CN105034305A - Plastic wrapping steel belt manufacturing method - Google Patents
Plastic wrapping steel belt manufacturing method Download PDFInfo
- Publication number
- CN105034305A CN105034305A CN201510553068.7A CN201510553068A CN105034305A CN 105034305 A CN105034305 A CN 105034305A CN 201510553068 A CN201510553068 A CN 201510553068A CN 105034305 A CN105034305 A CN 105034305A
- Authority
- CN
- China
- Prior art keywords
- steel band
- plastic
- plastic cement
- encapsulate
- steel belt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plastic wrapping steel belt manufacturing method, which comprises the following steps: preparation, a steel belt is prepared, and the steel belt is released at one end and is collected at the other end; preheating, the part, which is to be subjected to plastic wrapping, of the steel belt is preheated; plastic smearing, the steel belt which passes a die head is smeared with plastic by a plastic extruder and the die head according to a requirement, wherein a PVC/ABS/PE/EVA material or other material is adopted as the plastic; and cooling, the steel belt which is smeared with the plastic is cooled. According to the method, preparation, preheating, plastic smearing and cooling working procedures are adopted for assembly line type automatic production of steel belt plastic wrapping; compared with the existing handwork baking and curing method, the method has the advantages that the production efficiency is greatly improved; the health of a worker is prevented from being damaged by the existing production method; and the quality of a finished product can be improved.
Description
Technical field
The present invention relates to a kind of encapsulate steel band manufacture method.
Background technology
Encapsulate steel band is a kind of product worked in the presence of a harsh environment, and require the work of its energy long-time stable, encapsulate steel band outer surface needs to adopt corrosion resistant plastic cement material for this reason.The production method of existing encapsulate steel band is that then baking-curing is on steel band by being sprinkled upon on steel band by powder, and production efficiency is extremely low, indirectly adds production cost, for this reason, the invention provides a kind of encapsulate steel band manufacture method for solving the problem.
Summary of the invention
In order to solve the problem, the invention provides a kind of encapsulate steel band manufacture method.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of encapsulate steel band manufacture method, comprises the following steps:
A, preparation, prepare steel band, steel band is broadcasted in one end, and the other end receives steel band;
B, preheating, carry out preheating to the steel band part being about to carry out encapsulate;
C, smear plastic cement, by a plastic extruder and die head, the steel band to die head of passing through smears plastic cement on request;
D, cooling, cool smearing the steel band after plastic cement.
Also comprise a cleaning process between described step a and b, wiping is carried out to steel band, after wiping, again steel band is smeared the reagent being beneficial to steel band and plastic cement bonding.
In described step c, die head is provided with the through hole passed through for steel band, and the sidewall of through hole is provided with into glue passage, and enter glue passage end and be connected with plastic extruder, the other end is communicated with through hole.
Described steps d comprises warm water shower cooling and cold water soak cooling, is first tentatively cooled being coated with the steel band wiping plastic cement by warm water shower, is more thoroughly cooled steel band by cold water soak.
Also comprise water suction step and a printing step between described warm water shower cooling and cold water soak cooling, by after the surface moisture of the cooled steel band of warm water shower is removed, then print set information on plastic cement.
Described plastic cement adopts PVC or ABS or PE or EVA material.
The invention has the beneficial effects as follows: the present invention is by adopting preparation, preheating, smearing plastic cement and refrigerating work procedure carries out pipeline system automated production to steel band encapsulate, the production efficiency of relatively existing manual baking-curing method increases substantially, existing production method can be stopped to cause a hidden trouble to staff's health simultaneously, improve end product quality.
Accompanying drawing explanation
Below in conjunction with drawings and Examples, the present invention is further described:
Fig. 1 is schematic flow sheet of the present invention.
Detailed description of the invention
With reference to Fig. 1, the present invention is a kind of encapsulate steel band manufacture method, comprises the following steps:
A, preparation, prepare steel band, steel band is broadcasted in one end, and the other end receives steel band;
B, preheating, carry out preheating to the steel band part being about to carry out encapsulate;
C, smear plastic cement, by a plastic extruder and die head, the steel band to die head of passing through smears plastic cement on request, wherein plastic cement adopt PVC or ABS or PE or EVA material or other;
D, cooling, cool smearing the steel band after plastic cement.
The present invention is by adopting preparation, preheating, smearing plastic cement and refrigerating work procedure carries out pipeline system automated production to steel band encapsulate, the production efficiency of relatively existing manual baking-curing method increases substantially, existing production method can be stopped to cause a hidden trouble to staff's health simultaneously, improve end product quality.
As shown in the figure, a cleaning process is also comprised between step a and b, wiping is carried out to steel band, again steel band is smeared the reagent being beneficial to steel band and plastic cement bonding after wiping, in the sordid situation of steel strip surface, first the dirty of steel strip surface is cleaned out by cleaning process, and then smear reagent in steel strip surface, the bonding firmness of steel band and plastic cement can be increased further.
As shown in the figure, in step c, die head is provided with the through hole passed through for steel band, and the sidewall of through hole is provided with into glue passage, and enter glue passage end and be connected with plastic extruder, the other end is communicated with through hole.The setting of plastic extruder and die head can realize being coated on by plastic cement rapidly and uniformly passing through on the steel band of die head, and before thoroughly solving, the poor efficiency of baking-curing powder is produced.
As shown in the figure, steps d comprises warm water shower cooling and cold water soak cooling, is first tentatively cooled being coated with the steel band wiping plastic cement by warm water shower, is more thoroughly cooled steel band by cold water soak.Cool twice cooling through above-mentioned warm water shower cooling and cold water soak and fast by plastic cement cooling forming, and can not affect the performance of plastic cement.
As shown in the figure, between warm water shower cooling and cold water soak cooling, also comprise water suction step and a printing step, by after the surface moisture of the cooled steel band of warm water shower is removed, then print set information on plastic cement.Appointed information can be printed on plastic cement in printing step.
Above-described embodiment is preferred version of the present invention, and the present invention also can have other embodiments.Those skilled in the art also can make equivalent variations or replacement under the prerequisite without prejudice to spirit of the present invention, and these equivalent modification or replacement are all included in the scope set by the application's claim.
Claims (6)
1. an encapsulate steel band manufacture method, is characterized in that comprising the following steps:
A, preparation, prepare steel band, steel band is broadcasted in one end, and the other end receives steel band;
B, preheating, carry out preheating to the steel band part being about to carry out encapsulate;
C, smear plastic cement, by a plastic extruder and die head, the steel band to die head of passing through smears plastic cement on request;
D, cooling, cool smearing the steel band after plastic cement.
2. a kind of encapsulate steel band manufacture method as claimed in claim 1, is characterized in that also comprising a cleaning process between described step a and b, carries out wiping to steel band, steel band is smeared the reagent being beneficial to steel band and plastic cement bonding after wiping again.
3. a kind of encapsulate steel band manufacture method as claimed in claim 1, it is characterized in that in described step c, die head is provided with the through hole passed through for steel band, the sidewall of through hole is provided with into glue passage, and enter glue passage end and be connected with plastic extruder, the other end is communicated with through hole.
4. a kind of encapsulate steel band manufacture method as claimed in claim 1, it is characterized in that described steps d comprises warm water shower cooling and cold water soak cooling, first tentatively cooled being coated with the steel band wiping plastic cement by warm water shower, then by cold water soak, steel band is thoroughly cooled.
5. a kind of encapsulate steel band manufacture method as claimed in claim 4, it is characterized in that also comprising water suction step and a printing step between described warm water shower cooling and cold water soak cooling, by after the surface moisture of the cooled steel band of warm water shower is removed, then print set information on plastic cement.
6. a kind of encapsulate steel band manufacture method as claimed in claim 1, is characterized in that described plastic cement adopts PVC or ABS or PE or EVA material.