CN105039954A - Preparation method for steel surface treatment agent - Google Patents
Preparation method for steel surface treatment agent Download PDFInfo
- Publication number
- CN105039954A CN105039954A CN201510301221.7A CN201510301221A CN105039954A CN 105039954 A CN105039954 A CN 105039954A CN 201510301221 A CN201510301221 A CN 201510301221A CN 105039954 A CN105039954 A CN 105039954A
- Authority
- CN
- China
- Prior art keywords
- steel
- parts
- steel surface
- treatment agent
- surface treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method for a steel surface treatment agent and belongs to the field of metal surface treatment. The method includes the steps that firstly, polysiloxane, sodium pyrophosphate, potassium sorbate and sodium dodecyl sulfate are acquired to be mixed, deionized water is added to a mixture, the mixture is stirred evenly and heated to be at the temperature of 50 DEG C under the stirring condition, and the temperature is kept for 20 min; secondly, a solution acquired in the first step is cooled to be at the temperature of 25 DEG C and polyurethane and aluminum oxide are added and stirred for 10 min; and thirdly, caffeic acid and zinc nitrate are added to a solution acquired in the second step and evenly stirred so that the steel surface treatment agent can be acquired. The steel surface treatment agent is used for treating the surface of steel, a dense protective film can be formed on the surface of the steel, the surface of the steel is effectively prevented from being corroded by the external environment, the anti-oxidation capacity and the anti-corrosion capacity of the steel are enhanced, the luster of the surface of the steel can still be maintained after the steel is placed in air for a long time, and the treatment agent is free of pollution to the environment, degradable, low in cost, safe in use and beneficial to utilization and popularization.
Description
Technical field
The invention belongs to field of metal surface treatment, specifically, relate to a kind of preparation method of steel surface processing agent.
Background technology
Iron and steel is material the most frequently used in life, and the application of steel product in life is seen everywhere, but oxidation, corrosion etc. in various degree often can occur steel product in processing, process and use procedure, thus reduces work-ing life, waste metals resources.Therefore, need to process steel surface, increase its anti-oxidant, erosion-resisting ability, increase the service life.Steel corrosion is generally divided into chemical corrosion and galvanic corrosion, chemical corrosion: the corrosion that metallic surface and surrounding medium directly chemical reaction occur and cause.Galvanic corrosion: metallic substance (alloy or impure metal) and electrolyte solution contacts, the corrosion produced by electrode reaction.There is gap due to existing defects or surface in iron and steel, is easy to be corroded in external environment, therefore needs the defect that a kind of iron and steel treatment agent exists to make up iron and steel itself, reduces the corrosion of iron and steel and the waste of metals resources.
Summary of the invention
the problem that 1, will solve
Inevitable defect is there is for existing steel surface, corrosion-vulnerable, cause the problem of the waste of metals resources, the invention provides a kind of preparation method of steel surface processing agent, effectively can prevent oxidation, the corrosion of iron and steel, environmental pollution is minimum, can not damage HUMAN HEALTH in use procedure, and cost is low, be easy to promote.
2, technical scheme
For solving the problem, technical scheme of the present invention is:
A preparation method for steel surface processing agent, the steps include:
A () gets the mixing of 6-10 part polysiloxane, 1-3 part trisodium phosphate, 0.5-2.5 part potassium sorbate and 3-5 part sodium laurylsulfonate by mass fraction, add 70-80 part deionized water, stir, be under agitation heated to 50 DEG C, insulation 20min;
B solution that step (a) obtains by () is cooled to 25 DEG C, adds 3-8 part urethane and 8-12 part aluminum oxide, stirs 10min;
Add 2-5 part coffic acid and 1-3 part zinc nitrate in c solution that () obtains to step (b), stir and obtain steel surface processing agent.
Preferably, described polyoxy silane and the granular size of aluminum oxide are nano level.
Preferably, its component and massfraction as follows:
Polysiloxane 8 parts;
Trisodium phosphate 1 part;
Potassium sorbate 2.5 parts;
Sodium laurylsulfonate 5 parts;
Coffic acid 4 parts;
Urethane 8 parts;
8 parts, aluminum oxide;
Zinc nitrate 1 part;
Deionized water 75 parts.
3, beneficial effect
Compared to prior art, beneficial effect of the present invention is:
(1) treatment agent that prepared by the present invention is made up of polysiloxane, sodium phosphate, potassium sorbate, sodium laurylsulfonate, coffic acid, urethane, aluminum oxide, zinc nitrate and deionized water, this treatment agent is used to carry out steel surface processing the density that can improve steel surface, make up defect and the gap of iron and steel existence itself, effectively prevent the oxidation of steel surface, corrosion, keep steel surface light;
(2) the present invention use polyoxy silane and aluminum oxide, the protective membrane of one deck densification can be formed at steel surface, effectively prevent external environment to the infringement of iron and steel, what urethane can make polyoxy silane and alumina stable is attached to steel surface, plays the effect of lasting protection;
(3) low, the degradable of cost of the present invention, use safety, environmentally safe, is conducive to well promoting the use of.
embodiment:
Specific embodiment introduces the present invention in detail below.
embodiment 1
A kind of preparation method of steel surface processing agent, the steps include: that (a) gets 8 parts of polysiloxane, 1 part of trisodium phosphate, 2.5 parts of potassium sorbate and 5 parts of sodium laurylsulfonate mixing by mass fraction, add 75 parts of deionized waters, stir, under agitation be heated to 50 DEG C, insulation 20min; B solution that step (a) obtains by () is cooled to 25 DEG C, adds 8 parts of urethane and 8 parts of aluminum oxide, stirs 10min; Add 4 parts of coffic acids and 1 part of zinc nitrate in c solution that () obtains to step (b), stir and obtain steel surface processing agent.
Use the stainless steel work-piece of process of the present invention than not having extend 5 months the work-ing life processed, long-time exposure still can keep surface-brightening in atmosphere, the material erosion resistance of oxygenant and acid-basicity is significantly strengthened, waste water readily biodegradable after process, environmentally safe, and healthy harmless to operator.
embodiment 2
With embodiment 1, difference is the content of each material: polysiloxane 6 parts; Trisodium phosphate 2 parts; Potassium sorbate 0.5 part; Sodium laurylsulfonate 3 parts; Coffic acid 5 parts; Urethane 3 parts; 12 parts, aluminum oxide; Zinc nitrate 2 parts and deionized water 80 parts.
Use the stainless steel work-piece of process of the present invention than not having extend 4 months the work-ing life processed, long-time exposure still can keep surface-brightening in atmosphere, the material erosion resistance of oxygenant and acid-basicity is significantly strengthened, waste water readily biodegradable after process, environmentally safe, and healthy harmless to operator.
embodiment 3
With embodiment 1, difference is the content of each material: polysiloxane 10 parts; Trisodium phosphate 3 parts; Potassium sorbate 1 part; Sodium laurylsulfonate 4 parts; Coffic acid 2 parts; Urethane 6 parts; 9 parts, aluminum oxide; Zinc nitrate 3 parts and deionized water 70 parts.
Use the stainless steel work-piece of process of the present invention than not having extend 3 months the work-ing life processed, long-time exposure still can keep surface-brightening in atmosphere, the material erosion resistance of oxygenant and acid-basicity is significantly strengthened, waste water readily biodegradable after process, environmentally safe, and healthy harmless to operator.
Claims (3)
1. a preparation method for steel surface processing agent, the steps include:
A () gets the mixing of 6-10 part polysiloxane, 1-3 part trisodium phosphate, 0.5-2.5 part potassium sorbate and 3-5 part sodium laurylsulfonate by mass fraction, add 70-80 part deionized water, stir, be under agitation heated to 50 DEG C, insulation 20min;
B solution that step (a) obtains by () is cooled to 25 DEG C, adds 3-8 part urethane and 8-12 part aluminum oxide, stirs 10min;
Add 2-5 part coffic acid and 1-3 part zinc nitrate in c solution that () obtains to step (b), stir and obtain steel surface processing agent.
2. the preparation method of a kind of steel surface processing agent according to claim 1, is characterized in that, described polyoxy silane and the granular size of aluminum oxide are nano level.
3. the preparation method of a kind of steel surface processing agent according to claim 1, is characterized in that, component and massfraction as follows:
Polysiloxane 8 parts;
Trisodium phosphate 1 part;
Potassium sorbate 2.5 parts;
Sodium laurylsulfonate 5 parts;
Coffic acid 4 parts;
Urethane 8 parts;
8 parts, aluminum oxide;
Zinc nitrate 1 part;
Deionized water 75 parts.