CN104976439A - Production method for anticorrosive nodular cast iron pipe - Google Patents
Production method for anticorrosive nodular cast iron pipe Download PDFInfo
- Publication number
- CN104976439A CN104976439A CN201510269728.9A CN201510269728A CN104976439A CN 104976439 A CN104976439 A CN 104976439A CN 201510269728 A CN201510269728 A CN 201510269728A CN 104976439 A CN104976439 A CN 104976439A
- Authority
- CN
- China
- Prior art keywords
- iron pipe
- cast iron
- ductile iron
- nodular cast
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method for an anticorrosive nodular cast iron pipe and relates to the technical field of metal corrosion resistance. The production method comprises the steps that firstly, the surface of a nodular cast iron pipe base body is subjected to sand blasting treatment; secondly, the surface of the nodular cast iron pipe base body is blown clean through compressed air; and thirdly, the nodular cast iron pipe base body is heated to 50-55 DEG C; a component A and a component B of a polyurethane anticorrosive coating are mixed evenly according to the proportion of one to one, an airless sprayer is used for evenly spraying the coating onto the surface of the nodular cast iron pipe base body, and construction is carried out in a one-layer multipass spraying mode. Compared with the prior art, the coating is sprayed onto the nodular cast iron pipe base body uniformly and is high in adhesive force; the nodular cast iron pipe produced through the method is high in corrosion resistance; a corrosion resistant coating layer of the nodular cast iron pipe is not prone to stripping, and operation is easy and convenient.
Description
Technical field
The present invention relates to technical field of metal anti-corrosion, especially a kind of production method of corrosion resistant ductile iron pipe.
Background technique
Ductile iron pipe has the essence of iron, the performance of steel, the ductile iron pipe after annealing, and its metallographic structure is that ferrite adds a small amount of pearlite, satisfactory mechanical property, ductility is good, good sealing effect, install simple and easy, be mainly used in municipal administration, industrial and mining enterprise's feedwater, gas transmission, oil transportation etc.Because the ductile iron pipe decay resistance produced at present is lower, surface is easily corroded and gets rusty.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of production method of corrosion resistant ductile iron pipe, lower with the ductile iron pipe decay resistance solving the production of existing method, the surperficial problem of getting rusty that is easily corroded.
In order to solve the problem, the technical solution used in the present invention is: the production method of this corrosion resistant ductile iron pipe, comprises the following steps:
A. carry out sand blast to the surface of ductile iron pipe matrix, derusting grade reaches Sa2.5, surperficial depth of abrasion pattern 40 μm ~ 70 μm;
B. blow clean with the surface of pressurized air by ductile iron pipe matrix,
C. ductile iron pipe matrix is heated to 50 DEG C ~ 55 DEG C;
D. A, B two kinds of components of anti-corrosion polyurethane coating are mixed by 1:1, with airless sprayer by the surface of coating even application at ductile iron pipe matrix, construct by the spraying method of one deck multiple tracks, per pass coating thickness is 60 μm ~ 80 μm, 3min ~ 4, interval min sprays together, sprays 6 roads, road ~ 8;
E. treat that the coating of ductile iron pipe matrix surface parches, obtain this corrosion resistant ductile iron pipe.
Owing to have employed technique scheme, the present invention compared with prior art has following beneficial effect:
The present invention carries out sand blast to the surface of ductile iron pipe matrix, and is heated 50 DEG C ~ 55 DEG C, guarantees the adhesion of coating on ductile iron pipe matrix; With airless sprayer by the surface of coating even application at ductile iron pipe matrix, construct by the spraying method of one deck multiple tracks, coating is made to apply evenly on ductile iron pipe matrix, strong adhesion, the corrosion resistant ductile iron pipe antiseptic property that the method is produced is high, its anticorrosive paint layer difficult drop-off, and simple to operation.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1
A production method for corrosion resistant ductile iron pipe, concrete steps are as follows:
A. carry out sand blast to the surface of ductile iron pipe matrix, derusting grade reaches Sa2.5, surperficial depth of abrasion pattern 40 μm;
B. blow clean with the surface of pressurized air by ductile iron pipe matrix,
C. ductile iron pipe matrix is heated to 50 DEG C;
D. A, B two kinds of components of anti-corrosion polyurethane coating are mixed by 1:1, with airless sprayer by the surface of coating even application at ductile iron pipe matrix, construct by the spraying method of one deck multiple tracks, per pass coating thickness is 60 μm, interval 3min sprays together, sprays 6 roads;
E. treat that the coating of ductile iron pipe matrix surface parches, obtain this corrosion resistant ductile iron pipe.
Embodiment 2
A production method for corrosion resistant ductile iron pipe, concrete steps are as follows:
A. carry out sand blast to the surface of ductile iron pipe matrix, derusting grade reaches Sa2.5, surperficial depth of abrasion pattern 70 μm;
B. blow clean with the surface of pressurized air by ductile iron pipe matrix,
C. ductile iron pipe matrix is heated to 55 DEG C;
D. A, B two kinds of components of anti-corrosion polyurethane coating are mixed by 1:1, with airless sprayer by the surface of coating even application at ductile iron pipe matrix, construct by the spraying method of one deck multiple tracks, per pass coating thickness is 80 μm, interval 4 min sprays together, sprays 8 roads;
E. treat that the coating of ductile iron pipe matrix surface parches, obtain this corrosion resistant ductile iron pipe.
Claims (1)
1. a production method for corrosion resistant ductile iron pipe, is characterized in that comprising the following steps:
A. carry out sand blast to the surface of ductile iron pipe matrix, derusting grade reaches Sa2.5, surperficial depth of abrasion pattern 40 μm ~ 70 μm;
B. blow clean with the surface of pressurized air by ductile iron pipe matrix,
C. ductile iron pipe matrix is heated to 50 DEG C ~ 55 DEG C;
D. A, B two kinds of components of anti-corrosion polyurethane coating are mixed by 1:1, with airless sprayer by the surface of coating even application at ductile iron pipe matrix, construct by the spraying method of one deck multiple tracks, per pass coating thickness is 60 μm ~ 80 μm, 3min ~ 4, interval min sprays together, sprays 6 roads, road ~ 8;
E. treat that the coating of ductile iron pipe matrix surface parches, obtain this corrosion resistant ductile iron pipe.