CN104829767A - Styrene-acrylic emulsion coating paper substrate, and preparation method and application thereof - Google Patents
Styrene-acrylic emulsion coating paper substrate, and preparation method and application thereof Download PDFInfo
- Publication number
- CN104829767A CN104829767A CN201510236955.1A CN201510236955A CN104829767A CN 104829767 A CN104829767 A CN 104829767A CN 201510236955 A CN201510236955 A CN 201510236955A CN 104829767 A CN104829767 A CN 104829767A
- Authority
- CN
- China
- Prior art keywords
- base material
- benzene emulsion
- coated
- stationery base
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses styrene-acrylic emulsion coating a paper substrate and a preparation method thereof. The preparation method disclosed by the invention comprises the following steps: (1), adding a first mixed component in an emulsification tank, rapidly stirring, slowly adding a mixed monomer of a second mixed component in the emulsification tank, and stirring to form pre-emulsion; (2), adding a third mixed component into a reaction kettle to stir; (3), adding a fourth mixed component when the temperature of the reaction kettle is slowly increased to 76-92 DEG C; and (4), continuously stirring and reacting, simultaneously titrating reactants in the reaction kettle by using a fifth mixed component and the pre-emulsion obtained in the step (1) when the temperature of the reaction kettle is up to 82-95 DEG C, and continuously reacting with heat preservation after titrating so as to obtain the styrene-acrylic emulsion. The styrene-acrylic emulsion disclosed by the invention is reasonable in preparation process, steady in property, low in production cost and good in isolation anti-osmosis property and can be widely applied in all kinds of fields of sealing or sticking; and in particular, the styrene-acrylic emulsion is applied to an adhesive tape of the paper substrate and the like.
Description
Technical field
The present invention relates to a kind of benzene emulsion, particularly relate to and be a kind ofly applied to benzene emulsion playing insulation blocking and its preparation method and application on stationery.
Background technology
At present, common stationery base material cannot play insulation blocking when not being coated with benzene emulsion.Stationery base material can cause infiltration when coating silicone oil or pressure-sensitive adhesive coating, is unfavorable for operation, affects performance and the quality of adhesive tape.So carry out a certain amount of coating on the body paper of paper substrate class adhesive tape, reach insulation blocking effect; Ensure that certain glossiness and the stationery substrate surface of the pliability of body paper, stationery substrate surface are not clamminess simultaneously.Therefore in order to adapt to the needs in market, industry has invented benzene emulsion stationery base material being carried out to insulation blocking.But, after current benzene emulsion coating stationery base material, there is following defect: 1, general body paper, all can be partially hard after coating benzene emulsion, makes body paper lack pliability, the attachment of unfavorable affixed object; 2, general benzene emulsion is after coating stationery base material, and stationery substrate surface is sub-light, affects the attractive in appearance of stationery base material; 3, general benzene emulsion is after coating stationery base material, and stationery base material has the phenomenon that is clamminess, thus causes paper to glue rotten quality problem.4, conventional at present benzene emulsion generated time is long, and general needs more than 10 hours, cost is high, complicated operation.
Summary of the invention
In order to overcome the deficiencies in the prior art, the object of this invention is to provide that a kind of cost is reasonable, the reaction times is short, the benzene emulsion and its preparation method and application of isolated protective layer of waterproof, grease proofing infiltration can be formed on stationery base material.
Technical scheme of the present invention is: a kind of benzene emulsion be coated on stationery base material, and its raw material comprises the blending ingredients of following parts by weight:
Blending ingredients one: allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 4-12 part;
Disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 1-8 part;
Ionized water 160-260 part;
Blending ingredients two: vinylbenzene 180-250 part;
Butyl acrylate 180-250 part;
Vinylformic acid 5-9 part;
Vinylformic acid-2-hydroxyl ethyl ester 5-9 part;
Blending ingredients three: sodium bicarbonate 0.5-5 part;
Deionized water 150-250 part;
Blending ingredients four: Potassium Persulphate 0.5-5 part;
Deionized water 8-18 part;
Blending ingredients five: Potassium Persulphate 1.5-10 part;
Deionized water 20-50 part.
Present invention also offers a kind of preparation method of the benzene emulsion be coated on stationery base material, it comprises the following steps:
Step 1: blending ingredients one is added in emulsifying tank, and rapid stirring 15-30 minute; Then the mix monomer of blending ingredients two is slowly joined emulsifying tank, stir 10-20 minute, form pre-emulsion;
Step 2: blending ingredients three is added in the reactor of 60 DEG C, then open stirring;
Step 3: when reactor heat up gradually reach 76-92 DEG C time, add blending ingredients four;
Step 4: continue stirring reaction, when temperature of reaction kettle reaches 82-95 DEG C, the reactant while of the pre-emulsion that blending ingredients five and step 1 are obtained in drop reaction still, titration time is 2-6 hour, titration completes follow-up continuous insulation reaction 1-4 hour, obtains described benzene emulsion.
Further, the mixing speed in described step 1 is 800-1600 rev/min, and the mixing speed in described step 2 is 30-120 rev/min.
The preparation method of a kind of benzene emulsion be coated on stationery base material of the present invention, specifically comprises the following steps:
Step 1: allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 4-12 part, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 1-8 part, deionized water 160-260 part are added in emulsifying tank, then reacts 15-30 minute under the rapid stirring of 800-1600 rev/min; Then vinylbenzene 180-250 part, butyl acrylate 180-250 part, vinylformic acid 5-9 part, vinylformic acid-2-hydroxyl ethyl ester 5-9 part are slowly joined emulsifying tank, stir 10-20 minute, form pre-emulsion;
Step 2: by sodium bicarbonate 0.5-5 part, deionized water 150-250 part adds in the reactor of 60 DEG C, then opens stirring, and mixing speed is 30-120 rev/min;
Step 3: when reactor heat up gradually reach 76-92 DEG C time, add Potassium Persulphate 0.5-5 part, deionized water 8-18 part;
Step 4: continue stirring reaction, when temperature of reaction kettle reaches 82-95 DEG C, the reactant while of the pre-emulsion that the mixed solution formed Potassium Persulphate 1.5-10 part, deionized water 20-50 part and step 1 obtain in drop reaction still, titration time is 2-6 hour, titration completes follow-up continuous insulation reaction 1-4 hour, obtains described benzene emulsion.
The preparation method of a kind of benzene emulsion be coated on stationery base material of the present invention, it also comprises:
Step 5: start to lower the temperature after step 4 is incubated and carry out aftertreatment: (1) when temperature of reaction kettle is down to 80 DEG C, adding polyvinyl alcohol water solution 25-45 part that concentration is 10% in reactor; (2), when temperature of reaction kettle drops to 70 DEG C, in reactor, titration concentration is tertbutyl peroxide aqueous solution 0.3-1.3 part of 3.5%; (3), when temperature drops to 65 DEG C, in reactor, titration concentration is sodium bisulphite formaldehyde aqueous solution 0.3-1.3 part of 1.3%; (4) when temperature drops to 60 DEG C, toward reactor simultaneously titration concentration be 70% succinate sodium 2-ethylhexyl aqueous solution 0.2-0.9 part, concentration be 92% defoamer (defoamer 8034A can be used) aqueous solution 0.2-1.0 part; (5), when temperature drops to 55 DEG C, in reactor, titration concentration is benzoic ether aqueous solution 12-24 part of 98% simultaneously, is sodium polyacrylate salt brine solution 0.2-1.0 part of 45% with titration concentration; (6) when temperature drops to 50 DEG C, adding wax emulsion 12-24 part, is 25% ammoniacal liquor 3-10 part with concentration; (7), when temperature reaches 45 DEG C, after 150 order filter screen filtration impurity, benzene emulsion barrelling will be obtained and preserve.
Present invention also offers a kind of application of the benzene emulsion be coated on stationery base material, benzene emulsion is applied to and is coated on stationery base material, and benzene emulsion glue spread is 2-15g/m
2± 10%, stationery base material is formed the isolated protective layer of waterproof, grease proofing infiltration.
The method that described benzene emulsion is coated on stationery base material is: on stationery base material, be coated with the above-mentioned benzene emulsion coating prepared of at least one deck, to form the isolated protective layer of this substrate outer surface, described benzene emulsion glue spread is 2-15g/m
2± 10%.Concrete coating process is: adopt anilox roll or wheat tooth rod above-mentioned benzene emulsion to be coated the outside surface of stationery base material, solidification value when being wherein coated with is 80-120 DEG C, and benzene emulsion glue spread is 2-15g/m
2± 10%, surface covered is 15-90 ± 5m/min.
Described benzene emulsion coats the process after stationery base material:
One, stationery base material is placed more than 24 hours after coating benzene emulsion.
Two, the one side that stationery base material has been coated with benzene emulsion at it immediately after coating benzene emulsion continues painting fabric aqueous or oiliness silicone oil (parrots face to prevent from another side glues after pressure-sensitive acrylate, cause and be difficult to resolve volume), another surface coated pressure-sensitive acrylate adhesive of stationery base material is to form the adhesive-layer of stationery base material internal surface, after drying rolling, namely rewinding itemize forms stationery base material adhesive tape.
Three, stationery base material is after coating benzene emulsion, first in the one side that stationery base material is coated with benzene emulsion after printing pattern layer, at painting fabric aqueous or oiliness silicone oil, then at another surface coated pressure-sensitive acrylate adhesive of stationery base material to form the adhesive-layer of stationery base material internal surface, after drying rolling, namely rewinding itemize forms stationery base material adhesive tape.
Wherein, the above-mentioned method being coated with benzene emulsion on stationery base material is: adopt anilox roll or wheat tooth rod above-mentioned benzene emulsion to be coated the outside surface of stationery base material, solidification value when being wherein coated with is 80-120 DEG C, and benzene emulsion glue spread is 2-15g/m
2± 10%, surface covered is 15-90 ± 5m/min.
Owing to being coated with water-based or oiliness silicone oil at stationery substrate backside, prevent silicone oil from penetrating into stationery substrate surface, cause the performance of pressure sensitive adhesive to change, therefore coating benzene emulsion forms coating and substantially increases the anti-permeability of stationery base material.
The present invention prepares benzene emulsion owing to adopting vinylbenzene, butyl acrylate etc. for raw material, and is directly coated by formulated benzene emulsion on the outside surface of stationery base material, uses using the isolated protective layer as adhesive tape.Because benzene emulsion is a kind of organic polymer, at high temperature can there is polymerization crosslinking reaction, through drying the resilient coating of formation one deck, (concrete reason is the benzene emulsion of stationery substrate outer surface: butyl acrylate and vinylbenzene at high temperature polymerization reaction take place, forms the sticking coating of tool; Polyvinyl alcohol is auxiliary forms coating, and can reduce the viscosity of coating, thus generation has micro-sticky coating), so for the production of in adhesive tape process, insulation blocking effect can be played.Meanwhile, reduce coating viscosity through auxiliary the formation in coating procedure of polyvinyl alcohol, avoid producing paper and glue rotten problem.
The stationery base material stabilizing quality of benzene emulsion coating prepared by application the present invention, do not occur sticky rotten and there is certain glossiness and pliability.Due in last handling process, add wax emulsion, because wax emulsion has glossiness-giving effect, make the benzene emulsion coating after drying have certain glossiness; Meanwhile, again owing to adding benzoic ether in last handling process, because benzoic ether can soften certain coating hardness, so make the stationery base material of drying rear benzene emulsion coating have certain pliability.
The stationery base material being coated with benzene emulsion of the present invention can also substitute leaching membrane layer effect.Because the stationery base material adhesive tape of general film is because be difficult to keep the skin wet, in bake process, paper is caused easily to be out of shape.And benzene emulsion prepared by the present invention is coated on and forms coating after on stationery base material (surface because of the stationery base material adhesive tape of general film is rete, film material can not moisture in absorbed air), and make paper not easily not yielding in drying course, and be beneficial to environmental protection.
The preparation method of benzene emulsion of the present invention is simple, preparation time short (in 8 hours), thus effectively simplifies its progress and the production cost reducing adhesive tape.
Adhesive tape good stability made by the benzene emulsion utilizing the present invention to prepare, not easily occur paper glue rotten, come unstuck or degradation problem under physicals, adhesive tape qualification rate improves greatly, efficiently solves that existing adhesive tape easily permeates, Product processing operation is many, qualification rate is low and the problem such as production cost is high.
In a word, benzene emulsion preparation technology of the present invention rationally, stable performance, production cost is low, isolation anti-permeability is good, has certain economic benefit, can be widely used in various sealing or stickup field, is particularly useful for being used as stationery base material adhesive tape etc.
Embodiment
Embodiment 1
Be coated on the benzene emulsion on stationery base material, its raw material comprises the blending ingredients of following parts by weight:
Blending ingredients one: allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 12 parts;
Disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 1 part;
Ionized water 260 parts;
Blending ingredients two: vinylbenzene 180 parts;
Butyl acrylate 250 parts;
5 parts, vinylformic acid;
Vinylformic acid-2-hydroxyl ethyl ester 9 parts;
Blending ingredients three: sodium bicarbonate 5 parts;
Deionized water 230 parts;
Blending ingredients four: Potassium Persulphate 5 parts;
Deionized water 18 parts;
Blending ingredients five: Potassium Persulphate 6 parts;
Deionized water 30 parts.
Embodiment 2
Be coated on the benzene emulsion on stationery base material, its raw material comprises the blending ingredients of following parts by weight:
Blending ingredients one: allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 4 parts;
Disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 8 parts;
Ionized water 160 parts;
Blending ingredients two: vinylbenzene 250 parts;
Butyl acrylate 180 parts;
9 parts, vinylformic acid;
Vinylformic acid-2-hydroxyl ethyl ester 5 parts;
Blending ingredients three: sodium bicarbonate 4 parts;
Deionized water 250 parts;
Blending ingredients four: Potassium Persulphate 0.5 part;
Deionized water 8 parts;
Blending ingredients five: Potassium Persulphate 10 parts;
Deionized water 50 parts.
Embodiment 3
Be coated on the benzene emulsion on stationery base material, its raw material comprises the blending ingredients of following parts by weight:
Blending ingredients one: allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 7 parts;
Disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 5 parts;
Ionized water 220 parts;
Blending ingredients two: vinylbenzene 210 parts;
Butyl acrylate 220 parts;
7 parts, vinylformic acid;
Vinylformic acid-2-hydroxyl ethyl ester 7 parts;
Blending ingredients three: sodium bicarbonate 0.5 part;
Deionized water 150 parts;
Blending ingredients four: Potassium Persulphate 3 parts;
Deionized water 10 parts;
Blending ingredients five: Potassium Persulphate 1.5 parts;
Deionized water 20 parts.
Embodiment 4
The feed composition of the benzene emulsion of Application Example 1 is prepared the method for benzene emulsion, and it comprises the following steps:
Step 1: add in emulsifying tank by allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 12 parts, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 1 part, deionized water 260 parts, then reacts 15 minutes under the rapid stirring of 800 revs/min; Then vinylbenzene 180 parts, butyl acrylate 250 parts, 5 parts, vinylformic acid, vinylformic acid-2-hydroxyl ethyl ester 9 parts are slowly joined emulsifying tank, stir 20 minutes, form pre-emulsion;
Step 2: by sodium bicarbonate 5 parts, deionized water 230 parts adds in the reactor of 60 DEG C, then opens stirring, and mixing speed is 30 revs/min;
Step 3: when reactor heat up gradually reach 84-86 DEG C time, add Potassium Persulphate 5 parts, deionized water 18 parts;
Step 4: continue stirring reaction, when temperature of reaction kettle reaches 82-84 DEG C, the reactant while of the pre-emulsion that the mixed solution formed Potassium Persulphate 6 parts, deionized water 30 parts and step 1 obtain in drop reaction still, titration time is 2 hours, titration completes follow-up continuous insulation reaction 4 hours, obtains described benzene emulsion.
Embodiment 5
The feed composition of the benzene emulsion of Application Example 2 is prepared the method for benzene emulsion, and it comprises the following steps:
Step 1: add in emulsifying tank by allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 4 parts, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 8 parts, deionized water 160 parts, then reacts 30 minutes under the rapid stirring of 1600 revs/min; Then vinylbenzene 250 parts, butyl acrylate 180 parts, 9 parts, vinylformic acid, vinylformic acid-2-hydroxyl ethyl ester 5 parts are slowly joined emulsifying tank, stir 10 minutes, form pre-emulsion;
Step 2: by sodium bicarbonate 4 parts, deionized water 250 parts adds in the reactor of 60 DEG C, then opens stirring, and mixing speed is 120 revs/min;
Step 3: when reactor heat up gradually reach 76-80 DEG C time, add Potassium Persulphate 0.5 part, deionized water 8 parts;
Step 4: continue stirring reaction, when temperature of reaction kettle reaches 92-95 DEG C, the reactant while of the pre-emulsion that the mixed solution formed Potassium Persulphate 10 parts, deionized water 50 parts and step 1 obtain in drop reaction still, titration time is 6 hours, titration completes follow-up continuous insulation reaction 1 hour, obtains described benzene emulsion.
Step 5: start to lower the temperature after step 4 is incubated and carry out aftertreatment: (1) when temperature of reaction kettle is down to 80 DEG C, adding the polyvinyl alcohol water solution 25 parts that concentration is 10% in reactor; (2), when temperature of reaction kettle drops to 70 DEG C, in reactor, titration concentration is the tertbutyl peroxide aqueous solution 1.3 parts of 3.5%; (3), when temperature drops to 65 DEG C, in reactor, titration concentration is the sodium bisulphite formaldehyde aqueous solution 1.3 parts of 1.3%; (4) when temperature drops to 60 DEG C, toward reactor simultaneously titration concentration be 70% the succinate sodium 2-ethylhexyl aqueous solution 0.9 part, concentration be 92% the defoamer 8034A aqueous solution 0.2 part; (5), when temperature drops to 55 DEG C, in reactor, titration concentration is the benzoic ether aqueous solution 12 parts of 98% simultaneously, is the sodium polyacrylate salt brine solution 1.0 parts of 45% with titration concentration; (6) when temperature drops to 50 DEG C, adding wax emulsion 12 parts, is the ammoniacal liquor 10 parts of 25% with concentration; (7), when temperature reaches 45 DEG C, after 150 order filter screen filtration impurity, benzene emulsion barrelling will be obtained and preserve.
Embodiment 6
The feed composition of the benzene emulsion of Application Example 3 is prepared the method for benzene emulsion, and it comprises the following steps:
Step 1: add in emulsifying tank by allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 7 parts, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 5 parts, deionized water 220 parts, then reacts 25 minutes under the rapid stirring of 1200 revs/min; Then vinylbenzene 210 parts, butyl acrylate 220 parts, 7 parts, vinylformic acid, vinylformic acid-2-hydroxyl ethyl ester 7 parts are slowly joined emulsifying tank, stir 15 minutes, form pre-emulsion;
Step 2: by sodium bicarbonate 0.5 part, deionized water 150 parts adds in the reactor of 60 DEG C, then opens stirring, and mixing speed is 80 revs/min;
Step 3: when reactor heat up gradually reach 90-92 DEG C time, add Potassium Persulphate 3 parts, deionized water 10 parts;
Step 4: continue stirring reaction, when temperature of reaction kettle reaches 86-88 DEG C, the reactant while of the pre-emulsion that the mixed solution formed Potassium Persulphate 1.5 parts, deionized water 20 parts and step 1 obtain in drop reaction still, titration time is 4 hours, titration completes follow-up continuous insulation reaction 2 hours, obtains described benzene emulsion.
Step 5: start to lower the temperature after step 4 is incubated and carry out aftertreatment: (1) when temperature of reaction kettle is down to 80 DEG C, adding the polyvinyl alcohol water solution 45 parts that concentration is 10% in reactor; (2), when temperature of reaction kettle drops to 70 DEG C, in reactor, titration concentration is the tertbutyl peroxide aqueous solution 0.3 part of 3.5%; (3), when temperature drops to 65 DEG C, in reactor, titration concentration is the sodium bisulphite formaldehyde aqueous solution 0.3 part of 1.3%; (4) when temperature drops to 60 DEG C, toward reactor simultaneously titration concentration be 70% the succinate sodium 2-ethylhexyl aqueous solution 0.2 part, concentration be 92% the defoamer 8034A aqueous solution 1.0 parts; (5), when temperature drops to 55 DEG C, in reactor, titration concentration is the benzoic ether aqueous solution 24 parts of 98% simultaneously, is the sodium polyacrylate salt brine solution 0.2 part of 45% with titration concentration; (6) when temperature drops to 50 DEG C, adding wax emulsion 24 parts, is the ammoniacal liquor 3 parts of 25% with concentration; (7), when temperature reaches 45 DEG C, after 150 order filter screen filtration impurity, benzene emulsion barrelling will be obtained and preserve.
Embodiment 4 is as shown in table 1 to the performance of the benzene emulsion that embodiment 6 prepares.
Index | Outward appearance | Viscosity (mpa.s) | PH value | Solid content | Stability |
Embodiment 4 | Oyster white | 800 | 7 | 50% | Half a year |
Embodiment 5 | Oyster white | 200 | 8 | 45% | Half a year |
Embodiment 6 | Oyster white | 600 | 7 | 47% | Half a year |
Wherein, the testing method of viscosity adopts GB GB/T2794-1995, and the testing method of solid content adopts GB GB/T2793-1995.
As can be seen from Table 1, the benzene emulsion outward appearance adopting preparation method of the present invention to obtain is oyster white, and solid content is 45%-50%, good stability, and viscosity is 200-800mpa.s, and pH value is 7-8.
Being applied as of the benzene emulsion that what the present invention obtained be coated on stationery base material: described benzene emulsion is applied to and is coated on stationery base material, and benzene emulsion glue spread is 2-15g/m
2± 10%, stationery base material is formed the isolated protective layer of waterproof, grease proofing infiltration.
In the present invention, physicals and the production cost of benzene emulsion its proportioning solid content and adhesive tape when being used as isolation impermeable layer and using have certain associating.If benzene emulsion solid content is higher, then inconvenient operation during coating, production cost is high simultaneously, and glue spread is too much, causes paper hardness higher; If when benzene emulsion solid content is lower, then affect the viscosity of benzene emulsion, coating layer is thinner simultaneously, and affect anti-permeability to a certain extent, so generally will be coated with two-layer, such production cost also improves relatively.So adopt proportioning of the present invention, the benzene emulsion solid content of preparation is 45%-50%, and such solid content both can not cause the difficulty of coating, also can not affect the thickness of coating layer simultaneously.
Utilizing the benzene emulsion prepared by proportioning of embodiment 6 when being used as isolation impermeable layer, not only operating simple and easy during coating, and Stability Analysis of Structures, so guarantee constant product quality again on the easy basis of operation, production cost is low.
The concrete number of plies of above-mentioned isolation impermeable layer also can be determined according to the concrete needs that use, and can be one deck; Also can how two layers or even more multi-layered.The above-mentioned pressure-sensitive adhesive glue-line mentioned generally is made up of pressure-sensitive acrylate.
Embodiment 7
The method coated by the benzene emulsion that embodiment 4 prepares on stationery base material is: choose 25-70g/m
2with paper as base material, adopt anilox roll or wheat tooth rod benzene emulsion to be coated the outside surface of stationery base material, solidification value when being wherein coated with is 80 DEG C, and benzene emulsion glue spread is 2g/m
2± 10%, surface covered is 90 ± 5m/min, and stationery base material is formed the isolated protective layer of waterproof, grease proofing infiltration.
Described benzene emulsion coats the process after stationery base material: stationery base material is placed more than 24 hours after coating benzene emulsion.
Embodiment 8
The method coated by the benzene emulsion that embodiment 5 prepares on stationery base material is: choose 25-70g/m
2with paper as base material, adopt anilox roll or wheat tooth rod benzene emulsion to be coated the outside surface of stationery base material, solidification value when being wherein coated with is 120 DEG C, and benzene emulsion glue spread is 15g/m
2± 10%, surface covered is 40 ± 5m/min, and stationery base material is formed the isolated protective layer of waterproof, grease proofing infiltration.
Described benzene emulsion coats the process after stationery base material: stationery base material is placed more than 24 hours after coating benzene emulsion.
Embodiment 9
The method coated by the benzene emulsion that embodiment 5 prepares on stationery base material is: choose 25-70g/m
2with paper as base material, adopt anilox roll or wheat tooth rod benzene emulsion to be coated the outside surface of stationery base material, solidification value when being wherein coated with is 100 DEG C, and benzene emulsion glue spread is 8g/m
2± 10%, surface covered is 60 ± 5m/min, and stationery base material is formed the isolated protective layer of waterproof, grease proofing infiltration.
Process after described benzene emulsion coats stationery base material is: the one side that stationery base material has been coated with benzene emulsion at it immediately after coating benzene emulsion continues painting fabric aqueous or oiliness silicone oil (parrots face to prevent from another side glues after pressure-sensitive acrylate, cause and be difficult to resolve volume), another surface coated pressure-sensitive acrylate adhesive of stationery base material is to form the adhesive-layer of stationery base material internal surface, and the spread of adhesive-layer is 15 grams/m.After drying rolling, namely rewinding itemize forms stationery base material adhesive tape.
Embodiment 10
The method coated by the benzene emulsion that embodiment 6 prepares on stationery base material is: choose 25-70g/m
2with paper as base material, adopt anilox roll or wheat tooth rod benzene emulsion to be coated the outside surface of stationery base material, solidification value when being wherein coated with is 110 DEG C, and benzene emulsion glue spread is 9g/m
2± 10%, surface covered is 55 ± 5m/min, and stationery base material is formed the isolated protective layer of waterproof, grease proofing infiltration.
Described benzene emulsion coats the process after stationery base material: stationery base material is placed more than 24 hours after coating benzene emulsion, then first in the one side that stationery base material is coated with benzene emulsion after printing pattern layer, be coated with fabric aqueous or oiliness silicone oil again (to prevent from stickyly after pressure-sensitive acrylate on another side parroting face, cause and be difficult to resolve volume), then at another surface coated pressure-sensitive acrylate adhesive of stationery base material to form the adhesive-layer of stationery base material internal surface, the spread of adhesive-layer is 60 grams/m, after drying rolling, namely rewinding itemize forms stationery base material adhesive tape.Using the stationery base material adhesive tape obtained as base material with paper in industry referred to as and paper self-adhesive tape, for the application on indoor or outdoors finishing, play cover, provide protection.The stationery base material adhesive tape Performance Detection that this embodiment obtains is as follows:
The stationery base material adhesive tape that embodiment 7 is coated with benzene emulsion prepared by the present invention to embodiment 10 has glossiness, and pliability is good, and can prevent silicone oil from leaking into inner face, paper is not yielding, and qualification rate is high.
Claims (10)
1. be coated on the benzene emulsion on stationery base material, it is characterized in that: its raw material comprises the blending ingredients of following parts by weight:
Blending ingredients one: allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 4-12 part;
Disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 1-8 part;
Ionized water 160-260 part;
Blending ingredients two: vinylbenzene 180-250 part;
Butyl acrylate 180-250 part;
Vinylformic acid 5-9 part;
Vinylformic acid-2-hydroxyl ethyl ester 5-9 part;
Blending ingredients three: sodium bicarbonate 0.5-5 part;
Deionized water 150-250 part;
Blending ingredients four: Potassium Persulphate 0.5-5 part;
Deionized water 8-18 part;
Blending ingredients five: Potassium Persulphate 1.5-10 part;
Deionized water 20-50 part.
2. the preparation method of a kind of benzene emulsion be coated on stationery base material according to claim 1, is characterized in that:
It comprises the following steps:
Step 1: blending ingredients one is added in emulsifying tank, and rapid stirring 15-30 minute; Then the mix monomer of blending ingredients two is slowly joined emulsifying tank, stir 10-20 minute, form pre-emulsion;
Step 2: blending ingredients three is added in the reactor of 60 DEG C, then open stirring;
Step 3: when temperature of reaction kettle heat up gradually reach 76-92 DEG C time, add blending ingredients four;
Step 4: continue stirring reaction, when temperature of reaction kettle reaches 82-95 DEG C, the reactant while of the pre-emulsion that blending ingredients five and step 1 are obtained in drop reaction still, titration time is 2-6 hour, titration completes follow-up continuous insulation reaction 1-4 hour, obtains described benzene emulsion.
3. the preparation method of the benzene emulsion be coated on stationery base material according to claim 2, it is characterized in that: the mixing speed in described step 1 is 800-1600 rev/min, the mixing speed in described step 2 is 30-120 rev/min.
4. the preparation method of a kind of benzene emulsion be coated on stationery base material according to claim 3, is characterized in that:
It comprises the following steps:
Step 1: allyloxy Nonylphenoxy propyl alcohol polyoxyethylene ether ammonium sulfate 4-12 part, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 1-8 part, deionized water 160-260 part are added in emulsifying tank, then reacts 15-30 minute under the rapid stirring of 800-1600 rev/min; Then vinylbenzene 180-250 part, butyl acrylate 180-250 part, vinylformic acid 5-9 part, vinylformic acid-2-hydroxyl ethyl ester 5-9 part are slowly joined emulsifying tank, stir 10-20 minute, form pre-emulsion;
Step 2: by sodium bicarbonate 0.5-5 part, deionized water 150-250 part adds in the reactor of 60 DEG C, then opens stirring, and mixing speed is 30-120 rev/min;
Step 3: when reactor heat up gradually reach 76-92 DEG C time, add Potassium Persulphate 0.5-5 part, deionized water 8-18 part;
Step 4: continue stirring reaction, when temperature of reaction kettle reaches 82-95 DEG C, the reactant while of the pre-emulsion that the mixed solution formed Potassium Persulphate 1.5-10 part, deionized water 20-50 part and step 1 obtain in drop reaction still, titration time is 2-6 hour, titration completes follow-up continuous insulation reaction 1-4 hour, obtains described benzene emulsion.
5. the preparation method of a kind of benzene emulsion be coated on stationery base material according to claim 2 or 4, is characterized in that: it also comprises:
Step 5: start to lower the temperature after step 4 is incubated and carry out aftertreatment: (1) when temperature of reaction kettle is down to 80 DEG C, adding polyvinyl alcohol water solution 25-45 part that concentration is 10% in reactor; (2), when temperature of reaction kettle drops to 70 DEG C, in reactor, titration concentration is tertbutyl peroxide aqueous solution 0.3-1.3 part of 3.5%; (3), when temperature drops to 65 DEG C, in reactor, titration concentration is sodium bisulphite formaldehyde aqueous solution 0.3-1.3 part of 1.3%; (4) when temperature drops to 60 DEG C, toward reactor simultaneously titration concentration be 70% succinate sodium 2-ethylhexyl aqueous solution 0.2-0.9 part, concentration be 92% defoamer aqueous solution 0.2-1.0 part; (5), when temperature drops to 55 DEG C, in reactor, titration concentration is benzoic ether aqueous solution 12-24 part of 98% simultaneously, is sodium polyacrylate salt brine solution 0.2-1.0 part of 45% with titration concentration; (6) when temperature drops to 50 DEG C, adding wax emulsion 12-24 part, is 25% ammoniacal liquor 3-10 part with concentration; (7), when temperature reaches 45 DEG C, after 150 order filter screen filtration impurity, benzene emulsion will be obtained.
6. one kind is coated on the application of the benzene emulsion on stationery base material; it is characterized in that: described benzene emulsion is applied to and is coated on stationery base material; benzene emulsion glue spread is 2-15g/ ㎡ ± 10%, and stationery base material is formed the isolated protective layer of waterproof, grease proofing infiltration.
7. the application of a kind of benzene emulsion be coated on stationery base material according to claim 6, it is characterized in that: the method that described benzene emulsion is coated on stationery base material is: adopt anilox roll or wheat tooth rod benzene emulsion to be coated the outside surface of stationery base material, solidification value when being wherein coated with is 80-120 DEG C, benzene emulsion glue spread is 2-15g/ ㎡ ± 10%, and surface covered is 15-90 ± 5m/min.
8. the application of a kind of benzene emulsion be coated on stationery base material according to claim 7, is characterized in that: described benzene emulsion is coated the process after stationery base material and is: stationery base material is placed more than 24 hours after coating benzene emulsion.
9. the application of a kind of benzene emulsion be coated on stationery base material according to claim 7, it is characterized in that: the process after described benzene emulsion coats stationery base material is: the one side that stationery base material has been coated with benzene emulsion at it immediately after coating benzene emulsion continues to be coated with fabric aqueous or oiliness silicone oil, another surface coated pressure-sensitive acrylate adhesive of stationery base material is to form the adhesive-layer of stationery base material internal surface, after drying rolling, namely rewinding itemize forms stationery base material adhesive tape.
10. the application of a kind of benzene emulsion be coated on stationery base material according to claim 7, it is characterized in that: described benzene emulsion is coated the process after stationery base material and is: stationery base material is after coating benzene emulsion, first in the one side that stationery base material is coated with benzene emulsion after printing pattern layer, be coated with fabric aqueous or oiliness silicone oil again, then at another surface coated pressure-sensitive acrylate adhesive of stationery base material to form the adhesive-layer of stationery base material internal surface, after drying rolling, namely rewinding itemize forms stationery base material adhesive tape.