CN105113330A - Method for adding double-component retention and drainage aid in corrugated paper production process - Google Patents
Method for adding double-component retention and drainage aid in corrugated paper production process Download PDFInfo
- Publication number
- CN105113330A CN105113330A CN201510422256.6A CN201510422256A CN105113330A CN 105113330 A CN105113330 A CN 105113330A CN 201510422256 A CN201510422256 A CN 201510422256A CN 105113330 A CN105113330 A CN 105113330A
- Authority
- CN
- China
- Prior art keywords
- concentration
- retention
- drainage
- cationic polyacrylamide
- production process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for adding a double-component retention and drainage aid in a corrugated paper production process. The method comprises the following steps: 1, preparing an aqueous cationic polyacrylamide solution with the concentration of 1g/L and an aqueous modified bentonite solution with the concentration of 100g/L; and 2, placing a paper pulp with the mass concentration of 0.8% in a dynamic drainage jar, uniformly stirring at room temperature under a rotating speed of 700-800r/min, adding 12-14ml of the aqueous cationic polyacrylamide solution to every liter of the paper pulp, stirring for 15s, adding 4-8ml of the aqueous modified bentonite solution to every liter of the paper pulp, and stirring for 15s. The method adopting a double-component retention and drainage aiding system improves the retention rate of fine components and a filler, improves the water drainage performance of the pulp, substantially reduces the COD content of tray water, and plays a great role in realization of closed circulation and zero discharge of papermaking industry white water.
Description
Technical field
The invention belongs to paper industry retention aid and filtering aid technical field, be specifically related to a kind of method of adding double base retention and drainage aid agent in production process of corrugated paper.
Background technology
Flourish along with paper-making industry, paper industry also exposes more problem in producing, and mainly contains raw material, energy scarcity and problem of environmental pollution.In paper industry production process, along with the raising of paper machine speed, Secondary Fiber Recycling amount also increases thereupon, plain boiled water cycling rate is also higher, but this makes wet end of machine system decline to tiny component and the retention of other auxiliary agent and the water filtering performance of slurry thereupon, and it is serious to cause paper pulp fiber to run off with plain boiled water, heavy system plain boiled water pollutional load, reduces system cleanliness factor.All these put forward new requirement to becoming the retention and water filtering performance that improve wet end in paper process and reducing plain boiled water pollutional load.
In paper-making process, tiny component, filler and additive add the consumption that can reduce slurry and auxiliary material.This not only can reduce the consumption of slurry auxiliary material, but also can reduce concentration and the COD content thereof of plain boiled water, reduces production cost to a certain extent.So the tiny component should kept here in paper industry forming process in slurry and filler as far as possible, and strengthen the dehydration of wet end of machine, the effective way of less expensive uses efficient retention and drainage aid agent now as far as possible.
Paper retention and filter aid is of a great variety, and often kind of retention and drainage aid agent characteristic, effect, the scope of application are not quite similar.All adopt single retention and drainage aid agent in current traditional production process of corrugated paper, treatment effect or be that retention is low, or be exactly water filtering performance difference, cause the retention of the tiny component of slurry and filler low, machine water COD content is high.
Summary of the invention
Technical problem to be solved by this invention provides a kind of method of adding double base retention and drainage aid agent in production process of corrugated paper, to improve the retention of the tiny component of slurry and filler and to reduce the COD content of machine water.
The present invention solves the problems of the technologies described above with following technical scheme:
Add the method for double base retention and drainage aid agent in a kind of production process of corrugated paper of the present invention, comprise the following steps:
(1) the modified alta-mud aqueous solution of compound concentration to be the cationic polyacrylamide aqueous solution of 1g/L and concentration be 100g/L;
(2) by mass concentration be 0.8% pulp be placed in dynamic drainage instrument, at ambient temperature, stir under the rotating speed of 700 ~ 800r/min, then 12 ~ 14ml cationic polyacrylamide aqueous solution is added by 1L pulp, after stirring 15s, 4 ~ 8ml modified alta-mud aqueous solution is added again, after stirring 15s by 1L pulp.
The compound method of the described cationic polyacrylamide aqueous solution is: 0.1g cationic polyacrylamide is put into 100ml deionized water, stirs.
The compound method of the described modified alta-mud aqueous solution is: added in 200ml deionized water by 20g modified alta-mud, stir.
The molecular weight of described cationic polyacrylamide is greater than 500,000.
The inventive method adopts double base retention aid and filtering aid system, both the retention of tiny component and filler can have been improved, also can improve the water filtering performance of slurry, and reduce the COD content of machine water significantly, for realizing paper industry white water system and zero-emission plays a significant role.
The inventive method can effectively make the tiny component of slurry and the retention of filler improve 2.3 ~ 5.8% and 9.6 ~ 13.1% respectively, and significantly can reduce the COD content of filtrate, reaches 5.1 ~ 23.4%.On the one hand, the raising of the tiny component of slurry and filler retention, saves fibrous raw material, improves water filtering performance, improves paper machine operation speed, is conducive to reducing paper industry production cost; On the other hand, the COD of filtrate (i.e. plain boiled water) reduces, and makes wet end more clean, has promoted further developing of paper industry white water system and zero-emission.
Detailed description of the invention
Double base retention aid and filtering aid system in the present invention, use cationic polyacrylamide (CPAM) and modified alta-mud at ambient temperature, in dynamic drainage instrument (DDJ), simulation wet end system in paper machine comes the tiny component of test slurry and the retention of filler, and adopts Seal scatter by microwave COD method Quick testing instrument to measure the COD content of plain boiled water.
The modified alta-mud adopted in the present invention is commercially available prod, and it can be bought from emperor's son-in-law Ying Natu factory of Shandong Weifang City, is to belong to sodium soil bentonite in powder, and in its chemical composition, the content of Na base, much larger than Ca base content, belongs to Na soil.
The molecular weight of the cationic polyacrylamide (CPAM) that the present invention adopts is greater than 500,000.
Below in conjunction with embodiment, the present invention is described in further detail, but embodiments of the present invention are not limited thereto.
Embodiment 1
(1) by fetch from paper mill come slurry and plain boiled water furnishing mass concentration be the slurry of 0.8%.Claim 0.1g cationic polyacrylamide (CPAM) to be dissolved in 100ml deionized water, stir, join concentration is the CPAM solution of 1g/L.
(2) measure 1L mass concentration be 0.8% slurry join in dynamic drainage instrument, at ambient temperature, the CPAM solution that 12ml concentration is 1g/L is added after stirring under 700r/min rotating speed, the retention of the tiny component of slurry is measured after stirring 15s, get filtrate to install with mineral water bottle, adopt Seal scatter by microwave COD method Quick testing instrument to measure the COD content of filtrate.
Above-mentioned measured result is as shown in table 1.
Embodiment 2
(1) by fetch from paper mill come slurry and plain boiled water furnishing mass concentration be the slurry of 0.8%.Take 20g modified alta-mud to be dissolved in 200ml deionized water, stir, join concentration is the modified alta-mud solution of 100g/L.
(2) measure 1L mass concentration be 0.8% slurry join in dynamic drainage instrument, at ambient temperature, adding 4ml concentration after stirring under 700r/min rotating speed is 100g/L bentonite solution, tiny component and the filler retention of slurry is measured after stirring 15s, filtrate installs with mineral water bottle, adopts Seal scatter by microwave COD method Quick testing instrument to measure the COD content of filtrate.
Above-mentioned measured result is as shown in table 1.
Embodiment 3
(1) by fetch from paper mill come slurry and plain boiled water furnishing mass concentration be the slurry of 0.8%.Claim 0.1g cationic polyacrylamide (CPAM) to be dissolved in 100ml deionized water, stir, join concentration is the CPAM solution of 1g/L.Take 20g modified alta-mud to be dissolved in 200ml deionized water, stir, join concentration is the modified alta-mud solution of 100g/L.
(2) measure 1L mass concentration be 0.8% slurry join in dynamic drainage instrument, at ambient temperature, after stirring under 700r/min rotating speed, 12ml concentration is the CPAM solution of 1g/L, stir 15s, then the bentonite solution that 4ml concentration is 100g/L is added, measure tiny component and the filler retention of slurry after stirring 15s, filtrate installs with mineral water bottle, adopts Seal scatter by microwave COD method Quick testing instrument to measure the COD content of filtrate.
Above-mentioned measured result is as shown in table 1.
Embodiment 4
(1) by fetch from paper mill come slurry and plain boiled water furnishing mass concentration be the slurry of 0.8%.Claim 0.2g cationic polyacrylamide (CPAM) to be dissolved in 200ml deionized water, stir, join concentration is the CPAM solution of 1g/L.Take 30g modified alta-mud to be dissolved in 300ml deionized water, the obtained concentration that stirs is the modified alta-mud solution of 100g/L.
(2) measure 1L mass concentration be 0.8% slurry join in dynamic drainage instrument, at ambient temperature, after stirring under 750r/min rotating speed, 13ml concentration is the CPAM solution of 1g/L, stir 15s, then the bentonite solution that 6ml concentration is 100g/L is added, measure tiny component and the filler retention of slurry after stirring 15s, filtrate installs with mineral water bottle, adopts Seal scatter by microwave COD method Quick testing instrument to measure the COD content of filtrate.
Above-mentioned measured result is as shown in table 1.
Embodiment 5
(1) by fetch from paper mill come slurry and plain boiled water furnishing mass concentration be the slurry of 0.8%.Claim 0.3g cationic polyacrylamide (CPAM) to be dissolved in 300ml deionized water, stir, join concentration is the CPAM solution of 1g/L.Take 40g modified alta-mud to be dissolved in 400ml deionized water, the obtained concentration that stirs is the modified alta-mud solution of 100g/L.
(2) measure mass concentration be 0.8% slurry join in dynamic drainage instrument, at ambient temperature, after stirring under 800r/min rotating speed, 14ml concentration is 1g/LCPAM solution, stir 15s, then adding 8ml concentration is 100g/L bentonite solution, measure tiny component and the filler retention of slurry after stirring 15s, filtrate installs with mineral water bottle, adopts Seal scatter by microwave COD method Quick testing instrument to measure the COD content of filtrate.
Above-mentioned measured result is as shown in table 1.
The test result of the various example of table 1
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | |
Tiny component retention, % | 90.8 | 92.9 | 93.6 | 95.1 | 96.2 |
Filler retention, % | 81.9 | 89.8 | 91.1 | 92.6 | |
Liquor C OD | 4.32×10 3 | 4.10×10 3 | 3.85×10 3 | 3.31×10 3 | 3.08×10 3 |
As can be seen from the table, adopt in embodiments of the invention, embodiment 1 and embodiment 2 add single retention and drainage aid agent respectively, and after adopting double base retention aid and filtering aid system in embodiment 3,4,5, the tiny component of slurry and filler retention are obtained for raising, and the COD content of filtrate also declines thereupon simultaneously.Along with the increase of CPAM-modified alta-mud double base retention aid and filtering aid body agent consumption, the tiny component of slurry and the raising thereupon of filler retention, and the COD content of filtrate also correspondingly reduces.
Claims (4)
1. add a method for double base retention and drainage aid agent in production process of corrugated paper, it is characterized in that, comprise the following steps:
(1) the modified alta-mud aqueous solution of compound concentration to be the cationic polyacrylamide aqueous solution of 1g/L and concentration be 100g/L;
(2) by mass concentration be 0.8% pulp be placed in dynamic drainage instrument, at ambient temperature, stir under the rotating speed of 700 ~ 800r/min, then 12 ~ 14ml cationic polyacrylamide aqueous solution is added by 1L pulp, after stirring 15s, 4 ~ 8ml modified alta-mud aqueous solution is added again, after stirring 15s by 1L pulp.
2. add the method for double base retention and drainage aid agent according to claim 1 in production process of corrugated paper, it is characterized in that, the compound method of the described cationic polyacrylamide aqueous solution is: 0.1g cationic polyacrylamide is put into 100ml deionized water, stirs.
3. add the method for double base retention and drainage aid agent according to claim 1 in production process of corrugated paper, it is characterized in that, the compound method of the described modified alta-mud aqueous solution is: added in 200ml deionized water by 20g modified alta-mud, stir.
4. add the method for double base retention and drainage aid agent according to claim 1 in production process of corrugated paper, it is characterized in that, the molecular weight of cationic polyacrylamide is greater than 500,000.