CN105063851A - Manufacturing process of rice fiber fabric - Google Patents
Manufacturing process of rice fiber fabric Download PDFInfo
- Publication number
- CN105063851A CN105063851A CN201510461557.XA CN201510461557A CN105063851A CN 105063851 A CN105063851 A CN 105063851A CN 201510461557 A CN201510461557 A CN 201510461557A CN 105063851 A CN105063851 A CN 105063851A
- Authority
- CN
- China
- Prior art keywords
- rice
- paddy
- manufacture craft
- fibers fabric
- fermentation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing process of a rice fiber fabric. The manufacturing process comprises the following steps: (1)a rice stalk and a rice husk are selected as a raw material and then cleaning is carried out; (2), a zymophyte solution is prepared and fermentation treatment is carried out on the rice stalk and the rice husk to obtain a rice element after fermentation; (3), the rice element after fermentation is dried at a drying tower; (4), the dried rice element is processed by high-temperature treatment to manufacture a rice colloidal solution; and (5), the rice colloidal solution and a cotton fiber solution are mixed and then a spinning process, a cloth weaving process, and a printing and dyeing process are carried out to obtain a rice fiber fabric. According to the technical scheme, the operation is simple; the manufacturing process is easy to master; the obtained fiber fabric is flexible and soft; the hygroscopicity and air permeability are high.
Description
Technical field
The present invention relates to field of textiles, particularly relate to a kind of manufacture craft of rice fibers fabric.
Background technology
China is that rice does one of with the longest history, that rice genetic resource is the abundantest country, and Monitoring of Paddy Rice Plant Area is many, except good harvest rice, also can produce some adjuncts, and as dry in a large amount of paddy and rice husk, if irrational utilization, will pollute the environment.
Summary of the invention
The technical problem that the present invention mainly solves is to provide that a kind of soft comfortable, gas permeability are strong, the manufacture craft of the rice fibers fabric of good hygroscopicity.
For solving the problems of the technologies described above, the invention provides a kind of manufacture craft of rice fibers fabric, comprising the following steps:
(1) choose paddy bar and rice hulls as raw material, it cleaned,
(2) prepare zymocyte liquid, and fermentation process carried out to above-mentioned paddy bar and rice hulls, obtain the paddy element after fermenting,
(3) the paddy element after above-mentioned fermentation is carried out drying and processing by drying tower,
(4) paddy of above-mentioned oven dry element is passed through high-temperature process, obtained paddy colloidal solution,
(5) above-mentioned paddy colloidal solution is mixed with cotton fiber solution, and by spinning process, weaving process, dyeing and printing process, obtained rice fibers fabric.
In a preferred embodiment of the present invention, described zymocyte liquid and water proportion dilute according to the ratio of 1:100.
In a preferred embodiment of the present invention, described drying and processing temperature controls at 300-500 degree Celsius, and drying time period is 2-3 hour.
In a preferred embodiment of the present invention, described paddy colloidal solution mixes according to the proportion of 1:3 with cotton fiber solution blend gravity.
In a preferred embodiment of the present invention, described spinning process comprise blowing, comb and parallel cotton fibers prior to spinning, pre-also, rove and post processing.
The invention has the beneficial effects as follows: the manufacture craft of rice fibers fabric of the present invention, simple to operate, be convenient to control, the fabric lining soft comfortable knitted, good hygroscopicity, gas permeability is strong, purposes is wide.
Detailed description of the invention
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
The embodiment of the present invention comprises:
A manufacture craft for rice fibers fabric, comprises the following steps:
(1) choose paddy bar and rice hulls as raw material, it cleaned,
(2) prepare zymocyte liquid, and fermentation process carried out to above-mentioned paddy bar and rice hulls, obtain the paddy element after fermenting,
(3) the paddy element after above-mentioned fermentation is carried out drying and processing by drying tower,
(4) paddy of above-mentioned oven dry element is passed through high-temperature process, obtained paddy colloidal solution,
(5) above-mentioned paddy colloidal solution is mixed with cotton fiber solution, and by spinning process, weaving process, dyeing and printing process, obtained rice fibers fabric.
In addition, described zymocyte liquid and water proportion dilute according to the ratio of 1:100, and fermentation efficiency is high, quality good.
In addition, described drying and processing temperature controls at 300-500 degree Celsius, and drying time period is 2-3 hour.
In addition, described paddy colloidal solution mixes according to the proportion of 1:3 with cotton fiber solution blend gravity, the fabric lining soft comfortable of this ratio, good hygroscopicity.
In addition, described spinning process comprise blowing, comb and parallel cotton fibers prior to spinning, pre-also, rove and post processing, identical with normal spinning process, do not need to add more equipment, convenient operation.
Be different from prior art, the manufacture craft of rice fibers fabric of the present invention, simple to operate, be convenient to control, the fabric lining soft comfortable knitted, good hygroscopicity, gas permeability are strong.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. a manufacture craft for rice fibers fabric, is characterized in that, comprises the following steps:
(1) choose paddy bar and rice hulls as raw material, it cleaned,
(2) prepare zymocyte liquid, and fermentation process carried out to above-mentioned paddy bar and rice hulls, obtain the paddy element after fermenting,
(3) the paddy element after above-mentioned fermentation is carried out drying and processing by drying tower,
(4) paddy of above-mentioned oven dry element is passed through high-temperature process, obtained paddy colloidal solution,
(5) above-mentioned paddy colloidal solution is mixed with cotton fiber solution, and by spinning process, weaving process, dyeing and printing process, obtained rice fibers fabric.
2. the manufacture craft of rice fibers fabric according to claim 1, is characterized in that, described zymocyte liquid and water proportion dilute according to the ratio of 1:100.
3. the manufacture craft of rice fibers fabric according to claim 1, is characterized in that, described drying and processing temperature controls at 300-500 degree Celsius, and drying time period is 2-3 hour.
4. the manufacture craft of rice fibers fabric according to claim 1, is characterized in that, described paddy colloidal solution mixes according to the proportion of 1:3 with cotton fiber solution blend gravity.
5. the manufacture craft of rice fibers fabric according to claim 1, is characterized in that, described spinning process comprise blowing, comb and parallel cotton fibers prior to spinning, pre-also, rove and post processing.