CN104894463A - 一种柴油发动机排气歧管的铸造工艺 - Google Patents
一种柴油发动机排气歧管的铸造工艺 Download PDFInfo
- Publication number
- CN104894463A CN104894463A CN201510261851.6A CN201510261851A CN104894463A CN 104894463 A CN104894463 A CN 104894463A CN 201510261851 A CN201510261851 A CN 201510261851A CN 104894463 A CN104894463 A CN 104894463A
- Authority
- CN
- China
- Prior art keywords
- iron
- iron liquid
- casting process
- exhaust manifold
- spheroidization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种柴油发动机排气歧管的铸造工艺，其工艺步骤包括造型、制芯-熔化、浇注-落砂、清理，所述熔化、浇注步骤中的铁液在熔化之后，浇注之前加入稀土镁硅铁合金，并扒平；加盖QT420-15铸铁板；覆盖8～18mmFeSi75Al2.5硅铁孕育剂，最后出所述铁液，所述铁液出炉后将其总量的2/3进行球化处理，所述球化处理完毕后补加剩余的所述铁液。本发明在熔化、浇注过程中不光使用了硅铁孕育剂，而且还对铁液做了球化处理，其具有促进铁素体增加、抑制白口倾向、消除游离渗碳体、提高球化率和球墨圆整度、减小石墨球径、增加球墨个数、提高石墨分布均匀性的特点。
Description
技术领域
本发明涉及柴油发动机铸造工艺技术领域的应用，尤其涉及一种柴油发动机排气歧管的铸造工艺。
背景技术
柴油发动机的排气歧管工作在750℃以上的高温下，长时间经受高温、高压废气的加热与冲击，因此，要求其必须具有优良的耐热疲劳性、高温强度、抗高温腐蚀性能及高温尺寸稳定性。
现有技术使用球墨铸铁生产的柴油发动机排气歧管铸件不光生产周期长、能耗大、成本高，退火时易使铸件发生变形，出现氧化皮现象，而且全部退火时，易造成退火炉能力不足，成为制约生产的一大影响因素。
发明内容
为了解决背景技术所存在的问题，本发明的目的是提供一种柴油发动机排气歧管的铸造工艺。
为了实现上述目的，本发明的技术方案是这样实现的：一种柴油发动机排气歧管的铸造工艺，其工艺步骤包括造型、制芯-熔化、浇注-落砂、清理，所述熔化、浇注步骤中的铁液在熔化之后，浇注之前加入稀土镁硅铁合金，并扒平；加盖QT420-15铸铁板；覆盖8～18mmFeSi75Al2.5硅铁孕育剂，最后出所述铁液，所述铁液出炉后将其总量的2/3进行球化处理，所述球化处理完毕后补加剩余的所述铁液。
进一步地，所述球化处理的温度为1490～1510℃。
进一步地，所述浇注温度为1360～1420℃。
本发明具有以下有益效果：本发明在熔化、浇注过程中不光使用了硅铁孕育剂，而且还对铁液做了球化处理，其具有促进铁素体增加、抑制白口倾向、消除游离渗碳体、提高球化率和球墨圆整度、减小石墨球径、增加球墨个数、提高石墨分布均匀性的特点。
具体实施方式
本发明一种柴油发动机排气歧管的铸造工艺，其工艺步骤包括造型、制芯-熔化、浇注-落砂、清理。
本发明中所述熔化、浇注步骤中的铁液在熔化之后，浇注之前加入稀土镁硅铁合金，并扒平；加盖QT420-15铸铁板；覆盖8～18mmFeSi75Al2.5硅铁孕育剂，最后出所述铁液，所述铁液出炉后将其总量的2/3进行球化处理，所述球化处理的温度为1490～1510℃，所述球化处理完毕后补加剩余的所述铁液，保证所述铁液的化学成分为：C3.6～3.9%、Si3.1～3.4%、Mn≤0.3%、P≤0.045%、S≤0.02%、残余Mg0.025～0.05%、残余RE0.02～0.045%。
浇注前迅速扒净浮渣，浇注时所述铁液充满浇口杯，并且快速平稳地浇注，所述浇注温度为1360～1420℃。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，本领域普通技术人员对本发明的技术方案所做的其他修改或者等同替换，只要不脱离本发明技术方案的精神和范围，均应涵盖在本发明的权利要求范围当中。
Claims (3)
1.一种柴油发动机排气歧管的铸造工艺，其包括造型、制芯-熔化、浇注-落砂、清理，其特征在于，所述熔化、浇注步骤中的铁液在熔化之后，浇注之前加入稀土镁硅铁合金，并扒平；加盖QT420-15铸铁板；覆盖8～18mmFeSi75Al2.5硅铁孕育剂，最后出所述铁液，所述铁液出炉后将其总量的2/3进行球化处理，所述球化处理完毕后补加剩余的所述铁液。
2.根据权利要求1所述的一种柴油发动机排气歧管的铸造工艺，其特征在于，所述球化处理的温度为1490～1510℃。
3.根据权利要求1所述的一种柴油发动机排气歧管的铸造工艺，其特征在于，所述浇注温度为1360～1420℃。