CN104860627A - Environment-friendly building material with adjustable humidity - Google Patents

Abstract

The invention discloses an environment-friendly building material with adjustable humidity, formed by the following raw materials in parts by weight: 6-9 parts of calcium lignosulphonate, 2-4.5 parts of lubricating dispersant TAF, 2-3.5 parts of color master batch, 20-43 parts of superfine slag powder, 3-7 parts of zinc oxide, 8-16 parts of citric acid waste gypsum, 3-5 parts of flexibilizer, 5-8 parts of adhesive, 5-7 parts of attapulgite, 2-6 parts of coalescing agent, 12-24 parts of solid ammonii ichthyolsulphonas, 3-5 parts of hydroxyethyl cellulose, 7-21 parts of acrylic emulsion, 2-4 parts of color retention agent, 11-21 parts of calcium chloride solution and 2-6 parts of retarder. The environment-friendly building material with adjustable humidity has the advantages of being capable of effectively adjusting the humidity, good in moldproof and antibacterial effect, and free of polluting the environment.

Description

A kind of environment-friendly type building material of adjusting humidity

Technical field

The present invention relates to a kind of environment-friendly type building material of adjusting humidity.

Background technology

Along with the development of building, promoted the demand of material of construction, be market more refinement will be following development trend, such as southern material of construction will improve the performance of material of construction in conjunction with southern weather, the rainy water in south, high humidity, when the excess moisture in air, makes people produce humidity, the sense of discomfort such as uncomfortable in chest, bring out the diseases such as sacroiliitis, and construction wall be in for a long time in humidity can be easily mouldy, not only can reduce work-ing life, but also the physical and mental health of people can be unfavorable for.But material of construction in the market also also exists a lot of deficiency in adjustment humidity, and moistureproofness does not add, and soundproof effect is not ideal.Environmental protection always society advocated, so on the basis of environmental-protecting performance, works out and the material of construction of regulating effect can be had particularly important for construction industry to humidity.

Summary of the invention

For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of environment-friendly type building material of adjusting humidity, effectively can regulate humidity, antimildew and antibacterial effective, does not pollute the environment.

For solving prior art problem, technical scheme provided by the invention is, a kind of environment-friendly type building material of adjusting humidity, and it is made up of the raw material of following parts by weight:

Wooden calcium sulfonate 6-9 part, lubrication dispersing agent TAF2-4.5 part, Masterbatch 2-3.5 part, slag micropowder 20-43 part, zinc oxide 3-7 part, lemon acid waste gypsum 8-16 part, toughner 3-5 part, caking agent 5-8 part, attapulgite soil 5-7 part, film coalescence aid 2-6 part, solid stone ester 12-24 part, Natvosol 3-5 part, ACRYLIC EMULSION 7-21 part, color preserving agent 2-4 part, calcium chloride solution 11-21 part, retardant 2-6 part.

The invention has the beneficial effects as follows: the environment-friendly type building material of adjusting humidity of the present invention, effectively can regulate humidity that antimildew and antibacterial effective does not pollute the environment.

Embodiment

embodiment 1

An environment-friendly type building material for adjusting humidity, it is made up of the raw material of following parts by weight:

Wooden calcium sulfonate 6 parts, lubrication dispersing agent TAF2 part, Masterbatch 2 parts, slag micropowder 20 parts, 3 parts, zinc oxide, 8 parts, lemon acid waste gypsum, toughner 3 parts, caking agent 5 parts, attapulgite soil 5 parts, film coalescence aid 2 parts, solid stone ester 12 parts, Natvosol 3 parts, ACRYLIC EMULSION 7 parts, color preserving agent 2 parts, calcium chloride solution 11 parts, retardant 2 parts.

embodiment 2

An environment-friendly type building material for adjusting humidity, it is made up of the raw material of following parts by weight:

Wooden calcium sulfonate 9 parts, lubrication dispersing agent TAF4.5 part, Masterbatch 3.5 parts, slag micropowder 43 parts, 7 parts, zinc oxide, 16 parts, lemon acid waste gypsum, toughner 5 parts, caking agent 8 parts, attapulgite soil 7 parts, film coalescence aid 6 parts, solid stone ester 24 parts, Natvosol 5 parts, ACRYLIC EMULSION 21 parts, color preserving agent 4 parts, calcium chloride solution 21 parts, retardant 6 parts.

Claims (1)

1. an environment-friendly type building material for adjusting humidity, is characterized in that: it is made up of the raw material of following parts by weight:

Wooden calcium sulfonate 6-9 part, lubrication dispersing agent TAF2-4.5 part, Masterbatch 2-3.5 part, slag micropowder 20-43 part, zinc oxide 3-7 part, lemon acid waste gypsum 8-16 part, toughner 3-5 part, caking agent 5-8 part, attapulgite soil 5-7 part, film coalescence aid 2-6 part, solid stone ester 12-24 part, Natvosol 3-5 part, ACRYLIC EMULSION 7-21 part, color preserving agent 2-4 part, calcium chloride solution 11-21 part, retardant 2-6 part.