CN104888433A - Bottom board having anti-interference anion health function and applicable to table tennis rackets and manufacturing method of bottom board - Google Patents
Bottom board having anti-interference anion health function and applicable to table tennis rackets and manufacturing method of bottom board Download PDFInfo
- Publication number
- CN104888433A CN104888433A CN201510308338.8A CN201510308338A CN104888433A CN 104888433 A CN104888433 A CN 104888433A CN 201510308338 A CN201510308338 A CN 201510308338A CN 104888433 A CN104888433 A CN 104888433A
- Authority
- CN
- China
- Prior art keywords
- parts
- anion
- chinese medicine
- traditional chinese
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A bottom board having an anti-interference anion health function and applicable to table tennis rackets comprises a board body and a handle; the board body is composed of a core board layer, anion glue layers, herbal sandwich layers and bamboo panel layers; the upper and lower surfaces of the core board layer are glued to the herbal sandwich layers through the anion glue layers; the herbal sandwich layers are made from, by weight, 50 to 60 parts of sawdust, 30 to 40 parts of Rhamnus crenata root, 15 to 20 parts of Cyrtomium rhizome, 4 to 6 parts of Serissa serissoides herb, 20 to 25 parts of lavender, 15 to 20 part of rosemary, 3 to 5 parts of Hupeh anemone herb, 15 to 25 parts of elm bark, 4 to 6 parts of agilawood, 15 to 20 parts of grassleaf sweelflag rhizome, 1 to 3 parts of musk, 1 to 3 parts of mint, 1 to 3 parts of dandelion, 1 to 3 parts of wild chrysanthemum flower, 1.5 to 2.5 parts of sweet marjoram, 1.5 to 2 parts of sandalwood, 0.4 to 0.6 part of saffron essential oil, 0.3 to 0.5 part of geranium essential oil, and 10 to 12 parts of polyurethane glue. The bottom board is antibacterial, can release anions, is fragrant and is worthy of wide application.
Description
Technical field
The present invention relates to sports goods technical field, more particularly, relate to a kind of veneer and the manufacture method thereof with anti-interference anion health-care efficacy.
Background technology
Table tennis is the sports that people enjoy a lot, the material normally composite wood board of base plate of ping-pong bat, the number of plies is unrestricted, be mainly the domestic or pure wood of import, traditional table tennis bat function ratio is more single, do not possess antibacterial degerming effect, can not meet the multiple user demand of people.
On the one hand, along with the continuous rising of Global Temperature, the population of mosquito and quantity all will significantly improve, and just day by day threaten the health of the mankind.Mosquito sucks blood except directly stining thorn, harasses except sleep, more seriously propagates various diseases.The mosquito of China passes disease malaria, Filariasis, Japanese Type-B encephalitis and dengue fever (or dengue hemorrhagic fever) four class, and mosquito passes more important virosis and also has yellow fever and various equine encephalitis etc.
On the other hand, tourmaline has the function producing anion and far infrared, and by negative aeroion and far infrared Technology application in base plate of ping-pong bat product, the base plate of ping-pong bat after using can discharge negative aeroion for a long time, especially negative oxygen ion.Because it is structurally similar to ultra-oxygen anion free radical (O2-), therefore there is similar biologically active, the biological cell of living can be made electronegative, thus make virus lose attacking ability to cell.Such as, in artificial air's anion environment, in air, mould, bacterial population can reduce by more than 90% after measured.After negative oxygen ion is inhaled into human body, neural excitatory state can be regulated, improve the ventilatory of lung, improve blood circulation, enhance metabolism, strengthen immune system ability, make people in high spirits, increase work efficiency, it also has certain therapeutic action to numerous diseases such as hypertension, asthma, influenza, insomnia, arthritis, so people claims anion to be " vitamin in air " " long-lived element ".
So far, make traditional base plate of ping-pong bat have expelling mosquito simultaneously, the Technology design of function of antibacterial and anion releasing also do not have and see.
Summary of the invention
For the deficiency that prior art exists, one of technical problem to be solved by this invention is to provide a kind of veneer with anti-interference anion health-care efficacy, not only can effective expelling mosquito, also can discharge negative aeroion.In addition, also certain suppression, killing action is had to the multiple germs such as staphylococcus, tubercle bacillus, Pseudomonas aeruginosa, gram-negative bacteria and gram-positive bacteria and fungi; Fragrant odour simultaneously, character is gentle, also has certain effect to improving the state of mind.
Two of technical problem to be solved by this invention is to provide a kind of manufacture method with the veneer of anti-interference anion health-care efficacy.
The object of the invention is to be achieved through the following technical solutions:
A kind of veneer with anti-interference anion health-care efficacy, comprise clappers body and handle, it is characterized in that: described clappers body is made up of core layer, anion adhesive layer, Traditional Chinese medicine clamping plate layer and bamboo surface flaggy, the top and bottom of described core layer are glued together respectively by anion adhesive layer and described Traditional Chinese medicine clamping plate layer, and described bamboo surface flaggy glues together respectively by anion adhesive layer and described Traditional Chinese medicine clamping plate layer; Wherein, described anion adhesive layer comprises hydroxyl butadiene-styrene rubber and anion natural mineral matter powder, wherein the mass ratio of hydroxyl butadiene-styrene rubber and anion natural mineral matter powder is 6:1, described anion natural mineral matter powder is tourmaline, lanthanide rare composite salt and the titanium oxide mixture by weight 4:3:3, wherein tourmaline is dravite and the elbaite mixture by weight 3:2, and the granularity of described anion natural mineral matter powder is 400 object superfines;
Be made up of the raw material of following weight for the manufacture of the Traditional Chinese medicine clamping plate layer in base plate of ping-pong bat: sawdust 50-60 part, rhamnus crenata sieb.et zucc 30-40 part, rhizome of cyrtomium 15-20 part, serissa serissoides 4-6 part, lavender 20-25 part, rosemary 15-20 part, anemone vitifolia 3-5 part, elm bark 15-25 part, agalloch eaglewood 4-6 part, calamus 15-20 part, Moschus 1-3 part, peppermint 1-3 part, dandelion 1-3 part, mother chrysanthemum 1-3 part, sweet marjoram 1.5-2.5 part, santal 1.5-2 part, safron essential oil 0.4-0.6 part, Geranium Essential 0.3-0.5 part, polyurethane resin adhesive 10-12 part, the manufacture method of described Traditional Chinese medicine clamping plate layer comprises the following steps:
A. get respectively by above-mentioned each component: sawdust 50-60 part, rhamnus crenata sieb.et zucc 30-40 part, rhizome of cyrtomium 15-20 part, serissa serissoides 4-6 part, lavender 20-25 part, rosemary 15-20 part, anemone vitifolia 3-5 part, elm bark 15-25 part, agalloch eaglewood 4-6 part, calamus 15-20 part, Moschus 1-3 part, peppermint 1-3 part, dandelion 1-3 part, mother chrysanthemum 1-3 part, sweet marjoram 1.5-2.5 part, santal 1.5-2 part, drops in micronizer and is ground into 120 object mixed-powders;
B. safron essential oil 0.4-0.6 part will be added in the mixed-powder in step a, Geranium Essential 0.3-0.5 part, polyurethane resin adhesive 10-12 part, then add high speed dispersor and carry out stirring 20min one-tenth compound, for subsequent use;
C. the compound in step b is inserted the Chinese medicine sheet material that 1mm-1.1mm thickness is made in hot pressing in pressing machine, for subsequent use; Wherein, the press time is 4-5min, and pressure is 1-1.5Mpa/cm
2, temperature remains on 100 DEG C-110 DEG C;
D. the Chinese medicine sheet material in step c draws the trim line of the first base of base plate of ping-pong bat, cut, shape, obtain Traditional Chinese medicine clamping plate layer.
In a preferred embodiment, for improving repelling effect, surfactant 8-9 part, Metadelphene 0.2-0.3 part and cypress essential oil 0.4-0.6 part is also added in stepb.
There is a manufacture method for the veneer of anti-interference anion health-care efficacy, comprise the following steps:
S1. get dravite, elbaite, lanthanide rare composite salt and titanium dioxide respectively by each component, and drop in micronizer respectively and be crushed to 400 object anion natural mineral matter powder, for subsequent use;
S2. the anion natural mineral matter powder in step S1 is become anion adhesive with hydroxyl butadiene-styrene rubber mix and blend 15min, for subsequent use;
S3. core layer obtained for common process and bamboo surface flaggy are dried, make the moisture content of described core layer and bamboo surface flaggy be less than 10%, the thickness of wherein said core layer is 3.3mm-3.6mm, and the thickness of described bamboo surface flaggy is 0.3mm-0.4mm;
Further, in step s3, also following program is specifically comprised:
A. the bamboo of growth selection 4-6, the bamboo wood of bamboo wall thickness 8mm-12mm, is sawn into thick bamboo tube according to the length of 270mm;
B. select diameter at the timber of 100mm-200mm, be sawn into juggle according to the length of 270mm;
C. anti-mould and moth-proof agent stoste is diluted to the aqueous solution of 1%, carry out immersion and boiling to the thick bamboo tube in step a, boiling temperature is 100 DEG C of temperature, boiling 4 hours-5 hours;
D. timber softening agent stoste is diluted to the aqueous solution of 5%-8%, immersion 24-48 hour is carried out to the juggle in step b;
E. the thick bamboo tube in step a along the circumferential direction to be shootd off rascal with slicer, dig into the thin bamboo plate that thickness is 0.3mm-0.4mm, as bamboo surface flaggy; Juggle in step b is along the circumferential direction dug into the thin slice that thickness is 3.3mm-3.6mm, as core layer;
F. the core layer in step e and bamboo surface flaggy are Tumblied Dry respectively to moisture content and be less than 10%, for subsequent use;
S4. the core layer upper and lower surface in step S3 is coated respectively anion adhesive obtained in step S2, conventional coating weight is 70-90g/m
2, then two pieces of Traditional Chinese medicine clamping plate layers are glued together with the top and bottom of core layer respectively; Respectively anion adhesive is coated on the surface of two pieces of Traditional Chinese medicine clamping plate layers again, be stained with bamboo surface flaggy respectively, form composite plate;
S5. carry out hot-pressing processing to the composite plate in step S4, conventional hot-press gluing technique parameter is: hot pressing temperature 95 DEG C-130 DEG C, pressure 0.8MPa-1.5MPa, and hot pressing time is 1.5-5min;
S6. after step s 5 composite plate processed, polish, mounting handle, obtain a kind of veneer with anti-interference anion health-care efficacy.
The present invention is based on motherland's traditional medicine, with reference to modern Chinese herbal medicine pharmacological research, from the drug screening of existing Chinese medicine with repeatedly verify, give full play to each component and act synergistically, wherein the effect brief introduction of each raw material is as follows.
Rhamnus crenata sieb.et zucc:: machaka or dungarunga, Gen Pi or complete stool are used as medicine, and property is flat, bitter, dry, sterilization, desinsection.
Rhizome of cyrtomium: hardship is slightly cold, returns liver the spleen channel, slightly poisonous.Desinsection, clearing heat and detoxicating, hemostasis.
Serissa serissoides: toil, cool, " Chinese herbal medicine handbook is commonly used in Shanghai ": invigorate blood circulation, detumescence, dispel the wind, dampness elimination, has again strong effect.Control woman through closing, leukorrhea, dizzy unable.
Lavender: ant can be removed, except roach, except mite, when being placed under wardrobe, pillow, not only camphor ball can be replaced, the fragrance of one people that oozes can also be left, research finds, lavender has obvious antibacterial action, and the linalool contained in lavender is the antibacterial main component of lavender, and it can suppress the growth of 17 kinds of bacteriums (comprising gram-negative bacteria and gram-positive bacteria), 10 kinds of fungies.
Rosemary: have tranquilizing and allaying excitement, restoring consciouness effect, all have certain curative effect to indigestion and stomachache, have calmness, diuresis, also can be used for the various diseases such as Cure for insomnia, palpitaition, headache, indigestion, external application can treat wound and arthritis.Also there is strong heart, promote metabolism, promote the effects such as the blood circulation of peripheral vessel.
Anemone vitifolia: 1. " Shaanxi Chinese herbal medicine ": " bitter, cool, slightly poisonous." 2. " Chinese herbal medicine is commonly used in Sichuan ": " and toil, temperature, slightly poisonous." removing toxic substances, apocenosis myogenic, the Sweeling-eliminating medicine powder stasis of blood, has and kills maggot, wriggler, eliminate indigestion, detumescence, and the loose stasis of blood, controls stubborn dermatitis, the favus of the scalp, malaria, infantile malnutrition, dysentery, and carbuncle furuncle sore swells, scrofula, traumatic injury.
Elm bark: be dry bark or the root skin of Ulmaceae is sweet, flat, nontoxic; Li Shui, treating stranguria, detumescence, for urinary obstruction, stranguria with turbid discharge, oedema, ulcer carbuncle on the back, erysipelas, mange.
Agalloch eaglewood: " Compendium of Materia Medica " records that wood has strong antibacterial efficacy, fragrance enters spleen, clear god regulates the flow of vital energy, tonifying five zang organs, relieving cough and reducing sputum, warm stomach temperature spleen, analgesic therapy of ventilating, can be used as medicine is first-class medicinal material superfine product.
Calamus: its flower, stem aromatic flavour, have have one's ideas straightened out, eliminate the phlegm, effect of loose wind, epidemic disease of can dispelling intelligence development, to improve the health, spices or mosquito dispersing can be made.
Moschus: have and have one's ideas straightened out, wards off dirty, dredging collateral, effect of the loose stasis of blood; Control apoplexy, coma due to blocking of the respiratory system, frightened epilepsy, middle evil is unhappy, the trusted subordinate sudden and violent Tong ， Disorder lump in the abdomen hypochondriac lump, traumatic injury, swollen ulcer drug." herbal classic ": master wards off bad odor, a kind of malaria, epilepsy convulsion, goes three worms.
Dandelion: composite family, Dandelion herbaceos perennial, has and clearing heat and detoxicatingly can be used for heat toxin syndrome, especially kind removing heat from the liver, the hot red eye, swell pain for the treatment of liver, and multi-infection, purulent disease; Inhibitory action is had to staphylococcus aureus, typhoid bacillus; Permitted blue achorion to microsporon audouini, Trichophyton rubrum etc. have inhibitory action simultaneously.
Mother chrysanthemum: tool dispelling wind and heat from the body, subdhing swelling and detoxicating.The various active compositions such as its alantol contained, yejuhua lactone, amino acid, trace element.Kill or inhibit activities various pathogens, virus, the inhibit activities of water extract to staphylococcus aureus, shigella dysenteriae, EHEC, typhoid bacillus etc. is better than volatile oil; And have anti-inflammatory, anti-oxidant, analgesic activities.
Sweet marjoram: the depressed and addictive disease of mood can be improved, especially effective to liberal-mindedness and vigorous endurance stress symptom, can hemangiectasis, hypotensive, alleviate and burden, help to eliminate palpitaition, have excellent nerve to pacify and calm function.
Santal: be the heartwood of Santalaceae plant.Evergreen dungarunga, high 6 ~ 9 meters, tool parasitic root, " Dai Nationality's medicine record " is recorded: for regulating qi-flowing for harmonizing stomach, middle evil, desinsection.
Safron essential oil: Compendium of Material Medica is just recorded safron and there is the effects such as calmness, analgesia, blood circulation and promoting silt, there is powerful physiologically active, its column cap Asia and Europe as medicinal, have calmness, eliminate the phlegm, spasmolysis, external as calm, carminative, promoting blood circulation and removing blood stasis, removing pattogenic heat from the blood and toxic material from the body, resolving stagnation for tranquilization.Febrile virulent maculae, melancholy ruffian are vexed, palpitation with fear is gone mad.
Geranium Essential: there is hemostasis, vasoconstriction, asthma, liver and expelling toxin, gall stone, kidney toxin expelling, kidney stone, diuresis, DOMS, Oily, aging skin activates, bleb, ochrodermia, fat-reducing, promotes to scab, eczema, to burn sunburn, tinea, menstruation has some setbacks, engorgement of breasts inflammation, alleviate melancholy uneasy, there is deodorizing, antibacterial, the effect of sterilization.
Cypress essential oil: draw materials from cypress (formal name used at school: the cypressCypressus Cupressues sempervirens ssace.ae place of production: Spain), form with Fresh leaves and cone distillation, colourless or in extremely light yellow, have amber taste charming as wooden and face cream, antirheumatic, antibacterial, anti-spasm, suppress sweating, convergence, promotion scab, except underarm odor, diuresis, bring down a fever, stop blooding, sharp liver, desinsection, rehabilitation, calmness, astringing to arrest bleeding, benefit body, vasoconstriction.Dispelling fatigue, angry mood of releiving, alleviates heart anxiety and pressure, purifies one's soul.
Effect of the present invention:
The present invention not only has the function of expelling mosquito, for user provides an environment of exempting from interference by insects, also can discharge negative aeroion simultaneously, have certain health-care efficacy to user; In addition, also certain suppression, killing action is had to the multiple germs such as staphylococcus, tubercle bacillus, Pseudomonas aeruginosa, gram-negative bacteria and gram-positive bacteria and fungi; Fragrant odour, also having certain effect to improving the state of mind, having boundless application prospect simultaneously.
Accompanying drawing explanation
Fig. 1 is overall structure schematic diagram of the present invention.
Fig. 2 is cross-sectional cut-away schematic diagram of the present invention.
Detailed description of the invention
Embodiment 1:
Refer to schematic diagram of the present invention shown in Fig. 1 and Fig. 2, a kind of veneer with anti-interference anion health-care efficacy, comprise clappers body 1 and handle 2, described clappers body 1 is made up of core layer 10, anion adhesive layer (not shown), Traditional Chinese medicine clamping plate layer 11 and bamboo surface flaggy 12, the top and bottom of described core layer 10 are glued together respectively by anion adhesive layer (not shown) and described Traditional Chinese medicine clamping plate layer 11, and described bamboo surface flaggy 12 glues together respectively by anion adhesive layer and described Traditional Chinese medicine clamping plate layer 11; Wherein, described anion adhesive layer adopts prior art preparation and obtains, comprise hydroxyl butadiene-styrene rubber and anion natural mineral matter powder, wherein the mass ratio of hydroxyl butadiene-styrene rubber and anion natural mineral matter powder is 6:1, described anion natural mineral matter powder is tourmaline, lanthanide rare composite salt and the titanium oxide mixture by weight 4:3:3, wherein tourmaline is dravite and the elbaite mixture by weight 3:2, and the granularity of described anion natural mineral matter powder is 400 object superfines;
Be made up of the raw material of following weight for the manufacture of the Traditional Chinese medicine clamping plate layer 11 in base plate of ping-pong bat: 60 parts, sawdust, rhamnus crenata sieb.et zucc 30 parts, rhizome of cyrtomium 20 parts, serissa serissoides 4 parts, lavender 25 parts, rosemary 15 parts, anemone vitifolia 5 parts, elm bark 15 parts, agalloch eaglewood 6 parts, calamus 15 parts, 3 parts, Moschus, peppermint 1 part, dandelion 3 parts, mother chrysanthemum 1 part, sweet marjoram 2.5 parts, 1.5 parts, santal, safron essential oil 0.6 part, Geranium Essential 0.3 part, polyurethane resin adhesive 12 parts; The manufacture method of described Traditional Chinese medicine clamping plate layer 11 comprises the following steps:
A. 60 parts, sawdust is got respectively by above-mentioned each component, rhamnus crenata sieb.et zucc 30 parts, rhizome of cyrtomium 20 parts, serissa serissoides 4 parts, lavender 25 parts, rosemary 15 parts, anemone vitifolia 5 parts, elm bark 15 parts, agalloch eaglewood 6 parts, calamus 15 parts, 3 parts, Moschus, peppermint 1 part, dandelion 3 parts, mother chrysanthemum 1 part, sweet marjoram 2.5 parts, 1.5 parts, santal, drops in micronizer and is ground into 120 object mixed-powders;
B. will add safron essential oil 0.6 part in the mixed-powder in step a, Geranium Essential 0.3 part, polyurethane resin adhesive 12 parts, then add high speed dispersor and carry out stirring 20min one-tenth compound, for subsequent use;
C. the compound in step b is inserted the Chinese medicine sheet material that 1mm thickness is made in hot pressing in pressing machine, for subsequent use; Wherein, the press time is 4min, and pressure is 1.5Mpa/cm
2, temperature remains on 100 DEG C DEG C;
D. the Chinese medicine sheet material in step c draws the trim line of the first base of base plate of ping-pong bat, cut, shape, obtain Traditional Chinese medicine clamping plate layer 11.
In a preferred embodiment, for increasing repelling effect, surfactant 9kg, Metadelphene 0.2kg and cypress essential oil 0.6kg is also added in stepb.
There is a manufacture method for the veneer of anti-interference anion health-care efficacy, comprise the following steps:
S1. get dravite, elbaite, lanthanide rare composite salt and titanium dioxide respectively by each component, and drop in micronizer respectively and be crushed to 400 object anion natural mineral matter powder, for subsequent use;
S2. the anion natural mineral matter powder in step S1 is become anion adhesive with hydroxyl butadiene-styrene rubber mix and blend 15min, for subsequent use;
S3. core layer 10 obtained for common process and bamboo surface flaggy 12 are dried, the moisture content of described core layer 10 and bamboo surface flaggy 11 is made to be less than 10%, the thickness of wherein said core layer 10 is 3.3mm-3.6mm, and the thickness of described bamboo surface flaggy 12 is 0.3mm-0.4mm;
Further, in step s3, following program is specifically comprised:
A. the bamboo of growth selection 4-6, the bamboo wood of bamboo wall thickness 8mm-12mm, is sawn into thick bamboo tube according to the length of 270mm;
B. select diameter at the timber of 100mm-200mm, be sawn into juggle according to the length of 270mm;
C. anti-mould and moth-proof agent stoste is diluted to the aqueous solution of 1%, carry out immersion and boiling to the thick bamboo tube in step a, boiling temperature is 100 DEG C of temperature, boiling 4 hours-5 hours;
D. timber softening agent stoste is diluted to the aqueous solution of 5%-8%, immersion 24-48 hour is carried out to the juggle in step b;
E. the thick bamboo tube in step a along the circumferential direction to be shootd off rascal with slicer, dig into the thin bamboo plate that thickness is 0.3mm-0.4mm, as bamboo surface flaggy 12; Juggle in step b is along the circumferential direction dug into the thin slice that thickness is 3.3mm-3.6mm, as core layer 10;
F. the core layer 10 in step e and bamboo surface flaggy 12 are Tumblied Dry respectively to moisture content and be less than 10%, for subsequent use;
S4. core layer 10 upper and lower surface in step S3 is coated respectively anion adhesive obtained in step S2, conventional coating weight is 70-90g/m
2, then two pieces of Traditional Chinese medicine clamping plate layers 11 are glued together with the top and bottom of core layer 10 respectively; Respectively anion adhesive is coated on the surface of two pieces of Traditional Chinese medicine clamping plate layers 11 again, be stained with bamboo surface flaggy 12 respectively, form composite plate;
S5. carry out hot-pressing processing to the composite plate in step S4, conventional hot-press gluing technique parameter is: hot pressing temperature 95 DEG C-130 DEG C, pressure 0.8MPa-1.5MPa, and hot pressing time is 1.5-5min;
S6. after step s 5 composite plate processed, polish, mounting handle 2, obtain a kind of veneer with anti-interference anion health-care efficacy.
Embodiment 2:
A kind of veneer with anti-interference anion health-care efficacy, comprise clappers body 1 and handle 2, described clappers body 1 is made up of core layer 10, anion adhesive layer, Traditional Chinese medicine clamping plate layer 11 and bamboo surface flaggy 12, the top and bottom of described core layer 10 are glued together respectively by anion adhesive layer and described Traditional Chinese medicine clamping plate layer 11, and described bamboo surface flaggy 12 glues together respectively by anion adhesive layer and described Traditional Chinese medicine clamping plate layer 11; Wherein, described anion adhesive layer comprises hydroxyl butadiene-styrene rubber and anion natural mineral matter powder, wherein the mass ratio of hydroxyl butadiene-styrene rubber and anion natural mineral matter powder is 6:1, described anion natural mineral matter powder is tourmaline, lanthanide rare composite salt and the titanium oxide mixture by weight 4:3:3, wherein tourmaline is dravite and the elbaite mixture by weight 3:2, and the granularity of described anion natural mineral matter powder is 400 object superfines;
Be made up of the raw material of following weight for the manufacture of the Traditional Chinese medicine clamping plate layer 11 in base plate of ping-pong bat: 50 parts, sawdust, rhamnus crenata sieb.et zucc 40 parts, rhizome of cyrtomium 15 parts, serissa serissoides 6 parts, lavender 20 parts, rosemary 20 parts, anemone vitifolia 3 parts, elm bark 25 parts, agalloch eaglewood 4 parts, calamus 20 parts, 1 part, Moschus, peppermint 3 parts, dandelion 1 part, mother chrysanthemum 3 parts, sweet marjoram 1.5 parts, 2 parts, santal, safron essential oil 0.4 part, Geranium Essential 0.5 part, polyurethane resin adhesive 10 parts; The manufacture method of described Traditional Chinese medicine clamping plate layer 11 comprises the following steps:
A. 50 parts, sawdust is got respectively by above-mentioned each component, rhamnus crenata sieb.et zucc 40 parts, rhizome of cyrtomium 15 parts, serissa serissoides 6 parts, lavender 20 parts, rosemary 20 parts, anemone vitifolia 3 parts, elm bark 25 parts, agalloch eaglewood 4 parts, calamus 20 parts, 1 part, Moschus, peppermint 3 parts, dandelion 1 part, mother chrysanthemum 3 parts, sweet marjoram 1.5 parts, 2 parts, santal, drops in micronizer and is ground into 120 object mixed-powders;
B. will add safron essential oil 0.4 part in the mixed-powder in step a, Geranium Essential 0.5 part, polyurethane resin adhesive 10 parts, then add high speed dispersor and carry out stirring 20min one-tenth compound, for subsequent use;
C. the compound in step b is inserted the Chinese medicine sheet material that 1.1mm thickness is made in hot pressing in pressing machine, for subsequent use; Wherein, the press time is 5min, and pressure is 1Mpa/cm
2, temperature remains on 110 DEG C;
D. the Chinese medicine sheet material in step c draws the trim line of the first base of base plate of ping-pong bat, cut, shape, obtain Traditional Chinese medicine clamping plate layer 11.
In a preferred embodiment, surfactant 8kg, Metadelphene 0.3kg and cypress essential oil 0.4kg is also added in stepb.
All the other are with embodiment 1.
The scattering ratio of base plate of ping-pong bat after treatment reaches more than 90%.
Check the method for above-mentioned table tennis bat as follows:
(1) at the lab space of three 2 square metres, be respectively experiment 1 group, test 2 groups and control group, (test 1 group of corresponding embodiment 1, test 2 groups of corresponding embodiments 2) and experimental group and control group (common base plate of ping-pong bat) are put into the laboratory without extraneous interference by insects respectively, temperature all controls temperature 25 DEG C by temperature and humidity controller by experimental group and control group (common base plate of ping-pong bat), relative humidity 45%, base plate of ping-pong bat of the present invention is placed in experimental group, and control group is the common base plate of ping-pong bat not adding Chinese medical extract and anion adhesive layer made according to the inventive method, respectively to mosquito, flea, ant, cockroach, bedbug, flat lice, carpet beetle carries out class test, respectively 5, 10, 15, count in 24 hours, detect data in table 1.
Draw the scattering ratio of all kinds of insect in each time period by table 1, and draw table 2.
Scattering ratio is (putting into quantity-volume residual)/put into quantity.
From table 1 and table 2, deworming rates of the present invention can reach more than 98%, and 10 hours can reach close to 91%, within 15 hours, can more than 96% be reached, compared with control group (common base plate of ping-pong bat), anthelminthic effect of the present invention is obvious, and can reach 100% for the expeling rate of mosquito, bedbug and flat lice.
(2) smell inspection: sense organ, delicate fragrance, nonirritant peculiar smell.
(3) anionic textiles.
Adopt anion test instrument, mainly for timber, ore, ceramic material, negative ion powder to relevant make commodity (as anion clothing, necklace, woollen blanket) etc. the anion quantity that discharges make measurement.
Test result is in table 2.
| Sequence number | Test item | Unit | Measured result |
| Common base plate of ping-pong bat | Anion quantity | Individual/cm 3 | 0 |
| The embodiment of the present invention 1,2 | Anion quantity | Individual/cm 3 | >1200 |
Conclusion: the base plate of ping-pong bat in the embodiment of the present invention 1, embodiment 2 can sustained release negative aeroion, and compared with common base plate of ping-pong bat of the prior art, the present invention has obviously advantage.
(4) bactericidal effect detects.
After testing, its physical and chemical index is as follows for the base plate of ping-pong bat prepared according to the inventive method:
| project | standard index | testing index |
| bactericidal effect | to harmful bacteria (staphylococcus aureus, Escherichia coli, Pseudomonas aeruginosa) clearance rate>=70%, natural bacteria clearance rate>=70%. | staphylococcus aureus clearance rate is 90%, Escherichia coli can be removed substantially, Pseudomonas aeruginosa clearance rate is 92.6%; Natural bacteria clearance rate is 93%. |
Conclusion: base plate of ping-pong bat excellent in sterilization effect in the embodiment of the present invention 1 and embodiment 2, compared with common base plate of ping-pong bat of the prior art, the present invention has obviously advantage.
(5) to the test improving the state of mind.
In order to verify that the present invention is to the effect improving the state of mind, inventor cooperates with sports school of Zhongshan city, product of the present invention is sent with charge free to student's also invite participation on probation investigation on probation, that participates in investigation on probation has 600 people, be divided into 3 groups, base plate of ping-pong bat wherein in front 2 groups of trial editions invention in embodiment 1 and embodiment 2, 3rd group is control group (common base plate of ping-pong bat), by SCL-90 questionnaire (i.e. " Self-reporting inventory-SCL90 ", one of foremost Mental health test scale in the world), through continuing the follow-up investigation of 3 weeks, survey data is as following table (unit: people):
| Group on probation | Number on probation | Effective | Effect is better | Effect is general | Weak effect | To no effect |
| Embodiment 1 | 200 | 111 | 52 | 32 | 5 | 0 |
| Embodiment 2 | 200 | 99 | 65 | 34 | 2 | 0 |
| Control group | 200 | 17 | 30 | 79 | 59 | 15 |
Conclusion: the base plate of ping-pong bat in the embodiment of the present invention 1 and embodiment 2 is to carrying the respond well of battle array spirit aspect, and compared with common base plate of ping-pong bat of the prior art, the present invention has obviously advantage proposing the effect in battle array spirit.
Claims (2)
1. one kind has the veneer of anti-interference anion health-care efficacy, comprise clappers body (1) and handle (2), it is characterized in that: described clappers body (1) is made up of core layer (10), anion adhesive layer, Traditional Chinese medicine clamping plate layer (11) and bamboo surface flaggy (12), the top and bottom of described core layer (10) are glued together respectively by anion adhesive layer and described Traditional Chinese medicine clamping plate layer (11), and described bamboo surface flaggy (12) is glued together respectively by anion adhesive layer and described Traditional Chinese medicine clamping plate layer (11); Wherein, described anion adhesive layer comprises hydroxyl butadiene-styrene rubber and anion natural mineral matter powder, wherein the mass ratio of hydroxyl butadiene-styrene rubber and anion natural mineral matter powder is 6:1, described anion natural mineral matter powder is tourmaline, lanthanide rare composite salt and the titanium oxide mixture by weight 4:3:3, wherein tourmaline is dravite and the elbaite mixture by weight 3:2, and the granularity of described anion natural mineral matter powder is 400 object superfines;
Be made up of the raw material of following weight for the manufacture of the Traditional Chinese medicine clamping plate layer (11) in base plate of ping-pong bat: sawdust 50-60 part, rhamnus crenata sieb.et zucc 30-40 part, rhizome of cyrtomium 15-20 part, serissa serissoides 4-6 part, lavender 20-25 part, rosemary 15-20 part, anemone vitifolia 3-5 part, elm bark 15-25 part, agalloch eaglewood 4-6 part, calamus 15-20 part, Moschus 1-3 part, peppermint 1-3 part, dandelion 1-3 part, mother chrysanthemum 1-3 part, sweet marjoram 1.5-2.5 part, santal 1.5-2 part, safron essential oil 0.4-0.6 part, Geranium Essential 0.3-0.5 part, polyurethane resin adhesive 10-12 part, the manufacture method of described Traditional Chinese medicine clamping plate layer (11) comprises the following steps:
A. get respectively by above-mentioned each component: sawdust 50-60 part, rhamnus crenata sieb.et zucc 30-40 part, rhizome of cyrtomium 15-20 part, serissa serissoides 4-6 part, lavender 20-25 part, rosemary 15-20 part, anemone vitifolia 3-5 part, elm bark 15-25 part, agalloch eaglewood 4-6 part, calamus 15-20 part, Moschus 1-3 part, peppermint 1-3 part, dandelion 1-3 part, mother chrysanthemum 1-3 part, sweet marjoram 1.5-2.5 part, santal 1.5-2 part, drops in micronizer and is ground into 120 object mixed-powders;
B. will add safron essential oil 0.4-0.6 part in the mixed-powder in step a, Geranium Essential 0.3-0.5 part, polyurethane resin adhesive 10-12 part, then add high speed dispersor and carry out stirring 20min one-tenth compound, for subsequent use;
C. the compound in step b is inserted the Chinese medicine sheet material that 1mm-1.1mm thickness is made in hot pressing in pressing machine, for subsequent use; Wherein, the press time is 4-5min, and pressure is 1-1.5Mpa/cm
2, temperature remains on 100 DEG C-110 DEG C;
D. the Chinese medicine sheet material in step c draws the trim line of the first base of base plate of ping-pong bat, cut, sizing, obtains Traditional Chinese medicine clamping plate layer (11).
2. there is a manufacture method for the veneer of anti-interference anion health-care efficacy, it is characterized in that: comprise the following steps,
S1. get dravite, elbaite, lanthanide rare composite salt and titanium dioxide respectively by each component, and drop in micronizer respectively and be crushed to 400 object anion natural mineral matter powder, for subsequent use;
S2. the anion natural mineral matter powder in step S1 is become anion adhesive with hydroxyl butadiene-styrene rubber mix and blend 15min, for subsequent use;
S3. core layer (10) obtained for common process and bamboo surface flaggy (12) are dried, the moisture content of described core layer (10) and bamboo surface flaggy (11) is made to be less than 10%, the thickness of wherein said core layer (10) is 3.3mm-3.6mm, and the thickness of described bamboo surface flaggy (12) is 0.3mm-0.4mm;
S4. core layer (10) upper and lower surface in step S3 is coated respectively anion adhesive obtained in step S2, conventional coating weight is 70-90g/m
2, then two pieces of Traditional Chinese medicine clamping plate layers (11) are glued together with the top and bottom of core layer (10) respectively; Respectively anion adhesive is coated on the surface of two pieces of Traditional Chinese medicine clamping plate layers (11) again, be stained with bamboo surface flaggy (12) respectively, form composite plate;
S5. carry out hot-pressing processing to the composite plate in step S4, conventional hot-press gluing technique parameter is: hot pressing temperature 95 DEG C-130 DEG C, pressure 0.8MPa-1.5MPa, and hot pressing time is 1.5-5min;
S6. process composite plate after step s 5, polish, mounting handle (2), to obtain final product.