulates: added by containing silicone resin in pre-molten thing, then in pre-molten thing, add siliceous high molecular polymer while stirring, be stirred to and dissolve completely, obtained target product.
Preferably, in described step S2, in pre-molten thing, add siliceous high molecular polymer and after being stirred to and dissolving completely, in mixture, add spices and stir, obtained target product.
Preferably, in described step S2, after obtained target product, while hot target product is loaded in container.
Compared with prior art, the invention has the beneficial effects as follows: the present invention by with pure natural wax for main film forming matter and use Porous deproteinized bone aliphatic solvent make product more environmental protection; By adding containing silicone resin, product is made to have lacquer painting repair ability; Add siliceous high molecular polymer, make product have stronger lacquer painting gloss texture and hydrophobic ability.Product of the present invention can form hard, the fine and close wax protective layer of one deck on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish simultaneously; lacquer painting protective capability is excellent, and toxicity is little.
Embodiment
In order to understand technology contents of the present invention more fully, below in conjunction with specific embodiment, technical scheme of the present invention being described further and being illustrated.
Embodiment 1
The present embodiment provides a kind of lacquer painting crystal polishing to protect hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.Preparation method comprise successively in advance molten, modulation and tinning step, specific as follows:
(1) get the raw materials ready
Take 698g pure natural wax (398g beeswax, 300g palm wax), (25g contains synthetic resins/many alkoxysilane mixture of Si and C-structure to 50g containing silicone resin, 25g is containing the synthetic resins/fluorine TMOS of Si, C and F structure), 110g Porous deproteinized bone aliphatic solvent (60g straight-chain paraffin/D80,50g isoparaffin/Isopar), the siliceous high molecular polymer of 80g (main silane polymer/C30 alkylsiloxane containing Si and C), 60g silicone oil, 2g spices, for subsequent use.
(2) molten in advance: pure natural wax, silicone oil, Porous deproteinized bone aliphatic solvent is admixed together, then mixture is heated to 80 DEG C and mixture is dissolved, obtain pre-molten thing.
(3) modulate: containing silicone resin is added in pre-molten thing, then in pre-molten thing, add siliceous high molecular polymer while stirring, be stirred to and dissolve completely; Then in mixture, add spices and stir, obtained target product.Target product is pale yellow waxy thing, has aromatic odour, fusing point >=70 DEG C.
(4) tinning: target product also loads in container by filtered while hot, obtains finished product.
Product prepared by the present embodiment is for automobile; hard, the fine and close wax protective layer of one deck can be formed on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish, lacquer painting protective capability is excellent, and toxicity is little simultaneously.
Embodiment 2
The present embodiment provides a kind of lacquer painting crystal polishing to protect hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.Preparation method comprise successively in advance molten, modulation and tinning step.Only for the preparation of lacquer painting crystal polishing the protection raw material of hard wax and the different of embodiment 1 in the present embodiment, in advance molten, modulate and tinning step and embodiment 1 completely the same.Raw material for the preparation of lacquer painting crystal polishing protection hard wax is specific as follows:
Take 698g pure natural wax (398g beeswax, 300g haze tallow), (20g contains synthetic resins/many alkoxysilane mixture of Si and C-structure to 50g containing silicone resin, 30g is containing the synthetic resins/fluorine TMOS of Si, C and F structure), 110g Porous deproteinized bone aliphatic solvent (40g straight-chain paraffin/D80,70g isoparaffin/Isopar), the siliceous high molecular polymer of 80g (main silane polymer/C30 alkylsiloxane containing Si and C), 60g silicone oil, 2g spices, for subsequent use.
Product prepared by the present embodiment is for automobile; hard, the fine and close wax protective layer of one deck can be formed on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish, lacquer painting protective capability is excellent, and toxicity is little simultaneously.
Embodiment 3
The present embodiment provides a kind of lacquer painting crystal polishing to protect hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.Preparation method comprise successively in advance molten, modulation and tinning step.Only for the preparation of lacquer painting crystal polishing the protection raw material of hard wax and the different of embodiment 1 in the present embodiment, in advance molten, modulate and tinning step and embodiment 1 completely the same.Raw material for the preparation of lacquer painting crystal polishing protection hard wax is specific as follows:
Take 698g pure natural wax (beeswax), 50g containing silicone resin (synthetic resins/many alkoxysilane mixture containing Si and C-structure), 110g Porous deproteinized bone aliphatic solvent (straight-chain paraffin/D80), the siliceous high molecular polymer of 80g (main silane polymer/C30 alkylsiloxane containing Si and C), 60g silicone oil, 2g spices, for subsequent use.
Product prepared by the present embodiment is for automobile; hard, the fine and close wax protective layer of one deck can be formed on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish, lacquer painting protective capability is excellent, and toxicity is little simultaneously.
Embodiment 4
The present embodiment provides a kind of lacquer painting crystal polishing to protect hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.Preparation method comprise successively in advance molten, modulation and tinning step.Only for the preparation of lacquer painting crystal polishing the protection raw material of hard wax and the different of embodiment 1 in the present embodiment, in advance molten, modulate and tinning step and embodiment 1 completely the same.Raw material for the preparation of lacquer painting crystal polishing protection hard wax is specific as follows:
Take 698g pure natural wax (palm wax), 50g containing silicone resin (synthetic resins/fluorine TMOS containing Si, C and F structure), 110g Porous deproteinized bone aliphatic solvent (isoparaffin/Isopar), the siliceous high molecular polymer of 80g (main silane polymer/C30 alkylsiloxane containing Si and C), 60g silicone oil, 2g spices, for subsequent use.
Product prepared by the present embodiment is for automobile; hard, the fine and close wax protective layer of one deck can be formed on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish, lacquer painting protective capability is excellent, and toxicity is little simultaneously.
Embodiment 5
The present embodiment provides a kind of lacquer painting crystal polishing to protect hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.Preparation method comprise successively in advance molten, modulation and tinning step.Only for the preparation of lacquer painting crystal polishing the protection raw material of hard wax and the different of embodiment 1 in the present embodiment, in advance molten, modulate and tinning step and embodiment 1 completely the same.Raw material for the preparation of lacquer painting crystal polishing protection hard wax is specific as follows:
Take 698g pure natural wax (haze tallow), 50g containing silicone resin (synthetic resins/fluorine TMOS containing Si, C and F structure), 110g Porous deproteinized bone aliphatic solvent (straight-chain paraffin/D80), the siliceous high molecular polymer of 80g (main silane polymer/C30 alkylsiloxane containing Si and C), 60g silicone oil, 2g spices, for subsequent use.
Product prepared by the present embodiment is for automobile; hard, the fine and close wax protective layer of one deck can be formed on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish, lacquer painting protective capability is excellent, and toxicity is little simultaneously.
Embodiment 6
The present embodiment provides a kind of lacquer painting crystal polishing to protect hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.Preparation method comprise successively in advance molten, modulation and tinning step.Only for the preparation of lacquer painting crystal polishing the protection raw material of hard wax and the different of embodiment 1 in the present embodiment, in advance molten, modulate and tinning step and embodiment 1 completely the same.Raw material for the preparation of lacquer painting crystal polishing protection hard wax is specific as follows:
Take 610g pure natural wax (310g beeswax, 300g palm wax), (10g contains synthetic resins/many alkoxysilane mixture of Si and C-structure to 19g containing silicone resin, 9g is containing the synthetic resins/fluorine TMOS of Si, C and F structure), 150g Porous deproteinized bone aliphatic solvent (75g straight-chain paraffin/D80,75g isoparaffin/Isopar), the siliceous high molecular polymer of 200g (main silane polymer/C30 alkylsiloxane containing Si and C), 20g silicone oil, 10g spices, for subsequent use.
Product prepared by the present embodiment is for automobile; hard, the fine and close wax protective layer of one deck can be formed on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish, lacquer painting protective capability is excellent, and toxicity is little simultaneously.
Embodiment 7
The present embodiment provides a kind of lacquer painting crystal polishing to protect hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.Preparation method comprise successively in advance molten, modulation and tinning step.Only for the preparation of lacquer painting crystal polishing the protection raw material of hard wax and the different of embodiment 1 in the present embodiment, in advance molten, modulate and tinning step and embodiment 1 completely the same.Raw material for the preparation of lacquer painting crystal polishing protection hard wax is specific as follows:
Take 810g pure natural wax (410g beeswax, 400g palm wax), (5g contains synthetic resins/many alkoxysilane mixture of Si and C-structure to 10g containing silicone resin, 5g is containing the synthetic resins/fluorine TMOS of Si, C and F structure), 119g Porous deproteinized bone aliphatic solvent (60g straight-chain paraffin/D80,59g isoparaffin/Isopar), the siliceous high molecular polymer of 50g (main silane polymer/C30 alkylsiloxane containing Si and C), 10g silicone oil, 1g spices, for subsequent use.
Product prepared by the present embodiment is for automobile; hard, the fine and close wax protective layer of one deck can be formed on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish, lacquer painting protective capability is excellent, and toxicity is little simultaneously.
Embodiment 8
The present embodiment provides a kind of lacquer painting crystal polishing to protect hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.Preparation method comprise successively in advance molten, modulation and tinning step, specific as follows:
(1) get the raw materials ready: take 900g pure natural wax (450g beeswax, 450g palm wax), (2.5g contains synthetic resins/many alkoxysilane mixture of Si and C-structure to 5g containing silicone resin, 2.5g is containing the synthetic resins/fluorine TMOS of Si, C and F structure), 50g Porous deproteinized bone aliphatic solvent (25g straight-chain paraffin/D80,25g isoparaffin/Isopar), the siliceous high molecular polymer of 25g (main silane polymer/C30 alkylsiloxane containing Si and C), 17g silicone oil, 3g spices, for subsequent use.
(2) molten in advance: pure natural wax, silicone oil, Porous deproteinized bone aliphatic solvent is admixed together, then mixture is heated to 100 DEG C and mixture is dissolved, obtain pre-molten thing.
(3) modulate: containing silicone resin is added in pre-molten thing, then in pre-molten thing, add siliceous high molecular polymer while stirring, be stirred to and dissolve completely; Then in mixture, add spices and stir, obtained target product.Target product is pale yellow waxy thing, has aromatic odour, fusing point >=70 DEG C.
(4) tinning: target product also loads in container by filtered while hot, obtains finished product.
Product prepared by the present embodiment is for automobile; hard, the fine and close wax protective layer of one deck can be formed on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish, lacquer painting protective capability is excellent, and toxicity is little simultaneously.
Embodiment 9
The present embodiment provides a kind of lacquer painting crystal polishing to protect hard wax, and the preparation method of this kind of lacquer painting crystal polishing protection hard wax.Preparation method comprise successively in advance molten, modulation and tinning step, specific as follows:
(1) get the raw materials ready: take 600g pure natural wax (300g beeswax, 300g palm wax), (50g contains synthetic resins/many alkoxysilane mixture of Si and C-structure to 100g containing silicone resin, 50g is containing the synthetic resins/fluorine TMOS of Si, C and F structure), 100g Porous deproteinized bone aliphatic solvent (50g straight-chain paraffin/D80,50g isoparaffin/Isopar), the siliceous high molecular polymer of 100g (main silane polymer/C30 alkylsiloxane containing Si and C), 97g silicone oil, 3g spices, for subsequent use.
(2) molten in advance: pure natural wax, silicone oil, Porous deproteinized bone aliphatic solvent is admixed together, then mixture is heated to 50 DEG C and mixture is dissolved, obtain pre-molten thing.
(3) modulate: containing silicone resin is added in pre-molten thing, then in pre-molten thing, add siliceous high molecular polymer while stirring, be stirred to and dissolve completely; Then in mixture, add spices and stir, obtained target product.Target product is pale yellow waxy thing, has aromatic odour, fusing point >=70 DEG C.
(4) tinning: target product also loads in container by filtered while hot, obtains finished product.
Product prepared by the present embodiment is for automobile; hard, the fine and close wax protective layer of one deck can be formed on the lacquer painting of car body; wax protective layer gloss texture is good; there is excellent water-sprinkling; automobile finish can be prevented to be scratched and aging; acid rain and ultraviolet can be prevented the erosion of automobile finish, lacquer painting protective capability is excellent, and toxicity is little simultaneously.
The above only further illustrates technology contents of the present invention with embodiment, so that reader is easier to understand, but does not represent embodiments of the present invention and is only limitted to this, and any technology done according to the present invention extends or recreation, all by protection of the present invention.
Claims (10)
1. a lacquer painting crystal polishing protection hard wax; it is characterized in that; be made up of each component of following mass percent: the pure natural wax of 60-90%; the containing silicone resin of 0.5-10%; the Porous deproteinized bone aliphatic solvent of 5-15%; the siliceous high molecular polymer of 2.5-20%, the silicone oil of 1-10%, and each component sum is 100%.
2. hard wax is protected in a kind of lacquer painting crystal polishing according to claim 1; it is characterized in that; be made up of each component of following mass percent: the pure natural wax of 60-81%; the containing silicone resin of 1-10%; the Porous deproteinized bone aliphatic solvent of 10-15%; the siliceous high molecular polymer of 5-20%, the silicone oil of 2-10%, and each component sum is 100%.
3. a kind of lacquer painting crystal polishing protection hard wax according to claim 1 or 2, is characterized in that, also comprise the spices of 0.1-0.3%.
4. a kind of lacquer painting crystal polishing protection hard wax according to claim 1 or 2, it is characterized in that, described pure natural wax is at least one in beeswax, palm wax, haze tallow.
5. a kind of lacquer painting crystal polishing protection hard wax according to claim 1 or 2, is characterized in that, described Porous deproteinized bone aliphatic solvent is at least one in straight-chain paraffin and isoparaffin.
6. a kind of lacquer painting crystal polishing protection hard wax according to claim 1 or 2, is characterized in that, described containing silicone resin is the synthetic resins containing Si and C-structure and at least one contained in the synthetic resins of Si, C and F structure.
7. a kind of lacquer painting crystal polishing protection hard wax according to claim 1 or 2, it is characterized in that, described siliceous high molecular polymer is containing at least one in the silane polymer of Si and C.
8. a preparation method for hard wax is protected in the polishing of lacquer painting crystal as claimed in claim 1, it is characterized in that, comprises the following steps:
S1 is molten in advance: pure natural wax, silicone oil, Porous deproteinized bone aliphatic solvent is admixed together, then mixture is heated to 50-100 DEG C and mixture is dissolved, obtain pre-molten thing;
S2 modulates: added by containing silicone resin in pre-molten thing, then in pre-molten thing, add siliceous high molecular polymer while stirring, be stirred to and dissolve completely, obtained target product.
9. the preparation method of hard wax is protected in the polishing of lacquer painting crystal according to claim 8; it is characterized in that, in described step S2, in pre-molten thing, add siliceous high molecular polymer and be stirred to completely dissolve after; in mixture, add spices and stir, obtained target product.
10. the preparation method of hard wax is protected in the polishing of lacquer painting crystal according to claim 8 or claim 9, it is characterized in that, in described step S2, after obtained target product, is loaded in container by target product while hot.