CN104974428A - Novel rubber material being high in wear-resistant performance - Google Patents
Novel rubber material being high in wear-resistant performance Download PDFInfo
- Publication number
- CN104974428A CN104974428A CN201410144704.6A CN201410144704A CN104974428A CN 104974428 A CN104974428 A CN 104974428A CN 201410144704 A CN201410144704 A CN 201410144704A CN 104974428 A CN104974428 A CN 104974428A
- Authority
- CN
- China
- Prior art keywords
- carbon black
- rubber
- wear
- rubber material
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A novel rubber material being high in a wear-resistant performance includes following raw materials, by weight, 9 kg of ethylene-propylene rubber, 9-11 kg of hot-cracked carbon black, 1-2 kg of wear-resistant carbon black, 3-4 kg of calcium carbonate, 0.1-0.3 kg of an anti-aging agent polyethylene glycol, 0.15-0.3 kg of a dispersing agent polyethylene wax, 0.05-0.1 kg of an accelerant zinc dimethyldithiocarbamate, 0.1-0.2 kg of a vulcanizing agent sulfur, and 0.15-0.3 kg of a flame retardant ammonium polyphosphate. With the carbon black as a filling material being filled in the ethylene-propylene rubber at a large amount, not only is hardness of the rubber sealing material increased and is production cost of the rubber sealing material reduced, but also the carbon black greatly influences the physical characters of the rubber sealing material. When the hot-cracked carbon black is filled individually, only the objects of increasing the hardness and reducing the production cost are achieved, and when a less amount of the wear-resistant carbon black, which is high in activity, is added, the rubber material is significantly improved in wear resistance when being compared with the novel rubber material simply filled by the hot-cracked carbon black.
Description
Technical field
The present invention relates to rubber packing material, be applied to the wear resisting property improving rubber packing material.
Background technology
The preparation method of current rubber packing material adopts second third glue to be basic rubber raw material, with the lower thermal black of a certain amount of activity as raw material, through banburying, open refining, sulfuration process is prepared from, the feature of this carbon black is that particle is thicker, heat-dissipating is low, compression set is low, can fill in a large number, a large amount of filling can improve rubber hardness and can reduce sizing material cost, but adopts the carbon black that single activity is lower, can not increase the wear resistance of rubber packing material, therefore prepared rubber packing material wear resistance is lower.
Summary of the invention
The object of this invention is to provide a kind of Novel rubber material of high-wear resistance, improve the antiwear characteristic of rubber packing material.
In order to achieve the above object, the technical solution used in the present invention is:
A kind of Novel rubber material of high-wear resistance, preparing in the lower thermal black of activity that rubber packing material uses, add a small amount of active higher abrasion resistant carbon black mixing, raw material weight compares: second third glue 9KG, thermal black 9 ~ 11KG, abrasion resistant carbon black 1 ~ 2KG, calcium carbonate 3 ~ 4KG, anti-aging agent polyoxyethylene glycol 0.1 ~ 0.3 KG, polyethylene of dispersing agent wax 0.15 ~ 0.3KG, promotor ziram 0.05 ~ 0.1KG, vulcanizing agent sulphur 0.1 ~ 0.2KG, fire retardant gathers phosphorus ammonium fat 0.15 ~ 0.3KG.
Above-described elastomeric material, raw material weight compares: second third glue 9KG, thermal black 10KG, abrasion resistant carbon black 1.5KG, calcium carbonate 4KG, anti-aging agent polyoxyethylene glycol 0.2KG, polyethylene of dispersing agent wax 0.2KG, promotor ziram 0.1KG, vulcanizing agent sulphur 0.15KG, fire retardant gathers phosphorus ammonium fat 0.2KG.
The effect that the present invention reaches is: carbon black is as the weighting material of second third glue, a large amount of filling not only increases the hardness of rubber packing material and reduces production cost, and it is larger on the physical property impact of rubber packing material, simple filling thermal black, only play and increase the object that hardness reduces production cost, and after adding the higher abrasion resistant carbon black of a small amount of activity, the wear resistance of rubber packing material is obviously than high when adding merely thermal black.
Embodiment
Preparing in the lower thermal black of activity that rubber packing material uses, add a small amount of active higher abrasion resistant carbon black mixing.
Second third glue is adopted to be basic rubber raw material, a small amount of abrasion resistant carbon black that the thermal black mixed active lower with a certain amount of activity is higher, calcium carbonate, protective agent, dispersion agent, vulcanizing agent, the cooperations such as fire retardant, through banburying, open refining, the sealing material that sulfuration process is prepared from, wear resistance is obviously than high when adding merely thermal black.
Embodiment 1:
Raw material weight compares: second third glue 9KG, thermal black 11KG, abrasion resistant carbon black 2KG, calcium carbonate 4KG, anti-aging agent polyoxyethylene glycol (PEG-4000) 0.3 KG, polyethylene of dispersing agent wax 0.3KG, promotor ziram (PZ) 0.1KG, vulcanizing agent sulphur 0.2KG, fire retardant gathers phosphorus ammonium fat 0.3KG.
Embodiment 2:
Raw material weight compares: second third glue 9KG, thermal black 9KG, abrasion resistant carbon black 1KG, calcium carbonate 3KG, anti-aging agent polyoxyethylene glycol (PEG-4000) 0.1 KG, polyethylene of dispersing agent wax 0.15KG, promotor ziram (PZ) 0.05KG, vulcanizing agent sulphur 0.1KG, fire retardant gathers phosphorus ammonium fat 0.15KG.
Embodiment 3:
Raw material weight compares: second third glue 9KG, thermal black 10KG, abrasion resistant carbon black 1.5KG, calcium carbonate 4KG, anti-aging agent polyoxyethylene glycol (PEG-4000) 0.2 KG, polyethylene of dispersing agent wax 0.2KG, promotor ziram (PZ) 0.1KG, vulcanizing agent sulphur 0.15KG, fire retardant gathers phosphorus ammonium fat 0.2KG.
Preparation process in above embodiment 1-3: second third glue is placed in Banbury mixer and plasticates 60 ~ 80 seconds, add thermal black, abrasion resistant carbon black, calcium carbonate, PEG-4000, polyethylene wax banburying obtains one section of glue for 60 ~ 120 seconds.Plasticate and melting temperature control at 120 ~ 140 DEG C.Be placed in mill by one section of glue, add PZ and vulcanizing agent sulphur and fire retardant and gather phosphorus ammonium fat, at 55 ~ 70 DEG C, open refining even to section, obtains two sections of glue.By after two sections of gum formings on vulcanizer 170 ~ 185 DEG C of sulfurations within 8 ~ 10 minutes, obtain product.
It should be noted that above embodiment can not be considered to for limiting practical range of the present invention, all equalizations done according to the present patent application scope change and improve, and all should still belong within patent covering scope of the present invention.
Claims (2)
1. the Novel rubber material of a high-wear resistance, it is characterized in that, raw material weight compares: second third glue 9KG, thermal black 9 ~ 11KG, abrasion resistant carbon black 1 ~ 2KG, calcium carbonate 3 ~ 4KG, anti-aging agent polyoxyethylene glycol 0.1 ~ 0.3 KG, polyethylene of dispersing agent wax 0.15 ~ 0.3KG, promotor ziram 0.05 ~ 0.1KG, vulcanizing agent sulphur 0.1 ~ 0.2KG, fire retardant gathers phosphorus ammonium fat 0.15 ~ 0.3KG.
2. the Novel rubber material of high-wear resistance according to claim 1, it is characterized in that: raw material weight compares: second third glue 9KG, thermal black 10KG, abrasion resistant carbon black 1.5KG, calcium carbonate 4KG, anti-aging agent polyoxyethylene glycol 0.2KG, polyethylene of dispersing agent wax 0.2KG, promotor ziram 0.1KG, vulcanizing agent sulphur 0.15KG, fire retardant gathers phosphorus ammonium fat 0.2KG.