CN105131403A - Elastic plastic product - Google Patents

Elastic plastic product Download PDF

Info

Publication number
CN105131403A
CN105131403A CN201510625373.2A CN201510625373A CN105131403A CN 105131403 A CN105131403 A CN 105131403A CN 201510625373 A CN201510625373 A CN 201510625373A CN 105131403 A CN105131403 A CN 105131403A
Authority
CN
China
Prior art keywords
parts
plastic product
elastic plastic
maleic anhydride
plastelast
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510625373.2A
Other languages
Chinese (zh)
Inventor
邓义增
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Hebang Metal Products Co Ltd
Original Assignee
Wuxi Hebang Metal Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Hebang Metal Products Co Ltd filed Critical Wuxi Hebang Metal Products Co Ltd
Priority to CN201510625373.2A priority Critical patent/CN105131403A/en
Publication of CN105131403A publication Critical patent/CN105131403A/en
Pending legal-status Critical Current

Abstract

The invention discloses an elastic plastic product. The elastic plastic product is prepared from the following components in parts by weight: 10-40 parts of polypropylene homopolymer, 30-60 parts of polyethylene homopolymer, 4-7 parts of plasticizer, 2-3 parts of flame retardant, and 14-20 parts of maleic anhydride-styrene copolymer. The elastic plastic product is reasonable in component, thus being good in elasticity and unlikely to break under a low temperature.

Description

Plastelast goods
Technical field
The present invention relates to plastic products technology field, especially a kind of plastelast goods.
Background technology
Existing plastics, are used in a large number by every profession and trade, but due to the performance decision of resin own, its elasticity is all very low, easily broken, more easily broken especially at low ambient temperatures.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, propose a kind of plastelast goods, composition rationally, possesses elasticity at low temperatures, not easily broken.
In order to realize foregoing invention object, the invention provides following technical scheme: a kind of plastelast goods, be made up of the following composition of weight part: homopolymer polypropylene 10 ~ 40, Natene 30 ~ 60, softening agent 4 ~ 7, fire retardant 2 ~ 3, maleic anhydride-styrene copolymers 14 ~ 20.
Further, the weight part of each composition is as follows respectively: homopolymer polypropylene 10, Natene 60, softening agent 4, fire retardant 3, maleic anhydride-styrene copolymers 14.
Further, the weight part of each composition is as follows respectively: homopolymer polypropylene 40, Natene 30, softening agent 7, fire retardant 2, maleic anhydride-styrene copolymers 20.
Compared with prior art, the present invention has the following advantages: component is reasonable, makes the good springiness of plastics, not easily breaks at low temperatures.
Embodiment
Describe the present invention below in conjunction with embodiment, the description of this part is only exemplary and explanatory, should not have any restriction to protection scope of the present invention.
embodiment 1
A kind of plastelast goods, are made up of the following composition of weight part: homopolymer polypropylene 24, Natene 44, softening agent 6, fire retardant 2.3, maleic anhydride-styrene copolymers 18.
embodiment 2
A kind of plastelast goods, are made up of the following composition of weight part: homopolymer polypropylene 10, Natene 60, softening agent 4, fire retardant 3, maleic anhydride-styrene copolymers 14.
embodiment 3
A kind of plastelast goods, are made up of the following composition of weight part: homopolymer polypropylene 40, Natene 30, softening agent 7, fire retardant 2, maleic anhydride-styrene copolymers 20.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (3)

1. plastelast goods, is characterized in that: be made up of the following composition of weight part: homopolymer polypropylene 10 ~ 40, Natene 30 ~ 60, softening agent 4 ~ 7, fire retardant 2 ~ 3, maleic anhydride-styrene copolymers 14 ~ 20.
2. plastelast goods as claimed in claim 1, is characterized in that: the weight part of each composition is as follows respectively: homopolymer polypropylene 10, Natene 60, softening agent 4, fire retardant 3, maleic anhydride-styrene copolymers 14.
3. plastelast goods as claimed in claim 1, is characterized in that: the weight part of each composition is as follows respectively: homopolymer polypropylene 40, Natene 30, softening agent 7, fire retardant 2, maleic anhydride-styrene copolymers 20.
CN201510625373.2A 2015-09-28 2015-09-28 Elastic plastic product Pending CN105131403A (en)