CN104826911A - Processing method for automobile front door plate - Google Patents

Processing method for automobile front door plate Download PDF

Info

Publication number
CN104826911A
CN104826911A CN201510228643.6A CN201510228643A CN104826911A CN 104826911 A CN104826911 A CN 104826911A CN 201510228643 A CN201510228643 A CN 201510228643A CN 104826911 A CN104826911 A CN 104826911A
Authority
CN
China
Prior art keywords
parts
steel plate
processing method
front door
automobile front
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510228643.6A
Other languages
Chinese (zh)
Inventor
唐满宾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510228643.6A priority Critical patent/CN104826911A/en
Publication of CN104826911A publication Critical patent/CN104826911A/en
Pending legal-status Critical Current

Abstract

The invention discloses a processing method for an automobile front door plate. The processing method for the automobile front door plate comprises the following steps: heating a steel plate, putting the heated steel plate in a metal mould, stamping the steel plate at 670 DEG C, and cooling the stamped steel plate under a closed environment. The steel plate comprises the chemical components in parts by weight: 6 parts of carbon, 106 parts of silicon, 55 parts of manganese, 4 parts of phosphorus, 0.7 part of sulfur, 1.4 parts of thallium, 0.06 part of boron and 1.7 parts of nickel. According to the processing method for the automobile front door plate, the purpose of improving the security strength of an automobile is achieved.

Description

Automotive front door panels processing method
Technical field
The present invention relates to automobile manufacture field, particularly, relate to a kind of automotive front door panels processing method.
Background technology
At present, automobile is in the period of develop rapidly, people are also improving constantly the requirement of automotive safety, although automotive safety relates to the design of Integral automobile structure, but automobile steel still play important effect to safety, existing automobile steel material often adopts hot strength to mark the intensity of steel, but high its yield strength of steel of many hot strengths does not reach safety requirements under strong collision, thus makes many automobile part security intensities inadequate.
Summary of the invention
The object of the invention is to, for the problems referred to above, propose a kind of automotive front door panels processing method, to realize the advantage improving automotive safety intensity.
For achieving the above object, the technical solution used in the present invention is:
A kind of automotive front door panels processing method,
After steel plate is heated, put into metal die, under the hot conditions of 670 DEG C, carry out punching press, then cool under closed environment,
The mass parts of described steel plate chemical composition comprises: carbon: 6 parts, silicon: 106 parts, manganese: 55 parts, phosphorus: 4 parts, sulphur: 0.7 part, thallium; 1.4 parts, boron: 0.06 part, nickel: 1.7 parts.
Technical scheme of the present invention has following beneficial effect:
Technical scheme of the present invention, adds the compositions such as manganese, nickel and thallium in steel plate, thus increases the yield strength of steel plate, reaches the object improving automotive safety intensity.
Detailed description of the invention
A kind of automotive front door panels processing method,
After steel plate is heated, put into metal die, under the hot conditions of 670 DEG C, carry out punching press, then cool under closed environment,
The mass parts of steel plate chemical composition comprises: carbon: 6 parts, silicon: 106 parts, manganese: 55 parts, phosphorus: 4 parts, sulphur: 0.7 part, thallium; 1.4 parts, boron: 0.06 part, nickel: 1.7 parts.
Gallium 0.06 part is also added, chromium 15 parts in steel plate.Other is iron and a small amount of impurity.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.

Claims (1)

1. an automotive front door panels processing method, is characterized in that,
After steel plate is heated, put into metal die, under the hot conditions of 670 DEG C, carry out punching press, then cool under closed environment,
The mass parts of described steel plate chemical composition comprises: carbon: 6 parts, silicon: 106 parts, manganese: 55 parts, phosphorus: 4 parts, sulphur: 0.7 part, thallium; 1.4 parts, boron: 0.06 part, nickel: 1.7 parts.
CN201510228643.6A 2015-05-07 2015-05-07 Processing method for automobile front door plate Pending CN104826911A (en)