CN104911621A - Mechanical device surface cleaning agent - Google Patents
Mechanical device surface cleaning agent Download PDFInfo
- Publication number
- CN104911621A CN104911621A CN201510395709.0A CN201510395709A CN104911621A CN 104911621 A CN104911621 A CN 104911621A CN 201510395709 A CN201510395709 A CN 201510395709A CN 104911621 A CN104911621 A CN 104911621A
- Authority
- CN
- China
- Prior art keywords
- parts
- cleaning agent
- surface cleaning
- mechanical means
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a mechanical device surface cleaning agent, comprising the following components in parts by weight: 10-20 parts of benzyl triphenylphosphonium bromide, 10-25 parts of fatty alcohol-polyoxyethylene ether sulfate, 10-25 parts of sodium molybdate, 10-30 parts of tartaric acid, 10-25 parts of polyethylene oxide propyl glyceryl polyoxyethyl ether, 3-5 parts of oleic acid hydroxyethyl imidazoline, 2-4 parts of cocoamidopropyl betaine and 50-150 parts of deionized water. The cleaning agent is applicable to cleaning the surfaces of the mechanical devices, and is simple in preparation method and convenient to use.
Description
Technical field
The present invention relates to a kind of mechanical means surface cleaning agent, belong to mechanical means cleaning technique field.
Background technology
Matting is widely used in the incrustation scales on surface such as the rolling mill scale of heat-exchange equipment, heat transfer equipment, cooling apparatus, iron and steel and other metallic substance in each industrial sector (as electric power, petrochemical industry, metallurgy and electronics etc.) and zone of oxidation and the cleaning of metal dirt.From socioeconomic angle, matting can reduce the fuel brought because of dirt and expend; From the angle of environment protection, decrease exhaust combustion gases and topsoil; From the view of security, mechanical means in use forms all kinds of chemical pollutant gradually, and these pollutents reduce the intensity of steel, thus cause the generation of chemical accident, and can be ensured the normal operation of equipment by matting.
Summary of the invention
The object of the present invention is to provide a kind of mechanical means surface cleaning agent, to clean for mechanical means surface better, improve cleaning performance.
To achieve these goals, technical scheme of the present invention is as follows.
A kind of mechanical means surface cleaning agent, forms by the composition of following masses number is composite: benzyltriphenylphosphonium bromide phosphine 10 ~ 20 parts, fatty alcohol polyoxyethylene ether sulfate 10 ~ 25 parts, Sodium orthomolybdate 10 ~ 25 parts, 10 ~ 30 parts, tartrate, polyoxyethyl propyl polyoxyethanyl glyceryl ether 10 ~ 25 parts, oleic acid hydroxyethyl imidazole quinoline 3 ~ 5 parts, AMONYL 380LC 2 ~ 4 parts and deionized water 50 ~ 150 parts.
Further, above-mentioned clean agent preparation method is as follows:
(1) at room temperature benzyltriphenylphosphonium bromide phosphine, fatty alcohol polyoxyethylene ether sulfate, Sodium orthomolybdate, tartrate are joined in deionized water, fully stir, form initial soln;
(2) in the step (1) obtain in solution and add polyoxyethyl propyl polyoxyethanyl glyceryl ether, oleic acid hydroxyethyl imidazole quinoline and AMONYL 380LC, be warming up to 40 ~ 80 DEG C, stirred;
(3) above-mentioned solution is cooled to room temperature, namely obtains this product.
This beneficial effect of the invention is: Multiple components mixing composition in this clean agent, be applicable to cleaning for mechanical means surface, preparation method is simple, easy to use.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described, better to understand the present invention.
Embodiment 1
Mechanical means surface cleaning agent in the present embodiment, forms by the composition of following masses number is composite: benzyltriphenylphosphonium bromide phosphine 10 parts, fatty alcohol polyoxyethylene ether sulfate 10 parts, Sodium orthomolybdate 10 parts, 10 parts, tartrate, polyoxyethyl propyl polyoxyethanyl glyceryl ether 10 parts, oleic acid hydroxyethyl imidazole quinoline 3 parts, AMONYL 380LC 2 parts and deionized water 50 parts.
Above-mentioned clean agent preparation method is as follows:
(1) at room temperature benzyltriphenylphosphonium bromide phosphine, fatty alcohol polyoxyethylene ether sulfate, Sodium orthomolybdate, tartrate are joined in deionized water, fully stir, form initial soln;
(2) in the step (1) obtain in solution and add polyoxyethyl propyl polyoxyethanyl glyceryl ether, oleic acid hydroxyethyl imidazole quinoline and AMONYL 380LC, be warming up to 40 DEG C, stirred;
(3) above-mentioned solution is cooled to room temperature, namely obtains this product.
Clean agent in the present embodiment has well cleans corrosion inhibition, add the clean agent after composition for cleaning of the present invention, the erosion rate of unlike material is all less than to the corrosion of carbon steel speed≤2.0g/ (m of regulation in GB/T25146-2010 " industrial equipments matting inspection of quality specification "
2h), Corrosion of Stainless Steel speed≤1.0g/ (m
2h), brass corrosion speed <1.0g/ (m
2h), red copper erosion rate≤1.0g/ (m
2h), aluminium erosion rate≤1.0g/ (m
2h), incrustation scale cleans rate>=97%, and rust deposite cleans rate>=97%, and therefore, clean agent composition of the present invention can meet the cleaning requirement of multiple mechanical means surface incrustation scale and rust deposite.
Embodiment 2
Mechanical means surface cleaning agent in the present embodiment, forms by the composition of following masses number is composite: benzyltriphenylphosphonium bromide phosphine 15 parts, fatty alcohol polyoxyethylene ether sulfate 20 parts, Sodium orthomolybdate 18 parts, 20 parts, tartrate, polyoxyethyl propyl polyoxyethanyl glyceryl ether 20 parts, oleic acid hydroxyethyl imidazole quinoline 4 parts, AMONYL 380LC 3 parts and deionized water 100 parts.
Above-mentioned clean agent preparation method is as follows:
(1) at room temperature benzyltriphenylphosphonium bromide phosphine, fatty alcohol polyoxyethylene ether sulfate, Sodium orthomolybdate, tartrate are joined in deionized water, fully stir, form initial soln;
(2) in the step (1) obtain in solution and add polyoxyethyl propyl polyoxyethanyl glyceryl ether, oleic acid hydroxyethyl imidazole quinoline and AMONYL 380LC, be warming up to 60 DEG C, stirred;
(3) above-mentioned solution is cooled to room temperature, namely obtains this product.
Clean agent in the present embodiment has well cleans corrosion inhibition, add the clean agent after composition for cleaning of the present invention, the erosion rate of unlike material is all less than to the corrosion of carbon steel speed≤2.0g/ (m of regulation in GB/T25146-2010 " industrial equipments matting inspection of quality specification "
2h), Corrosion of Stainless Steel speed≤1.0g/ (m
2h), brass corrosion speed <1.0g/ (m
2h), red copper erosion rate≤1.0g/ (m
2h), aluminium erosion rate≤1.0g/ (m
2h), incrustation scale cleans rate>=96%, and rust deposite cleans rate>=96%, and therefore, clean agent composition of the present invention can meet the cleaning requirement of multiple mechanical means surface incrustation scale and rust deposite.
Embodiment 3
Mechanical means surface cleaning agent in the present embodiment, forms by the composition of following masses number is composite: benzyltriphenylphosphonium bromide phosphine 20 parts, fatty alcohol polyoxyethylene ether sulfate 25 parts, Sodium orthomolybdate 25 parts, 30 parts, tartrate, polyoxyethyl propyl polyoxyethanyl glyceryl ether 25 parts, oleic acid hydroxyethyl imidazole quinoline 5 parts, AMONYL 380LC 4 parts and deionized water 150 parts.
Above-mentioned clean agent preparation method is as follows:
(1) at room temperature benzyltriphenylphosphonium bromide phosphine, fatty alcohol polyoxyethylene ether sulfate, Sodium orthomolybdate, tartrate are joined in deionized water, fully stir, form initial soln;
(2) in the step (1) obtain in solution and add polyoxyethyl propyl polyoxyethanyl glyceryl ether, oleic acid hydroxyethyl imidazole quinoline and AMONYL 380LC, be warming up to 80 DEG C, stirred;
(3) above-mentioned solution is cooled to room temperature, namely obtains this product.
Clean agent in the present embodiment has well cleans corrosion inhibition, add the clean agent after composition for cleaning of the present invention, the erosion rate of unlike material is all less than to the corrosion of carbon steel speed≤2.0g/ (m of regulation in GB/T25146-2010 " industrial equipments matting inspection of quality specification "
2h), Corrosion of Stainless Steel speed≤1.0g/ (m
2h), brass corrosion speed <1.0g/ (m
2h), red copper erosion rate≤1.0g/ (m
2h), aluminium erosion rate≤1.0g/ (m
2h), incrustation scale cleans rate>=95%, and rust deposite cleans rate>=95%, and therefore, clean agent composition of the present invention can meet the cleaning requirement of multiple mechanical means surface incrustation scale and rust deposite.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (2)
1. a mechanical means surface cleaning agent, is characterized in that: form by the composition of following masses number is composite: benzyltriphenylphosphonium bromide phosphine 10 ~ 20 parts, fatty alcohol polyoxyethylene ether sulfate 10 ~ 25 parts, Sodium orthomolybdate 10 ~ 25 parts, 10 ~ 30 parts, tartrate, polyoxyethyl propyl polyoxyethanyl glyceryl ether 10 ~ 25 parts, oleic acid hydroxyethyl imidazole quinoline 3 ~ 5 parts, AMONYL 380LC 2 ~ 4 parts and deionized water 50 ~ 150 parts.
2. mechanical means surface cleaning agent according to claim 1, is characterized in that: described clean agent preparation method is as follows:
(1) at room temperature benzyltriphenylphosphonium bromide phosphine, fatty alcohol polyoxyethylene ether sulfate, Sodium orthomolybdate, tartrate are joined in deionized water, fully stir, form initial soln;
(2) in the step (1) obtain in solution and add polyoxyethyl propyl polyoxyethanyl glyceryl ether, oleic acid hydroxyethyl imidazole quinoline and AMONYL 380LC, be warming up to 40 ~ 80 DEG C, stirred;
(3) above-mentioned solution is cooled to room temperature, namely obtains this product.