CN105038423A - Derusting antirust colored heavy-duty single-component primer and production technique thereof - Google Patents
Derusting antirust colored heavy-duty single-component primer and production technique thereof Download PDFInfo
- Publication number
- CN105038423A CN105038423A CN201510512608.7A CN201510512608A CN105038423A CN 105038423 A CN105038423 A CN 105038423A CN 201510512608 A CN201510512608 A CN 201510512608A CN 105038423 A CN105038423 A CN 105038423A
- Authority
- CN
- China
- Prior art keywords
- parts
- derusting
- priming paint
- heavy antisepsis
- rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a derusting antirust colored heavy-duty single-component primer and a production technique thereof. The primer comprises the following components in parts by weight: 5-20 parts of deionized water, 20-25 parts of derusting rust inhibitor, 2-8 parts of film formation assistant, 2-4 parts of antifreezing agent, 0.1-0.2 part of thickener, 3-10 parts of color paste, 0.3-1 part of defoaming agent, 40-70 parts of film forming matter, 3-5 parts of adhesion modifier and 0.3-0.6 part of substrate wetting agent. The production technique comprises the following steps: mixing the components, and stirring and dispersing in a stainless steel reaction kettle; and after all the indexes are qualified through detection and the stirring is finished, filtering through a 100-mesh filter screen, and packaging. The 1318 or KX-123 product is used as the derusting rust inhibitor, the H602 emulsion is used as the film former, and the film formation assistant, substrate wetting agent, imported color paste and other pollution-free assistants are added to prepare the water-based environment-friendly derusting antirust colored single-component primer. The primer has the advantages of accessible raw materials, derusting labor saving, high antirust property, high safety, environment friendliness and high corrosion resistance.
Description
Technical field
The present invention relates to anti-corrosive primer coating in one, be specifically related in the irony base material heavy antisepsis fields such as a kind of water-based steel construction can derusting rust-proofing band look heavy antisepsis single-component priming paint.
Background technology
The amount that water-based anticorrosive paint uses at present in the usage quantity in heavy antisepsis field is also very low, and reason is complicated with many-sided.Some user is comparatively conservative, is unwilling to attempt based on new technology coating products; Still little at the environmental regulation of industrial circle; Compared with solvent based coating, the price of water-borne coatings is higher, poor-performing, has some to use limitation.Water-borne coatings using water as the benefit of solvent and thinner be obvious, not only cheap, and there is no poison, there is no smell, so there is no danger of detonating on fire, HUMAN HEALTH is also safe from harm.
The aqueous heavy anti-corrosion paint priming paint used in the market has aqueous inorganic zinc rich paint, aqueous double-component epoxy-based lacquers, alkyd or acrylic acid epoxy ester aqueous priming paint etc., pre-treatment requirement is there is high in construction process, easily cause and dodge rust, two component construction trouble, rate of drying is slow, the defects such as price is high, and VOC content is high.
Summary of the invention
Goal of the invention: the present invention is directed to deficiency of the prior art, propose a kind of safety, environmental protection, fast drying, can eliminate rust, strong, strong to metal adhesion, the water-fast salt-fog resistant time length of antirust ability can meet the high derusting rust-proofing band look heavy antisepsis single-component priming paint of the requirement of heavy antisepsis priming paint, paint film intensity hardness and production technique thereof.
Technical scheme: a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint of the present invention, comprises the component of following parts by weight:
Deionized water 5 ~ 20 parts
Rust-removing and-preventing agent 20 ~ 25 parts
Film coalescence aid 2 ~ 8 parts
Frostproofer 2 ~ 4 parts
Thickening material 0.1 ~ 0.2 part
Mill base 3 ~ 10 parts
Defoamer 0.3 ~ 1 part
Filmogen 40 ~ 70 parts
Sticking power properties-correcting agent 3 ~ 5 parts
Substrate wetting agents 0.3 ~ 0.6 part.
Further, described rust-removing and-preventing agent 1318 iron and steel protective material or kx-123 iron and steel protective material.
Further, described film coalescence aid adopts the one in alcohol ester 12, butyl glycol ether, propylene glycol monomethyl ether.
Further, described frostproofer adopts propylene glycol or glycol ether.
Further, described thickening material adopts 2% xanthan gum or polyethylene alcohol ether.
Further, described defoamer adopts sieve sub-DN-642 in ground or BASF 2410.
Further, described filmogen adopts vinyl multiple copolymer H602 emulsion, and solid content is 60%.
Further, described sticking power properties-correcting agent adopts GEM-03 epoxy resin.
Further, described substrate wetting agents adopts the peaceful 165F of a surname.
Further, described mill base adopts black color paste.
The invention also discloses a kind of production technique of derusting rust-proofing band look heavy antisepsis single-component priming paint: mix after being prepared by mass parts by each feed composition, and in stainless steel cauldron dispersed with stirring, dispersed with stirring 30 minutes, rotating speed is 500-800 rev/min; After the qualified rear stirring of indices detection terminates, 100 order filter screen filtration packagings.
Beneficial effect: the present invention relates to a kind of water-based heavy antisepsis single-component derusting rust-proofing band color bottom paint and preparation method thereof; it adopts metal-derusting; oil removing; phosphatization; passivation four-in-one iron and steel protective material carrys out alternative rust-stabilising pigment; the vinyl multi-copolymer emulsion produced with our company is for film forming matter; water is thinner; and be equipped with multiple auxiliary agent and filler is prepared from; it has safety, environmental protection, fast drying, can eliminate rust, and strong, strong to metal adhesion, the water-fast salt-fog resistant time length of antirust ability can meet the requirement of heavy antisepsis priming paint, paint film intensity hardness high.And more save time in construction, laborsaving, comprehensive cost is low, is widely used in the heavy antisepsis aspects such as steel construction, boats and ships, bridge, metallurgy, chemical industry equipment manufacture and maintenance, can substitutes zinc rich paint, two component epoxy priming paint.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A kind of derusting rust-proofing band look heavy antisepsis single-component priming paint, comprises the component of following parts by weight:
Deionized water 5 parts
1318 iron and steel protective materials 20 parts
Alcohol ester 12 parts
Propylene glycol 2 parts
2% xanthan gum 0.1 part
Black color paste 3 parts
The sub-DN-6420.3 part in sieve ground
H602 emulsion 40 parts
GEM-03 epoxy resin 3 parts
Declare peaceful 165F0.3 part.
The production technique of above-mentioned a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint: mix after each feed composition is prepared by mass parts, and in stainless steel cauldron dispersed with stirring, dispersed with stirring 30 minutes, rotating speed is 500-800 rev/min; After the qualified rear stirring of indices detection terminates, 100 order filter screen filtration packagings.
Embodiment 2
A kind of derusting rust-proofing band look heavy antisepsis single-component priming paint, comprises the component of following parts by weight:
Deionized water 20 parts
Kx-123 iron and steel protective material 25 parts
Butyl glycol ether 8 parts
Propylene glycol 4 parts
Polyethylene alcohol ether 0.2 part
Black color paste 10 parts
BASF 24101 parts
H602 emulsion 70 parts
GEM-03 epoxy resin 5 parts
Declare peaceful 165F0.6 part.
The production technique of above-mentioned a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint: mix after each feed composition is prepared by mass parts, and in stainless steel cauldron dispersed with stirring, dispersed with stirring 30 minutes, rotating speed is 500-800 rev/min; After the qualified rear stirring of indices detection terminates, 100 order filter screen filtration packagings.
Embodiment 3
A kind of derusting rust-proofing band look heavy antisepsis single-component priming paint, comprises the component of following parts by weight:
Deionized water 12 parts
1318 iron and steel protective materials 22 parts
Propylene glycol monomethyl ether 5 parts
Glycol ether 3 parts
2% xanthan gum 0.15 part
Black color paste 6 parts
The sub-DN-6420.6 part in sieve ground
H602 emulsion 45 parts
GEM-03 epoxy resin 4 parts
Declare peaceful 165F0.4 part.
The production technique of above-mentioned a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint: mix after each feed composition is prepared by mass parts, and in stainless steel cauldron dispersed with stirring, dispersed with stirring 30 minutes, rotating speed is 500-800 rev/min; After the qualified rear stirring of indices detection terminates, 100 order filter screen filtration packagings.
Following form is the technical indicator of above-mentioned three embodiments:
Derusting rust-proofing band look heavy antisepsis single-component priming paint of the present invention preferably exposes steel substrate when eliminating rust, and rusty scale can not be too thick, is generally suitable at 10-20 micron, is preferably used in hot-rolled steel sheet, above the section bars such as angle steel.Base material temperature can not be too high, many brushes several times time rust is heavy.
When carrying out pipeline corrosion protection, Specific construction mode is as follows:
1. substrate treatment: the floating rust that pipeline loosens, old paint film simple process are fallen, the iron rust of adhere firmly need not polish off completely;
2. be coated on pipeline with the product that the present invention is prepared by the technique of brushing and brush second time after three hours, paint film complete drying after 24 hours, μm total build >=40 μm, per pass build >=20, reach construction requirement completely through inspection.
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, although the present invention discloses as above with preferred embodiment, but and be not used to limit the present invention, any those skilled in the art, do not departing within the scope of technical solution of the present invention, make a little change when the technology contents of above-mentioned announcement can be utilized or be modified to the Equivalent embodiments of equivalent variations, in every case be the content not departing from technical solution of the present invention, according to any simple modification that technical spirit of the present invention is done above embodiment, equivalent variations and modification, all still belong in the scope of technical solution of the present invention.
Claims (10)
1. a derusting rust-proofing band look heavy antisepsis single-component priming paint, is characterized in that: the component comprising following parts by weight:
Deionized water 5 ~ 20 parts
Rust-removing and-preventing agent 20 ~ 25 parts
Film coalescence aid 2 ~ 8 parts
Frostproofer 2 ~ 4 parts
Thickening material 0.1 ~ 0.2 part
Mill base 3 ~ 10 parts
Defoamer 0.3 ~ 1 part
Filmogen 40 ~ 70 parts
Sticking power properties-correcting agent 3 ~ 5 parts
Substrate wetting agents 0.3 ~ 0.6 part.
2. a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint according to claim 1, is characterized in that: described rust-removing and-preventing agent adopts 1318 iron and steel protective materials or kx-123 iron and steel protective material.
3. a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint according to claim 1, is characterized in that: described film coalescence aid adopts the one in alcohol ester 12, butyl glycol ether, propylene glycol monomethyl ether.
4. a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint according to claim 1, is characterized in that: described frostproofer adopts propylene glycol or glycol ether.
5., according to a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint according to claim 1, it is characterized in that: described thickening material adopts 2% xanthan gum or polyethylene alcohol ether.
6. according to a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint according to claim 1, it is characterized in that: described defoamer adopts sieve sub-DN-642 in ground or BASF 2410.
7. according to a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint according to claim 1, it is characterized in that: described filmogen adopts vinyl multiple copolymer H602 emulsion, and solid content is 60%.
8. according to a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint according to claim 1, it is characterized in that: described sticking power properties-correcting agent adopts GEM-03 epoxy resin.
9. according to a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint according to claim 1, it is characterized in that: described substrate wetting agents adopts the peaceful 165F of a surname.
10. the production technique of a kind of derusting rust-proofing band look heavy antisepsis single-component priming paint according to arbitrary one of claim 1-9, it is characterized in that: mix after each feed composition is prepared by mass parts, and in stainless steel cauldron dispersed with stirring, dispersed with stirring 30 minutes, rotating speed is 500-800 rev/min; After the qualified rear stirring of indices detection terminates, 100 order filter screen filtration packagings.