CN104817910A - Glass transparent thermal-insulation paint - Google Patents
Glass transparent thermal-insulation paint Download PDFInfo
- Publication number
- CN104817910A CN104817910A CN201510261434.1A CN201510261434A CN104817910A CN 104817910 A CN104817910 A CN 104817910A CN 201510261434 A CN201510261434 A CN 201510261434A CN 104817910 A CN104817910 A CN 104817910A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass transparent
- insulating coating
- transparent insulating
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass transparent thermal-insulation paint which comprises the following components in parts by weight: 20-30 parts of modified acrylic resin, 15-25 parts of nano ATO (antimony tin oxide) slurry, 5-12 parts of nano zinc oxide, 1-5 parts of leveling agent, 2-8 parts of wetting agent, 3-9 parts of dispersing agent, 2-7 parts of defoaming agent and 30-40 parts of solvent. The glass transparent thermal-insulation paint has a barrier action on different radiation wave bands in sunlight, and can barrier most solar radiation heat. The visible light transmissivity is up to 80% above. The glass transparent thermal-insulation paint has the advantages of low influence on lighting, low cost and simple production technique, and is suitable for the field of application and heat insulation of building doors/windows and windshields.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of glass transparent insulating coating.
Background technology
Glass is widely used as building glass window, glass door, glass curtain wall, motor-vehicle glass window etc., and window is the passage of heat turnover, the thermal radiation of sunlight through window-glass to heating indoor; In order to save energy, people take the heat-insulating problem that various measure solves glass.Traditional way is on glass, stick film or the plated film that one deck has infrared external reflection function, and not only cost is high, and limited efficiency.
Transparent heat insulating dope is a kind of novel glass lagging material, its permeability had visible ray, the reflection had near infrared and UV-light, obstruct and sorption.
But there is the problems such as transmittance is low, effect of heat insulation is not good, complex process in transparent heat insulating dope in the market.
Summary of the invention
The object of the invention is to the deficiency overcoming the existence of above-mentioned prior art, the glass transparent insulating coating that a kind of transmittance is high, good heat-insulation effect, cost are low is provided.
For achieving the above object, the present invention is achieved by the following technical solutions:
A kind of glass transparent insulating coating, meter comprises following component by weight: acrylic resin modified 20 ~ 30 parts, nano ATO slurry 15 ~ 25 parts, nano zine oxide 5 ~ 12 parts, flow agent 1 ~ 5 part, wetting agent 2 ~ 8 parts, dispersion agent 3 ~ 9 parts, defoamer 2 ~ 7 parts, solvent 30 ~ 40 parts.
Preferably, described flow agent is any one in polydimethylsiloxane, PSI, polyester resin change properties of organic silicon oxygen alkane.
Preferably, described dispersion agent is any one in Yelkin TTS, trimethyl-glycine, glycerin fatty acid ester.
Preferably, described defoamer is any one in silicone emulsion, higher alcohols, phenylethyl alcohol oleic acid ester.
Preferably, described solvent is any one in butylacetate, Virahol, methyl acetoacetate.
Beneficial effect of the present invention:
Glass transparent insulating coating prepared by the present invention, all has iris action to the different radiation wave band in sunlight, can intercept most of solar radiation heat.And visible transmission ratio reaches more than 80%, little on the impact of daylighting, cost is low, and production technique is simple, is applicable to the heat insulation field of application of building window, windshield.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.Following examples will contribute to those skilled in the art and understand the present invention further, but not limit the present invention in any form.It should be pointed out that to those skilled in the art, without departing from the inventive concept of the premise, some distortion and improvement can also be made.These all belong to protection scope of the present invention.
A kind of glass transparent insulating coating, meter comprises following component by weight: acrylic resin modified 20 ~ 30 parts, nano ATO slurry 15 ~ 25 parts, nano zine oxide 5 ~ 12 parts, flow agent 1 ~ 5 part, wetting agent 2 ~ 8 parts, dispersion agent 3 ~ 9 parts, defoamer 2 ~ 7 parts, solvent 30 ~ 40 parts.
Glass transparent insulating coating prepared by the present invention, has that transmittance is high, good heat-insulation effect, low cost and other advantages.
Embodiment 1
Glass transparent insulating coating of the present invention, by weight meter comprise following component: acrylic resin modified 30 parts, nano ATO slurry 15 parts, nano zine oxide 12 parts, polydimethylsiloxane 1 part, wetting agent 8 parts, 3 parts, Yelkin TTS, silicone emulsion 7 parts, butylacetate 30 parts.
Embodiment 2
Glass transparent insulating coating of the present invention, by weight meter comprise following component: acrylic resin modified 20 parts, nano ATO slurry 25 parts, nano zine oxide 5 parts, PSI 5 parts, wetting agent 2 parts, trimethyl-glycine 9 parts, higher alcohols 2 parts, Virahol 40 parts.
Embodiment 3
Glass transparent insulating coating of the present invention, by weight meter comprise following component: acrylic resin modified 25 parts, nano ATO slurry 20 parts, nano zine oxide 8 parts, 3 parts, polyester resin change properties of organic silicon oxygen alkane, wetting agent 5 parts, glycerin fatty acid ester 6 parts, phenylethyl alcohol oleic acid ester 4 parts, methyl acetoacetate 35 parts.
Embodiment 4
Glass transparent insulating coating of the present invention, by weight meter comprise following component: acrylic resin modified 22 parts, nano ATO slurry 17 parts, nano zine oxide 6 parts, PSI 2 parts, wetting agent 2 ~ 8 parts, 6 parts, Yelkin TTS, higher alcohols 3 parts, Virahol 32 parts.
Embodiment 5
Glass transparent insulating coating of the present invention, by weight meter comprise following component: acrylic resin modified 28 parts, nano ATO slurry 23 parts, nano zine oxide 10 parts, 4 parts, polyester resin change properties of organic silicon oxygen alkane, wetting agent 6 parts, glycerin fatty acid ester 8 parts, phenylethyl alcohol oleic acid ester 6 parts, methyl acetoacetate 38 parts.
Embodiment 6
Glass transparent insulating coating of the present invention, by weight meter comprise following component: acrylic resin modified 20 parts, nano ATO slurry 18 parts, nano zine oxide 8 parts, polydimethylsiloxane 5 parts, wetting agent 2 ~ 8 parts, 4 parts, Yelkin TTS, silicone emulsion 7 parts, butylacetate 36 parts.
Performance test
Basic mechanical design feature of the present invention is as shown in table 1:
Table 1
As seen from Table 1, glass transparent insulating coating prepared by the present invention, has that transmittance is high, good heat-insulation effect, low cost and other advantages.
Above specific embodiments of the invention are described.It is to be appreciated that the present invention is not limited to above-mentioned particular implementation, those skilled in the art can make various distortion or amendment within the scope of the claims, and this does not affect flesh and blood of the present invention.
Claims (5)
1. a glass transparent insulating coating, it is characterized in that, by weight meter comprise following component: acrylic resin modified 20 ~ 30 parts, nano ATO slurry 15 ~ 25 parts, nano zine oxide 5 ~ 12 parts, flow agent 1 ~ 5 part, wetting agent 2 ~ 8 parts, dispersion agent 3 ~ 9 parts, defoamer 2 ~ 7 parts, solvent 30 ~ 40 parts.
2. glass transparent insulating coating according to claim 1, is characterized in that: described flow agent is any one in polydimethylsiloxane, PSI, polyester resin change properties of organic silicon oxygen alkane.
3. glass transparent insulating coating according to claim 1, is characterized in that: described dispersion agent is any one in Yelkin TTS, trimethyl-glycine, glycerin fatty acid ester.
4. glass transparent insulating coating according to claim 1, is characterized in that: described defoamer is any one in silicone emulsion, higher alcohols, phenylethyl alcohol oleic acid ester.
5. glass transparent insulating coating according to claim 1, is characterized in that: described solvent is any one in butylacetate, Virahol, methyl acetoacetate.