CN104861873A - Wax polish for automobiles - Google Patents

Abstract

Wax polish for automobiles is prepared from raw materials in parts by weight as follows: 4-7 parts of oleic acid, 8-15 parts of glycerin, 4-9 parts of coconut diethanolamide, 5-10 parts of palm wax, 13-24 parts of ethylene glycol, 2-6 parts of SDS (sodium dodecyl sulfonate), 1.2-2 parts of sodium metaborate, 2-5 parts of iron oxide red, 4-5 parts of a bactericide, 3-6 parts of modified wollastonite, 1-4 parts of ozokerite, 2-6 parts of alkyd resin and 3-5 parts of a dispersing agent. The wax polish for the automobiles has the benefits as follows: the wax polish for the automobiles has good waterproofness for automobile bodies and lasting brightness, can form a layer of hard protection film on the surface and can well protect the automobiles.

Description

A kind of automobile polish

Technical field

The present invention relates to a kind of automobile polish.

Background technology

Along with the demand of vehicle gets more and more, to Motor Maintenance also higher requirement, promote the development of polishing wax.Automobile leaks in the sunlight for a long time cruelly, and experiences rainwater and dust storm, maintains for automobile extremely important, not only can reach effect attractive in appearance, and can extend the work-ing life of automobile.But polishing wax in the market, if will reach good brightness effect, just need thicker wax layer, cost is high, and guard time is short.

Summary of the invention

For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of automobile polish, can have good water-repellancy, have lasting light at car body, can form the hard protective membrane of one deck, have good provide protection to automobile on surface.

For solving prior art problem, technical scheme provided by the invention is, a kind of automobile polish, and it is made up of the raw material of following parts by weight:

Oleic acid 4-7 part, glycerine 8-15 part, cocinic acid alkylolamide 4-9 part, palm wax 5-10 part, ethylene glycol 13-24 part, sodium laurylsulfonate 2-6 part, sodium metaborate 1.2-2 part, red iron oxide 2-5 part, sterilant 4-5 part, modified grammite 3-6 part, ceresine 1-4 part, Synolac 2-6 part, dispersion agent 3-5 part.

The invention has the beneficial effects as follows: automobile polish of the present invention can have good water-repellancy at car body, have lasting light, the hard protective membrane of one deck can be formed on surface, have good provide protection to automobile.

Embodiment

embodiment 1

A kind of automobile polish, it is made up of the raw material of following parts by weight:

Oleic acid 4 parts, glycerine 8 parts, cocinic acid alkylolamide 4 parts, palm wax 5 parts, ethylene glycol 13 parts, sodium laurylsulfonate 2 parts, sodium metaborate 1.2 parts, red iron oxide 2 parts, 4 parts, sterilant, modified grammite 3 parts, 1 part, ceresine, Synolac 2 parts, dispersion agent 3 parts.

embodiment 2

A kind of automobile polish, it is made up of the raw material of following parts by weight:

Oleic acid 7 parts, glycerine 15 parts, cocinic acid alkylolamide 9 parts, palm wax 10 parts, ethylene glycol 24 parts, sodium laurylsulfonate 6 parts, sodium metaborate 2 parts, red iron oxide 5 parts, 5 parts, sterilant, modified grammite 6 parts, 4 parts, ceresine, Synolac 6 parts, dispersion agent 5 parts.

Claims (1)

1. an automobile polish, is characterized in that: it is made up of the raw material of following parts by weight:

Oleic acid 4-7 part, glycerine 8-15 part, cocinic acid alkylolamide 4-9 part, palm wax 5-10 part, ethylene glycol 13-24 part, sodium laurylsulfonate 2-6 part, sodium metaborate 1.2-2 part, red iron oxide 2-5 part, sterilant 4-5 part, modified grammite 3-6 part, ceresine 1-4 part, Synolac 2-6 part, dispersion agent 3-5 part.