CN104893661A - High-temperature resistant automobile clutch disc material - Google Patents
High-temperature resistant automobile clutch disc material Download PDFInfo
- Publication number
- CN104893661A CN104893661A CN201510286363.0A CN201510286363A CN104893661A CN 104893661 A CN104893661 A CN 104893661A CN 201510286363 A CN201510286363 A CN 201510286363A CN 104893661 A CN104893661 A CN 104893661A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature resistant
- clutch disc
- disc material
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-temperature resistant automobile clutch disc material. The high-temperature resistant automobile clutch disc material is prepared from the following raw materials in parts by weight: 9 to 14 parts of carbon fiber, 3 to 10 parts of aromatic polyamide fiber, 5 to 10 parts of porous ceramic spheres, 1 to 5 parts of aedelforsite, 4 to 10 parts of polyfunctional-degree polyether, 3 to 9 parts of isocyanate, 7 to 14 parts of ceramic fiber, 2 to 5 parts of an anti-aging agent, 4.5 to 7.3 parts of magnesium hydroxide, 6 to 15 parts of polybutylene terephthalate, 2.5 to 8 parts of natural organic fiber, 8 to 13 parts of pp, 8 to 13 parts of linear low-density polyethylene and 3 to 9 parts of white feldspar. The high-temperature resistant automobile clutch disc material has the beneficial effects of high high-temperature resistance, high abrasive resistance and capability of finishing clutch operation of automobiles well.
Description
Technical field
The present invention relates to a kind of resistant to elevated temperatures automatic clutch sheet material.
Background technology
Clutch coupling is the parts be directly associated with engine in car transmissions, it is responsible for cut-out and the keying action of power and transmission system, so gentle start when can ensure vehicle starting, also can ensure shift gears time smooth-going, also prevent transmission system overload.Clutch coupling carrys out complete operation mainly through clutch-plate, and clutch-plate is a kind of material of good rub resistance, and the quality of its quality directly affects the reliability of mechanical means and the life security of operator.Therefore, the clutch-plate as automobile needs good wear resistance and thermotolerance.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of automatic clutch sheet material, have good resistant to elevated temperatures performance, and tool has good wearability, well completes the clutch operation of automobile.
For solving prior art problem, technical scheme provided by the invention is, a kind of resistant to elevated temperatures automatic clutch sheet material, and it is made up of the raw material of following parts by weight:
Carbon fiber 9-14 part, Kevlar 3-10 part, porous pottery ball 5-10 part, wollastonite 1-5 part, polyfunctionality polyethers 4-10 part, isocyanic ester 3-9 part, ceramic fiber 7-14 part, antiaging agent 2-5 part, magnesium hydroxide 4.5-7.3 part, polybutylene terephthalate 6-15 part, natural organic fiber 2.5-8 part, pp8-13 part, linear low density polyethylene 8-13 part, white feldspar 3-9 part.
The invention has the beneficial effects as follows: automatic clutch sheet material of the present invention, there is good resistant to elevated temperatures performance, and tool has good wearability, well complete the clutch operation of automobile.
Embodiment
embodiment 1
A kind of resistant to elevated temperatures automatic clutch sheet material, it is made up of the raw material of following parts by weight:
9 parts, carbon fiber, Kevlar 3 parts, porous pottery 5 parts, ball, wollastonite 1 part, polyfunctionality polyethers 4 parts, isocyanic ester 3 parts, ceramic fiber 7 parts, antiaging agent 2 parts, magnesium hydroxide 4.5 parts, polybutylene terephthalate 6 parts, natural organic fiber 2.5 parts, pp8 part, linear low density polyethylene 8 parts, white feldspar 3 parts.
embodiment 2
A kind of resistant to elevated temperatures automatic clutch sheet material, it is made up of the raw material of following parts by weight:
14 parts, carbon fiber, Kevlar 10 parts, porous pottery 10 parts, ball, wollastonite 5 parts, polyfunctionality polyethers 10 parts, isocyanic ester 9 parts, ceramic fiber 14 parts, antiaging agent 5 parts, magnesium hydroxide 7.3 parts, polybutylene terephthalate 15 parts, natural organic fiber 8 parts, pp13 part, linear low density polyethylene 13 parts, white feldspar 9 parts.
Claims (1)
1. a resistant to elevated temperatures automatic clutch sheet material, is characterized in that: it is made up of the raw material of following parts by weight:
Carbon fiber 9-14 part, Kevlar 3-10 part, porous pottery ball 5-10 part, wollastonite 1-5 part, polyfunctionality polyethers 4-10 part, isocyanic ester 3-9 part, ceramic fiber 7-14 part, antiaging agent 2-5 part, magnesium hydroxide 4.5-7.3 part, polybutylene terephthalate 6-15 part, natural organic fiber 2.5-8 part, pp8-13 part, linear low density polyethylene 8-13 part, white feldspar 3-9 part.