CN104944845A - Ceramic tile adhesive for building - Google Patents
Ceramic tile adhesive for building Download PDFInfo
- Publication number
- CN104944845A CN104944845A CN201510295267.2A CN201510295267A CN104944845A CN 104944845 A CN104944845 A CN 104944845A CN 201510295267 A CN201510295267 A CN 201510295267A CN 104944845 A CN104944845 A CN 104944845A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic tile
- tile adhesive
- building
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a ceramic tile adhesive for building and belongs to the technical field of building materials. The ceramic tile adhesive is prepared from the following raw materials, by weight, 10-30 parts of an acrylicester copolymer emulsion, 10-20 parts of maleic anhydride, 5-15 parts of hydroxyethylmethylcellulose, 5-15 parts of resin rubber powder, 10-30 parts of silicon powder, 5-15 parts of calcium bicarbonate, 5-15 parts of magnesium chloride and 1-10 parts of talcum powder. The ceramic tile adhesive is convenient to construct and can be used only by adding a proper amount of clear water and stirring. Ceramic tiles to be adhered need not be soaked in water but can directly be adhered. The ceramic tile adhesive has high bonding strength and fast hardening speed. Service life of various auxiliary materials can be greatly prolonged and decorative effect can be enhanced, and safety is high. The ceramic tile adhesive has good water-retaining property, peaceability and flow fall resistance, and is convenient to use.
Description
Technical field
The invention belongs to the technical field of material of construction, refer to a kind of construction tile binding agent especially.
Background technology
Along with the development of modern science and technology and the raising of people's living standard, people require more and more higher for the aesthetic feeling of building, and ceramic tile is with the performance of its excellence, safety, expressive force, construction and environment-friendly advantage, and one jumps and becomes the first-selection of people's house decoraton.But ceramic tile, when pasting, needs special tackiness agent to meet its service requirements; Tile adhesives is a kind of building adhesive for finishing material such as sticking brick, face brick, floor tiles just, can be widely used in the facing decoration places of the buildings such as inside and outside metope, ground, bathroom, kitchen.But, existing ceramic tile bond many employings sand-cement slurry, this mortar construction very inconvenience, and also its cohesive force is weak, poor durability, easily peels off; The mode of usual employing stirring and thick-layer construction, proportioning is unstable, and affect the weather resistance of ceramic tile, waste raw material, also affect speed of application, contaminate environment, its security can not be guaranteed, and is easy to occur security incident.
Summary of the invention
The invention provides a kind of construction tile binding agent, solve that ceramic tile bond cohesive force in prior art is weak, poor durability and the flaky problem of appearance.
A kind of construction tile binding agent of the present invention, it is mainly realized by the following technical programs: be made up of the raw material of following weight part: acrylate copolymer emulsion 10-30 part, maleic anhydride 10-20 part, hydroxyethylmethyl-cellulose 5-15 part, resin rubber powder 5-15 part, silica flour 10-30 part, Calcium hydrogen carbonate 5-15 part, magnesium chloride 5-15 part, talcum powder 1-10 part.
Preferably, be made up of the raw material of following weight part: acrylate copolymer emulsion 20 parts, maleic anhydride 15 parts, hydroxyethylmethyl-cellulose 10 parts, resin rubber powder 10 parts, silica flour 20 parts, Calcium hydrogen carbonate 10 parts, 10 parts, magnesium chloride, talcum powder 5 parts.
The invention has the beneficial effects as follows: ceramic tile bond easy construction of the present invention, only need add proper amount of clear water and stir and can use, the ceramic tile be stuck, without the need to soaked, can directly be pasted; Cohesive strength is high, and setting rate is fast, and greatly can improve work-ing life and the decorative effect of various dressing material, safety performance is high; Have good water-retentivity, workability, anti-current pendant property, good endurance, there will not be peeling phenomenon, easy to use.
Embodiment
Be clearly and completely described technical scheme of the present invention below in conjunction with specific embodiments of the invention, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
A kind of construction tile binding agent of the present invention, is made up of the raw material of following weight part: acrylate copolymer emulsion 10-30 part, maleic anhydride 10-20 part, hydroxyethylmethyl-cellulose 5-15 part, resin rubber powder 5-15 part, silica flour 10-30 part, Calcium hydrogen carbonate 5-15 part, magnesium chloride 5-15 part, talcum powder 1-10 part.
Preferably, be made up of the raw material of following weight part: acrylate copolymer emulsion 20 parts, maleic anhydride 15 parts, hydroxyethylmethyl-cellulose 10 parts, resin rubber powder 10 parts, silica flour 20 parts, Calcium hydrogen carbonate 10 parts, 10 parts, magnesium chloride, talcum powder 5 parts.
embodiment one
A kind of construction tile binding agent of the present invention, is made up of the raw material of following weight part: acrylate copolymer emulsion 10 parts, maleic anhydride 10 parts, hydroxyethylmethyl-cellulose 5 parts, resin rubber powder 5 parts, silica flour 10 parts, Calcium hydrogen carbonate 5 parts, 5 parts, magnesium chloride, talcum powder 1 part.
embodiment two
A kind of construction tile binding agent of the present invention, is made up of the raw material of following weight part: acrylate copolymer emulsion 20 parts, maleic anhydride 15 parts, hydroxyethylmethyl-cellulose 10 parts, resin rubber powder 10 parts, silica flour 20 parts, Calcium hydrogen carbonate 10 parts, 10 parts, magnesium chloride, talcum powder 5 parts.
embodiment three
A kind of construction tile binding agent of the present invention, is made up of the raw material of following weight part: acrylate copolymer emulsion 30 parts, maleic anhydride 20 parts, hydroxyethylmethyl-cellulose 15 parts, resin rubber powder 15 parts, silica flour 30 parts, Calcium hydrogen carbonate 15 parts, 15 parts, magnesium chloride, talcum powder 10 parts.
Get the embodiment of the present invention one to prepare to the construction tile binding agent of embodiment three and cement, quartz sand and obtain ceramic tile bond, carry out water resistance test experiments according to JC/T547-2005 " ceramic wall and floor bricks tackiness agent " standard, its performance test results is as shown in table 1.
The different ceramic tile bond the performance test results of table 1
Interventions Requested | Stretch gluing former intensity (Mpa) | Stretching adhesive strength (Mpa) after immersion | Tensile strength (Mpa) after thermal ageing | Stretching adhesive strength (Mpa) after freeze-thaw cycle |
Standard-required (C1) | ≥0.5 | ≥0.5 | ≥0.5 | ≥0.5 |
Embodiment one | 2.5 | 2.0 | 2.0 | 2.2 |
Embodiment two | 2.5 | 2.1 | 2.0 | 2.2 |
Embodiment three | 2.5 | 2.1 | 2.0 | 2.2 |
Certain ceramic tile bond commercially available | 1.8 | 1.2 | 1.3 | 1.6 |
As can be seen from Table 1, construction tile binding agent of the present invention is in ceramic tile water resistance test experiments, and stretching adhesive strength, the tensile strength after thermal ageing and the stretching adhesive strength after freeze-thaw cycle after its gluing former intensity that stretches, immersion all reach the requirement of JC/T547-2005 " ceramic wall and floor bricks tackiness agent " standard; Compared with existing certain ceramic tile bond commercially available, the performance of its above-mentioned four indices is also higher than the performance of existing ceramic tile bond; Therefore, construction tile binding agent of the present invention not only reaches the regulation of relevant criterion, and more existing commercially available ceramic tile bond mealiness can improve a lot.
Therefore, the invention has the beneficial effects as follows: ceramic tile bond easy construction of the present invention, only need add proper amount of clear water and stir and can use, the ceramic tile be stuck, without the need to soaked, can directly be pasted; Cohesive strength is high, and setting rate is fast, and greatly can improve work-ing life and the decorative effect of various dressing material, safety performance is high; Have good water-retentivity, workability, anti-current pendant property, good endurance, there will not be peeling phenomenon, easy to use.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. a construction tile binding agent, is characterized in that, is made up of the raw material of following weight part:
Acrylate copolymer emulsion 10-30 part, maleic anhydride 10-20 part, hydroxyethylmethyl-cellulose 5-15 part, resin rubber powder 5-15 part, silica flour 10-30 part, Calcium hydrogen carbonate 5-15 part, magnesium chloride 5-15 part, talcum powder 1-10 part.
2. construction tile binding agent according to claim 1, is characterized in that, is made up of the raw material of following weight part:
Acrylate copolymer emulsion 20 parts, maleic anhydride 15 parts, hydroxyethylmethyl-cellulose 10 parts, resin rubber powder 10 parts, silica flour 20 parts, Calcium hydrogen carbonate 10 parts, 10 parts, magnesium chloride, talcum powder 5 parts.