CN104861315A - Acid-and-alkali-resistant automobile rubber hose - Google Patents
Acid-and-alkali-resistant automobile rubber hose Download PDFInfo
- Publication number
- CN104861315A CN104861315A CN201510265523.3A CN201510265523A CN104861315A CN 104861315 A CN104861315 A CN 104861315A CN 201510265523 A CN201510265523 A CN 201510265523A CN 104861315 A CN104861315 A CN 104861315A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- rubber hose
- alkali
- automobile rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An acid-and-alkali-resistant automobile rubber hose is prepared from raw materials in parts by weight as follows: 6-14 parts of blast furnace slag micro-powder, 4-9 parts of fast extruding furnace black N550, 3-9 parts of carnauba wax, 4-7 parts of a friction property modifier, 2-6 parts of aluminum oxide, 3-6 parts of graphite, 4-9 parts of acetyl triethyl citrate, 1-3 parts of black soil, 3-9 parts of talc powder, 1-5 parts of a coupling agent, 4-9 parts of polyolefin elastomers, 3-6 parts of polypropylene resin, 4-10 parts of poly(4-methyl-1-pentene) and 6-14 parts of vinyl trimethoxy silane. The automobile rubber hose has the benefits as follows: the wear-resistant automobile rubber hose has good wear resistance and acid and alkali resistance, is long in service life and well guarantees the normal work of an automobile.
Description
Technical field
The present invention relates to a kind of automobile abrasive rubber sebific duct.
Background technology
Rubber hose is connecting engine and air filter, engine and radiator system, automotive air-conditioning system etc. mainly.Current automotive hose uses thermal contraction casing tube, in tubular construction.Current use paracril is as fuelpipe, and paracril is all not suitable for prime the fuel system, and major part existence is poor containing halogen, flame retardant properties.Therefore, well can not meet the use needs of automobile, cause the security of automobile to can not get ensureing; Simultaneously along with the development of society, people are more and more higher for the requirement of rubber hose.Therefore, high performance sebific duct is the direction that people pursue.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provide a kind of automobile abrasive rubber sebific duct, tool has good wearability and resistance to acids and bases, long service life, well ensure that the normal work of automobile.
For solving prior art problem, technical scheme provided by the invention is, a kind of automobile rubber sebific duct of acid and alkali-resistance, and it is made up of the raw material of following parts by weight:
Blast-furnace cinder micro-powder 6-14 part, fast extrusion carbon black N5504-9 part, carnauba wax 3-9 part, frictional property regulator 4-7 part, aluminium sesquioxide 2-6 part, graphite 3-6 part, acetyl triethyl citrate 4-9 part, black earth 1-3 part, talcum powder 3-9 part, coupling agent 1-5 part, polyolefin elastomer 4-9 part, acrylic resin 3-6 part, poly-4-methyl-1-pentene 4-10 part, vinyltrimethoxy silane 6-14 part.
The invention has the beneficial effects as follows: automobile abrasive rubber sebific duct of the present invention, tool has good wearability and resistance to acids and bases, long service life, well ensure that the normal work of automobile.
Embodiment
embodiment 1
An automobile rubber sebific duct for acid and alkali-resistance, it is made up of the raw material of following parts by weight:
Blast-furnace cinder micro-powder 6 parts, fast extrusion carbon black N5504 part, carnauba wax 3 parts, frictional property regulator 4 parts, aluminium sesquioxide 2 parts, 3 parts, graphite, acetyl triethyl citrate 4 parts, 1 part, black earth, talcum powder 3 parts, coupling agent 1 part, polyolefin elastomer 4 parts, acrylic resin 3 parts, poly-4-methyl-1-pentene 4 parts, vinyltrimethoxy silane 6 parts.
embodiment 2
An automobile rubber sebific duct for acid and alkali-resistance, it is made up of the raw material of following parts by weight:
Blast-furnace cinder micro-powder 14 parts, fast extrusion carbon black N5509 part, carnauba wax 9 parts, frictional property regulator 7 parts, aluminium sesquioxide 6 parts, 6 parts, graphite, acetyl triethyl citrate 9 parts, 3 parts, black earth, talcum powder 9 parts, coupling agent 5 parts, polyolefin elastomer 9 parts, acrylic resin 6 parts, poly-4-methyl-1-pentene 10 parts, vinyltrimethoxy silane 14 parts.
Claims (1)
1. an automobile rubber sebific duct for acid and alkali-resistance, is characterized in that: it is made up of the raw material of following parts by weight:
Blast-furnace cinder micro-powder 6-14 part, fast extrusion carbon black N5504-9 part, carnauba wax 3-9 part, frictional property regulator 4-7 part, aluminium sesquioxide 2-6 part, graphite 3-6 part, acetyl triethyl citrate 4-9 part, black earth 1-3 part, talcum powder 3-9 part, coupling agent 1-5 part, polyolefin elastomer 4-9 part, acrylic resin 3-6 part, poly-4-methyl-1-pentene 4-10 part, vinyltrimethoxy silane 6-14 part.