CN105060822A - Wear-resistant floor material and preparation method thereof - Google Patents
Wear-resistant floor material and preparation method thereof Download PDFInfo
- Publication number
- CN105060822A CN105060822A CN201510499418.6A CN201510499418A CN105060822A CN 105060822 A CN105060822 A CN 105060822A CN 201510499418 A CN201510499418 A CN 201510499418A CN 105060822 A CN105060822 A CN 105060822A
- Authority
- CN
- China
- Prior art keywords
- wear
- parts
- terrace material
- resisting terrace
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A wear-resistant floor material is prepared from raw materials in parts by weight as follows: 20-30 parts of nickel slag, 20-30 parts of coal gangue, 1-3 parts of a water reducer, 20-30 parts of cement, 5-10 parts of white cement, 3-8 parts of colored paint, 5-7 parts of epoxy acrylate, 5-7 parts of an anaerobic adhesive and 0.5-1 part of a defoaming agent. According to the wear-resistant floor material, industrial waste residues are used as raw materials, so that the cost is low, and the production technology and equipment are simple. Thus, the wear-resistant floor material prepared from industrial solid waste used as aggregate has good economic benefit, social benefit and environmental benefit and is suitable for industrial production, popularization and application.
Description
Technical field
The present invention relates to a kind of Wear-resisting terrace material and preparation method thereof, belong to waste ' s reclamation and material of construction fabricating technology field.
Background technology
Nickel slag is a kind of industrial residue discharged in the process of smelting ferronickel alloy, Rhometal is mainly used as producing stainless steel, thus nickel slag is also referred to as stainless steel slag or ferronickel slag, because China constantly increased substantially to stainless steel demand in recent years, thus a large amount of solid slags is also created, but these waste residues are not fully utilized, a large amount of air storage is around smeltery, not only occupy valuable land resources, and pollute environment around, thus the utilization of resources of nickel slag becomes pressing issues.
Coal gangue is the solid waste discharged in coal mining process and coal washing process, what affect Land resources utilizes coal gangue storage yard multidigit near well head, most next-door neighbour Residential areas, a large amount of stackings of coal gangue take a large amount of land areas on the one hand, also affecting than stacking the larger land resources of area on the other hand, make the arable land of surrounding become barren, can not be utilized.The air storage of atmosphere pollution coal gangue can produce a large amount of airborne dust, and this is mainly due to after the coal gangue of ground stacking is exposed to the sun and rain for a long time, will weathering pulverize; In addition, meeting disintegration after coal gangue water suction, thus be easy to produce dust.Under the action of the forces of the wind, the quality of mining area air will be worsened.
Terrace is the part of bottom and soil layer joint, requires to have very high intensity and hardness, and has protection against the tide, waterproof, warming, wear-resisting performance.At present, market being applied maximum is pvc industry ground slab and epoxy floor, and resistant to pressure, wear-resisting, erosion resistance is poor, and therefore their work-ing life is shorter, is difficult to the requirement meeting special engineering technology.The present invention utilizes nickel slag and coal gangue as aggregate to prepare wear-resisting floor material; not only there is the feature of the resistance to chemical attack that intensity is high, wear resistance good, shrinking percentage is little and good; and the new way of the industrial gaseous waste prepared using opened; protect physical environment, save resource and the energy.
Summary of the invention
The object of the invention is in order to solve traditional abrasion-proof terrace intensity low, wear no resistance, the problem such as resistance property difference, and provide a kind of Wear-resisting terrace material and preparation method thereof.
Described object is achieved by the following scheme:
A kind of Wear-resisting terrace material, be prepared from by following ratio of weight and number, nickel slag 20-30 part, coal gangue 20-30 part, water reducer 1-3 part, cement 20-30 part, white cement 5-10 part, colo(u)r coating 3-8 part, epoxy acrylate 5-7 part, anaerobic glue 5-7 part, defoamer 0.5-1 part.
Described a kind of Wear-resisting terrace material, nickel slag is the nickel slag that iron-holder is greater than 8%.
Described a kind of Wear-resisting terrace material, the median size of nickel slag is 5-10mm.
Described a kind of Wear-resisting terrace material, water reducer is SN-II type water reducer.
Described a kind of Wear-resisting terrace material, coal gangue particle diameter is 5-30mm.
Described a kind of Wear-resisting terrace material, cement is ordinary Portland cement.
Described a kind of Wear-resisting terrace material, defoamer is a kind of nonionogenic tenside containing polyoxyethylene glycol and inorganic carrier, is white powder.
Preparation method, according to formula weigh batching respectively, dilutes with warm water respectively by epoxy acrylate and anaerobic glue, mix and blend after dilution, forms the glue of high strength, each raw material is put into mixing machine uniform stirring, then add the glue of appropriate mixing water and high strength, stir.
Wear-resisting terrace material of the present invention has following characteristics:
1. the present invention utilizes nickel slag and coal gangue to make Wear-resisting terrace material; not only there is the features such as the resistance to chemical attack that intensity is high, wear resistance good, shrinking percentage is little and good; but also open the new way of a recycling for industrial solid castoff; while protecting environment, also a saving natural resources.
2. the present invention with the addition of the shrinking percentage that water reducer, epoxy acrylate, anaerobic glue and defoamer decrease product, enhances the intensity of product, has preservative efficacy, ensure that its weather resistance.
3. the present invention with the addition of colo(u)r coating, increases the individualized selection of user, enhances the decorative effect of building.
Embodiment
Elaborate the preferred embodiment of the present invention below.
embodiment 1:
A kind of Wear-resisting terrace material, be prepared from by following ratio of weight and number, nickel slag 20-30 part, coal gangue 20-30 part, water reducer 1-3 part, cement 20-30 part, white cement 5-10 part, colo(u)r coating 3-8 part, epoxy acrylate 5-7 part, anaerobic glue 5-7 part, defoamer 0.5-1 part.Preparation method is shown in embodiment 2.
embodiment 2:
A kind of Wear-resisting terrace material, clicks ratio of weight and number and is prepared from, nickel slag 20 parts, coal gangue 25 parts, water reducer 3 parts, cement 30 parts, white cement 5 parts, colo(u)r coating 3 parts, epoxy acrylate 5 parts, anaerobic glue 7 parts, defoamer 0.8 part.
preparation method:
According to formula weigh batching respectively, epoxy acrylate and anaerobic glue are diluted with warm water respectively, mix and blend after dilution, form the glue of high strength, each raw material is put into mixing machine uniform stirring, then adds the glue of appropriate mixing water and high strength, stir.
The concrete of the Wear-resisting terrace material prepared by this method and equal label compares in table 1.
Table one
| Title | 28d is anti-tears intensity/MPa open | 28d ultimate compression strength/MPa | Wear-resistant length/mm |
| Normal concrete | 3.5 | 35 | 37 |
| Wear-resisting terrace material | 3.75 | 37 | 34 |
embodiment 3:
A kind of Wear-resisting terrace material, clicks ratio of weight and number and is prepared from, nickel slag 25 parts, coal gangue 30 parts, water reducer 2 parts, cement 20 parts, white cement 8 parts, colo(u)r coating 8 parts, epoxy acrylate 7 parts, anaerobic glue 6 parts, defoamer 1 part.Preparation method is shown in embodiment 2.
The concrete of the Wear-resisting terrace material prepared by this method and equal label compares in table 2.
Table two
| Title | 28d is anti-tears intensity/MPa open | 28d ultimate compression strength/MPa | Wear-resistant length/mm |
| Normal concrete | 3.6 | 36 | 36.9 |
| Wear-resisting terrace material | 3.9 | 38 | 34.2 |
embodiment 4:
A kind of Wear-resisting terrace material, clicks ratio of weight and number and is prepared from, nickel slag 30 parts, coal gangue 20 parts, water reducer 1 part, cement 25 parts, white cement 10 parts, colo(u)r coating 5 parts, epoxy acrylate 6 parts, anaerobic glue 5 parts, defoamer 0.5 part.Preparation method is shown in embodiment 2.
The concrete of the Wear-resisting terrace material prepared by this method and equal label compares in table 3.
Table three
| Title | 28d is anti-tears intensity/MPa open | 28d ultimate compression strength/MPa | Wear-resistant length/mm |
| Normal concrete | 4.2 | 4.21 | 36.5 |
| Wear-resisting terrace material | 4.6 | 4.66 | 33 |
The present invention because of use industrial residue be raw material, with low cost, production technique and equipment simple.Therefore, utilize and as Wear-resisting terrace material prepared by aggregate, there is good economic benefit, social benefit and environmental benefit by industrial solid castoff, be suitable for suitability for industrialized production and apply.
Present embodiment does not just limit its protection domain to the exemplary illustration of this patent; those skilled in the art can also carry out local to it and change; as long as no the spirit exceeding this patent, be all considered as the equivalent replacement to this patent, all within the protection domain of this patent.
Claims (8)
1. a Wear-resisting terrace material, it is characterized in that: be prepared from by following ratio of weight and number, nickel slag 20-30 part, coal gangue 20-30 part, water reducer 1-3 part, cement 20-30 part, white cement 5-10 part, colo(u)r coating 3-8 part, epoxy acrylate 5-7 part, anaerobic glue 5-7 part, defoamer 0.5-1 part.
2. a kind of Wear-resisting terrace material according to claim 1, is characterized in that: nickel slag is the nickel slag that iron-holder is greater than 8%.
3. a kind of Wear-resisting terrace material according to claim 1, is characterized in that: the median size of nickel slag is 5-10mm.
4. a kind of Wear-resisting terrace material according to claim 1, is characterized in that: water reducer is SN-II type water reducer.
5. a kind of Wear-resisting terrace material according to claim 1, is characterized in that: coal gangue particle diameter is 5-30mm.
6. a kind of Wear-resisting terrace material according to claim 1, is characterized in that: cement is ordinary Portland cement.
7. a kind of Wear-resisting terrace material according to claim 1, is characterized in that: defoamer is a kind of nonionogenic tenside containing polyoxyethylene glycol and inorganic carrier, is white powder.
8. the preparation method of a Wear-resisting terrace material, it is characterized in that: formula according to claim 1 is weigh batching respectively, epoxy acrylate and anaerobic glue are diluted with warm water respectively, mix and blend after dilution, form the glue of high strength, each raw material is put into mixing machine uniform stirring, then adds the glue of appropriate mixing water and high strength, stir.