CN104959612B - The preparation method of porous filtering film and porous filtering film - Google Patents
The preparation method of porous filtering film and porous filtering film Download PDFInfo
- Publication number
- CN104959612B CN104959612B CN201510274885.9A CN201510274885A CN104959612B CN 104959612 B CN104959612 B CN 104959612B CN 201510274885 A CN201510274885 A CN 201510274885A CN 104959612 B CN104959612 B CN 104959612B
- Authority
- CN
- China
- Prior art keywords
- filtering film
- porous filtering
- porous
- porous membrane
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses it is a kind of easily reach that higher porosity ensure that preparation again when formability, the preparation method of the simple and practical porous membrane of preparation technology and porous membrane.The porous membrane thickness is 200~1500 μm, average pore size is 0.05~100 μm, and the step of porosity is 25~75%, its preparation method includes：(1) support membrane is obtained, the support membrane has forms once hole on cavernous first material, first material；(2) produce and contain the second powdered material in slurry, the slurry；(3) slurry is coated on support membrane and then base substrate is made；(4) base substrate is sintered, reaction generates cavernous 3rd material and and then generation and the secondary hole of a porosity communication between the first material and the second material during sintering；(5) cooling obtains porous membrane after sintering.Due at least containing once hole and secondary hole, therefore porous membrane easily reaches higher porosity.
Description
Technical field
The present invention relates to the preparation of porous membrane and porous membrane, more particularly to porous inorganic membrane, particularly porous gold
Belong to film.
Background technology
Sintering inorganic porous material such as sintering diamond bit, sinter ceramic porous material be mainly used as filter material
Material.In a particular application, the filter element of definite shape and construction need to be made into, filter element is then installed to filtering dress
In putting.Existing sintering inorganic porous material filter element is substantially all as rigid cast or plate profile structure.Their preparation
Principle is similar, i.e., substantially：Special mould is first passed through (typically to adopt the pressed compact that raw material powder is pressed into cast or template
With equal pressing forming technology), then pressed compact is sintered again, product is obtained after sintering.
The filter element of above-mentioned cast or template due to by its shape, construction and it is subsidiary and come to filter and be
The influence of the corresponding requirements of system, it is limited using scope.Because sintering inorganic porous material filter element is in the resistance of chemical erosion
Property, in terms of material irreversible membrane fouling repellence it is upper have compared to current filter element (such as organic filter film) it is stronger excellent
Gesture, therefore, develops the novel sintered inorganic porous material filtering for being capable of the original filter element of corresponding substitute in multiple fields
Element especially sintering diamond bit filter element is highly significant.
On above-mentioned background elementary, applicant successively have submitted Application No. 2014106089803, entitled " flexibility is more
Mesoporous metal paper tinsel and preparation method thereof ", Application No. 2015101531163, entitled " flexible, porous metal foil and flexible, porous gold
The preparation method of category paper tinsel " and Application No. 201510153106X, entitled " preparation method of multicellular metal foil " etc. are multinomial specially
Profit application, to develop with sintering inorganic porous material good characteristic, without support porous membrane, (implication of " no support " refers to
Porous membrane has self-supporting in itself, it is not necessary to is attached on support frame and just can be used) provide solution route.
However, applicant has found in practice：It is above-mentioned porous without supporting to prepare no matter to take which kind of current technique
The intensity of porous membrane is often conflicting after film, the porosity of porous membrane and the formability of material and shaping.For
The more preferable strainability of pursuit requires to improve the porosity of porous membrane, but improves the porosity of porous membrane and accordingly will
The formability for reducing porous membrane (is mainly reflected in situations such as material cracks and deformation in preparation process, product fraction defective is carried
Rise) and porous membrane product intensity.
The content of the invention
For above-mentioned situation, the technical problems to be solved by the invention are：There is provided and several easily reach higher porosity, again
The preparation method of the simple and practical porous membrane of formability, preparation technology when ensure that preparation and porous membrane.
The first porous membrane of the present invention, thickness is 5~200 μm, average pore size is 0.05~100 μm, and porosity is
25~75%, include the step of its preparation method：(1) support membrane is obtained, the support membrane has cavernous first material, institute
State and once hole is formed on the first material；(2) produce and contain the second powdered material in slurry, the slurry；(3) by institute
Slurry is stated to be coated on support membrane and then base substrate is made；(4) base substrate is sintered, the first material and the second material during sintering
Cavernous 3rd material of reaction generation and generation simultaneously and the secondary hole of a porosity communication between material；(5) it is cold after sintering
But porous membrane is obtained.When in the porous membrane that step (5) is obtained also containing the first material not reacted with the second material, institute
Step (6) can also be further comprised by stating preparation method, i.e., immersion is carried out to porous membrane so as in porous membrane with etching solution
Upper selectivity forms three holes after the first material is dissolved, and then porous membrane is dried and obtains finished product.
Second of porous membrane of the present invention, thickness is 5~200 μm, average pore size is 0.05~100 μm, and porosity is
25~75%, include the step of its preparation method：(1) support membrane is obtained, the support membrane has cavernous first material, the
Once hole is formed on one material；(2) produce and contain the second powdered material in slurry, the slurry；(3) by the slurry
Body is coated on support membrane and then base substrate is made；(4) base substrate is sintered, the second material autoreactivity is generated during sintering
The material of cellular the 3rd and then generation and the secondary hole of a porosity communication；(5) cooling obtains porous membrane after sintering.It is described
Preparation method can also further comprise step (6), i.e., immersion is carried out to porous membrane so as on porous membrane with etching solution
Selectivity forms three holes after being dissolved to the first material left, and then porous membrane is dried and obtains finished product.
The third porous membrane of the present invention, thickness is 200~1500 μm, average pore size is 0.05~100 μm, porosity
Include for 25~75%, the step of its preparation method：(1) support membrane is obtained, the support membrane has cavernous first material,
Once hole is formed on first material；(2) produce and contain the second powdered material in slurry, the slurry；(3) will
The slurry is coated on support membrane and then base substrate is made；(4) base substrate is sintered, the first material and second during sintering
Cavernous 3rd material of reaction generation and and then generation and the secondary hole of a porosity communication between material；(5) after sintering
Cooling obtains porous membrane.When in the porous membrane that step (5) is obtained also containing the first material not reacted with the second material,
The preparation method can also further comprise step (6), i.e., immersion is carried out to porous membrane so as to porous thin with etching solution
Three holes are formed after selectivity dissolves the first material on film, then porous membrane is dried and obtains finished product.
The 4th kind of porous membrane of the present invention, thickness is 200~1500 μm, average pore size is 0.05~100 μm, porosity
Include for 25~75%, the step of its preparation method：(1) support membrane is obtained, the support membrane has cavernous first material,
Once hole is formed on first material；(2) produce and contain the second powdered material in slurry, the slurry；(3) will be described
Slurry is coated on support membrane and then base substrate is made；(4) base substrate is sintered, the generation of the second material autoreactivity is more during sintering
Poroid 3rd material and then generation and the secondary hole of a porosity communication；(5) cooling obtains porous membrane after sintering.The system
Preparation Method can also further comprise step (6), i.e., carry out immersion to porous membrane to select on porous membrane with etching solution
Selecting property forms three holes after being dissolved to the first material left, and then porous membrane is dried and obtains finished product.
Support membrane is used in the preparation process of above-mentioned four kinds of porous membranes, the support membrane is final or constitutes porous thin
A part for film finished product, or etching solution dissolving is eclipsed, or part constitutes a part for porous membrane finished product and is partly etched molten
Liquid dissolves.In a word, because these four porous membranes at least contain once hole and secondary hole, therefore porous membrane easily reaches
To higher porosity；And due in the preparation process of porous membrane base substrate be supported by support membrane, it is fine to avoid burning
During knot situations such as material cracks and deformation, therefore it can effectively reduce the shaping difficulty without support porous membrane and improve shaping matter
Amount.
In the preparation process of above-mentioned four kinds of porous membranes, the support membrane used is preferably net type film, and its mesh size one
As be 20~1000 mesh.So-called " net type film " refers to the film for constructing similar screen cloth.It is in the present invention, the mesh of net type film is big
It is small to be set as that 20~1000 mesh are proper.If mesh further increases on the basis of this number range, during coating slurry
It is easily caused slurry and covers after imperfect, sintering and there is the defects such as trachoma on porous membrane；If mesh is on this number range basis
It is upper further to reduce, will because the coated weight of slurry is less and to porous membrane caused by some adversely affect.The mesh of net type film
Big I is more preferably 40~400 mesh.Certainly, support membrane can only not use net type film, using the porous material of non-net form
Expect that (such as the multicellular metal foil mentioned in background technology) is also feasible.
Above-mentioned the first porous membrane of the present invention and the third porous membrane are preferably a kind of to be made up of solid solution alloy
3rd material is the metal film of matrix phase, wherein, first material constitutes the solvent source of the solid solution alloy, the second material structure
Into the solute source of the solid solution alloy, diffusion pore-creating reaction partially occurs for the first material and the second material during sintering.For example, porous thin
Film is a kind of solid by Ag-Au solid solution, Ti-Zr solid solution, Mg-Cd solid solution, Fe-Cr solid solution, Ni-Cu solid solution, Cu-Al
The 3rd material that solution, Cu-Zn solid solution or Fe-C-Cr solid solution are constituted is the metal film of matrix phase.It is above-mentioned that the first is porous
Film and the third porous membrane generally have flexible, excellent corrosion resistance, can the characteristic such as high temperature resistant, wherein, this first
Porous membrane thinner thickness (5~200 μm), its waste heat recovery that industrially can be used in weaving and leather industry, medicament are returned
Receipts, contamination control, purification, concentration, sterilization, byproduct in food-processing industry are reclaimed, artificial in medicine and healthcare industry
Cleaner in tracheae, control release, blood filtration, Water warfare, auto industry；On civilian can as mouth mask dust-filtering
The curtain material of material and static electrification dedusting function；The third porous membrane thickness is thicker (200~1500 μm), therefore intensity is more
Height, a typical example application is the filter bag for being fabricated to filtering, so as to replace the filter element in current sack cleaner
" cloth bag ".It can be seen that, the first porous membrane and the third porous membrane have the purposes of differentiation.In addition, in the above
" the diffusion pore-creating reaction partially " referred to actually refers to Kinkendal Effect (kirkendall effect), belongs to powder sintered nothing
Conventional pore-creating means in the preparation of machine porous material.
In the preparation process of above-mentioned second of porous membrane of the invention and the 4th kind of porous membrane, second material is preferred
Including at least two powders, formed during at least two powder sintering by the 3rd material that solid solution alloy is matrix phase, this
One of which powder constitutes the solvent source of the solid solution alloy in two kinds of powders, and another powder constitutes the molten of the solid solution alloy
Diffusion pore-creating reaction partially occurs between matter source, at least two powders described in during sintering；First material is then one kind described
Sintering condition under show as inert metal material relative to the second material.For example, the second material autoreactivity generation
With Ag-Au solid solution, Ti-Zr solid solution, Mg-Cd solid solution, Fe-Cr solid solution, Ni-Cu solid solution, Cu-Al solid solution, Cu-
Zn solid solution or the 3rd material that Fe-C-Cr solid solution is matrix phase；When the 3rd material is made up of Ni-Cu solid solution,
The first material selection is 304 stainless steels.Above-mentioned second of porous membrane and the 4th kind of porous membrane generally have it is flexible,
Excellent corrosion resistance, can the characteristic such as high temperature resistant, wherein, second of porous membrane is relatively thin, its industrially can be used for weaving and
Waste heat recovery, medicament in leather industry are reclaimed, contamination control, purification, concentration in food-processing industry, sterilization, byproduct
Reclaim, medicine and the artificial tracheae in healthcare industry, control release, blood filtration, Water warfare, the cleaner in auto industry；
On civilian can as mouth mask dust-filtering material and the curtain material of static electrification dedusting function；4th kind of porous membrane
Metal film it is thicker, intensity is higher, and a typical example application is the filter bag for being fabricated to filtering, so as to replace " cloth bag ".
It can be seen that, second of porous membrane and the 4th kind of porous membrane equally purposes with differentiation.
The preparation method of the first porous membrane of the present invention, its step includes：(1) Cu nets are used for support membrane, by institute
The thickness for stating support membrane is set as 0.05~0.1 millimeter, and mesh size is set as 40~200 mesh；(2) it is -400 purposes by particle diameter
Ni powder is by dispersant of ethanol, PVB is binding agent by adding 2~5 grams of PVB, 50~100 grams of Ni powder in every 100 milliliters of ethanol
Proportional arrangement is into slurry；(3) slurry is coated on support membrane and dried and base substrate is made；(4) segmented is carried out to base substrate
Sintering, the first stage rises to 120~250 DEG C from room temperature and is incubated 120~180 minutes, and second stage is warming up to 500~600 DEG C
And 60~240 minutes are incubated, the phase III is warming up to 900~1090 DEG C and is incubated 90~240 minutes；(5) system is cooled down after sintering
Obtain porous membrane.When in porous membrane also containing the Cu not reacted with Ni powder, methods described can also further comprise step
(6), i.e., with the FeCl that concentration is 0.5~1mol/L3Solution carries out immersion 20~40 minutes so as to porous thin to porous membrane
Selectivity dissolves Cu to form three holes on film, and then porous membrane is dried and obtains finished product.This method can be prepared
Go out to belong to the Ni-Cu flexible, porous metal foils of the first above-mentioned porous membrane.The advantage of Ni-Cu flexible, porous metal foils can be from
Recognize in the file that background of invention part is cited, therefore will not be repeated here.
The preparation method of second of porous membrane of the present invention, its step includes：(1) 304 stainless (steel) wires are used for support
Film, is set as 0.05~0.1 millimeter, mesh size is set as 60~400 mesh by the thickness of support membrane；(2) it is 3~5 μ by particle diameter
M Ni powder and Cu powder that particle diameter is -400 mesh are 20~40% to be configured to mixed powder by Cu percentage by weight, then with ethanol
It is binding agent by the proportional arrangement that 2~5 grams of PVB, 50~100 grams of mixed powders are added in every 100 milliliters of ethanol for dispersant, PVB
Into slurry；(3) slurry is coated on support membrane and dried and base substrate is made；(4) segmented sintering, first are carried out to base substrate
Stage from room temperature rise to 120~250 DEG C and be incubated 120~180 minutes, second stage be warming up to 500~600 DEG C and be incubated 60~
240 minutes, the phase III was warming up to 900~1090 DEG C and is incubated 90~240 minutes；(5) cooled down after sintering and be made described porous
Film.Method can also further comprise step (6), i.e., with the FeCl that concentration is 0.4~0.8mol/L2Solution enters to porous membrane
Row immersion dissolves 304 stainless steels to form three holes for 30~60 minutes so as to selective on porous membrane, then to porous
Film, which is dried, obtains finished product.This method can prepare the Ni-Cu bases flexible, porous gold for belonging to above-mentioned second of porous membrane
Belong to paper tinsel.
The preparation method of the third porous membrane of the present invention, its step includes：(1) Cu nets are used for support membrane, by institute
The thickness for stating support membrane is set as 0.5~1 millimeter, and mesh size is set as 40~200 mesh；(2) by Ni of the particle diameter for -400 mesh
Powder is by dispersant of ethanol, PVB is binding agent by the ratio that 2~5 grams of PVB, 50~100 grams of Ni powder are added in every 100 milliliters of ethanol
Example is configured to slurry；(3) slurry is coated on support membrane and dried and base substrate is made；(4) segmented burning is carried out to base substrate
Knot, the first stage rises to 120~250 DEG C from room temperature and is incubated 120~180 minutes, and second stage is warming up to 500~600 DEG C simultaneously
Insulation 60~240 minutes, the phase III is warming up to 900~1090 DEG C and is incubated 90~240 minutes；(5) cool down and be made after sintering
Porous membrane.When in porous membrane also containing the Cu not reacted with Ni powder, methods described can also further comprise step (6),
I.e. with the FeCl that concentration is 0.5~1mol/L3Solution carries out immersion 20~40 minutes so as on porous membrane to porous membrane
Selectivity dissolves Cu to form three holes, and then porous membrane is dried and obtains finished product.This method can prepare category
In the Ni-Cu flexible, porous metal foils of the third above-mentioned porous membrane.
The preparation method of the 4th kind of porous membrane of the present invention, its step includes：(1) 304 stainless (steel) wires are used for support
Film, is set as 0.5~1 millimeter, mesh size is set as 60~400 mesh by the thickness of the support membrane；(2) it is 3~5 by particle diameter
μm Ni powder and particle diameter be that the Cu powder of -400 mesh by Cu percentage by weight is 20~40% to be configured to mixed powder, then with ethanol
It is binding agent by the proportional arrangement that 2~5 grams of PVB, 50~100 grams of mixed powders are added in every 100 milliliters of ethanol for dispersant, PVB
Into slurry；(3) slurry is coated on support membrane and dried and base substrate is made；(4) segmented sintering, first are carried out to base substrate
Stage from room temperature rise to 120~250 DEG C and be incubated 120~180 minutes, second stage be warming up to 500~600 DEG C and be incubated 60~
240 minutes, the phase III was warming up to 900~1090 DEG C and is incubated 90~240 minutes；(5) cooled down after sintering and be made described porous
Film.Method can also further comprise step (6), i.e., with the FeCl that concentration is 0.4~0.8mol/L2Solution enters to porous membrane
Row immersion dissolves 304 stainless steels to form three holes for 30~60 minutes so as to selective on porous membrane, then to porous
Film, which is dried, obtains finished product.This method can prepare the Ni-Cu bases flexible, porous gold for belonging to above-mentioned 4th kind of porous membrane
Belong to paper tinsel.
Embodiment
With reference to embodiment, the present invention will be further described.The additional aspect of the present invention and advantage will be retouched in following
State middle part to give out, partly will become apparent from the description below, or recognized by the practice of the present invention.
Embodiment 1
The step of preparing porous membrane includes：(1) Cu nets are used for support membrane (outsourcing red copper screen cloth), by the support membrane
Thickness be set as 0.08 millimeter, mesh size is set as 200 mesh；(2) by Ni powder (purity 99.7%) of the particle diameter for -400 mesh
By dispersant of ethanol, PVB be binding agent by adding the proportional arrangement of 3 grams of PVB, 70 grams of Ni powder in every 100 milliliters of ethanol into slurry
Body；(3) slurry is sprayed on support membrane (quantity for spray of slurry is that every square metre of support membrane sprays 500g slurries) and
Base substrate is made after being dried 4 hours at 60 DEG C；(4) segmented sintering is carried out to base substrate, the first stage rises to 220 DEG C from room temperature and protected
Temperature 150 minutes, the main function in the stage is to remove moisture and impurity remaining in base substrate, it is ensured that film is in later stage sintering process
Cause the phenomenon of cracking without other undesirable elements, second stage is warming up to 550 DEG C and is incubated 200 minutes, the main work in the stage
Be remove material in PVB make subsequent reactions abundant, it is ensured that the uniformity of strength character, the phase III is warming up to 1000 DEG C
And 220 minutes are incubated, the main function in the stage is Ni-Cu alloys is mutually homogenized, and second stage heating rate is 1 during sintering
~3 DEG C/min, 5~7 DEG C/min of phase III heating rate；(5) cooled down after sintering and porous membrane is made.The porous membrane
Thickness is 0.12mm, 15 μm of average pore size, and porosity is 54%, and air permeability is 1500m3/m2Hkpa (is represented in every kpa mistakes
Per hour per m under filtering pressure2Filter area under air infiltration capacity (press m3Represent)).
Embodiment 2
The porous membrane preparation process of embodiment 2 and embodiment 1 is substantially the same, but difference is：The 3rd during sintering
Stage is warming up to after 1000 DEG C only insulation 120 minutes, so that the Cu elements in support membrane do not react all with Ni；Hereafter, use
Concentration is 0.5mol/L FeCl3Solution carries out immersion 35 minutes so as to porous thin to the porous membrane obtained by step (5)
Selectivity dissolves Cu to form three holes on film, and then porous membrane is dried and obtains finished product.It is last obtained porous
The thickness of film be 0.12mm, 17 μm of average pore size, porosity is 63%, and air permeability is 1820m3/m2·h·kpa。
Embodiment 3
The step of preparing porous membrane includes：(1) 304 stainless (steel) wires are used for support membrane (stainless steel mesh of outsourcing 304),
The thickness of support membrane is set as 0.08 millimeter, mesh size is set as 250 mesh；(2) it is 3~5 μm of Ni powder and grain by particle diameter
Footpath is that the Cu powder of -400 mesh by Cu percentage by weight is 30% to be configured to mixed powder, then by dispersant of ethanol, PVB be viscous
Tie agent and press the proportional arrangement that 3 grams of PVB, 70 grams of mixed powders are added in every 100 milliliters of ethanol into slurry；(3) slurry is sprayed
(quantity for spray of slurry is every square metre of support membrane spraying 400g slurries) and it is made on support membrane after being dried 4 hours at 60 DEG C
Base substrate (4) to base substrate carry out segmented sintering, the first stage from room temperature rise to 220 DEG C and be incubated 150 minutes, the stage it is main
Effect is to remove moisture and impurity remaining in base substrate, it is ensured that film causes cracking in later stage sintering process without other undesirable elements
Phenomenon, second stage is warming up to 550 DEG C and is incubated 200 minutes, and the main function in the stage is after the PVB removed in material makes
Continuous reaction is abundant, it is ensured that the uniformity of strength character, and the phase III is warming up to 1050 DEG C and is incubated 220 minutes, the stage
Main function is Ni-Cu alloys is mutually homogenized, and second stage heating rate is 1~3 DEG C/min, phase III liter during sintering
Warm 5~7 DEG C/min of speed；(5) cooled down after sintering and the porous membrane is made.The thickness of the porous membrane is 0.12mm, average
13 μm of aperture, porosity is 52%, and air permeability is 1490m3/m2·h·kpa。
Embodiment 4
Embodiment 4 further includes step (6) on the basis of embodiment 3, i.e., be 0.5mol/L's with concentration
FeCl2Solution carries out immersion 45 minutes so as to which 304 stainless steels are dissolved to form three by selectivity on porous membrane to porous membrane
Secondary hole, is then dried to porous membrane and obtains finished product.The thickness of last obtained porous membrane is 0.12mm, average hole
18 μm of footpath, porosity is 72%, and air permeability is 2050m3/m2·h·kpa。
Embodiment 5
The step of preparing porous membrane includes：(1) Cu nets are used for support membrane (outsourcing red copper screen cloth), by the support membrane
Thickness be set as 0.2 millimeter, mesh size is set as 80 mesh；(2) by particle diameter for -400 mesh Ni powder (purity 99.7%) with
Ethanol is that dispersant, PVB are binding agent by adding the proportional arrangement of 3 grams of PVB, 70 grams of Ni powder in every 100 milliliters of ethanol into slurry；
(3) slurry is sprayed on support membrane (quantity for spray of slurry is that every square metre of support membrane sprays 500g slurries) and at 60 DEG C
Base substrate is made after 4 hours in lower drying；(4) segmented sintering is carried out to base substrate, the first stage rises to 220 DEG C from room temperature and is incubated
150 minutes, the main function in the stage was to remove moisture and impurity remaining in base substrate, it is ensured that film nothing in later stage sintering process
Other undesirable elements cause the phenomenon of cracking, and second stage is warming up to 550 DEG C and is incubated 200 minutes, the main function in the stage
It is that the PVB removed in material makes subsequent reactions abundant, it is ensured that the uniformity of strength character, the phase III is warming up to 1000 DEG C simultaneously
Insulation 220 minutes, the main function in the stage is Ni-Cu alloys is mutually homogenized, during sintering second stage heating rate be 1~
3 DEG C/min, 5~7 DEG C/min of phase III heating rate；(5) cooled down after sintering and porous membrane is made.The thickness of the porous membrane
Spend for 0.3mm, 23 μm of average pore size, porosity is 45%, and air permeability is 800m3/m2·h·kpa。
Embodiment 6
The porous membrane preparation process of embodiment 6 and embodiment 5 is substantially the same, but difference is：The 3rd during sintering
Stage is warming up to after 1000 DEG C only insulation 120 minutes, so that the Cu elements in support membrane do not react all with Ni；Hereafter, use
Concentration is 0.5mol/L FeCl3Solution carries out immersion 35 minutes so as to porous thin to the porous membrane obtained by step (5)
Selectivity dissolves Cu to form three holes on film, and then porous membrane is dried and obtains finished product.It is last obtained porous
The thickness of film be 0.3mm, 25 μm of average pore size, porosity is 50%, and air permeability is 1000m3/m2·h·kpa。
Embodiment 7
The step of preparing porous membrane includes：(1) 304 stainless (steel) wires are used for support membrane (stainless steel mesh of outsourcing 304),
The thickness of support membrane is set as 0.2 millimeter, mesh size is set as 80 mesh；(2) it is 3~5 μm of Ni powder and particle diameter by particle diameter
By Cu percentage by weight be 30% to be configured to mixed powder for the Cu powder of -400 mesh, then by dispersant of ethanol, PVB be cohesive
Agent presses the proportional arrangement that 3 grams of PVB, 70 grams of mixed powders are added in every 100 milliliters of ethanol into slurry；(3) slurry is sprayed on
(quantity for spray of slurry is every square metre of support membrane spraying 500g slurries) and base is made after being dried 4 hours at 60 DEG C on support membrane
Body (4) carries out segmented sintering to base substrate, and the first stage rises to 220 DEG C from room temperature and is incubated 150 minutes, the main work in the stage
With being to remove remaining moisture and impurity in base substrate, it is ensured that film causes cracking in later stage sintering process without other undesirable elements
Phenomenon, second stage is warming up to 550 DEG C and is incubated 200 minutes, and the main function in the stage is that the PVB removed in material makes subsequently
Reaction is abundant, it is ensured that the uniformity of strength character, and the phase III is warming up to 1050 DEG C and is incubated 220 minutes, the master in the stage
It is Ni-Cu alloys is mutually homogenized to act on, and second stage heating rate is 1~3 DEG C/min during sintering, phase III heating
5~7 DEG C/min of speed；(5) cooled down after sintering and the porous membrane is made.The thickness of the porous membrane is 0.3mm, average hole
21 μm of footpath, porosity is 44%, and air permeability is 650m3/m2·h·kpa。
Embodiment 8
Embodiment 8 further includes step (6) on the basis of embodiment 7, i.e., be 0.5mol/L's with concentration
FeCl2Solution carries out immersion 45 minutes so as to which 304 stainless steels are dissolved to form three by selectivity on porous membrane to porous membrane
Secondary hole, is then dried to porous membrane and obtains finished product.The thickness of last obtained porous membrane is 0.3mm, average hole
24 μm of footpath, porosity is 48%, and air permeability is 900m3/m2·h·kpa。
Claims (8)
1. a kind of porous filtering film, thickness is 200~1500 μm, average pore size is 0.05~100 μm, porosity is 25~
75%, it is characterised in that：The step of its preparation method, includes：(1) support membrane is obtained, the support membrane has cavernous first
Once hole is formed on material, first material, the support membrane is net type film, and its mesh size is 20~1000 mesh；
(2) produce and contain the second powdered material in slurry, the slurry, the slurry is matched somebody with somebody by feed powder dispersant and binding agent
The thick slurry put；(3) slurry is coated on support membrane and then base substrate is made；(4) base substrate is carried out
Sintering, cavernous 3rd material of reaction generation is simultaneously produced and a hole simultaneously between the first material and the second material during sintering
The secondary hole of connection；(5) cooling obtains the porous filtering film integrally changed by the base substrate after sintering；It is described porous
Filtration membrane is the metal film that a kind of the 3rd material being made up of solid solution alloy is matrix phase, and first material constitutes this and consolidated
The solvent source of solution alloy, the second material constitutes the solute source of the solid solution alloy.
2. porous filtering film as claimed in claim 1, it is characterised in that：The mesh size of the support membrane is further selected
For 40~400 mesh.
3. porous filtering film as claimed in claim 1 or 2, it is characterised in that：In the step (4), the first material during sintering
With the second material diffusion pore-creating reaction partially occurs for material.
4. porous filtering film as claimed in claim 3, it is characterised in that：Be one kind by Ag-Au solid solution, Ti-Zr solid solutions
Body, Mg-Cd solid solution, Fe-Cr solid solution, Ni-Cu solid solution, Cu-Al solid solution, Cu-Zn solid solution or Fe-C-Cr solid solution
The 3rd material constituted is the metal film of matrix phase.
5. porous filtering film as claimed in claim 1 or 2, it is characterised in that：When in porous filtering film also containing not with
During the first material of the second material reaction, the preparation method also includes step (6), i.e., with etching solution to porous filtering film
Three holes will be formed so as to selective on porous filtering film after the dissolving of the first material by carrying out immersion, then to porous filtering
Film, which is dried, obtains finished product.
6. the preparation method of porous filtering film, its step includes：(1) Cu nets are used for support membrane, by the thickness of the support membrane
Degree is set as 0.5~1 millimeter, and mesh size is set as 40~200 mesh；(2) by Ni powder that particle diameter is -400 mesh using ethanol as point
Powder, PVB are that binding agent presses the proportional arrangement that 2~5 grams of PVB, 50~100 grams of Ni powder are added in every 100 milliliters of ethanol into slurry；
(3) slurry is coated on support membrane and dried and base substrate is made；(4) to base substrate carry out segmented sintering, the first stage from
Room temperature rises to 120~250 DEG C and is incubated 120~180 minutes, and second stage is warming up to 500~600 DEG C and 60~240 points of insulation
Clock, the phase III is warming up to 900~1090 DEG C and is incubated 90~240 minutes；(5) cooled down after sintering and porous filtering film is made.
7. method as claimed in claim 6, it is characterised in that：Second stage heating rate≤5 DEG C/min during sintering, the 3rd
Stage heating rate≤10 DEG C/min.
8. method as claimed in claims 6 or 7, it is characterised in that：Do not reacted when also containing in porous filtering film with Ni powder
Cu when, methods described also include step (6), i.e., with concentration be 0.5~1mol/L FeCl3Solution enters to porous filtering film
Row immersion dissolves Cu to form three holes for 20~40 minutes so as to selective on porous filtering film, then to porous filtering
Film, which is dried, obtains finished product.