CN104927708A - Cigarette polypropylene fiber filter rod forming solid adhesive and preparation method thereof - Google Patents
Cigarette polypropylene fiber filter rod forming solid adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN104927708A CN104927708A CN201510305193.6A CN201510305193A CN104927708A CN 104927708 A CN104927708 A CN 104927708A CN 201510305193 A CN201510305193 A CN 201510305193A CN 104927708 A CN104927708 A CN 104927708A
- Authority
- CN
- China
- Prior art keywords
- parts
- copolymer
- obtains
- ethylene
- cross
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cigarette polypropylene fiber filter rod forming solid adhesive which is prepared from the following raw materials in parts by weight: 1-2 parts of divinyl benzene, 4-6 parts of epoxy butyl oleate, 60-70 parts of microcrystalline paraffin, 10-14 parts of powdery butyronitrile, 2-3 parts of 2-mercaptobenzothiazole, 10-15 parts of sisal fiber, 0.8-2 parts of sp-80, 0.3-0.4 part of a nitric acid solution with the concentration of 10-12 mol/l, 200-210 parts of ethylene-ethyl acrylate copolymer, 1.3-2 parts of zirconium oxychloride, 0.5-1 part of lactic acid and 0.6-1 part of glycerin. According to the invention, by using lactic acid/glycerol organic zirconium, which has an obvious temperature-sensitive cross-linking characteristic, as a cross-linking agent, and ethylene-ethyl acrylate copolymer fiber base fluid as a thickening agent, and through cross-linking action, gel with good temperature resistance and shearing resistance can be formed. Since fiber-treated copolymer base fluid is adopted, the surface activity of the copolymer is improved, a cross-linking effect is promoted and viscoelasticity and thixotropy are improved.
Description
Technical field
The present invention relates to a kind of tackiness agent, particularly relate to a kind of propene fibre filter stick formation solid binder for cigarette and preparation method thereof.
Background technology
Traditional vegetable jelly tackiness agent, at high temperature facile hydrolysis, poor to the protectiveness of base material, and the thickening capabilities of ethylene-ethyl acrylate copolymer is strong, heat resistance is good;
The most frequently used linking agent of usual acquisition polymer gel is organic boron or organic zirconium, and organic borate cross-linker heatproof is the highest can only reach 150 DEG C, and organic zirconium can be cross-linked in acid condition, and heatproof is high, can reach 200 DEG C, has broad application prospects.
Summary of the invention
Object of the present invention is just to provide a kind of propene fibre filter stick formation solid binder for cigarette and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of propene fibre filter stick formation solid binder for cigarette, it is made up of the raw material of following weight parts:
Vinylstyrene 1-2, epoxyoleic acid butyl ester 4-6, microcrystalline wax 60-70, powdered nitrile rubber 10-14,2-thiol group benzimidazolyl 2-3, the salpeter solution 0.3-0.4 of sisal fibers 10-15, sp-80 0.8-2,10-12mol/l, ethylene-ethyl acrylate copolymer 200-210, zirconium oxychloride 1.3-2, lactic acid 0.5-1, glycerol 0.6-1.
A preparation method for propene fibre filter stick formation solid binder for cigarette, comprises the following steps:
(1) by powdered nitrile rubber, ethylene-ethyl acrylate copolymer mixing, raised temperature is 70-80 DEG C, adds Vinylstyrene, and insulation reaction 40-50 minute obtains polymer blend;
(2) sisal fibers being joined concentration is infiltrate 3-4 hour in the bisulfite potassium solution of 5-7%, take out post-drying abrasive dust, mix with sp-80, join in 50-60 times of water, drip the salpeter solution of above-mentioned 10-12mol/l, be heated to boiling, add polymer blend, adjustment PH is 6-6.5, is stirred to normal temperature, obtains copolymer fibre base fluid;
(3) joined by zirconium oxychloride in 2-3 times of water, stirring and dissolving, adds lactic acid, glycerol, and regulation system pH value, to 4-5, is uniformly mixed 4-5 hour, obtains organic zirconium crosslinker;
(4) joined in 3-4 times of dehydrated alcohol by 2-thiol group benzimidazolyl, stirring and dissolving, obtains oxidation resistance liquid;
(5) by copolymer fibre base fluid, organic zirconium crosslinker mixing, in the constant temperature oil bath of 80-90 DEG C, stir 20-30 minute, period drips above-mentioned oxidation resistance liquid, dropwises rear discharging cooling, obtains organic zirconium gel;
(6) mix with residue each raw material by organic zirconium gel, raised temperature is 170-180 DEG C, insulated and stirred 2-3 hour, cools, cuts off shaping, centrifugally to dry, to obtain final product through tank.
Advantage of the present invention is:
The present invention with lactic acid/glycerol organic zirconium for linking agent, it has obvious temperature sensitive crosslinking feature, with ethylene-ethyl acrylate copolymer fiber base fluid for viscosifying agent, pass through crosslinked action, the gel with good temperature and shearing sustainability can be formed, adopt the multipolymer base fluid of fiber treatment, multipolymer surfactivity can be improved, promote cross-linking effect, improve visco-elasticity and thixotropy.
Adhesive storage stability of the present invention is good, being conducive to the quality improving mouth rod, after heat fused, spraying with calming the anger, and makes polypropylene fiber ambient cure become rod.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail:
Embodiment 1:
A kind of propene fibre filter stick formation solid binder for cigarette, it is made up of the raw material of following weight parts:
Vinylstyrene 1, epoxyoleic acid butyl ester 6, microcrystalline wax 60, powdered nitrile rubber 14,2-thiol group benzimidazolyl 2, sisal fibers 15, sp-80 0.8, the salpeter solution 0.4 of 12mol/l, ethylene-ethyl acrylate copolymer 210, zirconium oxychloride 1.3, lactic acid 0.5, glycerol 0.6.
A preparation method for propene fibre filter stick formation solid binder for cigarette, comprises the following steps:
(1) by powdered nitrile rubber, ethylene-ethyl acrylate copolymer mixing, raised temperature is 80 DEG C, adds Vinylstyrene, and insulation reaction 40 minutes, obtains polymer blend;
(2) sisal fibers being joined concentration is infiltrate 4 hours in the bisulfite potassium solution of 5-7%, take out post-drying abrasive dust, mix with sp-80, join in 50 times of water, drip the salpeter solution of above-mentioned 12mol/l, be heated to boiling, add polymer blend, regulate PH to be 6.5, be stirred to normal temperature, obtain copolymer fibre base fluid;
(3) joined by zirconium oxychloride in 2 times of water, stirring and dissolving, adds lactic acid, glycerol, and regulation system pH value to 4 is uniformly mixed 4 hours, obtains organic zirconium crosslinker;
(4) joined in 3-4 times of dehydrated alcohol by 2-thiol group benzimidazolyl, stirring and dissolving, obtains oxidation resistance liquid;
(5) by copolymer fibre base fluid, organic zirconium crosslinker mixing, stir 20 minutes in the constant temperature oil bath of 90 DEG C, period drips above-mentioned oxidation resistance liquid, dropwises rear discharging cooling, obtains organic zirconium gel;
(6) mix with residue each raw material by organic zirconium gel, raised temperature is 1180 DEG C, insulated and stirred 2 hours, cools, cuts off shaping, centrifugally to dry, to obtain final product through tank.
Performance test:
Cohesive strength: 3.6MPa;
Viscosity: 3600mPa.s.
Claims (2)
1. a propene fibre filter stick formation solid binder for cigarette, is characterized in that what it was made up of the raw material of following weight parts:
Vinylstyrene 1-2, epoxyoleic acid butyl ester 4-6, microcrystalline wax 60-70, powdered nitrile rubber 10-14,2-thiol group benzimidazolyl 2-3, the salpeter solution 0.3-0.4 of sisal fibers 10-15, sp-80 0.8-2,10-12mol/l, ethylene-ethyl acrylate copolymer 200-210, zirconium oxychloride 1.3-2, lactic acid 0.5-1, glycerol 0.6-1.
2. a preparation method for propene fibre filter stick formation solid binder for cigarette as claimed in claim 1, is characterized in that comprising the following steps:
(1) by powdered nitrile rubber, ethylene-ethyl acrylate copolymer mixing, raised temperature is 70-80 DEG C, adds Vinylstyrene, and insulation reaction 40-50 minute obtains polymer blend;
(2) sisal fibers being joined concentration is infiltrate 3-4 hour in the bisulfite potassium solution of 5-7%, take out post-drying abrasive dust, mix with sp-80, join in 50-60 times of water, drip the salpeter solution of above-mentioned 10-12mol/l, be heated to boiling, add polymer blend, adjustment PH is 6-6.5, is stirred to normal temperature, obtains copolymer fibre base fluid;
(3) joined by zirconium oxychloride in 2-3 times of water, stirring and dissolving, adds lactic acid, glycerol, and regulation system pH value, to 4-5, is uniformly mixed 4-5 hour, obtains organic zirconium crosslinker;
(4) joined in 3-4 times of dehydrated alcohol by 2-thiol group benzimidazolyl, stirring and dissolving, obtains oxidation resistance liquid;
(5) by copolymer fibre base fluid, organic zirconium crosslinker mixing, in the constant temperature oil bath of 80-90 DEG C, stir 20-30 minute, period drips above-mentioned oxidation resistance liquid, dropwises rear discharging cooling, obtains organic zirconium gel;
(6) mix with residue each raw material by organic zirconium gel, raised temperature is 170-180 DEG C, insulated and stirred 2-3 hour, cools, cuts off shaping, centrifugally to dry, to obtain final product through tank.