CN104927019A - Polyurethane mop sponge and production method thereof - Google Patents
Polyurethane mop sponge and production method thereof Download PDFInfo
- Publication number
- CN104927019A CN104927019A CN201510358662.0A CN201510358662A CN104927019A CN 104927019 A CN104927019 A CN 104927019A CN 201510358662 A CN201510358662 A CN 201510358662A CN 104927019 A CN104927019 A CN 104927019A
- Authority
- CN
- China
- Prior art keywords
- component
- urethane
- mop sponge
- mop
- polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of polyurethane products and particularly relates to a polyurethane mop sponge and a production method thereof. The polyurethane mop sponge comprises a component A and a component B. The component A comprises polyether polyol DEP-3600H, polyether polyol DMN-550E, polyether polyol POP-H45, water, foam stabilizing agent, amine catalyst, crosslinking agent, chain extender and mill base. The component B comprises modified black material. The polyurethane mop sponge is good in filter performance, easy to clean, high in water absorption performance, elastic, hard to tear, less prone to deformation, soft in texture, anti-bacterial and resistant to odor.
Description
Technical field
The invention belongs to polyurethane product technical field, be specifically related to a kind of urethane mop sponge and preparation method thereof.
Background technology
The mop that present material does not easy cleaning, perishable, easily there are the shortcomings such as addle is forced out.And polyurethane sponge mop has good strainability, easy cleaning, very strong water-absorbent, flexible, not easily tear, not yielding, quality is soft, and antibacterial deodourizing, has different shapes and color to select, and is the preferably selection of family's daily cleaning.
Summary of the invention
The object of this invention is to provide a kind of urethane mop sponge, have complete processing simple, production efficiency is high, has good strainability, easy cleaning, and very strong water-absorbent is flexible, not easily tears, not yielding, and quality is soft, the advantage of antibacterial deodourizing; Invention also provides the preparation method of urethane mop sponge, scientific and reasonable, simple.
Urethane mop sponge of the present invention, is made up of component A and B component, with weight parts,
Component A:
B component:
Modification black material 45-75 part.
Described polyether glycol DEP-3600H is the polyether glycol of 3 functionality, molecular weight 6000; By Zibo moral, this polyethers believes that federal chemical Industrial Co., Ltd produces, the product surface skinning made of this kind of polyvalent alcohol is good, and demould time is fast.
Described polyether glycol DMN-550E is the polyether glycol of 3 functionality, molecular weight 300; By Zibo moral, this polyethers believes that federal chemical Industrial Co., Ltd produces, the goods water absorbing properties made of this kind of polyvalent alcohol is good.
Described polyether glycol POP-H45 is the grafted polyether polyol of 3 functionality, molecular weight 8000; By Zibo moral, this polyethers believes that federal chemical Industrial Co., Ltd produces, the goods good hand touch made of this kind of polyvalent alcohol, hardness is large.
Described suds-stabilizing agent is suds-stabilizing agent Y-10366; The suds-stabilizing agent Y-10366 stepping figure production has stable foam and regulates abscess, the effect of emulsification foam material.
Described amine catalyst is amine catalyst A33; The A33 that aerification chemical product company of the U.S. produces, mainly utilizes its high reactivity, plays stronger katalysis to gel reaction and foamable reaction.
Described linking agent is diethanolamine, has certain katalysis while stable foam structure to polyurethane reaction.
Described chainextender is BDO, and the molecular chain in reaction is expanded further, increases the snappiness of goods.
The black material of described modification is WANNATE 8019, NCO content (%) 26.0-27.0, outward appearance: brown, and liquid viscosity (25 DEG C) mPa.s :≤70-170, ten thousand China produces.
The preparation method of described urethane mop sponge of the present invention, step is as follows:
Each for component A raw material is added agitator mix, adjust constant material temperature 25 ± 2 DEG C, regulate agitator speed to 4000-4500r/min, the B component being preheated to 25 ± 2 DEG C is poured in component A and stirs 4-5s, mixture is poured in the mould being preheated to 40 ± 5 DEG C, the demoulding after 5-10min, obtains product.
The present invention compared with prior art, has following beneficial effect:
(1) the present invention has good strainability, easy cleaning, and very strong water-absorbent is flexible, not easily tears, not yielding, and quality is soft, antibacterial deodourizing.
(2) preparation method of the present invention is simple and easy to implement.
Embodiment
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
Raw material is composed as follows:
Component A:
B component:
WANNATE 8019 45kg。
Each for component A raw material is added agitator mix, adjust constant material temperature 25 DEG C, regulate agitator speed to 4200r/min, the B component being preheated to 25 DEG C is poured in component A and stirs 4.5s, poured into by mixture in the mould being preheated to 40 DEG C, the demoulding after 6min, obtains product.
Product index is in table 1.
Table 1 embodiment 1 product index
Embodiment 2
Raw material is composed as follows:
Component A:
B component:
WANNATE 8019 75kg。
Each for component A raw material is added agitator mix, adjust constant material temperature 23 DEG C, regulate agitator speed to 4000r/min, the B component being preheated to 23 DEG C is poured in component A and stirs 4s, poured into by mixture in the mould being preheated to 35 DEG C, the demoulding after 5min, obtains product.
Product index is in table 2.
Table 2 embodiment 2 product index
Tensile strength (MP) | Pants type tear strength | Hardness (Shao-C) |
(N/mm) | ||
4.9 | 6.5 | 32 |
Embodiment 3
Raw material is composed as follows:
Component A:
B component:
WANNATE 8019 60kg。
Each for component A raw material is added agitator mix, adjust constant material temperature 27 DEG C, regulate agitator speed to 4500r/min, the B component being preheated to 27 DEG C is poured in component A and stirs 5s, poured into by mixture in the mould being preheated to 45 DEG C, the demoulding after 10min, obtains product.
Product index is in table 3.
Table 3 embodiment 3 product index
Claims (10)
1. a urethane mop sponge, is characterized in that being made up of component A and B component, with weight parts,
Component A:
B component:
Modification black material 45-75 part.
2. urethane mop sponge according to claim 1, is characterized in that described polyether glycol DEP-3600H is the polyether glycol of 3 functionality, molecular weight 6000.
3. urethane mop sponge according to claim 1, is characterized in that described polyether glycol DMN-550E is the polyether glycol of 3 functionality, molecular weight 300.
4. urethane mop sponge according to claim 1, is characterized in that described polyether glycol POP-H45 is the grafted polyether polyol of 3 functionality, molecular weight 8000.
5. urethane mop sponge according to claim 1, is characterized in that described suds-stabilizing agent is suds-stabilizing agent Y-10366.
6. urethane mop sponge according to claim 1, is characterized in that described amine catalyst is amine catalyst A33.
7. urethane mop sponge according to claim 1, is characterized in that described linking agent is diethanolamine.
8. urethane mop sponge according to claim 1, is characterized in that described chainextender is BDO.
9. urethane mop sponge according to claim 1, is characterized in that the black material of described modification is WANNATE8019.
10. a preparation method for the arbitrary described urethane mop sponge of claim 1-9, is characterized in that step is as follows:
Each for component A raw material is added agitator mix, adjust constant material temperature 25 ± 2 DEG C, regulate agitator speed to 4000-4500r/min, the B component being preheated to 25 ± 2 DEG C is poured in component A and stirs 4-5s, mixture is poured in the mould being preheated to 40 ± 5 DEG C, the demoulding after 5-10min, obtains product.