CN104858232A - 一种泡沫金属差厚钣金件的制备方法 - Google Patents

一种泡沫金属差厚钣金件的制备方法 Download PDF

Info

Publication number
CN104858232A
CN104858232A CN201510272314.1A CN201510272314A CN104858232A CN 104858232 A CN104858232 A CN 104858232A CN 201510272314 A CN201510272314 A CN 201510272314A CN 104858232 A CN104858232 A CN 104858232A
Authority
CN
China
Prior art keywords
foam metal
foam
metal plate
foaming
foamed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510272314.1A
Other languages
English (en)
Other versions
CN104858232B (zh
Inventor
刘志民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510272314.1A priority Critical patent/CN104858232B/zh
Publication of CN104858232A publication Critical patent/CN104858232A/zh
Application granted granted Critical
Publication of CN104858232B publication Critical patent/CN104858232B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种泡沫金属差厚钣金件的制备方法，其特征在于：1)首先将至少两块金属板进行堆叠，并在两金属板的接触面喷涂发泡剂；2)然后通过轧制设备对两金属板进行第一次轧制，得到具有待发泡区的一次轧制金属板；3)将一次轧制金属板从待发泡区处分隔为两块；4)将两块一次轧制金属板堆叠并进行二次轧制，得到具有待发泡区的泡沫金属板；5)将泡沫金属板放置于加热炉内预热，得到具有发泡区的泡沫金属板；6)将预热后的泡沫金属板放置于冲压模具内加热，直至发泡区达到发泡温度；7)通过冲压模具将达到发泡温度的泡沫金属板进行热冲压成型，并进行保压以完成发泡区的二次发泡，进而得到泡沫金属差厚钣金件。本发明方法制备的泡沫金属差厚钣金件，可满足不同部位零件的性能要求，使钣金件碰撞吸能效果提高40％以上。

Description

一种泡沫金属差厚钣金件的制备方法
技术领域
本发明涉及一种泡沫金属差厚钣金件的制备方法，属于汽车零件加工领域。
背景技术
对于汽车车身而言，为提高碰撞安全性能，一般采用高强度的等厚金属板材来制备车身钣金件。但这样的车身结构设计不利于减重，而且会增加汽车燃料消耗，造成环境污染。因此，随着能源危机和环境问题的加剧，汽车轻量化技术成为了一项减少燃料消耗，降低排气污染的重要举措。汽车轻量化主要有两种途径：一种是对零件材料轻量化，另一种是对零件结构进行优化，其中，前者较为直接且效果明显。
差厚板做为一种变截面薄板材料，可根据车身零部件所受载荷以及成形过程数值模拟结果，优化差厚板的厚度、强度分布位置和大小，以提高碰撞吸能性，使车身零部件的质量最大限度减轻，而其刚度、抗凹性、成形性能不降低。因此，差厚板成为一种很有前景的车身轻量化新材料。目前，用于制造车身轻量化的差厚钣金件分为两种：一种是TWB钣金件(Tailor Welded Blanks，拼焊板)，其制备方法是将至少2块不同厚度的平板料焊接在一起并进行冲压，得到满足不同部位零件的性能要求的钣金件；而另一种TRB钣金件(Tailor Rolled Blanks，连续变截面板)，是先通过柔性轧制工艺得到TRB板，然后再进行冲压得到TRB差厚钣金件，由于现有工艺制备的金属钣金件质量较重，不能很好的满足车身轻量化要求，并且金属钣金件的晶粒细化不够，导致抗拉强度也不能很好的满足使用要求。
发明内容
针对上述问题，本发明的目的是提供一种能够使金属板质量更轻、抗拉强度更高且碰撞吸能性更好的泡沫金属差厚钣金件的制备方法。
为实现上述目的，本发明采取以下技术方案：一种泡沫金属差厚钣金件的制备方法，其包括以下步骤：
1)首先将至少两块金属板进行堆叠，并在两金属板的接触面喷涂发泡剂；
2)然后通过轧制设备对两金属板进行第一次轧制，得到轧制为一体且具有待发泡区的一次轧制金属板；
3)将一次轧制金属板从待发泡区处分隔为两块；
4)将两块一次轧制金属板堆叠并使两待发泡区相对，然后通过轧制设备进行第二次轧制，得到具有待发泡区的泡沫金属板；
5)将泡沫金属板放置于加热炉内进行预热，使待发泡区进行第一次预发泡，得到具有发泡区的泡沫金属板；
6)将预热后的泡沫金属板放置于冲压模具内进行加热，直至泡沫金属板的发泡区达到发泡温度；
7)通过冲压模具将达到发泡温度的泡沫金属板进行热冲压成型，并在成型后进行保压以完成发泡区的二次发泡，进而得到具有局部闭孔泡沫先驱体特征的泡沫金属差厚钣金件。
金属板采用钢板、铝板、铜板和镍板之一。
发泡剂采用氢化钛或氢化锆发泡剂。
本发明由于采取以上技术方案，其具有以下优点：1、本发明方法制备的泡沫金属差厚钣金件，可满足不同部位零件的性能要求，使钣金件碰撞吸能效果提高40％以上。2、本发明方法制备的泡沫金属差厚钣金件与现有金属差厚钣金件相比，减重至少20％以上。3、本发明方法制备的泡沫金属差厚钣金件晶粒细化程度高，因此抗拉强度比现有金属差厚钣金件提高40％以上。4、本发明方法由于采用冲压模具对泡沫金属板进行热冲压成型，并在成型后进行保压以完成发泡区的二次发泡，因此显著提高了二次发泡效率和生产效率。5、本发明方法采用的局部闭孔泡沫先驱体板料制备和热冲压及二次发泡相结合的方法，是材料、工艺和结构的一体化体现。本发明广泛应用于军事、航天航空、汽车等领域。
附图说明
图1是本发明的制备方法中步骤1的示意图；
图2是本发明的制备方法中步骤2的示意图；
图3是本发明的制备方法中步骤3的示意图；
图4是本发明的制备方法中步骤4的示意图；
图5是本发明的制备方法中步骤5的示意图；
图6是本发明的制备方法中步骤6的示意图；
图7是本发明的制备方法中步骤7的示意图；
图8是本发明的泡沫金属差厚钣金件的整体结构示意图。
具体实施方式
下面结合附图和实施例对本发明进行详细的描述。
本发明提供的一种泡沫金属差厚钣金件的制备方法，其包括以下步骤：
1)首先将至少两块金属板1进行堆叠，并在两金属板1的接触面喷涂发泡剂2(如图1所示)；
2)然后通过轧制设备3对两金属板1进行第一次轧制，得到轧制为一体且具有待发泡区4的一次轧制金属板5(如图2所示)；
3)将一次轧制金属板5从待发泡区4处分隔为两块(如图3所示)；
4)将两块一次轧制金属板5堆叠并使两待发泡区4相对，然后通过轧制设备3进行第二次轧制，得到具有待发泡区4的泡沫金属板6(如图4所示)；
5)将泡沫金属板6放置于加热炉7内进行预热，使待发泡区4进行第一次预发泡，得到具有发泡区10的泡沫金属板6(如图5所示)；
6)将预热后的泡沫金属板6放置于冲压模具8内进行加热，直至泡沫金属板6的发泡区10达到发泡温度(如图6所示)；
7)通过冲压模具8将达到发泡温度的泡沫金属板6进行热冲压成型，并在成型后进行保压以完成发泡区10的二次发泡(如图7所示)，进而得到具有局部闭孔泡沫先驱体特征的泡沫金属差厚钣金件9(如图8所示)。
上述实施例中，金属板1可采用钢板、铝板、铜板和镍板之一。
上述实施例中，发泡剂2采用TiH2(氢化钛)或ZrH2(氢化锆)发泡剂。
上述各实施例仅用于说明本发明，其中各部件的结构、连接方式等都是可以有所变化的，凡是在本发明技术方案的基础上进行的等同变换和改进，均不应排除在本发明的保护范围之外。

Claims (3)

1.一种泡沫金属差厚钣金件的制备方法，其包括以下步骤：
1)首先将至少两块金属板进行堆叠，并在两金属板的接触面喷涂发泡剂；
2)然后通过轧制设备对两金属板进行第一次轧制，得到轧制为一体且具有待发泡区的一次轧制金属板；
3)将一次轧制金属板从待发泡区处分隔为两块；
4)将两块一次轧制金属板堆叠并使两待发泡区相对，然后通过轧制设备进行第二次轧制，得到具有待发泡区的泡沫金属板；
5)将泡沫金属板放置于加热炉内进行预热，使待发泡区进行第一次预发泡，得到具有发泡区的泡沫金属板；
6)将预热后的泡沫金属板放置于冲压模具内进行加热，直至泡沫金属板的发泡区达到发泡温度；
7)通过冲压模具将达到发泡温度的泡沫金属板进行热冲压成型，并在成型后进行保压以完成发泡区的二次发泡，进而得到具有局部闭孔泡沫先驱体特征的泡沫金属差厚钣金件。
2.如权利要求1所述的一种泡沫金属差厚钣金件的制备方法，其特征在于：金属板采用钢板、铝板、铜板和镍板之一。
3.如权利要求1或2所述的一种泡沫金属差厚钣金件的制备方法，其特征在于：发泡剂采用氢化钛或氢化锆发泡剂。
CN201510272314.1A 2015-05-25 2015-05-25 一种泡沫金属差厚钣金件的制备方法 Expired - Fee Related CN104858232B (zh)