CN104993154A - Graphene-containing lead alloy for lead storage battery grids, and preparation method thereof - Google Patents
Graphene-containing lead alloy for lead storage battery grids, and preparation method thereof Download PDFInfo
- Publication number
- CN104993154A CN104993154A CN201510266049.6A CN201510266049A CN104993154A CN 104993154 A CN104993154 A CN 104993154A CN 201510266049 A CN201510266049 A CN 201510266049A CN 104993154 A CN104993154 A CN 104993154A
- Authority
- CN
- China
- Prior art keywords
- lead
- graphene
- calcium
- centrifugal blender
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a graphene-containing lead alloy for lead storage battery grids. The graphene-containing lead alloy includes 0.015-0.15% of graphene, 1.0-1.5% of tin, 0.02-0.04% of aluminum, 0.05-0.1% of calcium and 98.21-98.915% of lead. A preparation method of the graphene-containing lead alloy comprises the following steps: putting 2/3 of lead in a lead melting pot, and heating to 680DEG C in order to melt lead; adding graphene to molten lead; adding pure tin strips and pure aluminum strips 20min later, and stirring and mixing for above 0.5h; adding lead sheath packaged calcium, pressing calcium into the bottom of the molten lead by using a bell jar with the bottom provided with leakage holes, slowly stirring and mixing for above 0.5h when the molten lead does not bubble, adding the residual lead into the lead melting pot, continuously stirring after the lead is completely molten, and carrying out ingot casting 1h later. The preparation method has the advantages of simplicity, reliability, simple structure of a used device, and low cost; and the grids made by using the lead alloy prepared through the method have strong creep and corrosion resistance, and can meet deep cycle and heavy current charge and discharge requirements.
Description
Technical field
The invention belongs to Lead-acid Battery Technology field, relate to a kind of lead accumulator grid lead alloy containing Graphene and preparation method thereof.
Background technology
In recent years, along with the deterioration of environment, green energy resource just more and more causes the concern of society, one of effective way that electric automobile and micro-mixed automobile address this problem just.The reliable lead acid accumulator of with low cost, technology maturation as traditional electrical source of power also anxious pending technological improvement to adapt to the development need of electric automobile.The performance of lead acid accumulator depends primarily on pole plate, and grid is then the important component part of pole plate, determines the useful life, dehydration, large current discharging capability etc. of battery.The battery of plumbous antimony cadmium positive grid alloy manufacture has the feature of resistance to deeper cavity charging and discharging capabilities, is accepted extensively by market, but due to the cadmium element in lead-antimony alloy very large to harm, forbidden producing and using by China; At present, the alloy that lead acid accumulator plate grid the most generally uses is lead-calcium alloy, owing to easily forming the phenomenon of pore in the grid ubiquity cast panel process of lead-calcium alloy, grid creep-resistant property and corrosion resistant performance poor, easily the shortcomings such as barrier layer are formed after battery deep discharge, cannot meet the requirement of deeper cavity and high current charge-discharge, useful life is short.
Graphene is a kind of new material of the individual layer laminated structure be made up of carbon atom.Be a kind ofly form with sp2 hybridized orbit the flat film that hexangle type is honeycomb lattice by carbon atom, only have the two-dimensional material of a carbon atom thickness.The scientific circles that appear at of Graphene have evoked huge great waves, it is found that, Graphene has excellent electric conductivity, exceeds the intensity of iron and steel decades of times and fabulous light transmission, for improving lead alloy and lead plaster performance provides strong support.Say in theory, Graphene is mixed in storage battery lead alloy, utilize the electric conductivity of Graphene excellence and strength character can increase substantially the high rate during charging-discharging of pole plate and the creep resistant of grid and decay resistance, but be how perplex the key factor that lead carbon battery develops by the graphene dispersion of nano material to differing with its proportion in larger lead alloy always.At present, though there are some to relate to the preparation method of Graphene lead alloy, have plenty of and directly Graphene is mixed with other metal oxide, then carry out redox, generate Graphene foundry alloy; Have plenty of by by graphite and strong acid or other Strong oxdiative material by carry out after be oxidized ultrasonic disperse or HTHP instantaneously voltage drop method be prepared into graphene oxide, then to restore after graphene oxide is mixed with the oxide of other metal as Graphene foundry alloy; The plumbous liquid finally Graphene foundry alloy being placed in melting is made.There is following problem in these preparation methods: 1, relates to a large amount of and the smelting of specialty, combination reaction equipment and raw material, and to the sealing of equipment, bearing capacity, workshop condition etc. require very strict, and general lead alloy factory cannot realize.2, reduction reaction is chronic, and often need dozens of hour even more of a specified duration, need HTHP, oxygen-free environment, technical difficulty is larger, is difficult to universal production.
Summary of the invention
Object of the present invention solves problems of the prior art exactly, a kind of lead accumulator grid lead alloy containing Graphene and preparation method thereof is provided, the grid creep resistant that this lead alloy is made and corrosion resistant performance strong, the requirement of deeper cavity and high current charge-discharge can be met, mechanical strength is high, long service life; This preparation method is simple and reliable, and the device structure of use is simple, and cost is low.
For achieving the above object, technical scheme of the present invention is: a kind of lead accumulator grid lead alloy containing Graphene, counts by weight percentage, it comprises the Graphene of 0.015 ~ 0.15%, the tin of 1.0 ~ 1.5%, the aluminium of 0.02 ~ 0.04%, the calcium of 0.05 ~ 0.1% and the lead of 98.21 ~ 98.915%.
Graphene described above is one or more in single-layer graphene, bilayer graphene, few layer graphene or graphene microchip.Described Graphene can adopt physical method to produce, and chemical method also can be adopted to produce.
The preparation method of the lead accumulator grid lead alloy containing Graphene described above, it comprises the following steps:
(1) lead of 2/3 of described amount is inserted in market pot, be heated to 680 ° of C and melt completely to lead; (2) then open centrifugal blender, slowly add the Graphene of described amount continuously or be interrupted interpolation in batches joining in plumbous liquid when moderate-speed mixer; After (3) 20 minutes, successively add pure tin bar and the fine aluminium bar of described amount, centrifugal blender continues to be uniformly mixed half an hour more than; (4) close centrifugal blender, add the calcium encapsulated with sheet lead of described amount, the calcium bottom of being encapsulated by sheet lead has the bell jar of small opening to be pressed into bottom plumbous liquid, when plumbous liquid no longer bubbling time, start centrifugal blender low rate mixing mixing; (5) after half an hour, close centrifugal blender, the lead of surplus is added in market pot, treats that lead melts completely, open centrifugal blender, continue low rate mixing, ingot casting after a hour.
The feature of a kind of lead accumulator grid lead alloy containing Graphene of the present invention and preparation method thereof is:
1, by after graphene uniform blending is in lead-calcium alloy, Graphene is in the alloy with grid configuration existence closely, form favourable conductive mesh, after being made into grid, it is inner and surperficial that the conductive network that Graphene is formed spreads all over whole grid, and the Graphene on surface directly contacts with active material, can suitably reduce grid surface corrosion condition, the conductive network that Graphene is formed and active material and alloy grid compact siro spinning technology, thoroughly solve PCL-1, PCL-2, PCL-3.In addition, Graphene, at grid Intranet lattice distribution, adds its distinctive mechanical strength, can be used as the skeletal support of grid, strengthens grid mechanical strength.In a word, the battery grid that the Graphene lead alloy that adopts manufacture method of the present invention to make makes, effectively can strengthen the conductance of grid, improves the mechanical strength of grid, and in the process of battery high current charge-discharge in the future, grid is not yielding, lead plaster difficult drop-off.Graphene add the phenomenon suitably alleviating grid surface oxide etch in battery use procedure, and thoroughly can solve shortcoming grid electric conductivity being declined because of corrosion layer, and then enhance battery charging and discharging serviceability and cycle life.
2, the preparation method of a kind of lead accumulator grid lead alloy containing Graphene of the present invention, do not recycle redox mode and make Graphene foundry alloy, but Graphene finished product is added in the process of allotment lead-calcium alloy, mechanical agitation in addition, Graphene and metal is made to form eutectic, it not only can be dispersed in Graphene in lead-calcium alloy well, and whole preparation process only needs to complete for 3 to 4 hours, compare other redox mode and make Graphene alloy and can save 5 ~ 15 hours;
3, whole preparation process only needs market pot and some simple mechanical stirring devices to realize, compare some other redox mode and make in the preparation process of Graphene alloy a large amount of professional smelting equipment and combination reaction equipment that need, the equipment wanted required for the present invention and technical conditions are simply and easily realize, the conventional production equipment smelting factory at lead alloy can complete, and relative cost reduces a lot.
Embodiment
Below in conjunction with embodiment and experiment detect the present invention is described further:
Embodiment 1, a kind of lead accumulator grid lead alloy containing Graphene, calculate by weight, it comprises the Graphene of 0.015%, the tin of 1.0%, the aluminium of 0.02%, the sponge calcium of 0.05% and the lead of 98.915%.Its preparation method comprises the following steps: the electrolytic lead of 2/3 of described amount is inserted in market pot by (1), is heated to 680 ° of C and melts completely to electrolytic lead; (2) then open centrifugal blender, slowly add the Graphene of described amount continuously or be interrupted interpolation in batches joining in plumbous liquid when moderate-speed mixer; After (3) 20 minutes, successively add pure tin bar and the fine aluminium bar of described amount, centrifugal blender continues to be uniformly mixed half an hour more than; (4) centrifugal blender is closed; add the sponge calcium encapsulated with sheet lead of described amount; the sponge calcium bottom of being encapsulated by sheet lead has the bell jar of small opening to be pressed into bottom plumbous liquid; encapsulate with sheet lead when adding sponge calcium, then have the bell jar of small opening to be pressed into bottom plumbous liquid with bottom, allow sponge calcium slowly melt bottom plumbous liquid; because calcium is very active metal; at high temperature easy firing loss, encapsulates with sheet lead for this reason before addition, to reduce the loss of sponge calcium.When plumbous liquid no longer bubbling time, start centrifugal blender low rate mixing mixing; (5) after half an hour, the electrolytic lead of surplus is added in market pot, lead to be electrolysed melts completely, continues to stir, ingot casting after a hour.Graphene described above is one or more in single-layer graphene, bilayer graphene, few layer graphene or graphene microchip.Graphene can adopt physical method to produce, and chemical method also can be adopted to produce.
Embodiment 2, a kind of lead accumulator grid lead alloy containing Graphene, count by weight percentage, it comprises the Graphene of 0.03%, the tin of 1.2%, the aluminium of 0.04%, the sponge calcium of 0.08% and the lead of 98.65%.Its preparation method comprises the following steps: the electrolytic lead of 2/3 of described amount is inserted in market pot by (1), is heated to 680 ° of C and melts completely to electrolytic lead; (2) then open centrifugal blender, slowly add the Graphene of described amount continuously or be interrupted interpolation in batches joining in plumbous liquid when moderate-speed mixer; After (3) 20 minutes, successively add pure tin bar and the fine aluminium bar of described amount, centrifugal blender continues to be uniformly mixed half an hour more than; (4) centrifugal blender is closed; add the sponge calcium encapsulated with sheet lead of described amount; the sponge calcium bottom of being encapsulated by sheet lead has the bell jar of small opening to be pressed into bottom plumbous liquid; encapsulate with sheet lead when adding sponge calcium, then have the bell jar of small opening to be pressed into bottom plumbous liquid with bottom, allow sponge calcium slowly melt bottom plumbous liquid; because calcium is very active metal; at high temperature easy firing loss, encapsulates with sheet lead for this reason before addition, to reduce the loss of sponge calcium.When plumbous liquid no longer bubbling time, start centrifugal blender low rate mixing mixing; (5) after half an hour, the electrolytic lead of surplus is added in market pot, lead to be electrolysed melts completely, continues to stir, ingot casting after a hour.Graphene described above is one or more in single-layer graphene, bilayer graphene, few layer graphene or graphene microchip.Graphene can adopt physical method to produce, and chemical method also can be adopted to produce.
Embodiment 3, a kind of lead accumulator grid lead alloy containing Graphene, count by weight percentage, it comprises the Graphene of 0.06%, the tin of 1.2%, the aluminium of 0.04%, the sponge calcium of 0.1% and the lead of 98.6%.Its preparation method comprises the following steps: the electrolytic lead of 2/3 of described amount is inserted in market pot by (1), is heated to 680 ° of C and melts completely to electrolytic lead; (2) then open centrifugal blender, slowly add the Graphene of described amount continuously or be interrupted interpolation in batches joining in plumbous liquid when moderate-speed mixer; After (3) 20 minutes, successively add pure tin bar and the fine aluminium bar of described amount, centrifugal blender continues to be uniformly mixed half an hour more than; (4) centrifugal blender is closed; add the sponge calcium encapsulated with sheet lead of described amount; the sponge calcium bottom of being encapsulated by sheet lead has the bell jar of small opening to be pressed into bottom plumbous liquid; encapsulate with sheet lead when adding sponge calcium, then have the bell jar of small opening to be pressed into bottom plumbous liquid with bottom, allow sponge calcium slowly melt bottom plumbous liquid; because calcium is very active metal; at high temperature easy firing loss, encapsulates with sheet lead for this reason before addition, to reduce the loss of sponge calcium.When plumbous liquid no longer bubbling time, start centrifugal blender low rate mixing mixing; (5) after half an hour, the electrolytic lead of surplus is added in market pot, lead to be electrolysed melts completely, continues to stir, ingot casting after a hour.Graphene described above is one or more in single-layer graphene, bilayer graphene, few layer graphene or graphene microchip.Graphene can adopt physical method to produce, and chemical method also can be adopted to produce.
Embodiment 4, a kind of lead accumulator grid lead alloy containing Graphene, count by weight percentage, it comprises the Graphene of 0.09%, the tin of 1.1%, the aluminium of 0.025%, the sponge calcium of 0.07% and the lead of 98.715%.Its preparation method comprises the following steps: the electrolytic lead of 2/3 of described amount is inserted in market pot by (1), is heated to 680 ° of C and melts completely to electrolytic lead; (2) then open centrifugal blender, slowly add the Graphene of described amount continuously or be interrupted interpolation in batches joining in plumbous liquid when moderate-speed mixer; After (3) 20 minutes, successively add pure tin bar and the fine aluminium bar of described amount, centrifugal blender continues to be uniformly mixed half an hour more than; (4) centrifugal blender is closed; add the sponge calcium encapsulated with sheet lead of described amount; the sponge calcium bottom of being encapsulated by sheet lead has the bell jar of small opening to be pressed into bottom plumbous liquid; encapsulate with sheet lead when adding sponge calcium, then have the bell jar of small opening to be pressed into bottom plumbous liquid with bottom, allow sponge calcium slowly melt bottom plumbous liquid; because calcium is very active metal; at high temperature easy firing loss, encapsulates with sheet lead for this reason before addition, to reduce the loss of sponge calcium.When plumbous liquid no longer bubbling time, start centrifugal blender low rate mixing mixing; (5) after half an hour, the electrolytic lead of surplus is added in market pot, lead to be electrolysed melts completely, continues to stir, ingot casting after a hour.Graphene described above is one or more in single-layer graphene, bilayer graphene, few layer graphene or graphene microchip.Graphene can adopt physical method to produce, and chemical method also can be adopted to produce.
Embodiment 5, a kind of lead accumulator grid lead alloy containing Graphene, count by weight percentage, it comprises the Graphene of 0.12%, the tin of 1.2%, the aluminium of 0.035%, the sponge calcium of 0.09% and the lead of 98.555%.Its preparation method comprises the following steps: the electrolytic lead of 2/3 of described amount is inserted in market pot by (1), is heated to 680 ° of C and melts completely to electrolytic lead; (2) then open centrifugal blender, slowly add the Graphene of described amount continuously or be interrupted interpolation in batches joining in plumbous liquid when moderate-speed mixer; After (3) 20 minutes, successively add pure tin bar and the fine aluminium bar of described amount, centrifugal blender continues to be uniformly mixed half an hour more than; (4) centrifugal blender is closed; add the sponge calcium encapsulated with sheet lead of described amount; the sponge calcium bottom of being encapsulated by sheet lead has the bell jar of small opening to be pressed into bottom plumbous liquid; encapsulate with sheet lead when adding sponge calcium, then have the bell jar of small opening to be pressed into bottom plumbous liquid with bottom, allow sponge calcium slowly melt bottom plumbous liquid; because calcium is very active metal; at high temperature easy firing loss, encapsulates with sheet lead for this reason before addition, to reduce the loss of sponge calcium.When plumbous liquid no longer bubbling time, start centrifugal blender low rate mixing mixing; (5) after half an hour, the electrolytic lead of surplus is added in market pot, lead to be electrolysed melts completely, continues to stir, ingot casting after a hour.Graphene described above is one or more in single-layer graphene, bilayer graphene, few layer graphene or graphene microchip.Graphene can adopt physical method to produce, and chemical method also can be adopted to produce.
Embodiment 6, a kind of lead accumulator grid lead alloy containing Graphene, count by weight percentage, it comprises the Graphene of 0.15%, the tin of 1.5%, the aluminium of 0.04%, the sponge calcium of 0.1% and the lead of 98.21%.Its preparation method comprises the following steps: the electrolytic lead of 2/3 of described amount is inserted in market pot by (1), is heated to 680 ° of C and melts completely to electrolytic lead; (2) then open centrifugal blender, slowly add the Graphene of described amount continuously or be interrupted interpolation in batches joining in plumbous liquid when moderate-speed mixer; After (3) 20 minutes, successively add pure tin bar and the fine aluminium bar of described amount, centrifugal blender continues to be uniformly mixed half an hour more than; (4) centrifugal blender is closed; add the sponge calcium encapsulated with sheet lead of described amount; the sponge calcium bottom of being encapsulated by sheet lead has the bell jar of small opening to be pressed into bottom plumbous liquid; encapsulate with sheet lead when adding sponge calcium, then have the bell jar of small opening to be pressed into bottom plumbous liquid with bottom, allow sponge calcium slowly melt bottom plumbous liquid; because calcium is very active metal; at high temperature easy firing loss, encapsulates with sheet lead for this reason before addition, to reduce the loss of sponge calcium.When plumbous liquid no longer bubbling time, start centrifugal blender low rate mixing mixing; (5) after half an hour, the electrolytic lead of surplus is added in market pot, lead to be electrolysed melts completely, continues to stir, ingot casting after a hour.Graphene described above is one or more in single-layer graphene, bilayer graphene, few layer graphene or graphene microchip.Graphene can adopt physical method to produce, and chemical method also can be adopted to produce.
Respectively the hardness of Graphene lead alloy obtained in embodiment 1 ~ 6, tensile strength and resistivity are detected, and draw following data:
After Graphene lead alloy obtained in embodiment 1 ~ 6 is made the resultant battery of 6-DZM-20, test, battery initial capacity is 22.6Ah, through 150 times shallow fill deep discharge after, residual capacity is respectively 21.1Ah, 21.3Ah, 21.5Ah, 21.7Ah, 21.8Ah, 21.8Ah, does not find barrier layer phenomenon, continues circulation, after 350 100% DOD circulations, residual capacity is respectively 20.2Ah, 20.1Ah, 20.4Ah, 20.5Ah, 20.6Ah, 20.5Ah.Dissection and analysis, finds the existing a small amount of corrosion of grid and active material ruckbildung.But small on battery performance impact, absolutely prove that Graphene can slow down grid corrosion situation, and thoroughly can solve the series of negative impact produced because of grid corrosion.
Can be found out by above experimental data, Graphene addition is more, and grid hardness is higher, and tensile strength is better, and resistivity is lower, is enough to illustrate can improve grid mechanical strength adding of Graphene, reduces grid deflection, strengthens grid conductivity.As long as the hardness that in producing conventional, we sum up grid reaches the requirement that 22N/mm2 just can meet painting cream, we show that Graphene content is 0.015% time by experiment, grid is through short-term timeliness, its hardness just can reach the requirement of conventional coated plate, and tensile strength and resistivity also all surmount in Standard.The higher grid performance of Graphene content is better, but when Graphene content higher than 0.15% time, alloy grid performance is far more than Standard, and large help is not had yet again to battery performance, add the also just waste of more Graphene, so the desired contents of Graphene should control in 0.015 ~ 0.15% scope.
Claims (3)
1. the lead accumulator grid lead alloy containing Graphene, it is characterized in that: count by weight percentage, it comprises the Graphene of 0.015 ~ 0.15%, the tin of 1.0 ~ 1.5%, the aluminium of 0.02 ~ 0.04%, the calcium of 0.05 ~ 0.1% and the lead of 98.21 ~ 98.915%.
2. the lead accumulator grid lead alloy containing Graphene according to claim 1, is characterized in that: described Graphene is one or more in single-layer graphene, bilayer graphene, few layer graphene or graphene microchip.
3. a method processed for the lead accumulator grid lead alloy containing Graphene described in claim 1 or 2, is characterized in that: it comprises the following steps:
(1) lead of 2/3 of described amount is inserted in market pot, be heated to 680 ° of C and melt completely to lead; (2) then open centrifugal blender, slowly add the Graphene of described amount continuously or be interrupted interpolation in batches joining in plumbous liquid when moderate-speed mixer; After (3) 20 minutes, successively add pure tin bar and the fine aluminium bar of described amount, centrifugal blender continues to be uniformly mixed half an hour more than; (4) close centrifugal blender, add the calcium encapsulated with sheet lead of described amount, the calcium bottom of being encapsulated by sheet lead has the bell jar of small opening to be pressed into bottom plumbous liquid, when plumbous liquid no longer bubbling time, start centrifugal blender low rate mixing mixing; (5) after half an hour, close centrifugal blender, the lead of surplus is added in market pot, treats that lead melts completely, open centrifugal blender, continue low rate mixing, ingot casting after a hour.