CN104844030A - Cement production method by adding fatty alcohol sulphosalts air-entraining agent - Google Patents
Cement production method by adding fatty alcohol sulphosalts air-entraining agent Download PDFInfo
- Publication number
- CN104844030A CN104844030A CN201510228571.5A CN201510228571A CN104844030A CN 104844030 A CN104844030 A CN 104844030A CN 201510228571 A CN201510228571 A CN 201510228571A CN 104844030 A CN104844030 A CN 104844030A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- grinding
- fatty alcohol
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cement production method by adding fatty alcohol sulphosalts air-entraining agent, which includes the following steps of breaking raw materials for cement production to form coarse materials; grinding the coarse materials into fine powder through a grinding machine by a powder concentrator, and then collecting the powder by utilizing a dust collector to be used as raw material powder; after further mixing the raw material powder uniformly, conveying the raw material powder to a cement kiln to generate clinker after being preheated to decompose. Cement grinding aid is added during the grinding by the grinding machine; the cement grinding aid includes the following components in parts by weight: 13 parts of triethanolamine, 52 parts of diethylene glycol, 10 parts of sodium tripolyphosphate, 105 parts of xylitol, 12 parts of sodium thiosulfate, 6 parts of fatty alcohol sulphosalts air-entraining agent, 64 parts of water. The advantage of abundant grinding of cement raw materials is realized.
Description
Technical field
The present invention relates to field of cement production, particularly, relate to a kind of method for production of cement adding fatty alcohol sulfonate class air entrapment agent.
Background technology
At present, China is manufacture of cement and uses big country, and cement is a kind of highly energy-consuming high pollutive industries, the raw material of cement mostly is the bulk matter such as Wingdale, iron ore, clay and coal, need aborning to carry out pulverization process to bulk raw, thus reduce the object that cement burns till hear rate in cement kiln.But in raw material pulverizing process, as the problem directly adopting milling equipment grinding that raw material grinding then can be caused insufficient.
Summary of the invention
The object of the invention is to, for the problems referred to above, propose a kind of method for production of cement adding fatty alcohol sulfonate class air entrapment agent, to realize the sufficient advantage of cement raw material grinding.
For achieving the above object, the technical solution used in the present invention is:
Add a method for production of cement for fatty alcohol sulfonate class air entrapment agent, comprise and the raw material producing cement is carried out fragmentation formation coarseparticulate material;
By powder separating machine, coarse particles material is become fine powder by milling equipment grinding, then utilize dust collection device to collect and be raw meal powder;
After pre-thermolysis, be delivered to cement kiln after being mixed further by raw meal powder generate grog;
Cement grinding aid is added above by during milling equipment grinding;
Described cement grinding aid, weight is as follows:
Trolamine 13 parts; Glycol ether 52 parts; Tripoly phosphate sodium STPP 10 parts; Xylitol 105 parts; 12 parts, Sulfothiorine; Fatty alcohol sulfonate class air entrapment agent 6 parts; 64 parts, water.
Technical scheme of the present invention has following beneficial effect:
Technical scheme of the present invention, adds cement grinding aid in manufacture of cement, thus reaches the sufficient object of cement raw material grinding.
Embodiment
Add a method for production of cement for fatty alcohol sulfonate class air entrapment agent, comprise and the raw material producing cement is carried out fragmentation formation coarseparticulate material; By powder separating machine, coarse particles material is become fine powder by milling equipment grinding, then utilize dust collection device to collect and be raw meal powder; After pre-thermolysis, be delivered to cement kiln after being mixed further by raw meal powder generate grog; Cement grinding aid is added above by during milling equipment grinding; Described cement grinding aid, weight is as follows: trolamine 13 parts; Glycol ether 52 parts; Tripoly phosphate sodium STPP 10 parts; Xylitol 105 parts; 12 parts, Sulfothiorine; Fatty alcohol sulfonate class air entrapment agent 6 parts; 64 parts, water.
Magnetization treatment is carried out by after each for above-mentioned cement grinding aid component mixing.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (1)
1. add a method for production of cement for fatty alcohol sulfonate class air entrapment agent, it is characterized in that, comprise and the raw material producing cement is carried out fragmentation formation coarseparticulate material;
By powder separating machine, coarse particles material is become fine powder by milling equipment grinding, then utilize dust collection device to collect and be raw meal powder;
After pre-thermolysis, be delivered to cement kiln after being mixed further by raw meal powder generate grog;
Cement grinding aid is added above by during milling equipment grinding;
Described cement grinding aid, weight is as follows:
Trolamine 13 parts; Glycol ether 52 parts; Tripoly phosphate sodium STPP 10 parts; Xylitol 105 parts; 12 parts, Sulfothiorine; Fatty alcohol sulfonate class air entrapment agent 6 parts; 64 parts, water.