CN105088028A - Aluminium magnesium alloy - Google Patents
Aluminium magnesium alloy Download PDFInfo
- Publication number
- CN105088028A CN105088028A CN201510656940.0A CN201510656940A CN105088028A CN 105088028 A CN105088028 A CN 105088028A CN 201510656940 A CN201510656940 A CN 201510656940A CN 105088028 A CN105088028 A CN 105088028A
- Authority
- CN
- China
- Prior art keywords
- magnesium alloy
- aluminium
- aluminum magnesium
- manganese
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an aluminium magnesium alloy. The aluminium magnesium alloy comprises the following specific materials by weight percent: 12%-18% of magnesium, 78%-85% of aluminium, 1%-1.5% of calcium, 0.5%-0.8% of manganese, 0.5%-1% of ferrum and 0.5%-2% of copper. The aluminium magnesium alloy material prepared from the materials through the material proportion has the characteristics of being hard, light in weight, relatively strong in pressure resistance and well applicable to car body materials.
Description
Technical field
The present invention relates to technical field of metal, particularly relate to a kind of aluminum magnesium alloy.
Background technology
As a kind of important metal alloy compositions, hydronalium is widely used in daily life; Wherein, for aluminum magnesium alloy, its principal element is aluminium, then mixes a small amount of magnesium or other metallic substance to strengthen its hardness.Aluminum magnesium alloy essence take Mg as the aluminium alloy of main adding elements, because its corrosion stability is good, also known as rust-preventing aluminum alloy.Cause inherently metal, its heat conductivility and intensity are particularly outstanding.
Along with the development of automotive industry, automobile becomes the vehicles of a kind of family necessity gradually.Along with the environmental protection and energy saving of automobile require more and more higher, increasing automobile starts to adopt hydronalium to replace original steel.
Summary of the invention
The object of the present invention is to provide a kind of aluminum magnesium alloy, this aluminum magnesium alloy matter heavily fortified point amount is light and crushing resistance is comparatively strong, can be advantageously applied in body of a motor car material.
For achieving the above object, the present invention is achieved through the following technical solutions.
A kind of aluminum magnesium alloy, includes the material of following weight part, is specially:
Magnesium 12%-18%
Aluminium 78%-85%
Calcium 1%-1.5%
Manganese 0.5%-0.8%
Iron 0.5%-1%
Copper 0.5%-2%.
Further, this aluminum magnesium alloy includes the material of following weight part, is specially:
Magnesium 12%-16%
Aluminium 80%-85%
Calcium 1%-1.5%
Manganese 0.5%-0.8%
Iron 0.5%-1%
Copper 0.5%-1.5%.
Further, this aluminum magnesium alloy includes the material of following weight part, is specially:
Magnesium 15%
Aluminium 81%
Calcium 1%
Manganese 0.8%
Iron 1%
Copper 1.2%.
Beneficial effect of the present invention is: a kind of aluminum magnesium alloy of the present invention, and it includes the material of following weight part, is specially: magnesium 12%-18%, aluminium 78%-85%, calcium 1%-1.5%, manganese 0.5%-0.8%, iron 0.5%-1%, copper 0.5%-2%; By above-mentioned material proportion, the hydronalium be prepared from by above-mentioned material possesses matter heavily fortified point and measures light and that crushing resistance is stronger feature, namely can be advantageously applied in body of a motor car material.
Embodiment
Below in conjunction with concrete embodiment, the present invention will be described.
Embodiment one, a kind of aluminum magnesium alloy includes the material of following weight part, is specially:
Magnesium 15%
Aluminium 81%
Calcium 1%
Manganese 0.8%
Iron 1%
Copper 1.2%.
By above-mentioned material proportion, the aluminum magnesium alloy of the present embodiment one possesses matter heavily fortified point and measures light and that crushing resistance is stronger feature, namely can be advantageously applied in body of a motor car material.
Embodiment two, a kind of aluminum magnesium alloy includes the material of following weight part, is specially:
Magnesium 12%
Aluminium 85%
Calcium 1%
Manganese 0.5%
Iron 0.5%
Copper 1%.
By above-mentioned material proportion, the aluminum magnesium alloy of the present embodiment two possesses matter heavily fortified point and measures light and that crushing resistance is stronger feature, namely can be advantageously applied in body of a motor car material.
Embodiment three, a kind of aluminum magnesium alloy includes the material of following weight part, is specially:
Magnesium 18%
Aluminium 78%
Calcium 1%
Manganese 0.5%
Iron 1%
Copper 1.5%.
By above-mentioned material proportion, the aluminum magnesium alloy of the present embodiment three possesses matter heavily fortified point and measures light and that crushing resistance is stronger feature, namely can be advantageously applied in body of a motor car material.
Above content is only preferred embodiment of the present invention, and for those of ordinary skill in the art, according to thought of the present invention, all will change in specific embodiments and applications, this description should not be construed as limitation of the present invention.
Claims (3)
1. an aluminum magnesium alloy, is characterized in that, includes the material of following weight part, is specially:
Magnesium 12%-18%
Aluminium 78%-85%
Calcium 1%-1.5%
Manganese 0.5%-0.8%
Iron 0.5%-1%
Copper 0.5%-2%.
2. a kind of aluminum magnesium alloy according to claim 1, is characterized in that, includes the material of following weight part, is specially:
Magnesium 12%-16%
Aluminium 80%-85%
Calcium 1%-1.5%
Manganese 0.5%-0.8%
Iron 0.5%-1%
Copper 0.5%-1.5%.
3. a kind of aluminum magnesium alloy according to claim 2, is characterized in that, includes the material of following weight part, is specially:
Magnesium 15%
Aluminium 81%
Calcium 1%
Manganese 0.8%
Iron 1%
Copper 1.2%.