CN105002691A - High-strength rayon-based activated carbon fiber fabric - Google Patents
High-strength rayon-based activated carbon fiber fabric Download PDFInfo
- Publication number
- CN105002691A CN105002691A CN201510305769.9A CN201510305769A CN105002691A CN 105002691 A CN105002691 A CN 105002691A CN 201510305769 A CN201510305769 A CN 201510305769A CN 105002691 A CN105002691 A CN 105002691A
- Authority
- CN
- China
- Prior art keywords
- viscose
- carbon fiber
- fiber fabric
- strength
- activated carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength rayon-based activated carbon fiber fabric. Viscose is used as base material, and the high-strength rayon-based activated carbon fiber fabric is obtained by fire retardant soaking, squeezing, drying, carbonization and excitation. The fineness of the viscose is 6D, the viscose is composed of 55 to 65% of wood pulp, 20 to 30% of cotton pulp, 1 to 5% of polyacrylonitrile and margin pitch fibers. The high-strength rayon-based activated carbon fiber fabric has the advantages of being high in strength, long in service life, being able to resist washing and good in working performance.
Description
Technical field
The present invention relates to a kind of viscose-based active carbon fiber fabric.
Background technology
Along with the development of industry, protecting and improving human environment becomes a urgent task of the mankind; Along with the national style of economic increase changes to intensive style from extensive style, improve economic growth benefit and service of goods quality, reduce the outstanding feature that environmental pollution has become measurement modern enterprise.
The performance how improving active carbon fibre dimensional fabric is a vital task of this area.
Summary of the invention
The object of the present invention is to provide that a kind of intensity is large, the high-strength viscose-based active carbon fiber fabric of long service life.
Technical solution of the present invention is:
A kind of high-strength viscose-based active carbon fiber fabric, is characterized in that: adopt viscose as base material, obtains through dipping fire retardant, extruding drying, charing, activation; The fineness of described viscose is 6D, is made up of the pitch fibers of wood pulp 55 ~ 65%, cotton pulp 20-30%, 1-5% polyacrylonitrile and surplus.
The fineness of described viscose is 6D, is made up of the pitch fibers of wood pulp 58%, cotton pulp 25%, 5% polyacrylonitrile and surplus.
The fineness of described viscose is 6D, is made up of the pitch fibers of wood pulp 60%, cotton pulp 30%, 3% polyacrylonitrile and surplus.
Product strength of the present invention is high, long service life, wash resistant, and service behaviour is excellent.
Below in conjunction with embodiment, the invention will be further described.
Detailed description of the invention
Embodiment 1: a kind of high-strength viscose-based active carbon fiber fabric, adopts viscose as base material, obtains through dipping fire retardant, extruding drying, charing, activation; The fineness of described viscose is 6D, is made up of the pitch fibers of wood pulp 58%, cotton pulp 25%, 5% polyacrylonitrile and surplus.
Embodiment 2: the fineness of described viscose is 6D, is made up of the pitch fibers of wood pulp 60%, cotton pulp 30%, 3% polyacrylonitrile and surplus.All the other are with embodiment 2.
Claims (3)
1. a high-strength viscose-based active carbon fiber fabric, is characterized in that: adopt viscose as base material, obtains through dipping fire retardant, extruding drying, charing, activation; The fineness of described viscose is 6D, is made up of the pitch fibers of wood pulp 55 ~ 65%, cotton pulp 20-30%, 1-5% polyacrylonitrile and surplus.
2. high-strength viscose-based active carbon fiber fabric according to claim 1, is characterized in that: the fineness of described viscose is 6D, is made up of the pitch fibers of wood pulp 58%, cotton pulp 25%, 5% polyacrylonitrile and surplus.
3. high-strength viscose-based active carbon fiber fabric according to claim 1, is characterized in that: the fineness of described viscose is 6D, is made up of the pitch fibers of wood pulp 60%, cotton pulp 30%, 3% polyacrylonitrile and surplus.