CN104945802B - A kind of buried high voltage power cable high temperature resistant PVC C sleeve pipes - Google Patents
A kind of buried high voltage power cable high temperature resistant PVC C sleeve pipes Download PDFInfo
- Publication number
- CN104945802B CN104945802B CN201510283970.1A CN201510283970A CN104945802B CN 104945802 B CN104945802 B CN 104945802B CN 201510283970 A CN201510283970 A CN 201510283970A CN 104945802 B CN104945802 B CN 104945802B
- Authority
- CN
- China
- Prior art keywords
- parts
- solution
- mass concentration
- temperature resistant
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of buried high voltage power cable high temperature resistant PVC C sleeve pipes, it is mixed by the raw material components of following parts by weight meter：100 parts of chlorinated polyethylene resin, 20 30 parts of polyvinyl chloride resin, 25 35 parts of light calcium carbonate powder, 58 parts of high temperature resistant reinforced modifier, 46 parts of styrene N phenyl maleimides maleic anhydride terpolymer, modified micaceous 35 parts, 35 parts of glass fibre, 23 parts of calcium zinc stabilizer, 0.5 0.8 parts of dispersant, 12 parts of lubricant, 12 parts of toughener, 1 1.5 parts of ACR processing aids.The present invention has excellent insulating properties, well higher intensity and resistance to elevated temperatures.
Description
Technical field
The present invention relates to a kind of PVC-C sleeve pipes, more particularly to a kind of buried high voltage power cable is covered with high temperature resistant PVC-C
Pipe.
Background technology
Cable protecting sleeve is a kind of new casing material promoted the use of in power engineering.As imbedded power cable applies
If engineering develops rapidly, to the requirements at the higher level of cable sleeve proposition, cable protecting sleeve is generally use polythene PE material
It is made, it is a kind of electric insulating tube for protecting electric wire and cable the most frequently used.But use and find PE tube capacity easily by external force
And deform, the normal laying of later stage cable is have impact on, is not suitable for type ground-buried power cable protecting pipe.
PVC-C sleeve pipes are green products generally acknowledged at present using PVC-C resins as main material, its excellent materialization
Performance is just increasingly paid attention to by industry.Conventional PVC-C sleeve pipes are resistant to higher temperature and with preferably intensity, but
It is under some particular surroundings, can not still meets its intensity and high temperature resistant demand.Conventional PVC-C sleeve pipes also have preferably absolutely
Edge, but to high voltage power cable in use, in order to meet insulating properties, it has to increase thickness to meet, can so lead
Cause the increase of installation and transportation difficulty.
The content of the invention
It is an object of the invention to provide a kind of buried high voltage power cable high temperature resistant PVC-C sleeve pipes, have excellent
Insulating properties, higher intensity and well resistance to elevated temperatures.
The technical solution adopted for the present invention to solve the technical problems is：
A kind of buried high voltage power cable high temperature resistant PVC-C sleeve pipes, mixed by the raw material components of following parts by weight meter
It is made：100 parts of chlorinated polyethylene resin, polyvinyl chloride resin 20-30 parts, light calcium carbonate powder 25-35 parts, high temperature resistant reinforced modifier 5-8 parts,
Styrene-N-phenylmaleimide-maleic anhydride terpolymer 4-6 parts, modified micaceous 3-5 parts, glass fibre 3-5 parts,
Calcium zinc stabilizer 2-3 parts, dispersant 0.5-0.8 parts, lubricant 1-2 parts, toughener 1-2 parts, ACR processing aid 1-1.5 parts.
The addition of glass fibre can play humidification, material surface hardness, rigidity, impact strength to PVC-C sleeve pipes
Have and be greatly improved etc. mechanical performance, while shrinkage factor diminishes, dimensional stability increase.Modified micaceous addition can play increase
Anti-flammability, especially increase electrical insulating property effect, high voltage power cable can be well adapted for, anti-electrical breakdown performance carries significantly
Height, it can need not increase the thickness of PVC-C sets and then excellent electrical insulation capability.And styrene-N- benzyl maleimides
Amine-maleic anhydride terpolymer can also increase substantially the heat resistance of product, be acted synergistically with other components, also carry simultaneously
The high mechanical performance of material.
Preferably, being used after the light calcium carbonate powder surface treated, the surface treatment is specially：First by 100kg fine particle calcium carbonates
Powder adds in aluminate coupling agent solution and mixes 60-90min, then adds silane coupler solution, mixes 40-60min, most
After be dried in vacuo.
Light calcium carbonate powder is easily reunited when in use, is caused in matrix resin（Chlorinated polyethylene resin+polyvinyl chloride resin）Disperse not
Uniformly, influence material property, and light calcium carbonate powder is inorganic material, when unprocessed and matrix resin bond strength it is not high, influence
Material property.Inventor develops specific process of surface treatment through studying for a long period of time, secondary to light calcium carbonate powder using different coupling agents
Surface treatment, effectively can prevent light calcium carbonate powder from reuniting, and strengthen the bond strength of light calcium carbonate powder and matrix resin.
The present invention first passes through carries out one-time surface processing using aluminate coupling agent to light calcium carbonate powder, can effectively improve fine particle calcium carbonate
Dispersiveness between powder and the dispersiveness in organic matter, then carry out secondary surface treatment, aluminium by adding silane coupler again
Acid esters coupling agent and silane coupler synergy can effectively wrap up light calcium carbonate powder, so can effectively solve asking for light calcium carbonate powder reunion
Topic, and surface active groups are provided to light calcium carbonate powder, strengthen the bond strength of light calcium carbonate powder and matrix resin, so improve fine particle calcium carbonate
The availability of powder, improve the performance of material.Last vacuum drying can reclaim ethanol.
Preferably, the aluminate coupling agent solution is the solution that aluminate coupling agent is mixed to form with absolute ethyl alcohol,
The mass concentration of aluminate coupling agent is 30-40% in aluminate coupling agent solution, and the dosage of aluminate coupling agent is light calcium carbonate powder weight
The 0.3-0.5% of amount；The silane coupler solution is the solution that silane coupler is mixed to form with absolute ethyl alcohol, silane coupled
The mass concentration of silane coupler is 30-40% in agent solution, and the dosage of silane coupler is the 0.1-0.3% of light calcium carbonate powder weight.
Preferably, the high temperature resistant reinforced modifier by weight percentage by 70%-80% modified carbon nano-tube and
30-40% nano aluminum nitride composition；The preparation method of the modified carbon nano-tube is as follows：
（1）Carbon nanotube powders are added in mass concentration 35-45% methanol solution and are uniformly mixed to obtain premixed liquid, will
Premixed liquid is with acid solution according to 1:3-5 volume ratio mixing, mechanical agitation 30-60min, filtering, respectively with water and absolute ethyl alcohol
CNT is washed, 3-4h is then dried in vacuo at 50-60 DEG C obtains primary modified carbon nano-tube；The acid solution is that quality is dense
Phosphoric acid solution that the salpeter solution for 4-6% is 10-12% with mass concentration is spent according to 1:The mixture of 1-2 volume ratios；Passing through will
CNT is added in mass concentration 35-45% methanol solution, enables to CNT to be uniformly dispersed, and is so beneficial to follow-up
Acid solution oxidation modification.Acid solution enables to carbon nanotube hydrophilicity to reduce, lipophile increase, so as to improve CNT
With the adhesion of matrix resin, increase enhancing effect.
（2）Primary modified carbon nano-tube is added in silane coupler-ethanol solution that mass concentration is 6-8%, lead to nitrogen
Under the conditions of gas, 50-80min is heated at 55-65 DEG C, absolute ethyl alcohol is dried in vacuo 3-5h at washing 3-4 times, 70-80 DEG C must be modified
CNT.
The present invention uses modified carbon nano-tube, makes carbon pipe surface functional groupization, to remove CNT in matrix resin
Reuniting effect lifting carbon pipe dispersiveness, while the covalent bond that can be interlinked with matrix resin is produced in carbon pipe surface, made
Organic/inorganic two forms powerful covalently bonded between interface, can be by impact energy when composite is by external impacts
The matrix resin weaker from intensity is transferred on the stronger carbon pipe of intensity, by the deformation of carbon tubular elastic or distortion, and then will impact
Energy dissipation falls, and reaches optimal toughened and reinforced effect.
Silane coupled agent molecule produces silanol base after hydrolyzing, and CNT carries in its surface tentatively modified
Hydroxyl, silanol base can be sloughed a hydrone retraction and are combined, make silane coupler and carbon nanometer with hydroxyl row condensation reaction
Linked together between pipe so that covalently bonded is powerful, and assign CNT new functional group, this functional group can enter one
Step acts on matrix resin, further improves binding ability, the intensity and toughness of reinforcing material.
The present invention by adding high temperature resistant reinforced modifier, can not only reinforcing material intensity and toughness, while can improve
The resistance to elevated temperatures of material.High temperature resistant reinforced modifier is by 70%-80% modified carbon nano-tube and 30-40% nano aluminum nitride
Composition, CNT obtain heat dispersion with preferable in itself, can improve the resistance to elevated temperatures of material, nano aluminum nitride powder has excellent
Different heat conductivility, modified carbon nano-tube be linked to be in the base it is netted, formed skeleton, provide dispersing matrixes for aluminium nitride, nitridation
Aluminium is attached on CNT wall, high efficiency and heat radiation net is formed, so as to improve the resistance to elevated temperatures of material.
Preferably, being used after the modified processing of glass fibre, the method for modification is：Glass fibre is immersed
Mass concentration is in 15-20% salpeter solution, is ultrasonically treated 10-15min, is then 10%- in mass concentration by glass fibre
15-30min is impregnated in 20% silane coupler-ethanol solution, glass fibre is taken out, 5- is dried in vacuo at 40-50 DEG C
8h.Handled by the way that glass fibre is immersed in salpeter solution solution, to remove the impurity on glass surface and make fiberglass surfacing
Thick good fortune increase specific surface area, to lift the bond strength with matrix resin.Silane coupler-ethanol solution modified glass
After fiber, the bond strength of glass fibre and matrix resin can be lifted.
Preferably, the toughener is Methacrylate-butadiene-styrene.
Preferably, the modified micaceous preparation method comprises the following steps：
（1）Mica flake calcined at 700-800 DEG C to 1-1.5 hours obtains ripe mica material, then crosses 5-10 mesh sieves；Calcining
To slough the partially crystallizable water in micaceous structure, mica flake is set to become along perpendicular to the expansion of the direction of cleavage surface, layering, quality
It is soft；Calcining can also allow the impurity such as the crystallization stone being present in mica flake, silt to become ash content, be easy to clean.
（2）Ripe mica material after sieving is impregnated into 1-2 hours in mass concentration 70-85% sodium bicarbonate solutions；Impregnated carbon
After sour hydrogen sodium, it can decompose in lower step cracking reaction and produce great amount of carbon dioxide, act on mica flake from inside to outside, promote
Mica fragmentation.
（3）By ammoniacal liquor that the ripe mica material after dipping and mass concentration are 30-40% according to 1:2-4 weight is stirred than mixing
350-450 DEG C of holding 1-2 hour is heated under the conditions of mixing；Ripe mica material after dipping is mixed with ammoniacal liquor, first ammoniacal liquor and carbon
Sour hydrogen sodium reacts, and can promote mica fragmentation, and secondly, while reaction and reacted product can produce under heating stirring
Raw substantial amounts of carbon dioxide and ammonia, act on mica flake, promote mica fragmentation so that mica, which is sufficiently separated, to be obtained from inside to outside
Obtain less scale.
（4）By step（3）Mica clinker after processing is with water according to 1:8-10 part by weight is added in reactor, from anti-
Answer bottom portion to lead to steam into reactor and reactor is heated to 120-130 DEG C, maintain 40-70 minutes to obtain ripe mica slurry, ripe cloud
Mother's slurry dry, pulverize, and cross 400-600 mesh sieves.The heat source of reactor is steam, and steam is passed through in reactor bottom, so
Strong stirring action is played simultaneously in heating, further such that mica, which is sufficiently separated, obtains less scale, energy and matrix
Resin preferably mixes.
Preferably, the dispersant is Tissuemat E.
Preferably, the lubricant is calcium stearate.
The beneficial effects of the invention are as follows：With excellent insulating properties, higher intensity and well resistance to elevated temperatures, peace
Fill convenient transportation.
Embodiment
Below by specific embodiment, technical scheme is described in further detail.
In the present invention, if not refering in particular to, used raw material and equipment etc. are commercially available or commonly used in the art.
Method in following embodiments, it is the conventional method of this area unless otherwise instructed.
Chlorinated polyethylene resin, polyvinyl chloride resin in the present invention（Model SG-5）, light calcium carbonate powder（400-500 mesh）, styrene-N-
Phenyl maleimide-maleic anhydride terpolymer, calcium zinc stabilizer, ACR processing aids etc. are commercially available prod.
Embodiment 1：
A kind of buried high voltage power cable high temperature resistant PVC-C sleeve pipes, mixed by the raw material components of following parts by weight meter
It is made：100 parts of chlorinated polyethylene resin, 20 parts of polyvinyl chloride resin, 25 parts of light calcium carbonate powder, 5 parts of high temperature resistant reinforced modifier, styrene-N-
6 parts of phenyl maleimide-maleic anhydride terpolymer, modified micaceous 3 parts, 5 parts of glass fibre, calcium zinc stabilizer（Calcium zinc
Compound stabilizer, it is commercially available）2 parts, dispersant（Tissuemat E）0.5 part, lubricant（Calcium stearate）1 part, toughener（Metering system
Acid-BS, MBS are commercially available）1 part, 1 part of ACR processing aids.
Used after the modified processing of glass fibre, the method for modification is：Glass fibre is immersed into mass concentration
For in 15% salpeter solution, be ultrasonically treated 15min, then by glass fibre mass concentration be 10% Silane coupling agent KH550-
30min is impregnated in ethanol solution, glass fibre is taken out, 8h is dried in vacuo at 40 DEG C.
The high temperature resistant reinforced modifier is by weight percentage by 70%-80% modified carbon nano-tube and receiving for 30-40%
Rice aluminium nitride composition；The preparation method of the modified carbon nano-tube is as follows：
（1）Carbon nanotube powders are added in the methanol solution of mass concentration 35% and are uniformly mixed to obtain premixed liquid, 1g carbon is received
Mitron powder uses 10ml methanol solutions, by premixed liquid and acid solution according to 1:5 volume ratio mixing, mechanical agitation 60min, mistake
Filter, washs CNT with water and absolute ethyl alcohol respectively, and 4h is then dried in vacuo at 50 DEG C obtains primary modified carbon nano-tube；Institute
State acid solution be salpeter solution and mass concentration that mass concentration is 4% be 12% phosphoric acid solution according to 1:The mixing of 1 volume ratio
Thing；
（2）Primary modified carbon nano-tube is added into the silane coupler that mass concentration is 6%（KH550）- ethanol solution
In, lead under condition of nitrogen gas, 80min is heated at 55 DEG C, vacuum drying 5h obtains modified carbon nano tube at absolute ethyl alcohol washs 3 times, 70 DEG C
Pipe.
The modified micaceous preparation method comprises the following steps：
（1）Mica flake is calcined 1.5 hours to obtain to ripe mica material at 700 DEG C, then crosses 5 mesh sieves；
（2）Ripe mica material after sieving is impregnated 2 hours in the sodium bicarbonate solution of mass concentration 70%；
（3）By ammoniacal liquor that the ripe mica material after dipping and mass concentration are 30% according to 1:4 weight is than mixing, stirring bar
350 DEG C are heated under part to be kept for 2 hours；
（4）By step（3）Mica clinker after processing is with water according to 1:8 part by weight is added in reactor, from reaction
Bottom portion leads to steam into reactor and reactor is heated into 120 DEG C, maintains to obtain within 70 minutes ripe mica slurry, and ripe mica starches drying,
Crush, cross 400 mesh sieves.
Embodiment 2：
A kind of buried high voltage power cable high temperature resistant PVC-C sleeve pipes, mixed by the raw material components of following parts by weight meter
It is made：100 parts of chlorinated polyethylene resin, 30 parts of polyvinyl chloride resin, 35 parts of light calcium carbonate powder, 8 parts of high temperature resistant reinforced modifier, styrene-N-
4 parts of phenyl maleimide-maleic anhydride terpolymer, modified micaceous 5 parts, 3 parts of glass fibre, calcium zinc stabilizer（Calcium zinc
Compound stabilizer, it is commercially available）3 parts, dispersant（Tissuemat E）0.8 part, lubricant（Calcium stearate）2 parts, toughener（Metering system
Acid-BS, MBS are commercially available）2 parts, 1.5 parts of ACR processing aids.
Used after the modified processing of glass fibre, the method for modification is：Glass fibre is immersed into mass concentration
In 20% salpeter solution, to be ultrasonically treated 10min, being then 20% silane coupler KH560- in mass concentration by glass fibre
15min is impregnated in ethanol solution, glass fibre is taken out, 5h is dried in vacuo at 50 DEG C.
The high temperature resistant reinforced modifier is by weight percentage by 70%-80% modified carbon nano-tube and receiving for 30-40%
Rice aluminium nitride composition；The preparation method of the modified carbon nano-tube is as follows：
（1）Carbon nanotube powders are added in the methanol solution of mass concentration 45% and are uniformly mixed to obtain premixed liquid, 1g carbon is received
Mitron powder uses 10ml methanol solutions, by premixed liquid and acid solution according to 1:3 volume ratio mixing, mechanical agitation 30min, mistake
Filter, washs CNT with water and absolute ethyl alcohol respectively, and 3h is then dried in vacuo at 60 DEG C obtains primary modified carbon nano-tube；Institute
State acid solution be salpeter solution and mass concentration that mass concentration is 6% be 10% phosphoric acid solution according to 1:The mixing of 2 volume ratios
Thing；
（2）Primary modified carbon nano-tube is added into the silane coupler that mass concentration is 8%（KH550）- ethanol solution
In, lead under condition of nitrogen gas, 50min is heated at 65 DEG C, vacuum drying 3h obtains carbon modified and received at absolute ethyl alcohol washs 4 times, 80 DEG C
Mitron.
The modified micaceous preparation method comprises the following steps：
（1）Mica flake is calcined 1 hour to obtain to ripe mica material at 800 DEG C, then crosses 10 mesh sieves；
（2）Ripe mica material after sieving is impregnated 1 hour in the sodium bicarbonate solution of mass concentration 85%；
（3）By ammoniacal liquor that the ripe mica material after dipping and mass concentration are 40% according to 1:2 weight is than mixing, stirring bar
450 DEG C are heated under part to be kept for 1 hour；
（4）By step（3）Mica clinker after processing is with water according to 1:10 part by weight is added in reactor, from anti-
Answer bottom portion to lead to steam into reactor and reactor is heated to 130 DEG C, maintain 40 minutes to obtain ripe mica slurry, ripe mica is starched dry
It is dry, crush, cross 500 mesh sieves.
Embodiment 3：
A kind of buried high voltage power cable high temperature resistant PVC-C sleeve pipes, mixed by the raw material components of following parts by weight meter
It is made：100 parts of chlorinated polyethylene resin, 25 parts of polyvinyl chloride resin, 30 parts of light calcium carbonate powder, 6 parts of high temperature resistant reinforced modifier, styrene-N-
5 parts of phenyl maleimide-maleic anhydride terpolymer, modified micaceous 4 parts, 4 parts of glass fibre, calcium zinc stabilizer（Calcium zinc
Compound stabilizer, it is commercially available）2.5 parts, dispersant（Tissuemat E）0.6 part, lubricant（Calcium stearate）1.5 parts, toughener（Methyl
Acryl-butadiene-styrol copolymer, MBS are commercially available）1.5 parts, 1.2 parts of ACR processing aids.
Used after the modified processing of glass fibre, the method for modification is：Glass fibre is immersed into mass concentration
In 18% salpeter solution, to be ultrasonically treated 12min, being then 15% silane coupler KH570- in mass concentration by glass fibre
230min is impregnated in ethanol solution, glass fibre is taken out, 6h is dried in vacuo at 45 DEG C.
The high temperature resistant reinforced modifier is by weight percentage by 70%-80% modified carbon nano-tube and receiving for 30-40%
Rice aluminium nitride composition；The preparation method of the modified carbon nano-tube is as follows：
（1）Carbon nanotube powders are added in the methanol solution of mass concentration 40% and are uniformly mixed to obtain premixed liquid, 1g carbon is received
Mitron powder uses 10ml methanol solutions, by premixed liquid and acid solution according to 1:4 volume ratio mixing, mechanical agitation 50min, mistake
Filter, washs CNT with water and absolute ethyl alcohol respectively, and 3.5h is then dried in vacuo at 55 DEG C obtains primary modified carbon nano-tube；
The acid solution is the salpeter solution that mass concentration is 5% and the phosphoric acid solution that mass concentration is 10% according to 1:1.5 volume ratios
Mixture；
（2）Primary modified carbon nano-tube is added into the silane coupler that mass concentration is 7%（KH550）- ethanol solution
In, lead under condition of nitrogen gas, 60min is heated at 60 DEG C, vacuum drying 4h obtains modified carbon nano tube at absolute ethyl alcohol washs 3 times, 75 DEG C
Pipe.
The modified micaceous preparation method comprises the following steps：
（1）Mica flake is calcined 1.2 hours to obtain to ripe mica material at 750 DEG C, then crosses 10 mesh sieves；
（2）Ripe mica material after sieving is impregnated 1.5 hours in the sodium bicarbonate solution of mass concentration 80%；
（3）By ammoniacal liquor that the ripe mica material after dipping and mass concentration are 35% according to 1:3 weight is than mixing, stirring bar
400 DEG C are heated under part to be kept for 1.5 hours；
（4）By step（3）Mica clinker after processing is with water according to 1:9 part by weight is added in reactor, from reaction
Bottom portion leads to steam into reactor and reactor is heated into 125 DEG C, maintains to obtain within 60 minutes ripe mica slurry, and ripe mica starches drying,
Crush, cross 600 mesh sieves.
Embodiment 4：
With embodiment 3, difference is to be surface-treated light calcium carbonate powder the formula and preparation method of the present embodiment,
Specially：First 100kg light calcium carbonate powders are added in aluminate coupling agent solution and mix 60min, it is molten then to add silane coupler
Liquid, 60min is mixed, is finally dried in vacuo, aluminate coupling agent solution is what aluminate coupling agent was mixed to form with absolute ethyl alcohol
Solution, aluminate coupling agent in aluminate coupling agent solution（It is commercially available）Mass concentration be 30%, the dosage of aluminate coupling agent is
The 0.3% of light calcium carbonate powder weight；Silane coupler solution is silane coupler（It is commercially available, KH560）It is mixed to form with absolute ethyl alcohol molten
Liquid, the mass concentration of silane coupler is 30% in silane coupler solution, and the dosage of silane coupler is light calcium carbonate powder weight
0.3%。
Embodiment 5：
With embodiment 3, difference is to be surface-treated light calcium carbonate powder the formula and preparation method of the present embodiment,
Specially：First 100kg light calcium carbonate powders are added in aluminate coupling agent solution and mix 90min, it is molten then to add silane coupler
Liquid, 40min is mixed, is finally dried in vacuo, aluminate coupling agent solution is what aluminate coupling agent was mixed to form with absolute ethyl alcohol
Solution, the mass concentration of aluminate coupling agent is 40% in aluminate coupling agent solution, and the dosage of aluminate coupling agent is light calcium carbonate powder
The 0.5% of weight；The solution that silane coupler solution is mixed to form for silane coupler with absolute ethyl alcohol, silane coupler solution
The mass concentration of middle silane coupler is 40%, and the dosage of silane coupler is the 0.1% of light calcium carbonate powder weight.
Embodiment 6：
With embodiment 3, difference is to be surface-treated light calcium carbonate powder the formula and preparation method of the present embodiment,
Specially：First 100kg light calcium carbonate powders are added in aluminate coupling agent solution and mix 80min, it is molten then to add silane coupler
Liquid, 50min is mixed, is finally dried in vacuo, aluminate coupling agent solution is what aluminate coupling agent was mixed to form with absolute ethyl alcohol
Solution, the mass concentration of aluminate coupling agent is 35% in aluminate coupling agent solution, and the dosage of aluminate coupling agent is light calcium carbonate powder
The 0.4% of weight；The solution that silane coupler solution is mixed to form for silane coupler with absolute ethyl alcohol, silane coupler solution
The mass concentration of middle silane coupler is 35%, and the dosage of silane coupler is the 0.2% of light calcium carbonate powder weight.
Each raw material components according to a conventional method, need to only be well mixed in the preparation, then enter twin-screw and squeeze by the present invention
Go out machine melting, extrusion molding.
Product of the present invention has preferably high temperature resistant and ageing resistace, and it is short because overloading using process to adapt to high-tension cable
Road and caused high temperature, have high insulation resistance and specific insulation；Flexible and compression strength is big, anti-differential settlement, production
Product long lifespan.
According to QB/T 2479-2005 standard detection, the standard compliant rule of testing result of PVC-C sleeve pipes of the present invention
Fixed, partial parameters are as follows：
Vicat softening temperature reaches 105 DEG C；Longitudinal welds ＜ 1.0%；Specific insulation >=1.85 × 1011Ω.m；Pipe
Flatten 70% crack-free in footpath；Do not occur rupturing during the standard drop hammer impulse detection and crack.
Embodiment described above is a kind of preferable scheme of the present invention, not the present invention is made any formal
Limitation, there are other variants and remodeling on the premise of without departing from the technical scheme described in claim.
Claims (5)
1. a kind of buried high voltage power cable high temperature resistant PVC-C sleeve pipes, it is characterised in that by the raw material of following parts by weight meter
Component is mixed：100 parts of chlorinated polyvinyl chloride resin, polyvinyl chloride resin 20-30 parts, light calcium carbonate powder 25-35 parts, high temperature resistant enhancing change
Property agent 5-8 parts, styrene-N-phenylmaleimide-maleic anhydride terpolymer 4-6 parts, modified micaceous 3-5 parts, glass
Fiber 3-5 parts, calcium zinc stabilizer 2-3 parts, dispersant 0.5-0.8 parts, lubricant 1-2 parts, toughener 1-2 parts, ACR processing aids
1-1.5 part；
The high temperature resistant reinforced modifier is by weight percentage by 70%-80% modified carbon nano-tube and 30-40% nanometer nitrogen
Change aluminium composition；The preparation method of the modified carbon nano-tube is as follows：
（1）Carbon nanotube powders are added in mass concentration 35-45% methanol solution and are uniformly mixed to obtain premixed liquid, will be premixed
Liquid is with acid solution according to 1:3-5 volume ratio mixing, mechanical agitation 30-60min, filtering, is washed with water and absolute ethyl alcohol respectively
CNT, 3-4h is then dried in vacuo at 50-60 DEG C and obtains primary modified carbon nano-tube；The acid solution is that mass concentration is
4-6% salpeter solution and mass concentration is 10-12% phosphoric acid solution according to 1:The mixture of 1-2 volume ratios；
（2）Primary modified carbon nano-tube is added in silane coupler-ethanol solution that mass concentration is 6-8%, lead to nitrogen bar
Under part, 50-80min is heated at 55-65 DEG C, vacuum drying 3-5h obtains carbon modified and received at absolute ethyl alcohol washs 3-4 times, 70-80 DEG C
Mitron；
The modified micaceous preparation method comprises the following steps：
（1）Mica flake calcined at 700-800 DEG C to 1-1.5 hours obtains ripe mica material, then crosses 5-10 mesh sieves；
（2）Ripe mica material after sieving is impregnated into 1-2 hours in mass concentration 70-85% sodium bicarbonate solutions；
（3）By ammoniacal liquor that the ripe mica material after dipping and mass concentration are 30-40% according to 1:2-4 weight is than mixing, stirring bar
350-450 DEG C of holding 1-2 hour is heated under part；
（4）By step（3）Mica clinker after processing is with water according to 1:8-10 part by weight is added in reactor, from reactor
Bottom leads to steam into reactor and reactor is heated into 120-130 DEG C, maintains 40-70 minutes to obtain ripe mica slurry, ripe mica slurry
It dry, pulverize, cross 400-600 mesh sieves；
Used after the light calcium carbonate powder surface treated, the surface treatment is specially：It is even that 100kg light calcium carbonate powders are first added into Aluminate
60-90min is mixed in connection agent solution, then adds silane coupler solution, 40-60min is mixed, is finally dried in vacuo；
Used after the modified processing of glass fibre, the method for modification is：It is 15- by glass fibre immersion mass concentration
In 20% salpeter solution, be ultrasonically treated 10-15min, then by glass fibre mass concentration be 10%-20% silane couplers-
15-30min is impregnated in ethanol solution, glass fibre is taken out, 5-8h is dried in vacuo at 40-50 DEG C.
A kind of 2. buried high voltage power cable high temperature resistant PVC-C sleeve pipes according to claim 1, it is characterised in that：
The aluminate coupling agent solution is the solution that aluminate coupling agent and absolute ethyl alcohol are mixed to form, in aluminate coupling agent solution
The mass concentration of aluminate coupling agent is 30-40%, and the dosage of aluminate coupling agent is the 0.3-0.5% of light calcium carbonate powder weight；It is described
Silane coupler solution is the solution that silane coupler and absolute ethyl alcohol are mixed to form, silane coupler in silane coupler solution
Mass concentration be 30-40%, the dosage of silane coupler is the 0.1-0.3% of light calcium carbonate powder weight.
A kind of 3. buried high voltage power cable high temperature resistant PVC-C sleeve pipes according to claim 1, it is characterised in that：
The toughener is Methacrylate-butadiene-styrene.
A kind of 4. buried high voltage power cable high temperature resistant PVC-C sleeve pipes according to claim 1, it is characterised in that：
The dispersant is Tissuemat E.
A kind of 5. buried high voltage power cable high temperature resistant PVC-C sleeve pipes according to claim 1, it is characterised in that：
The lubricant is calcium stearate.