CN105086948A - 一种相变储热材料及其制备方法与应用以及相变储热装置 - Google Patents

一种相变储热材料及其制备方法与应用以及相变储热装置 Download PDF

Info

Publication number
CN105086948A
CN105086948A CN201510506394.2A CN201510506394A CN105086948A CN 105086948 A CN105086948 A CN 105086948A CN 201510506394 A CN201510506394 A CN 201510506394A CN 105086948 A CN105086948 A CN 105086948A
Authority
CN
China
Prior art keywords
change heat
storage material
phase
phase change
heat storage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510506394.2A
Other languages
English (en)
Other versions
CN105086948B (zh
Inventor
栗世芳
栗世明
白因必力
辛双全
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hannover smart energy technology (Inner Mongolia) Co.,Ltd.
Original Assignee
栗世芳
栗世明
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 栗世芳, 栗世明 filed Critical 栗世芳
Priority to CN201510506394.2A priority Critical patent/CN105086948B/zh
Publication of CN105086948A publication Critical patent/CN105086948A/zh
Application granted granted Critical
Publication of CN105086948B publication Critical patent/CN105086948B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种相变储热材料及其制备方法与应用以及相变储热装置。一种相变储热材料，由以下质量份数的原料组成：60-75份的水合盐、0.5-3份的成核剂、1-3份的防过冷剂、1-3份的分相防止剂、1-5份的导热增强材料、1-5份的稀土化合物。其制备方法为：将各种原料混合，并熔融、混匀，冷却后研磨成粉即可。相变储热材料在集热器中的应用。一种相变储热装置，由壳体与设置在壳体中的相变储热材料组成。本发明的相变储热材料具有较高的相变潜热，毒性小，腐蚀性弱；本发明将相变储热材料封装在壳体内，再将壳体放置在集热器内，避免了相变储热材料直接接触集热器的器壁导致的腐蚀或结垢问题；本发明的相变导热材料在太阳能发电领域，具有较好的应用前景。

Description

一种相变储热材料及其制备方法与应用以及相变储热装置
技术领域
本发明涉及一种相变储热材料及其制备方法与应用以及相变储热装置。
背景技术
相变储热材料具有较为独特的潜热性能：在物相变化的过程中，可从外界环境中吸收热量或放出热量，因此，可以实现出储热的功能。在现有技术中，应用较广泛的为：固液相变材料以及固固相变材料。固液相变材料的特点是廉价，但缺点也很明显，例如腐蚀容器，容易泄露，容易分相或者存在过冷现象。
另一方面，石油危机，使得世界各国加强了清洁能源和新能源的开发力度，包括太阳能发电等，太阳能发电系统通常是利用反射镜将阳光反射聚焦到集热器上，集热器再将辐射能转变为热能，然后传导至集热器中的工作介质，进而蒸发水产生动力。现有技术中，往往将熔盐作为集热器中的工作介质；但由于熔盐直接放置在集热器内，容易堵住或结垢，或者腐蚀集热器器壁。
发明内容
本发明的目的在于提供一种相变储热材料及其制备方法与应用以及相变储热装置。
本发明所采取的技术方案是：
一种相变储热材料，由以下质量份数的原料组成：60-75份的水合盐、0.5-3份的成核剂、1-3份的防过冷剂、1-3份的分相防止剂、1-5份的导热增强材料、1-5份的稀土化合物。
所述的水合盐为三水合醋酸钠、十水合硫酸钠、十水合碳酸钠、五水合硫代硫酸钠、十二水合磷酸氢钠中的至少一种。
所述的成核剂为所述的成核剂为活性炭、二氧化硅中的至少一种。
所述的防过冷剂为硼砂。
所述的分相防止剂为交联聚丙烯酸钠。
所述的导热增强材料为石墨、碳粉、金属粉中的至少一种。
将各种原料混合，并熔融、混匀，冷却后研磨成粉即可。
所述的相变储热材料在集热器中的应用。
一种相变储热装置，由壳体与设置在壳体中的相变储热材料组成。
所述的壳体的表面的几何性质为：包含至少一个不可导的点；或者，所述的壳体为棒状壳体。
本发明的有益效果是：
本发明的相变储热材料具有较高的相变潜热，毒性小，腐蚀性弱；
本发明将相变储热材料封装在壳体内，再将壳体放置在集热器内，避免了相变储热材料直接接触集热器的器壁导致的腐蚀或结垢问题；
本发明的相变导热材料在太阳能发电领域，具有较好的应用前景。
具体实施方式
一种相变储热材料，由以下质量份数的原料组成：60-75份的水合盐、0.5-3份的成核剂、1-3份的防过冷剂、1-3份的分相防止剂、1-5份的导热增强材料、1-5份的稀土化合物。
优选的，所述的水合盐为三水合醋酸钠、十水合硫酸钠、十水合碳酸钠、五水合硫代硫酸钠、十二水合磷酸氢钠中的至少一种；进一步优选的，为三水合醋酸钠、十水合硫酸钠、十水合碳酸钠质量比为1:(0.8-1.2):(0.8-1.2)的混合物。
优选的，所述的成核剂为所述的成核剂为活性炭、二氧化硅中的至少一种。
优选的，所述的防过冷剂为硼砂。
优选的，所述的分相防止剂为交联聚丙烯酸钠。
优选的，所述的导热增强材料为石墨、碳粉、金属粉中的至少一种；进一步优选的，为石墨。
优选的，所述的稀土化合物为稀土盐或稀土氧化物，稀土氧化物如氧化镧、氧化铈、氧化铕等；稀土盐如硝酸镧、硝酸铈、氯化铈等。
该储热材料的制备方法为：将各种原料混合，并熔融、混匀，冷却后研磨成粉即可。
所述的相变储热材料在集热器中的应用。
一种相变储热装置，由壳体与设置在壳体中的相变储热材料组成。
优选的，所述的壳体的表面的几何性质为：包含至少一个不可导的点；进一步优选的，为多面体如八面体或六面体；或者，所述的壳体为棒状壳体。
下面结合具体实施例对本发明做进一步的说明：
实施例1：
一种相变储热材料，由以下质量份数的原料组成：60份的水合盐（三水合醋酸钠、十水合硫酸钠、十水合碳酸钠质量比为1:1:1的混合物）、0.5份的成核剂活性炭、1份的防过冷剂硼砂、1份的分相防止剂交联聚丙烯酸钠、1份的导热增强材料石墨、1份的稀土化合物硝酸铈。
该相变储热材料的制备方法为：将各种原料混合，并熔融、混匀，冷却后研磨成粉即可。
一种相变储热装置，由壳体与设置在壳体中的上述相变储热材料组成；所述的壳体为正八面体。
实施例2：
一种相变储热材料，由以下质量份数的原料组成：75份的水合盐（三水合醋酸钠、十水合硫酸钠、十水合碳酸钠质量比为1:1:1的混合物）、3份的成核剂活性炭、3份的防过冷剂硼砂、3份的分相防止剂交联聚丙烯酸钠、5份的导热增强材料石墨、5份的稀土化合物硝酸铈。
该相变储热材料的制备方法为：将各种原料混合，并熔融、混匀，冷却后研磨成粉即可。
一种相变储热装置，由壳体与设置在壳体中的上述相变储热材料组成；所述的壳体为正八面体。
实施例3：
一种相变储热材料，由以下质量份数的原料组成：72份的水合盐（三水合醋酸钠、十水合硫酸钠、十水合碳酸钠质量比为1:1:1的混合物）、2份的成核剂活性炭、2份的防过冷剂硼砂、2份的分相防止剂交联聚丙烯酸钠、2份的导热增强材料石墨、2份的稀土化合物（硝酸铈、硝酸镧质量比1:1的混合物）。
该相变储热材料的制备方法为：将各种原料混合，并熔融、混匀，冷却后研磨成粉即可。
一种相变储热装置，由壳体与设置在壳体中的上述相变储热材料组成；所述的壳体为正六面体。
本发明实施例1-3制备的相变储热材料的相变潜热为150-155J/g，相变范围是395-402℃。

Claims (10)

1.一种相变储热材料，由以下质量份数的原料组成：60-75份的水合盐、0.5-3份的成核剂、1-3份的防过冷剂、1-3份的分相防止剂、1-5份的导热增强材料、1-5份的稀土化合物。
2.根据权利要求1所述的一种相变储热材料，其特征在于：所述的水合盐为三水合醋酸钠、十水合硫酸钠、十水合碳酸钠、五水合硫代硫酸钠、十二水合磷酸氢钠中的至少一种。
3.根据权利要求1所述的一种相变储热材料，其特征在于：所述的成核剂为所述的成核剂为活性炭、二氧化硅中的至少一种。
4.根据权利要求1所述的一种相变储热材料，其特征在于：所述的防过冷剂为硼砂。
5.根据权利要求1所述的一种相变储热材料，其特征在于：所述的分相防止剂为交联聚丙烯酸钠。
6.根据权利要求1所述的一种相变储热材料，其特征在于：所述的导热增强材料为石墨、碳粉、金属粉中的至少一种。
7.权利要求1-6中任一项所述的一种相变储热材料的制备方法，其特征在于：将各种原料混合，并熔融、混匀，冷却后研磨成粉即可。
8.权利要求1-6所述的相变储热材料在集热器中的应用。
9.一种相变储热装置，其特征在于：由壳体与设置在壳体中的相变储热材料组成，所述的相变储热材料为权利要求1-6所述的相变储热材料。
10.根据权利要求9所述的一种相变储热装置，其特征在于：所述的壳体的表面的几何性质为：包含至少一个不可导的点；或者，所述的壳体为棒状壳体。
CN201510506394.2A 2015-08-18 2015-08-18 一种相变储热材料及其制备方法与应用以及相变储热装置 Active CN105086948B (zh)