CN105128461A - Anti-smashing composite glass capable of preventing splashes on back surface and production technology of glass - Google Patents
Anti-smashing composite glass capable of preventing splashes on back surface and production technology of glass Download PDFInfo
- Publication number
- CN105128461A CN105128461A CN201510592432.0A CN201510592432A CN105128461A CN 105128461 A CN105128461 A CN 105128461A CN 201510592432 A CN201510592432 A CN 201510592432A CN 105128461 A CN105128461 A CN 105128461A
- Authority
- CN
- China
- Prior art keywords
- layer
- transparent
- float glass
- flaggy
- abrasionproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a piece of anti-smashing composite glass capable of preventing splashes on the back surface and a production technology of the glass. Through press-fitting molding of float glass layers, a transparent PC (polycarbonate) board layer, middle PU (polyurethane) film layers and a single-side anti-scratch transparent PC board layer, the prevention performance of the glass is reliable when the glass is subjected to terrorist attacks; regardless of the kind of impact on the anti-impact outer surface, the outer surface for preventing the splashes is safe, sound, flat, smooth and free of any splashes, enhances the safety and can deter intruders as long as the set prevention level is not exceeded; after the float glass layers, the transparent PC board layer, the middle PU film layers and the single-side anti-scratch transparent PC board layer are laminated in order, heating, pressurization and vacuum pumping molding are performed, the technology is simple, and the obtained composite glass is light in mass, high in impact resistance, capable of preventing the splashes on the back surface and high in terrorist attack prevention level.
Description
Technical field
The present invention relates to and prevent pounding compound glass field, compound glass and manufacture craft thereof are pounded without the anti-of splash in a kind of back side specifically.
Background technology
Current anti-ly pound compound glass structurally, in design, on materials'use, processing technology is not quite similar.Be that A level is anti-equally to pound, some thickness need reach 30mm, and the every square metre of 70Kg that weighs, some 10mm are thick just can be realized, and weight per square meter only has 19Kg, and reason is the power of intermediate layer impact resistance.Because standard does not specify anti-thickness and the Unit Weight pounding compound glass at different levels, occur that above-mentioned technical difference also belongs to normal.What no matter adopt which kind of technology to process anti-ly pounds compound glass, and the back side still belongs to blank at present without the anti-compound glass technology of pounding of splash.
Summary of the invention
The object of this invention is to provide a kind of back side and pound compound glass and manufacture craft thereof without the anti-of splash.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
Compound glass is pounded without the anti-of splash in a kind of back side, comprise some float glass layers, 1 layer of transparent flaggy of PC, some PU middle film layer and 1 layer of one side abrasionproof draw the transparent flaggy of PC, and formed by pressing and forming between each adjacent layer, be float glass layer for shock proof outer surface layer, outer surface layer for anti-splashing thing is that one side abrasionproof draws the transparent flaggy of PC, the transparent flaggy of PC is arranged between two float glass layers, PU middle film layer is arranged on float glass layer and the transparent flaggy of PC, float glass layer and one side abrasionproof are drawn between the transparent flaggy of PC and adjacent two layers float glass layer, the thickness of described float glass layer is 3 ~ 12mm, the thickness of the transparent flaggy of PC is 3 ~ 10mm, the thickness of PU middle film layer is 0.5 ~ 1.2mm, the thickness that one side abrasionproof draws the transparent flaggy of PC is 1.5 ~ 2mm,
Described float glass layer is 2 layers, and PU middle film layer is 3 layers;
The thickness of the thickness of described float glass layer to be the thickness of the transparent flaggy of 12mm, PC be 10mm, PU middle film layer is 1.2mm, and the thickness that one side abrasionproof draws the transparent flaggy of PC is 2mm;
The transparent flaggy of described PC and one side abrasionproof are drawn the transparent flaggy of PC and are made by Merlon;
The abrasionproof that described one side abrasionproof draws the transparent flaggy of PC is drawn surface and is scribbled silication coating;
The back side as above, without an anti-manufacture craft of pounding compound glass for splash, comprises the following steps:
Step one: get float glass, PC transparent panel, PU intermediate coat and one side abrasionproof and draw PC transparent panel, cutting is needed according to size and the number of plies, some float glass layers, 1 layer of transparent flaggy of PC, some PU middle film layer and 1 layer of one side abrasionproof draw the transparent flaggy of PC, for subsequent use;
Step 2: the float glass layer after cutting, the transparent flaggy of PC and one side abrasionproof are drawn the transparent flaggy edging of PC;
Step 3: the float glass layer after edging is developed a film, the transparent flaggy of the PC after edging and one side abrasionproof are drawn the transparent flaggy of PC and are carried out Electrostatic Treatment;
Step 4: some float glass layers, 1 layer of transparent flaggy of PC, some PU middle film layer and 1 layer of one side abrasionproof are drawn PC transparent panel laminated sheet, wherein using float glass layer as shock proof outer surface layer, one side abrasionproof is drawn the outer surface layer of the transparent flaggy of PC as anti-splashing thing, be arranged on by transparent for PC flaggy between two float glass layers, PU middle film layer is arranged on float glass layer and the transparent flaggy of PC, float glass layer and one side abrasionproof are drawn between the transparent flaggy of PC and adjacent two layers float glass layer;
Step 5: molded by taking out under temperature≤150 DEG C, pressure≤1.3MPa, vacuum 0.06 ~-0.1MPa condition after each laminated sheet, obtains the back side and pounds compound glass without the anti-of splash;
Temperature in described step 5 is 150 DEG C;
Pressure 1.3MPa in described step 5.
Beneficial effect of the present invention:
Compound glass is pounded without the anti-of splash in the back side provided by the invention, is drawn the pressing and forming of the transparent flaggy of PC by float glass layer, the transparent flaggy of PC, PU middle film layer and one side abrasionproof, and when suffering cruelly probably to attack, it takes precautions against dependable performance; No matter which type of meets with for shock proof outer surface to impact, as long as do not exceed the strick precaution rank of setting, the outer surface for anti-splashing thing is just safe and sound, and flat smooth, without any splash, highlights safety, also form deterrence to invader; The back side provided by the invention is without the anti-manufacture craft of pounding compound glass of splash, float glass layer, the transparent flaggy of PC, PU middle film layer and one side abrasionproof are drawn after the transparent flaggy of PC closes sheet in order, shaping through heating, pressurizeing, vacuumize, technique is simple, gained compound glass quality is light, strong shock resistance, and the back side is without splash, anti-riot probably attack rank is high.
Accompanying drawing explanation
Fig. 1 structural representation of the present invention;
Fig. 2 present invention process flow chart;
Reference numeral: 1, float glass layer, 2, the transparent flaggy of PC, 3, PU middle film layer, 4, one side abrasionproof draws the transparent flaggy of PC.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is further elaborated.
Embodiment 1
Compound glass is pounded without the anti-of splash in a kind of back side, comprise 2 layers of float glass layer 1, 1 layer of transparent flaggy 2 of PC, 3 layers of PU middle film layer 3 and 1 layer of one side abrasionproof draw the transparent flaggy 4 of PC, and formed by pressing and forming between each adjacent layer, be float glass layer 1 for shock proof outer surface layer, outer surface layer for anti-splashing thing is that one side abrasionproof draws the transparent flaggy 4 of PC, the transparent flaggy 2 of PC is arranged between two float glass layers 1, PU middle film layer 3 is arranged on float glass layer 1 and the transparent flaggy of PC 2 and float glass layer 1 and one side abrasionproof and draws between the transparent flaggy 4 of PC, the thickness of described float glass layer 1 is 12mm, the thickness of the transparent flaggy 2 of PC is 10mm, the thickness of PU middle film layer 3 is 1.2mm, the thickness that one side abrasionproof draws the transparent flaggy 4 of PC is 2mm.
The material that the transparent flaggy of PC 2 and one side abrasionproof draw the transparent flaggy 4 of PC is all Merlon, and common PC transparent panel case hardness is very low, does not reach HB level, wipes just can cause scuffing with rag, is not suitable for preventing pounding compound glass surface.And one side abrasionproof to draw PC transparent panel be surface thereof has been done the process of silication coating, make its case hardness can reach more than 2H, firmly wipe with rag and also can not cause scuffing, be so just applicable to being placed in and anti-ly pound compound glass inner surface.No matter which type of outer surface meets with is impacted, as long as do not exceed the strick precaution rank of setting, inner surface is just safe and sound, and flat smooth, without any splash.
Two outer surface differences of the present invention, have directionality.Shock proof outer surface is float glass layer 1, and the outer surface of anti-splashing thing is that abrasionproof draws the transparent flaggy 4 of PC.During installation, shock proof outer surface is placed in outdoor, and the outer surface of anti-splashing thing is placed in indoor.
The back side as above, without an anti-manufacture craft of pounding compound glass for splash, comprises the following steps:
Step one: get float glass, PC transparent panel, PU intermediate coat and one side abrasionproof and draw PC transparent panel, need cutting according to size and the number of plies, obtains 2 layers of float glass layer, 1 layer of transparent flaggy of PC, 3 layers of PU middle film layer and 1 layer of one side abrasionproof and draws the transparent flaggy of PC, for subsequent use;
Step 2: the float glass layer after cutting, the transparent flaggy of PC and one side abrasionproof are drawn the transparent flaggy edging of PC;
Step 3: the float glass layer after edging is developed a film, the transparent flaggy of the PC after edging and one side abrasionproof are drawn the transparent flaggy of PC and are carried out Electrostatic Treatment;
Step 4: 2 layers of float glass layer, 1 layer of transparent flaggy of PC, 3 layers of PU middle film layer and 1 layer of one side abrasionproof are drawn PC transparent panel laminated sheet, wherein using float glass layer as shock proof outer surface layer, one side abrasionproof is drawn the outer surface layer of the transparent flaggy of PC as anti-splashing thing, be arranged on by transparent for PC flaggy between two float glass layers, PU middle film layer is arranged on float glass layer and the transparent flaggy of PC and float glass layer and one side abrasionproof and draws between the transparent flaggy of PC;
Step 5: molded by taking out under temperature 150 DEG C, pressure 1.3MPa, vacuum 0.06 ~-0.1MPa condition after each laminated sheet, obtains the back side and pounds compound glass without the anti-of splash.
Embodiment 2
Compound glass is pounded without the anti-of splash in a kind of back side, comprise 3 layers of float glass layer 1, 1 layer of transparent flaggy 2 of PC, 4 layers of PU middle film layer 3 and 1 layer of one side abrasionproof draw the transparent flaggy 4 of PC, and formed by pressing and forming between each adjacent layer, be float glass layer 1 for shock proof outer surface layer, outer surface layer for anti-splashing thing is that one side abrasionproof draws the transparent flaggy 4 of PC, the transparent flaggy 2 of PC is arranged between two float glass layers 1, PU middle film layer 3 is arranged on float glass layer 1 and the transparent flaggy 2 of PC, float glass layer 1 and one side abrasionproof are drawn between the transparent flaggy 4 of PC and adjacent two layers float glass layer 1, the thickness of described float glass layer 1 is 3mm, the thickness of the transparent flaggy 2 of PC is 3mm, the thickness of PU middle film layer 3 is 0.5mm, the thickness that one side abrasionproof draws the transparent flaggy 4 of PC is 1.5mm.
The material that the transparent flaggy of PC 2 and one side abrasionproof draw the transparent flaggy 4 of PC is all Merlon, and common PC transparent panel case hardness is very low, does not reach HB level, wipes just can cause scuffing with rag, is not suitable for preventing pounding compound glass surface.And one side abrasionproof to draw PC transparent panel be surface thereof has been done the process of silication coating, make its case hardness can reach more than 2H, firmly wipe with rag and also can not cause scuffing, be so just applicable to being placed in and anti-ly pound compound glass inner surface.No matter which type of outer surface meets with is impacted, as long as do not exceed the strick precaution rank of setting, inner surface is just safe and sound, and flat smooth, without any splash.
Two outer surface differences of the present invention, have directionality.Shock proof outer surface is float glass layer 1, and the outer surface of anti-splashing thing is that abrasionproof draws the transparent flaggy 4 of PC.During installation, shock proof outer surface is placed in outdoor, and the outer surface of anti-splashing thing is placed in indoor.
The back side as above, without an anti-manufacture craft of pounding compound glass for splash, comprises the following steps:
Step one: get float glass, PC transparent panel, PU intermediate coat and one side abrasionproof and draw PC transparent panel, need cutting according to size and the number of plies, obtains 3 layers of float glass layer, 1 layer of transparent flaggy of PC, 4 layers of PU middle film layer and 1 layer of one side abrasionproof and draws the transparent flaggy of PC, for subsequent use;
Step 2: the float glass layer after cutting, the transparent flaggy of PC and one side abrasionproof are drawn the transparent flaggy edging of PC;
Step 3: the float glass layer after edging is developed a film, the transparent flaggy of the PC after edging and one side abrasionproof are drawn the transparent flaggy of PC and are carried out Electrostatic Treatment;
Step 4: 3 layers of float glass layer, 1 layer of transparent flaggy of PC, 4 layers of PU middle film layer and 1 layer of one side abrasionproof are drawn PC transparent panel laminated sheet, wherein using float glass layer as shock proof outer surface layer, one side abrasionproof is drawn the outer surface layer of the transparent flaggy of PC as anti-splashing thing, be arranged on by transparent for PC flaggy between two float glass layers, PU middle film layer is arranged on float glass layer and the transparent flaggy of PC, float glass layer and one side abrasionproof are drawn between the transparent flaggy of PC and adjacent two layers float glass layer;
Step 5: molded by taking out under temperature 130 DEG C, pressure 1.0MPa, vacuum 0.06 ~-0.1MPa condition after each laminated sheet, obtains the back side and pounds compound glass without the anti-of splash.
The back side provided by the invention is without the anti-manufacture craft of pounding compound glass of splash, float glass layer, the transparent flaggy of PC, PU middle film layer and one side abrasionproof are drawn after the transparent flaggy of PC closes sheet in order, shaping through heating, pressurizeing, vacuumize, technique is simple, gained compound glass quality is light, strong shock resistance, and the back side is without splash, anti-riot probably attack rank is high.
According to the difference of taking precautions against rank, in structure of the present invention, the number of plies of float glass layer 1, the transparent flaggy of PC 2, PU middle film layer 3 is not necessarily identical.Meanwhile, to draw the thickness of PC flaggy 4 also not necessarily identical for float glass layer 1, the transparent flaggy of PC 2, PU middle film layer 3, one side abrasionproof.The Thickness scope of float glass layer 1 is 3 ~ 12mm; The Thickness scope of the transparent flaggy 2 of PC is 3 ~ 10mm; The Thickness scope of PU middle film layer 3 is 0.5 ~ 1.2mm; The thickness that one side abrasionproof draws PC flaggy 4 is 1.5 ~ 2mm.
Claims (8)
1. compound glass is pounded without the anti-of splash in a back side, it is characterized in that: comprise some float glass layers (1), 1 layer of transparent flaggy of PC (2), some PU middle film layer (3) and 1 layer of one side abrasionproof draw the transparent flaggy of PC (4), and formed by pressing and forming between each adjacent layer, be float glass layer (1) for shock proof outer surface layer, outer surface layer for anti-splashing thing is that one side abrasionproof draws the transparent flaggy of PC (4), the transparent flaggy of PC (2) is arranged between two float glass layers (1), PU middle film layer (3) is arranged on float glass layer (1) and the transparent flaggy of PC (2), float glass layer (1) and one side abrasionproof are drawn between the transparent flaggy of PC (4) and adjacent two layers float glass layer (1), the thickness of described float glass layer (1) is 3 ~ 12mm, the thickness of the transparent flaggy of PC (2) is 3 ~ 10mm, the thickness of PU middle film layer (3) is 0.5 ~ 1.2mm, the thickness that one side abrasionproof draws the transparent flaggy of PC (4) is 1.5 ~ 2mm.
2. compound glass is pounded without the anti-of splash in the back side as claimed in claim 1, it is characterized in that: described float glass layer (1) is 2 layers, and PU middle film layer (3) is 3 layers.
3. compound glass is pounded without the anti-of splash in the back side as claimed in claim 1, it is characterized in that: the thickness of described float glass layer (1) is 12mm, the thickness of the transparent flaggy of PC (2) is 10mm, the thickness of PU middle film layer (3) is 1.2mm, and the thickness that one side abrasionproof draws the transparent flaggy of PC (4) is 2mm.
4. compound glass is pounded without the anti-of splash in the back side as claimed in claim 1, it is characterized in that: the transparent flaggy of described PC (2) and one side abrasionproof are drawn the transparent flaggy of PC (4) and made by Merlon.
5. compound glass is pounded without the anti-of splash in the back side as claimed in claim 1, it is characterized in that: the abrasionproof that described one side abrasionproof draws the transparent flaggy of PC (4) is drawn surface and scribbled silication coating.
6. the back side as claimed in claim 1 is without an anti-manufacture craft of pounding compound glass for splash, it is characterized in that, comprises the following steps:
Step one: get float glass, PC transparent panel, PU intermediate coat and one side abrasionproof and draw PC transparent panel, cutting is needed according to size and the number of plies, some float glass layers, 1 layer of transparent flaggy of PC, some PU middle film layer and 1 layer of one side abrasionproof draw the transparent flaggy of PC, for subsequent use;
Step 2: the float glass layer after cutting, the transparent flaggy of PC and one side abrasionproof are drawn the transparent flaggy edging of PC;
Step 3: the float glass layer after edging is developed a film, the transparent flaggy of the PC after edging and one side abrasionproof are drawn the transparent flaggy of PC and are carried out Electrostatic Treatment;
Step 4: some float glass layers, 1 layer of transparent flaggy of PC, some PU middle film layer and 1 layer of one side abrasionproof are drawn PC transparent panel laminated sheet, wherein using float glass layer as shock proof outer surface layer, one side abrasionproof is drawn the outer surface layer of the transparent flaggy of PC as anti-splashing thing, be arranged on by transparent for PC flaggy between two float glass layers, PU middle film layer is arranged on float glass layer and the transparent flaggy of PC, float glass layer and one side abrasionproof are drawn between the transparent flaggy of PC and adjacent two layers float glass layer;
Step 5: molded by taking out under temperature≤150 DEG C, pressure≤1.3MPa, vacuum 0.06 ~-0.1MPa condition after each laminated sheet, obtains the back side and pounds compound glass without the anti-of splash.
7. the back side as claimed in claim 6 is without the anti-manufacture craft of pounding compound glass of splash, it is characterized in that: the temperature in described step 5 is 150 DEG C.
8. the back side as claimed in claim 6 is without the anti-manufacture craft of pounding compound glass of splash, it is characterized in that: the pressure in described step 5 is 1.3MPa.