CN104911468A - Cold rolling die - Google Patents
Cold rolling die Download PDFInfo
- Publication number
- CN104911468A CN104911468A CN201410094684.6A CN201410094684A CN104911468A CN 104911468 A CN104911468 A CN 104911468A CN 201410094684 A CN201410094684 A CN 201410094684A CN 104911468 A CN104911468 A CN 104911468A
- Authority
- CN
- China
- Prior art keywords
- parts
- mould
- cold rolling
- rolling die
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a cold rolling die, which comprises the following the components by weight parts: 0.5-0.9 parts of carbon, 0.3-0.5 parts of palladium, 0.05-0.08 parts of ruthenium, 0.06-0.12 parts of epoxy resin, 0.23-0.58 parts of potassium, 0.35-0.68 parts of lithium, 0.12-0.35 parts of sodium and 80-95 parts of iron. The cold rolling die has the advantages that the composition proportion is scientific and reasonable, crack phenomenon can not be generated after long-term usage, wear rate is low, and usage life is greatly prolonged.
Description
Technical field
The present invention relates to a kind of mould for cold milling.
Background technology
Operationally, because the resistance to deformation of machined material is larger, the working portion of mould bears the large pressure of very large cold-work die steel, bending force, surging force and frictional force to cold-work die steel.Cold-work die wear rate is high.Also have because of fracture, collapse power and be out of shape overproof and premature failure.Greatly reduce work-ing life, the demand of enterprise can not be met.
Therefore, for solving the problem, spy provides a kind of new technical scheme.
Summary of the invention
The invention provides a kind of mould for cold milling.
The technical solution used in the present invention is:
A kind of mould for cold milling, comprises the composition of following weight part:
Carbon 0.5-0.9 part;
Palladium 0.3-0.5 part;
Ruthenium 0.05-0.08 part;
Epoxy resin 0.06-0.12 part;
Potassium 0.23-0.58 part;
Lithium 0.35-0.68 part;
Sodium 0.12-0.35 part;
Iron 80-95 part.
Preferably, the calcium of 0.36-0.58 weight part can also be added.
Preferably, the manganese of 0.23-0.35 weight part can also be added.
Preferably, the copper of 0.011-0.1 weight part can also be added.
Advantage of the present invention is: the component of this kind of mould is scientific and reasonable, and be in use not easy the phenomenon occurring fracture, wear rate is low, substantially prolongs work-ing life.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment 1
A kind of mould for cold milling, comprises the composition of following weight part:
0.5 part, carbon;
Palladium 0.3 part;
Ruthenium 0.05 part;
Epoxy resin 0.06 part;
0.23 part, potassium;
Lithium 0.35 part;
0.12 part, sodium;
Calcium 0.36 part;
Iron 80 parts.
Embodiment 2
A kind of mould for cold milling, comprises the composition of following weight part:
0.75 part, carbon;
Palladium 0.4 part;
Ruthenium 0.065 part;
Epoxy resin 0.08 part;
0.35 part, potassium;
Lithium 0.45 part;
0.24 part, sodium;
0.3 part, manganese;
Iron 88 parts.
Embodiment 3
A kind of mould for cold milling, comprises the composition of following weight part:
0.9 part, carbon;
Palladium 0.5 part;
Ruthenium 0.08 part;
Epoxy resin 0.12 part;
0.58 part, potassium;
Lithium 0.68 part;
0.35 part, sodium;
Copper 0.1 part;
Iron 95 parts.
Advantage of the present invention is: the component of this kind of mould is scientific and reasonable, and be in use not easy the phenomenon occurring fracture, wear rate is low, substantially prolongs work-ing life.
The above is only preferred embodiment of the present invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (4)
1. a mould for cold milling, is characterized in that: the composition comprising following weight part:
Carbon 0.5-0.9 part;
Palladium 0.3-0.5 part;
Ruthenium 0.05-0.08 part;
Epoxy resin 0.06-0.12 part;
Potassium 0.23-0.58 part;
Lithium 0.35-0.68 part;
Sodium 0.12-0.35 part;
Iron 80-95 part.
2. a kind of mould for cold milling according to claim 1, is characterized in that: the calcium that can also add 0.36-0.58 weight part.
3. a kind of mould for cold milling according to claim 1, is characterized in that: the manganese that can also add 0.23-0.35 weight part.
4. a kind of mould for cold milling according to claim 1, is characterized in that: the copper that can also add 0.011-0.1 weight part.