CN104886848A - Silicon coating polyester fabric and fabrication process thereof - Google Patents
Silicon coating polyester fabric and fabrication process thereof Download PDFInfo
- Publication number
- CN104886848A CN104886848A CN201510249408.7A CN201510249408A CN104886848A CN 104886848 A CN104886848 A CN 104886848A CN 201510249408 A CN201510249408 A CN 201510249408A CN 104886848 A CN104886848 A CN 104886848A
- Authority
- CN
- China
- Prior art keywords
- silica
- surface layer
- parts
- polyester fabric
- release paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a silicon coating polyester fabric. The fabric comprises a fabric body, a bonding layer and a surface layer. The surface layer comprises 100 parts of silicon resins, 5 parts to 20 parts of silicon bridging agents, 0 part to 10 parts of slip agents and 0 part to 0.5 part of stripping agents. A fabrication process of the fabric comprises fabricating surface layer size; fabricating bonding layer size; putting release paper into a NO.1 oven in a range of 8m/min to 18m/min, enabling the release paper to reach a NO.1 coating table after preheating at 60 DEG C, and coating the surface layer size on the surface of the release paper on the NO.1 coating table; enabling the release paper to enter a NO.2 oven to be dried at the temperature ranging from 100 DEG C to 160 DEG C to be delivered to a NO.2 coating table, coating the bonding layer size on the surface layer size of the release paper, delivering the release paper to a NO.3 oven to be baked to be half dry at the temperature ranging from 80 DEG C to 130 DEG C, feeding the release paper to a laminating machine to be subjected to cloth pasting, performing drying at 150 DEG C after cloth pasting, performing rolling to feed the cloth into an 80-DEG C curing chamber to be cured for more than 48 hours, and performing isolation packaging to obtain finished products.
Description
Technical field
The present invention relates to a kind of silica-gel coating polyester fabric, and the manufacture craft of silica-gel coating polyester fabric.
Background technology
At present, along with the high speed development of artificial leather technology industry, the artificial leather of polyurethane resin manufacture is widely used in the every field such as clothes, case and bag, automobile.Along with the lifting of mankind's environmental consciousness, government is to the increasingly stringent management and control of environmental protection, and the conventional artificial progressively eliminating contaminated environment removes from office production.But the production of polyurethane artificial leather instantly mainly contains traditional solvent-borne artificial leather and water-based artificial leather.Solvent-borne type artificial leather is the main product of instantly removing from office factory, need with a large amount of toluene, butanone, DMF equal solvent, volatile when using these solvents, very large pollution is caused to environment, and be unfavorable for the health of workman, in addition artificial leather also can residual fraction harmful substance, may damage consumer health; The surface layer of water-based artificial leather, adhesive linkage all use polyurethane resins, its performance and solvent-borne type artificial leather also have very large gap, and cost intensive, and technology is not mature enough, and enterprise's acceptance is not high, more difficult popularization.
Summary of the invention
One of the technical problem to be solved in the present invention, is to provide a kind of silica-gel coating polyester fabric.
The present invention is achieved in that a kind of silica-gel coating polyester fabric, comprises cloth body, adhesive linkage and surface layer; Described surface layer comprises each component of following parts by weight:
Silica column 100 parts, silica gel bridging agent 5-20 part, slipping agent 0-10 part and remover 0-0.5 part.
Further, the slurry viscosity of described surface layer is 2000-5000cps/25 DEG C.
Further, described adhesive linkage comprises each component of following parts by weight:
Silica column 100 parts, silica gel bridging agent 5-20 part, diluent 0-15 part and mill base 5-20 part.
The technical problem to be solved in the present invention two, is the manufacture craft providing a kind of described silica-gel coating polyester fabric.
The present invention is achieved in that a kind of manufacture craft of described silica-gel coating polyester fabric, comprises the following steps:
(1) make surface layer slurry: after silica column 100 parts, silica gel bridging agent 5-20 part, slipping agent 0-10 part and the abundant mix and blend of remover 0-0.5 part, adjust viscosity to 2000-5000cps/25 DEG C, standing and defoaming;
(2) adhesive linkage slurry is made: by silica column 100 parts, silica gel bridging agent 5-20 part, diluent 0-15 part and mill base 5-20 part mix and blend, standing and defoaming;
(3) be coated with: a release liners is entered a baking oven with speed 8 ~ 18m/min, at 60 DEG C, arrive No. one after preheating be coated with platform, the surface layer slurry in (1) is coated with painting on platform at No. one and scrapes on release liners surface; Then release liners enters after No. two baking ovens are dried with 100-160 DEG C and is delivered to No. two painting platforms again, being coated with by adhesive linkage slurry in (2) scrapes on the surface layer slurry of release liners again, then release liners enter No. three baking ovens be dried at 80-130 DEG C half-dried after, send into make-up machine patch, with 150 DEG C of oven dry after patch, rolling is sent into 80 DEG C of curing chamber slakings more than 48 hours separation and is packaged to be finished product.
The invention has the advantages that: produce artificial leather and silica-gel coating polyester fabric with silica column, the present invention does not use any solvent in whole production, environment-protecting asepsis, obtained product has good water proofing property, gas permeability, high fire resistance, and soft comfortable.
Accompanying drawing explanation
The present invention is further illustrated in conjunction with the embodiments with reference to the accompanying drawings.
Fig. 1 is the flow chart of silica-gel coating polyester fabric manufacture craft in the present invention.
Detailed description of the invention
A kind of silica-gel coating polyester fabric, comprises cloth body, adhesive linkage and surface layer; Described surface layer comprises each component of following parts by weight:
Silica column 100 parts, silica gel bridging agent 5-20 part, slipping agent 0-10 part and remover 0-0.5 part; And the slurry viscosity of described surface layer is 2000-5000cps/25 DEG C.
Described adhesive linkage comprises each component of following parts by weight:
Silica column 100 parts, silica gel bridging agent 5-20 part, diluent 0-15 part and mill base 5-20 part.
For more clearly describing the present invention, especially exemplified by following embodiment, raw material and the proportioning situation of each embodiment are as shown in the table:
Manufacture craft following (see Fig. 1) for the silica-gel coating polyester fabric of the various embodiments described above:
(1) surface layer slurry is made: after silica column, silica gel bridging agent, slipping agent and the abundant mix and blend of remover, adjustment viscosity, standing and defoaming;
(2) adhesive linkage slurry is made: by silica column, silica gel bridging agent, diluent and mill base mix and blend, standing and defoaming;
(3) be coated with: a release liners is entered a baking oven with speed 8 ~ 18m/min (embodiment 1,2,3,4 adopts 8m/min, 10m/min, 13m/min, 18m/min respectively), at 60 DEG C, arrive No. one after preheating be coated with platform, the surface layer slurry in (1) is coated with painting on platform at No. one and scrapes on release liners surface, then release liners enters No. two baking ovens with 100-160 DEG C of (embodiment 1, 2, 3, 4 adopt 100 DEG C respectively, 120 DEG C, 130 DEG C, 160 DEG C) dry after be delivered to again No. two be coated with platforms, being coated with by adhesive linkage slurry in (2) scrapes on the surface layer slurry of release liners again, then release liners enters No. three baking ovens 80-130 DEG C of (embodiment 1, 2, 3, 4 adopt 100 DEG C respectively, 80 DEG C, 130 DEG C, 110 DEG C) under be dried to half-dried after, send into make-up machine patch, with 150 DEG C of oven dry after patch, rolling is sent into 80 DEG C of curing chamber slakings more than 48 hours separation and is packaged to be finished product.
Silica-gel coating polyester fabric of the present invention is carried out 3 grades of flammability tests in ISO14116, test result is as follows:
Wherein, the duration of ignition: 10 seconds; Y: be; N: no; NIL: mist
Rank:
1 grade:
Flame or the damage of hole shape is not allowed to spread to most top margin or vertical edges
Sample is not allowed to occur burning or melting dropping
Sample is not allowed to occur glowing from carbonized region and spread to not damaging region.
2 grades:
Do not allow propagation of flame to most top margin or vertical edges
Sample is not allowed to occur burning or melting dropping
Sample is not allowed to occur glowing from carbonized region and spread to not damaging region
Hole shape is damaged not allow sample to occur.
3 grades:
Do not allow propagation of flame to most top margin or vertical edges
Sample is not allowed to occur burning or melting dropping
Sample is not allowed to occur glowing from carbonized region and spread to not damaging region.
Hole shape is damaged not allow sample to occur.
The average after flame time of 6 samples can not more than 2 seconds.
From the result of upper table, silica-gel coating polyester fabric of the present invention is by the flammability test of 3 grades in ISO14116.
The present invention also has the following advantages:
The wearability of A, product silica-gel coating polyester fabric of the present invention is far above the like product on market, and can reach more than 5000 turns without damaged according to EN530 (sand paper specification GRIT100) test, average hydrostatic pressing is at more than 10000mm.
B, relative to existing product, weatherability, the hydrolysis of silica-gel coating polyester fabric of the present invention improve 3 times, have increased considerably service life.
Folding resistance and the cold tolerance of C, silica-gel coating polyester fabric are good, and under normal temperature, 300,000 nothings are damaged, 100,000 flawlesses at-20 DEG C.
D, silica-gel coating polyester fabric have advantage soft, comfortable and easy to wear, and production technology of the present invention is simple, and convenient popularization, cutting can be produced into clothes as required.
Claims (4)
1. a silica-gel coating polyester fabric, is characterized in that: comprise cloth body, adhesive linkage and surface layer; Described surface layer comprises each component of following parts by weight:
Silica column 100 parts, silica gel bridging agent 5-20 part, slipping agent 0-10 part and remover 0-0.5 part.
2. silica-gel coating polyester fabric as claimed in claim 1, is characterized in that: the slurry viscosity of described surface layer is 2000-5000cps/25 DEG C.
3. silica-gel coating polyester fabric as claimed in claim 1, is characterized in that: described adhesive linkage comprises each component of following parts by weight:
Silica column 100 parts, silica gel bridging agent 5-20 part, diluent 0-15 part and mill base 5-20 part.
4. a manufacture craft for silica-gel coating polyester fabric as claimed in claim 1, is characterized in that: comprise the following steps:
(1) make surface layer slurry: after silica column 100 parts, silica gel bridging agent 5-20 part, slipping agent 0-10 part and the abundant mix and blend of remover 0-0.5 part, adjust viscosity to 2000-5000cps/25 DEG C, standing and defoaming;
(2) adhesive linkage slurry is made: by silica column 100 parts, silica gel bridging agent 5-20 part, diluent 0-15 part and mill base 5-20 part mix and blend, standing and defoaming;
(3) be coated with: a release liners is entered a baking oven with speed 8 ~ 18m/min, at 60 DEG C, arrive No. one after preheating be coated with platform, the surface layer slurry in (1) is coated with painting on platform at No. one and scrapes on release liners surface; Then release liners enters after No. two baking ovens are dried with 100-160 DEG C and is delivered to No. two painting platforms again, being coated with by adhesive linkage slurry in (2) scrapes on the surface layer slurry of release liners again, then release liners enter No. three baking ovens be dried at 80-130 DEG C half-dried after, send into make-up machine patch, with 150 DEG C of oven dry after patch, rolling is sent into 80 DEG C of curing chamber slakings more than 48 hours separation and is packaged to be finished product.