CN105088380A - Compound type non-woven collar interlining - Google Patents
Compound type non-woven collar interlining Download PDFInfo
- Publication number
- CN105088380A CN105088380A CN201510338178.1A CN201510338178A CN105088380A CN 105088380 A CN105088380 A CN 105088380A CN 201510338178 A CN201510338178 A CN 201510338178A CN 105088380 A CN105088380 A CN 105088380A
- Authority
- CN
- China
- Prior art keywords
- hot melt
- melt adhesive
- powder
- nonwoven fabric
- compound type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of non-woven adhesive interlining, and discloses a compound type non-woven collar interlining. Glue points of a hot melt glue are distributed on one face of a non-woven base fabric, and each glue point of the hot melt adhesive is of an upper and lower double-layer structure; preparation of the non-woven base fabric comprises the steps: (1) taking a natural spice, adding the natural spice to water, dispersing evenly, then adding a halloysite powder to the solution, to obtain a mixed solution, allowing the mixed liquid to stand under a vacuum condition, and carrying out centrifugation and drying treatment, to obtain a halloysite powder loaded with the natural spice; (2) additionally taking a halloysite powder, aluminum chloride, polyethylene oxide, carboxymethyl cellulose, a dispersing agent, a silane coupling agent and the prepared halloysite powder loaded with the natural spice, and mixing evenly, to obtain a mixture; (3) successively adding isotactic polypropylene slices and the prepared mixture to a screw extruder, melting, spinning, drafting, forming a net, carrying out hot rolling, and thus obtaining the non-woven base fabric. The collar interlining has the advantages of good hygroscopicity, good permeability, stiff and smooth texture and low cost, and can emit fragrance.
Description
Technical field
The present invention relates to nonwoven fabric adhesive lining field, particularly relate to a kind of compound type non-woven fabric collar support.
Background technology
Adhesive lining is a kind of lining scribbling hot melt adhesive, is that cloth art makes one of auxiliary material often used.Adhesive lining is through heating pressing, hot melt adhesive coating melted by heat in adhesive lining, thus be attached to the back side of cloth, can be embodied by adding adhesive lining when cloth needs to express well-pressed, thickness, or cloth is too soft smooth when being difficult to operation, adds adhesive lining and cloth can be made to become well-behaved in obedient.
Adhesive lining can be divided into by base fabric classification:
1. woven adhesive lining: the lining cloth being made base fabric by woven fabric.
2. knitting adhesive lining: the lining cloth being made base fabric by woven fabric.
3. bondedfibre fabric adhesive lining: the lining cloth being made base fabric by bondedfibre fabric.
Nonwoven adhesive interlining is with non-weaving cloth (nonwoven fabric) for base fabric, more dominant in relative cloth matter adhesive lining price, but quality is slightly inferior undoubtedly.Non-woven lining is applicable to some corner, limit Angle Position, such as opens bag, buttonhole etc.Non-woven lining also has dividing of thickness, and their thickness can be embodied directly in used position, and this selects as required.
Due to the low price, convenient for production of nonwoven fabric adhesive lining, the application of nonwoven fabric adhesive lining is also more and more wider, and in order to the Ji Bu making nonwoven fabric be applicable to the adhesive lining of different purposes, many manufacturing enterprises have developed the adhesive lining nonwoven fabric with various function.Wherein, for the nonwoven fabric base cloth being used as the adhesive lining such as collar support, sock, sportswear adhesive lining, need that there is outstanding ability of sweat absorption.Although nonwoven fabric is relative to other fabrics, inherently have good hygroscopicity and gas permeability, still can not satisfy the demands.
Active carbon nonwoven fabric has stronger absorption property, but active carbon nonwoven fabric is black, cannot be used as white or light collar support, make practical application obtain restriction.
Authorization Notice No. is that the Chinese invention patent of CN102409537B discloses a kind of crease and shrink resistance, the postfinishing process of hydroscopic fast-drying type shirt collar support: the quick-drying hygroscopic agent 30-40g/L of modifier as post-finishing agent choosing polyethylene siloxanes, with the resin of finite concentration amount, catalyst preparation become pH value be 4.5 padding liquid; To treat that finish fabric is placed in padding liquid again, and when the rate of padding reaches 80%, carry out preliminary drying and bake two steps.Play the modifier for polyethylene siloxanes of primary absorbent quick-drying effect in padding finishing liquid of the present invention, be applicable to cotton, wash and the arrangement of blended fabric hydroscopic fast-drying, and give fabric splendid soft feel.But the weak point of this invention is: the fabric after Final finishing is comparatively soft, and stiffness is not high enough, if it is well-pressed to be not used as collar support.
Authorization Notice No. is the multifunction shoe pads that the Chinese invention patent of CN102326921B discloses a kind of environmental protection, comprise surface layer and basic unit, basic unit is the high density needle punched non-woven fabrics that bamboo-carbon fibre and Far Infrared Polyester Fiber are made, wherein bamboo-carbon fibre and Far Infrared Polyester Fiber are by weight being 1:1, and this nonwoven fabric has good absorbing sweat, permeability.But its weak point is, bamboo-carbon fibre and Far Infrared Polyester Fiber cost higher, be not suitable for use in the Ji Bu of adhesive lining, and preparation technology's relative complex.
Summary of the invention
In order to solve the problems of the technologies described above, the invention provides a kind of compound type non-woven fabric collar support, this collar support hygroscopicity and good permeability, cost are low, and quality is well-pressed, can be fragrant, and preparation technology is simple.
Concrete technical scheme of the present invention is: a kind of compound type non-woven fabric collar support, grey cloth is nonwoven fabric base cloth, the wherein one side of described nonwoven fabric base cloth is distributed with hot melt adhesive glue point, and each hot melt adhesive glue point is Dual-layer structure, it is hot melt adhesive basal layer at the middle and upper levels, and lower floor is hot melt adhesive adhesive layer; The preparation technology of described nonwoven fabric base cloth is as follows:
(1) get 5-10 part natural perfume material and added in 1000 parts of water and be uniformly dispersed, then in solution, add 10-15 part galapectite powder obtain mixed liquor, after mixed liquor is left standstill 3-5h under vacuumized conditions, obtain through centrifugal, dry process the galapectite powder that load has natural perfume material.
Galapectite is a kind of silicate mineral, mainly exists and occurring in nature with nanotube-shaped form, is hollow structure, therefore has outstanding absorption property because it is nanotube-shaped.Be immersed in by galapectite powder in natural perfume material solution, galapectite powder can adsorb natural perfume material powder.
(2) separately get 5-10 part galapectite powder, 5-10 part aluminium chloride, 0.5-1.5 part polyethylene glycol oxide, 3-5 part carboxymethyl cellulose, 0.5-1.5 part dispersant, 1-5 part silane coupler have the galapectite powder of natural perfume material to mix with above-mentioned obtained load, obtain mixture.
(3) successively the section of 120-150 part isotactic polypropylene, above-mentioned obtained mixture are added to screw extruder and carry out melting, then obtain nonwoven fabric base cloth after spinning, drawing-off, one-tenth net, hot rolling.
Each step all substances number is parts by weight above.
The mixture of the galapectite powder of natural perfume material, aluminium chloride, polyethylene glycol oxide, carboxymethyl cellulose, silane coupler, dispersant and isotactic polypropylene is had to carry out the heat of mixing melting galapectite powder, load, preparing nonwoven fabric through spinning, galapectite powder is being distributed in non-woven fabrics fiber and goes.For the feature easily sweat in neck position, because in galapectite, load has natural perfume material, obtained collar support nonwoven fabric finished product can be fragrant, can cover the sweat odor of neck, and can play the effect of producing refreshing effect to the mind, and after galapectite adsorbed fragrance matter, also there is slow-release function, fragrance matter can be discharged lentamente, can't discharge rapidly, and fragrance matter has had galapectite carrier, the also not easily wash-out easily when nonwoven fabric is washed.On the other hand, due to the existence with galapectite powder that adds of polyethylene glycol oxide, numerous fine pore passage structure in non-woven fabrics fiber, is had, there is the specific area of super large, moisture pick-up properties and the gas permeability of nonwoven fabric can be increased, thus can even quick absorbing sweat sweat is volatilized, weaken sweat odor; And alundum (Al2O3) has certain hardness in galapectite powder and product, the stiffness of nonwoven fabric is improved, becomes well-pressed, be suitable for the nonwoven fabric base cloth making collar support, not easily fold.
In addition, this collar support select polypropylene be the nonwoven fabric of matrix as grey cloth, price is relatively cheap, and compared with the nonwoven fabric of bamboo-carbon fibre, active carbon compound, galapectite cost is also lower.
As preferably, the particle diameter of described galapectite powder is 0.3-3 micron, and described natural perfume material is selected from as one or more in sandalwood powder, camphortree leaf powder, and the particle diameter of natural perfume material is 50-100 nanometer.Natural perfume material is nontoxic, is beneficial to health.The particle diameter of galapectite powder is not easily excessive, otherwise affects the spinning properties of polymer.The particle diameter of natural perfume material can not be excessive, otherwise can not be adsorbed by galapectite powder.
As preferably, one or both in acid activation process or thermal activation treatment of described galapectite powder.Galapectite powder is after acid activation or thermal activation, and it has stronger absorption property.
As preferably, the relative molecular weight of described polyethylene glycol oxide is 800000-1200000.
As preferably, described dispersant is polypropylene wax.
As preferably, in step (1), after described galapectite powder load natural perfume material, also pass through further flavouring process, concrete grammar is as follows: get Peppermint essential oil and in closed container, carry out heating under reduced pressure to it, load there is the galapectite powder of natural perfume material to be positioned in closed container above Peppermint essential oil, take out after suffocating treatment 2-4h.
Further flavouring is carried out to the galapectite powder of load natural perfume material, and the suction type adopting solid natural perfume material powder to combine with Peppermint essential oil, take full advantage of the space of galapectite powder to inside, increase the adsorbance of fragrance matter.
As preferably, the preparation method of described Peppermint essential oil is as follows: get peppermint stem and leaf and grind it, after crossing 200 orders, getting 10-15 part peppermint stem and leaf powder, to add 100 parts of concentration to be in the ethanol water of 60-80wt%, then the ethanol water being added with peppermint stem and leaf powder is carried out microwave abstracting at microwave extracter, extraction conditions is microwave power 400-600W, extraction time 1-3h, extraction temperature 60-75 DEG C; Obtain peppermint extract after extraction, also carry out pressure reduction with classification distillation to described peppermint extract and obtain mint extract, then mint extract and ethanol are dissolved each other and obtain Peppermint essential oil, wherein the mass ratio of mint extract and ethanol is 3:7; Above all substances number is parts by weight.
The Peppermint essential oil prepared as stated above, extraction quantity is large, and developability is strong, is easily adsorbed by galapectite.
As preferably, the material of described hot melt adhesive basal layer is polyurethane, and basal layer can prevent hot melt adhesive reverse osmosis, and the material of described hot melt adhesive adhesive layer is polyesteramide, and adhesive layer makes collar support and fabric bond and portion's strike-through.
As preferably, described hot melt adhesive glue point is distributed on described nonwoven fabric base cloth in order, and the coating weight of hot melt adhesive glue point on nonwoven fabric base cloth is 9-11 gram/every square metre.
Be compared with the prior art, the invention has the beneficial effects as follows:
1. the nonwoven fabric prepared by present invention process has delicate fragrance function, can cover sweat odor.
2. the nonwoven fabric prepared by present invention process has outstanding moisture pick-up properties and gas permeability, and this nonwoven fabric is used as collar support nonwoven fabric, can effectively play absorbing sweat effect, and good gas permeability can enable sweat be evaporated fast simultaneously, keeps neck salubrious.
3. the nonwoven fabric hardness prepared by present invention process is better, well-pressed as collar after collar support nonwoven fabric, not easily gauffer.
4. the cost of material adopted in the present invention is relatively cheap, is conducive to reducing costs.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1
A kind of compound type non-woven fabric collar support, grey cloth is nonwoven fabric base cloth, and the wherein one side of described nonwoven fabric base cloth is distributed with hot melt adhesive glue point, and each hot melt adhesive glue point is Dual-layer structure, it is hot melt adhesive basal layer at the middle and upper levels, and lower floor is hot melt adhesive adhesive layer; The material of described hot melt adhesive basal layer is polyurethane, and the material of described hot melt adhesive adhesive layer is polyesteramide.Described hot melt adhesive glue point is distributed on described nonwoven fabric base cloth in order, and the coating weight of hot melt adhesive glue point on nonwoven fabric base cloth is 9-11 gram/every square metre.
Wherein, the preparation technology of nonwoven fabric base cloth is as follows:
(1) get 8 parts of natural perfume materials and added in 1000 parts of water and be uniformly dispersed, then in solution, add 12 parts of galapectite powder obtain mixed liquor, after mixed liquor is left standstill 4h under vacuumized conditions, obtain through centrifugal, dry process the galapectite powder that load has natural perfume material.
The particle diameter of above-mentioned galapectite powder is 0.3-1 micron; Described natural perfume material is the mixture of sandalwood powder and camphortree leaf powder, and the particle diameter of natural perfume material is 50-80 nanometer; The relative molecular weight of described polyethylene glycol oxide is 800000-1200000; Described dispersant is polypropylene wax.
(2) separately get 7 parts of galapectite powder, 7 parts of aluminium chloride, 1 part of polyethylene glycol oxide, 4 parts of carboxymethyl celluloses, 1 part of dispersant, 3 parts of silane couplers have the galapectite powder of natural perfume material to mix with above-mentioned obtained load, obtain mixture;
(3) successively 135 parts of isotactic polypropylene sections, above-mentioned obtained mixtures are added to screw extruder and carry out melting, then obtain nonwoven fabric base cloth after spinning, drawing-off, one-tenth net, hot rolling;
Each step all substances number is parts by weight above.
Embodiment 2
A kind of compound type non-woven fabric collar support, grey cloth is nonwoven fabric base cloth, and the wherein one side of described nonwoven fabric base cloth is distributed with hot melt adhesive glue point, and each hot melt adhesive glue point is Dual-layer structure, it is hot melt adhesive basal layer at the middle and upper levels, and lower floor is hot melt adhesive adhesive layer; The material of described hot melt adhesive basal layer is polyurethane, and the material of described hot melt adhesive adhesive layer is polyesteramide.Described hot melt adhesive glue point is distributed on described nonwoven fabric base cloth in order, and the coating weight of hot melt adhesive glue point on nonwoven fabric base cloth is 9-11 gram/every square metre.
Wherein, the preparation technology of nonwoven fabric base cloth is as follows:
(1) get 8 parts of natural perfume materials and added in 1000 parts of water and be uniformly dispersed, then in solution, add 12 parts of galapectite powder obtain mixed liquor, after mixed liquor is left standstill 4h under vacuumized conditions, obtain through centrifugal, dry process the galapectite powder that load has natural perfume material.
After galapectite powder load natural perfume material, get Peppermint essential oil and in closed container, heating under reduced pressure is carried out to it, load being had the galapectite powder of natural perfume material to be positioned in closed container above Peppermint essential oil, take out after suffocating treatment 3h.
The preparation method of described Peppermint essential oil is as follows: get peppermint stem and leaf and grind it, after crossing 200 orders, getting 12 parts of peppermint stem and leaf powder, to add 100 parts of concentration to be in the ethanol water of 70wt%, then the ethanol water being added with peppermint stem and leaf powder is carried out microwave abstracting at microwave extracter, extraction conditions is microwave power 500W, extraction time 2h, extraction temperature 70 DEG C; Obtain peppermint extract after extraction, also carry out pressure reduction with classification distillation to described peppermint extract and obtain mint extract, then mint extract and ethanol are dissolved each other and obtain Peppermint essential oil, wherein the mass ratio of mint extract and ethanol is 3:7.
The particle diameter of above-mentioned galapectite powder is 0.5-2 micron, and galapectite powder is through acid activation process.Described natural perfume material is selected from the mixture into sandalwood powder and camphortree leaf powder, and the particle diameter of natural perfume material is 50-100 nanometer; The relative molecular weight of described polyethylene glycol oxide is 800000-1200000; Described dispersant is polypropylene wax.
(2) separately get 7 parts of galapectite powder, 7 parts of aluminium chloride, 1 part of polyethylene glycol oxide, 4 parts of carboxymethyl celluloses, 1 part of dispersant, 3 parts of silane couplers have the galapectite powder of natural perfume material to mix with above-mentioned obtained load, obtain mixture;
(3) successively 130 parts of isotactic polypropylene sections, above-mentioned obtained mixtures are added to screw extruder and carry out melting, then obtain nonwoven fabric base cloth after spinning, drawing-off, one-tenth net, hot rolling;
Each step all substances number is parts by weight above.
Embodiment 3
A kind of compound type non-woven fabric collar support, grey cloth is nonwoven fabric base cloth, and the wherein one side of described nonwoven fabric base cloth is distributed with hot melt adhesive glue point, and each hot melt adhesive glue point is Dual-layer structure, it is hot melt adhesive basal layer at the middle and upper levels, and lower floor is hot melt adhesive adhesive layer; The material of described hot melt adhesive basal layer is polyurethane, and the material of described hot melt adhesive adhesive layer is polyesteramide.Described hot melt adhesive glue point is distributed on described nonwoven fabric base cloth in order, and the coating weight of hot melt adhesive glue point on nonwoven fabric base cloth is 9-11 gram/every square metre.
Wherein, the preparation technology of nonwoven fabric base cloth is as follows:
(1) get 5 parts of natural perfume materials and added in 1000 parts of water and be uniformly dispersed, then in solution, add 10 parts of galapectite powder obtain mixed liquor, after mixed liquor is left standstill 3h under vacuumized conditions, obtain through centrifugal, dry process the galapectite powder that load has natural perfume material.
After galapectite powder load natural perfume material, get Peppermint essential oil and in closed container, heating under reduced pressure is carried out to it, load being had the galapectite powder of natural perfume material to be positioned in closed container above Peppermint essential oil, take out after suffocating treatment 4h.
The preparation method of described Peppermint essential oil is as follows: get peppermint stem and leaf and grind it, after crossing 200 orders, getting 10 parts of peppermint stem and leaf powder, to add 100 parts of concentration to be in the ethanol water of 60wt%, then the ethanol water being added with peppermint stem and leaf powder is carried out microwave abstracting at microwave extracter, extraction conditions is microwave power 600W, extraction time 2h, extraction temperature 75 DEG C; Obtain peppermint extract after extraction, also carry out pressure reduction with classification distillation to described peppermint extract and obtain mint extract, then mint extract and ethanol are dissolved each other and obtain Peppermint essential oil, wherein the mass ratio of mint extract and ethanol is 3:7.
The particle diameter of above-mentioned galapectite powder is 1-3 micron, and galapectite powder is through thermal activation treatment.Described natural perfume material is selected from as sandalwood powder, and the particle diameter of natural perfume material is 50-70 nanometer; The relative molecular weight of described polyethylene glycol oxide is 800000-1200000; Described dispersant is polypropylene wax.
(2) separately get 10 parts of galapectite powder, 5 parts of aluminium chloride, 1.5 parts of polyethylene glycol oxides, 5 parts of carboxymethyl celluloses, 0.5 part of dispersant, 2 parts of silane couplers have the galapectite powder of natural perfume material to mix with above-mentioned obtained load, obtain mixture;
(3) successively 150 parts of isotactic polypropylene sections, above-mentioned obtained mixtures are added to screw extruder and carry out melting, then obtain nonwoven fabric base cloth after spinning, drawing-off, one-tenth net, hot rolling;
Each step all substances number is parts by weight above.
Embodiment 4
A kind of compound type non-woven fabric collar support, grey cloth is nonwoven fabric base cloth, and the wherein one side of described nonwoven fabric base cloth is distributed with hot melt adhesive glue point, and each hot melt adhesive glue point is Dual-layer structure, it is hot melt adhesive basal layer at the middle and upper levels, and lower floor is hot melt adhesive adhesive layer; The material of described hot melt adhesive basal layer is polyurethane, and the material of described hot melt adhesive adhesive layer is polyesteramide.Described hot melt adhesive glue point is distributed on described nonwoven fabric base cloth in order, and the coating weight of hot melt adhesive glue point on nonwoven fabric base cloth is 9-11 gram/every square metre.
Wherein, the preparation technology of nonwoven fabric base cloth is as follows:
(1) get 10 parts of natural perfume materials and added in 1000 parts of water and be uniformly dispersed, then in solution, add 15 parts of galapectite powder obtain mixed liquor, after mixed liquor is left standstill 5h under vacuumized conditions, obtain through centrifugal, dry process the galapectite powder that load has natural perfume material.
After galapectite powder load natural perfume material, get Peppermint essential oil and in closed container, heating under reduced pressure is carried out to it, load being had the galapectite powder of natural perfume material to be positioned in closed container above Peppermint essential oil, take out after suffocating treatment 5h.
The preparation method of described Peppermint essential oil is as follows: get peppermint stem and leaf and grind it, after crossing 200 orders, getting 15 parts of peppermint stem and leaf powder, to add 100 parts of concentration to be in the ethanol water of 80wt%, then the ethanol water being added with peppermint stem and leaf powder is carried out microwave abstracting at microwave extracter, extraction conditions is microwave power 400W, extraction time 3h, extraction temperature 65 DEG C; Obtain peppermint extract after extraction, also carry out pressure reduction with classification distillation to described peppermint extract and obtain mint extract, then mint extract and ethanol are dissolved each other and obtain Peppermint essential oil, wherein the mass ratio of mint extract and ethanol is 3:7.
The particle diameter of above-mentioned galapectite powder is 1-3 micron, and galapectite powder is through thermal activation treatment.Described natural perfume material is selected from as sandalwood powder, and the particle diameter of natural perfume material is 50-70 nanometer; The relative molecular weight of described polyethylene glycol oxide is 800000-1200000; Described dispersant is polypropylene wax.
(2) separately get 10 parts of galapectite powder, 6 parts of aluminium chloride, 0.5 part of polyethylene glycol oxide, 4 parts of carboxymethyl celluloses, 1.5 parts of dispersants, 5 parts of silane couplers have the galapectite powder of natural perfume material to mix with above-mentioned obtained load, obtain mixture;
(3) successively 120 parts of isotactic polypropylene sections, above-mentioned obtained mixtures are added to screw extruder and carry out melting, then obtain nonwoven fabric base cloth after spinning, drawing-off, one-tenth net, hot rolling;
Each step all substances number is parts by weight above.
By the compound type non-woven fabric collar support that the inventive method is obtained, can be fragrant, and compared with common collar support, stiffness improves 20-40%, hygroscopic capacity improves about 10-13%, and moisture adsorption and releasing speed is fast.
The above; it is only preferred embodiment of the present invention; not the present invention is imposed any restrictions, every above embodiment is done according to the technology of the present invention essence any simple modification, change and equivalent transformation, all still belong to the protection domain of technical solution of the present invention.
Claims (9)
1. a compound type non-woven fabric collar support, grey cloth is nonwoven fabric base cloth, it is characterized in that: the wherein one side of described nonwoven fabric base cloth is distributed with hot melt adhesive glue point, and each hot melt adhesive glue point is Dual-layer structure, it is hot melt adhesive basal layer at the middle and upper levels, and lower floor is hot melt adhesive adhesive layer; The preparation technology of described nonwoven fabric base cloth is as follows:
(1) get 5-10 part natural perfume material and added in 1000 parts of water and be uniformly dispersed, then in solution, add 10-15 part galapectite powder obtain mixed liquor, after mixed liquor is left standstill 3-5h under vacuumized conditions, obtain through centrifugal, dry process the galapectite powder that load has natural perfume material;
(2) separately get 5-10 part galapectite powder, 5-10 part aluminium chloride, 0.5-1.5 part polyethylene glycol oxide, 3-5 part carboxymethyl cellulose, 0.5-1.5 part dispersant, 1-5 part silane coupler have the galapectite powder of natural perfume material to mix with above-mentioned obtained load, obtain mixture;
(3) successively the section of 120-150 part isotactic polypropylene, above-mentioned obtained mixture are added to screw extruder and carry out melting, then obtain nonwoven fabric base cloth after spinning, drawing-off, one-tenth net, hot rolling;
Each step all substances number is parts by weight above.
2. compound type non-woven fabric collar support as claimed in claim 1, it is characterized in that, the particle diameter of described galapectite powder is 0.3-3 micron, and described natural perfume material is selected from as one or more in sandalwood powder, camphortree leaf powder, and the particle diameter of natural perfume material is 50-100 nanometer.
3. compound type non-woven fabric collar support as claimed in claim 1, is characterized in that, one or both in acid activation process or thermal activation treatment of described galapectite powder.
4. compound type non-woven fabric collar support as claimed in claim 1, it is characterized in that, the relative molecular weight of described polyethylene glycol oxide is 800000-1200000.
5. compound type non-woven fabric collar support as claimed in claim 1, it is characterized in that, described dispersant is polypropylene wax.
6. compound type non-woven fabric collar support as claimed in claim 1, it is characterized in that, in step (1), after described galapectite powder load natural perfume material, also pass through further flavouring process, concrete grammar is as follows: get Peppermint essential oil and in closed container, carry out heating under reduced pressure to it, load is had the galapectite powder of natural perfume material to be positioned in closed container above Peppermint essential oil, takes out after suffocating treatment 2-4h.
7. compound type non-woven fabric collar support as claimed in claim 6, it is characterized in that, the preparation method of described Peppermint essential oil is as follows: get peppermint stem and leaf and grind it, after crossing 200 orders, getting 10-15 part peppermint stem and leaf powder, to add 100 parts of concentration to be in the ethanol water of 60-80wt%, and then the ethanol water being added with peppermint stem and leaf powder is carried out microwave abstracting at microwave extracter, extraction conditions is microwave power 400-600W, extraction time 1-3h, extraction temperature 60-75 DEG C; Obtain peppermint extract after extraction, also carry out pressure reduction with classification distillation to described peppermint extract and obtain mint extract, then mint extract and ethanol are dissolved each other and obtain Peppermint essential oil, wherein the mass ratio of mint extract and ethanol is 3:7; Above all substances number is parts by weight.
8. compound type non-woven fabric collar support as claimed in claim 1, it is characterized in that, the material of described hot melt adhesive basal layer is polyurethane, and the material of described hot melt adhesive adhesive layer is polyesteramide.
9. compound type non-woven fabric collar support as claimed in claim 1, it is characterized in that, described hot melt adhesive glue point is distributed on described nonwoven fabric base cloth in order, and the coating weight of hot melt adhesive glue point on nonwoven fabric base cloth is 9-11 gram/every square metre.